Oxidation of chemically-vapor-deposited silicon nitride and single-crystal silicon

The present 1000 C and 1300 C oxidation tests on 111-oriented single-crystal Si and dense CVD Si3N4 notes the oxidation rates of the latter in wet O2, dry O2, wet inert gas, and steam atmosphere conditions to be several orders of magnitude lower than the rates for the former in identical atmospheric conditions. Although the parabolic rate constant for Si increased linearly as the water vapor pressure increased, the parabolic rate constant for Si3N4 exhibited a nonlinear dependency on water vapor pressure in the presence of O2. NO and NH3 formation at the reaction interface of Si3N4, and the counterpermeation of these reaction products, are noted to dominate reaction kinetics.

Choi, Doo J.↗

High-Temperature Oxidation Behavior of Iridium-Rhenium Alloys

The life-limiting mechanism for radiation-cooled rockets made from iridium-coated rhenium (Ir/Re) is the diffusion of Re into the Ir layer and the subsequent oxidation of the resulting Ir-Re alloy from the inner surface. In a previous study, a life model for Ir/Re rockets was developed. It incorporated Ir-Re diffusion and oxidation data to predict chamber lifetimes as a function of temperature and oxygen partial pressure. Oxidation testing at 1540 deg C suggested that a 20-wt percent Re concentration at the inner wall surface should be established as the failure criterion. The present study was performed to better define Ir-oxidation behavior as a function of Re concentration and to supplement the data base for the life model. Samples ranging from pure Ir to Ir-40 wt percent Re (Ir-40Re) were tested at 1500 deg C, in two different oxygen environments. There were indications that the oxidation rate of the Ir-Re alloy increased significantly when it went from a single-phase solid solution to a two-phase mixture, as was suggested in previous work. However, because of testing anomalies in this study, there were not enough dependable oxidation data to definitively raise the Ir/Re rocket failure criterion from 20-wt percent Re to a Re concentration corresponding to entry into the two-phase region.

Reed, Brian D.↗

PYROLYTIC GRAPHITE ROCKET THRUST CHAMBER INVESTIGATION PROJECT. MONTHLY LETTER

This is the Monthly Letter Progress Report for the eighth month of a twelve month technical study directed toward the following objectives: A. Determining analytically and experimentally the feasibility and attractiveness of using free-standing pyrolytic graphite for a radiation cooled liquid rocket thrust chamber and exit nozzle for space application. B. Establishing through analysis and experimental demonstration, a set of design principles to facilitate the design of a reliable pyrolytic graphite thrust chamber assembly for a specific range of operating conditions. C. Demonstrate by means of test firings of complete thrust chamber assemblies, the validity of the design data and principles developed during the program. Preparations have been completed for test firing the two 100 lb. thrust Boron Pyralloy chambers at Marquardt during the first week in March 1962. These two chambers will first be static pressure checked with water to a pressure of 135 psig. The chambers will then be test fired with N204/N2H4-MMH propellants . Test samples of eleven different pyrolytic carbide and nitride materials have been ordered for high temperature oxidation tests and should be delivered by the end of March for evaluation in the plasma torch facility. The specific materials ordered in free- standing condition in thicknesses from 0.030 inch to 0.065 inch were as follows: (a) Pyrolytic graphite (on hand) (b) Pyrolytic graphite-boron alloy (on hand) (c) Pyrolytic graphite-tungsten alloy (d)Boron nitride (e) Titanium nitride (f) Silicon carbide (g) Titanium carbide (h) Zirconium carbide (i) Hafnium carbide (j) Niobium carbide (k) Tantalum carbide (l) High density (1 1-90) graphite (m) High density graphite (heat treated) These materials were ordered from Raytheon, HTM, and American Meta 1 Products . A summary of the available data on the oxidation rates of pyrolytic materials under slow air and rocket motor conditions is shown in Figure 1. High Temperature Materials, Inc. has been contacted relative to providing Pyrographite thrust chambers with extra-thick walls . They believe they can deliver chambers with substantially thicker walls than were possible a short time ago. Such a configuration, with acceptable residual stresses, would provide a longer firing life since it is ultimately limited by the oxidation rate of the chamber wall material. Stress and structural studies have continued. The analytical stress studies point out some of the problems associated with the experimental determination of the elastic constants of this highly anisotropic material. Further analysis may shed light on improved techniques for making these experimental determinations. The large potential weight saving available with the use of pyrolytic graphite as a thrust chamber wall material in a radiation cooled rocket motor has been calculated and is shown graphically in Figure 2. Figure A presents the program progress schedule and the actual expenditures as of 7 February 1962.

ROCKET ENGINE↗

Oxidation of boron nitride in an arc heated jet.

Two grades of hot pressed boron nitride and a boron nitride composite were subjected to oxidation tests in a 2.5 megawatt atmospheric arc jet. The results showed that fabrication and/or composition influenced thermal shock and oxidation resistance. Changes in surface structure and recession due to oxidation suggest correlation with specimen composition. The boron nitride composite reacted with the oxygen in the hot subsonic airstream to produce a glassy coating on the hot face surface.

Buckley, J. D.↗

Long-term high-velocity oxidation and hot corrosion testing of several NiCrAl and FeCrAl base oxide dispersion strengthened alloys

Several oxide dispersion strengthened (ODS) alloys have been tested for cyclic, long-term, high gas-velocity resistance to oxidation at 1100 C and hot corrosion at 900 C. Both nominally Ni-16Cr-4Al and Fe-20Cr-4.5Al ODS alloys were subjected up to about 2500 cycles, where each cycle consisted of 1 hr in a hot, Mach 0.3 combusted gas stream followed by a 3-min quench in an ambient temperature, Mach 0.3 air blast. For comparison to existing technology, a coated superalloy was simultaneously tested. The ODS iron alloy exhibited clearly superior behavior, surviving 3800 oxidation and 2300 hot corrosion cycles essentially unscathed. While the ODS nickel alloys exhibited adequate oxidation resistance, the long-term hot corrosion resistance could be marginal, since the best life for such alloys under these conditions was only about 1100 cycles. However, the hot corrosion resistance of the ODS Ni-base alloys is excellent in comparison to that of traditional superalloys.

Lowell, C. E.↗

Stressed Oxidation of C/SiC Composites

Constant load, stressed oxidation testing was performed on T-300 C/SiC composites with a SiC seal coat. Test conditions included temperatures ranging from 350 C to 1500 C at stresses of 69 MPa and 172 MPa (10 and 25 ksi). The coupon subjected to stressed oxidation at 550 C/69 MPa for 25 hours had a room temperature residual strength one-half that of the as-received coupons. The coupon tested at the higher stress and all coupons tested at higher temperatures failed in less than 25 hr. Microstructural analysis of the fracture surfaces, using SEM (scanning electron microscopy), revealed the formation of reduced cross-sectional fibers with pointed tips. Analysis of composite cross-sections show pathways for oxygen ingress. The discussion will focus on fiber/matrix interphase oxidation and debonding as well as the formation and implications of the fiber tip morphology.

Halbig, Michael C.↗

High-velocity-oxidation performance of metal-chromium-aluminum (MCrAl), cermet, and modified aluminide coatings on IN-100 and type VIA alloys at 1093 C

Cermet, MCrAl, and modified aluminide types of coatings applied to IN-100 and NASA-TRW-VIA alloy specimens were cyclically oxidation tested in a high velocity (Mach 1) gas flame at 1093 C. Several coating compositions of each type were evaluated for oxidation resistance. The modified aluminide coating, Pt-Al, applied to alloy 6A proved to be the best, providing oxidation protection to approximately 750 hours based on weight change measurements. The second best, a CoCrAlY coating applied to 6A, provided protection to 450 hours. The third best was a cermet + aluminide coating on 6A with a protection time to 385 hours.

Deadmore, D. L.↗

Oxidation and Emittance Studies of Coated Mo-Re

A commercially available Fe-Cr-Si coating (R512E) and a silicide coating were evaluated regarding their ability to protect Mo-Re from oxidation. The R512E coating provided very good oxidation protection at 1260 C in atmospheric air. Oxidation tests were also performed at Mach 4 in the HYMETS facility at NASA Langley Research Center where again the R512E provided good oxidation protection but for much shorter times. Emittance measurements as a function of wavelength were also obtained for the R512E coating on Mo-Re after exposure to the Mach 4 environment at 1150 C and 1230 C.

Glass, David E.↗

Alloyed coatings for dispersion strengthened alloys

Processing techniques were developed for applying several diffusion barriers to TD-Ni and TD-NiCr. Barrier coated specimens of both substrates were clad with Ni-Cr-Al and Fe-Cr-Al alloys and diffusion annealed in argon. Measurement of the aluminum distribution after annealing showed that, of the readily applicable diffusion barriers, a slurry applied tungsten barrier most effectively inhibited the diffusion of aluminum from the Ni-Cr-Al clad into the TD-alloy substrates. No barrier effectively limited interdiffusion of the Fe-Cr-Al clad with the substrates. A duplex process was then developed for applying Ni-Cr-Al coating compositions to the tungsten barrier coated substrates. A Ni-(16 to 32)Cr-3Si modifier was applied by slurry spraying and firing in vacuum, and was then aluminized by a fusion slurry process. Cyclic oxidation tests at 2300 F resulted in early coating failure due to inadequate edge coverage and areas of coating porosity. EMP analysis showed that oxidation had consumed 70 to 80 percent of the aluminum in the coating in less than 50 hours.

Wermuth, F. R.↗

Optimization of an oxide dispersion strengthened Ni-Cr-Al alloy for gas turbine engine vanes

The investigation was carried out to determine the optimum alloy within the Ni-16Cr-Al-Y2O3 system for use as a vane material in advanced aircraft gas turbine engines. Six alloys containing nominally 4%, 5% and 6% Al with Y2O3 levels of 0.8% and 1.2% were prepared by mechanical attrition. Six small-scale, rectangular extrusions were produced from each powder lot for property evaluation. The approximate temperatures for incipient melting were found to be 1658 K (2525 F), 1644 K (2500 F) and 1630 K (2475 F) for the 4%, 5% and 6% aluminum levels, respectively. With the exception of longitudinal crystallographic texture, the eight extrusions selected for extensive evaluation either exceeded or were close to mechanical property goals. Major differences between the alloys became apparent during dynamic oxidation testing, and in particular during the 1366 K (2000 F)/500 hour Mach 1 tests carried out by NASA-Lewis. An aluminum level of 4.75% was subsequently judged to be optimum based on considerations of dynamic oxidation resistance, susceptibility to thermal fatigue cracking and melting point.

Klarstrom, D. L.↗

Effect of 0.1 at. pct Zirconium on the cyclic oxidation resistance of beta-NiAl

The effect of 0.1 at. pct Zr on the cyclic oxidation of hipped beta-NiAl was studied. Oxidation testing was performed in static air at 1100-1200 C, using 1-hr exposure cycles for test times up to 3000 hr. The weight change versus time data were modeled with the COSP computer program to analyze and predict cyclic-oxidation behavior. Zr additions significantly change the nature of the scale-spalling process during cooling, so that the oxide spalls near the oxide-air interface at a relatively low depth within the scale. Without Zr, the predominantly alpha-Al2O3 scale tends to spall randomly to bare metal at relatively high effective-scale-loss rates, particularly at 1150 C and 1200 C. This leads to higher rates of Al consumption for the Zr-free aluminide and much earlier depletion of Al, leading to eventual breakaway (i.e., failure).

Barrett, Charles A.↗

Development of Protective Coatings for Chromium-Base Alloys

Chromium alloy sheet was clad with 5 to 10-mil-thick oxidation-resistant nickel-base alloy foils. Specimens also contained 1/2 to 1-mil-thick intermediate layers of platinum, tungsten, and/or W-25Re. Cladding was done by the isostatic hot gas-pressure bonding,.process. The clad chromium-alloy specimens were cyclic oxidation tested at 2100 F and 2300 F for up to 200 hours to determine the effectiveness of these metal claddings in protecting the chromium alloy Cr-5W from oxidation and contamination. Cladding systems consisting of 5-mil-thick Ni-20Cr-20W modified with 3 to 5 weight percent aluminum and containing a 1 /2-mil tungsten diffusion barrier demonstrated potential for long-time service at temperatures as high as 2300 F.

English, J. J.↗

The effect of 0.1 atomic percent zirconium on the cyclic oxidation behavior of beta-NiAl for 300 hours at 1200 C

The long time effect of 0.1 at percent Zr (0.2 wt percent Zr) on the cyclic oxidation behavior of hipped beta-NiAl was studied. Oxidation testing was performed in static air at 1200 C for up to 3000 one-hour exposure cycles. Specific weight change versus time data was modeled with the COSP computer program to analyze cyclic oxidation behavior. The Zr-free stoichiometric alloy oxidized and spalled randomly to bare metal between cycles at a rate high enough to deplete Al to a low enough level that oxidation breakaway took place as nonprotective NiO replaced the alpha-Al2O3/NiAl2O4 scale as the controlling oxide. The Zr minimized this severe type of spalling maintaining the protective alpha-Al2O3 scale even out to 3000 hours for the stoichiometric alloy with no significant Al depletion. A third beta-NiAl alloy containing 0.1 at percent Zr but with 10 percent less Al than the stoichiometric alloy was also tested and showed some depletion of Al, but the protective Al2O3/NiAl2O4 was still maintained to close to 2700 hours.

Barrett, C. A.↗

The effect of 0.1 atomic percent zirconium on the cyclic oxidation behavior of beta-NiAl for 3000 hours at 1200 C

The long time effect of 0.1 at percent Zr (0.2 wt percent Zr) on the cyclic oxidation behavior of hipped beta-NiAl was studied. Oxidation testing was performed in static air at 1200 C for up to 3000 one-hour exposure cycles. Specific weight change versus time data was modeled with the COSP computer program to analyze cyclic oxidation behavior. The Zr-free stoichiometric alloy oxidized and spalled randomly to bare metal between cycles at a rate high enough to deplete Al to a low enough level that oxidation breakaway took place as nonprotective NiO replaced the alpha-Al203/NiAl204 scale as the controlling oxide. The Zr minimized this severe type of spalling maintaining the protective alpha-Al203 scale even out to 3000 hours for the stoichiometric alloy with no significant Al depletion. A third beta-NiAl alloy containing 0.1 at percent Zr but with 10 percent less Al than the stoichiometric alloy was also tested and showed some depletion of Al, but the protective Al203/NiAl204 was still maintained to close to 2700 hours.

Barrett, C. A.↗