DOE OSTI2020
This paper details the very first in-depth study of the glass transition temperature (T g ) for planetary balled milled (PBM) Na 4 P 2 S 7-x O x (NaPSO), where 0 ≤ x ≤ 7, glasses. For 0 ≤ x ≤ 5, fully amorphous, homogeneous, and chemically reacted compositions can be prepared. For samples with 5 < x ≤ 7, partially amorphous but fully chemically reacted glass-ceramics can be produced. The reproducible, thermally cyclable onset T g and the onset crystallization temperature, T c , were investigated as a function of the composition and of the short-range order (SRO) structures of the glasses. Additionally, we examined the extreme sub-T g exothermic relaxations present due to the high energy milling processing and correspondingly high effective quenching rate. Using a differential scanning calorimeter (DSC) and scanning from well below the onset T g , the glasses are observed to relax exothermally below T g . The integrated relaxation enthalpy, ΔH rel , is ~ 0 for the x = 2 glass, but is significantly exothermic for lower and higher values of x. Once the high fictive state of these glasses has been erased by scanning to above the T g , but below the T c of the glass, the DSC scans of the glasses recover normal behavior for a normally cooled glass without any relaxation exotherm. The T g s of these glasses remain relatively constant for 0 ≤ x ≤ 3, but for glasses with 3 < x ≤ 5, T g increases sharply following the combined effects of the phosphate chain length increasing caused by the formation of bridging oxygens and the increasing concentration of more charge dense non-bridging oxygens (NBOs). For x > 5, both T g and Tc decrease sharply, becoming nearly identical at x = 7 where glass formation essentially ceases. For smaller values of x, T c increases with both chain length and the structural complexity of the composition but decreases sharply for glass-ceramics of x > 5.