Results for “Microstructural Refinement” — Page 3

NASA NTRS1994

Magnetic properties and magnetic hardening mechansim of Pt-Co-B alloys

The intrinsic coercivity is found to be maximized in the Pt42Co45B13 ternary alloy which is undercooled and rapidly solidified (quenched using a 70 m/s wheel speed after undercooling), and then annealed (800 C for 2400 min). The same alloy, processed at slower cooling rates and annealed in the same way, has a much larger scale microstructure and a much lower resulting magnetic coercivity. The microstructure which would optimize the coercitvity of this coercivity of this ternary alloy is a completely ordered L1(sub zero) Pt-Co matrix with a submicron magnetic single-domion Co-boride precipitate. The L1(sub zero) phase is highly anistropic magnetically while the Co-boride precipate is somewhat less so. Annealing treatments designed to produced single-domain Co-boride precipitates enhance the coercivity. This suggests that the refined microstructures is responsible for the high coercivities found in the rapidly solidified and annealed alloy. The magnetic domain wall thickness for a Co-boride precipitate is determined from both experimental observation and theoretical calculation in order to evaluate its influence on the coercivity of the alloy. The effects of the pinning of domain walls and the barrier to the nucleation of reverse domains on the coercivity are discussed. Both microstrucutral analysis and theoretical calculation indicate that the high coercivities in the Pt42Co45B13 alloy are due to the difficult nucleation of reverse magnetic domains.

Qiu, Ning↗

DOE OSTI2026

Beyond the eutectic paradigm: nanolamellar patterns in a rapidly solidified peritectic alloy

Peritectic transformations are central to many structural alloys, yet pattern formation remains poorly understood due to complex growth dynamics and limited three-dimensional data. Here, we report an unusual two-phase microstructure in a Zn–Ag peritectic alloy subjected to rapid solidification by laser surface remelting. Synchrotron X-ray nanotomography reveals a lamellar structure of primary 𝜀-AgZn 3 and peritectic Zn with ∼700 nm spacing. Although resembling a eutectic morphology, this pattern forms without a eutectic reaction through non-steady coupled growth from the liquid. SEM and TEM-EDS confirm interface shapes and phase compositions. These findings expand the design space of peritectics for refined microstructural control.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Strong yet ductile nanolamellar high-entropy alloys by additive manufacturing

Additive manufacturing produces net-shaped components layer by layer for engineering applications. The additive manufacture of metal alloys by laser powder bed fusion (L-PBF) involves large temperature gradients and rapid cooling, which enables microstructural refinement at the nanoscale to achieve high strength. However, high-strength nanostructured alloys produced by laser additive manufacturing often have limited ductility. In this work, we use L-PBF to print dual-phase nanolamellar high-entropy alloys (HEAs) of AlCoCrFeNi 2.1 that exhibit a combination of a high yield strength of about 1.3 gigapascals and a large uniform elongation of about 14 percent, which surpasses those of other state-of-the-art additively manufactured metal alloys. The high yield strength stems from the strong strengthening effects of the dual-phase structures that consist of alternating face-centred cubic and body-centred cubic nanolamellae; the body-centred cubic nanolamellae exhibit higher strengths and higher hardening rates than the face-centred cubic nanolamellae. The large tensile ductility arises owing to the high work-hardening capability of the as-printed hierarchical microstructures in the form of dual-phase nanolamellae embedded in microscale eutectic colonies, which have nearly random orientations to promote isotropic mechanical properties. The mechanistic insights into the deformation behaviour of additively manufactured HEAs have broad implications for the development of hierarchical, dual- and multi-phase, nanostructured alloys with exceptional mechanical properties.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Evolution of carbide precipitates in Haynes® 282 superalloy processed by wire arc additive manufacturing

Precipitation hardening regulated with heat treatments is a critical technique for tuning the mechanical properties of Ni-based superalloys fabricated with additive manufacturing, where mechanical deformation is no longer viable for microstructural refinement. As one of the key precipitates, carbides prevail in the additively manufactured alloys, whose precipitation kinetics remain largely vague. This work studies the influence of heat treatments on the evolution of MC- and M 23 C 6 -type carbides within a Haynes® 282 superalloy prepared by wire arc additive manufacturing (WAAM). SEM-EDS analysis was performed to identify the evolution pathways of the carbides, and TEM and XRD characterizations were carried out to track the crystallographic features. The MC-type carbides are originally present in the as-printed alloy, which distribute uniformly across the whole material and remain largely unchanged in size during the heat treatments. By contrast, the incipiently non-existent M 23 C 6 -type carbides precipitate during an aging treatment at 1010 °C, which majorly extend along the grain boundaries as kinetically feasible sites. Further experimental and computational analysis confirms the enhancing effect of the M 23 C 6 -type carbides on the Vickers hardness. For the first time, this work revealed the evolution pathways of carbides within a Haynes® 282 superalloy prepared by WAAM, providing critical information for tunning the microstructure and mechanical properties. Finally, the carbide evolution kinetics established in this work can be potentially extended to other alloys prepared with WAAM, providing critical information to prevent mechanical failures associated with carbide coarsening.

36 MATERIALS SCIENCE↗

DOE OSTI2025

Laser Powder Directed Energy Deposition of Steels for Nuclear Applications

This comprehensive investigation examines the structure–property relationships in two nuclear alloy systems—Alloy 709 (A709) austenitic stainless steel and Grade 92 (G-92) ferritic/martensitic (F/M) steel—manufactured via directed energy deposition (DED) for sodium-cooled fast reactor applications. This study establishes the fundamental mechanisms for controlling microstructures for optimizing the mechanical performance of additively manufactured nuclear materials through systematic heat treatment optimization and multiscale characterization. As-deposited A709 steel develops a complex multiscale strengthening architecture consisting of a fine cellular solidification structure with diameter of 2-3 µm within10–50 µm grains, elevated dislocation densities from rapid thermal cycling, and grain boundary precipitates that activate concurrent Hall–Petch, dislocation, and precipitation hardening mechanisms to achieve exceptional properties [yield strength (YS): 603 MPa, ultimate tensile strength (UTS): 844 MPa, Vickers hardness: 220 HV] that achieve a 44% superior strength compared to that of the wrought material. Heat treatments produce different results. Solution annealing (SA) dissolves the cellular structure and reduces the hardness to 190 HV. Precipitation treatment (PT) keeps the cellular structure but adds carbides, allowing the hardness to reach 205 HV. The best approach combines both treatments (SA+PT) and creates uniform precipitate distributions with M 23 C 6 carbides at the grain boundaries and MX carbonitrides in the matrix, achieving a hardness of 195 HV. However, directional differences persist, with a 12%–15% strength variation between orientations due to the inherited layered microstructural architecture that survives aggressive heat treatment. While tensile testing at 550°C demonstrates 40%–50% thermal softening with dynamic strain aging, DED A709 steel still maintains a 71% higher YS than that of the wrought material. Ion irradiation studies (100–400 dpa) of DED A709 steel reveal progressive radiation damage with increasing void density and radiation-induced segregation causing nickel enrichment and chromium depletion, which will ultimately compromise mechanical properties. As-deposited G-92 exhibits exceptional strength (UTS: 1650–1700 MPa, 430 HV) through a complex microstructure containing both ferrite and martensite phases, a high geometrically necessary dislocation (GND) density (17.04×10 14 /m 2 ), and fine carbides. Heat treatments create distinct changes. Normalizing produces fresh martensite with the highest hardness (460 HV) and an increased GND density (20.23×10 14 /m 2 ). Tempering develops dual precipitation systems and reduces the hardness to 290 HV. The optimal approach uses sequential normalizing plus tempering, achieving balanced properties with the lowest hardness (250 HV) and a reduced GND density (11.01×10 14 /m 2 ). A processing-dependent anisotropy is observed: horizontal specimens achieve superior ductile behavior, while vertical specimens exhibit brittle failure. A tempering heat treatment successfully mitigates this anisotropic behavior by transforming the hard martensitic as-deposited structure into tempered martensite enabling both horizontal and vertical specimens to exhibit similar stress–strain characteristics with visible necking behavior. Remarkably, testing at 550°C reveals a reversal in the anisotropy, where as-deposited specimens achieve near isotropy with superior thermal stability (a 15%–20% strength reduction), while tempered specimens develop an orientation dependence with a 25%–30% strength reduction. Both alloy systems demonstrate that DED processing creates specimens with a superior strength through refined microstructural features, though with distinct strengthening mechanisms—austenitic through cellular structures and precipitates versus F/M through phase transformations and precipitates. Heat treatment optimization requires alloy-specific approaches, with A709 benefiting from controlled precipitation while G-92 requires careful phase transformation control. The results show that DED manufacturing can produce nuclear materials with exceptional performance, but directional effects and temperature-dependent behavior must be carefully considered for reactor component design and qualification.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2022

Phase evolution of U-Zr system in a thermal cycling neutron diffraction experiment: as-cast U-35Zr and U-50Zr

Here, phase evolution of as-cast U-35 wt% Zr and U-50 wt% Zr alloys during thermal cycling (303–1073 K) was investigated using in-situ neutron diffraction. Analysis was performed using Rietveld crystal and microstructure refinements from time-of-flight neutron diffraction data, with a focus on evolution of lattice parameter, atom ordering, unit cell volume, and weight fractions during the thermal cycling. Disordered δ-UZr 2 and residual γ-(U,Zr) phase are retained in the field of δ of the U-Zr equilibrium phase diagram for the U-50Zr sample, and in the field between δ and α-U for the U-35Zr sample. The α phase that is present in the reported phase diagrams of U-Zr was not observed in the diffraction patterns. The evolutions of lattice parameter and unit cell volume of δ and γ are affected by both thermal expansion and chemistry.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2025

Friction surface layer deposition of triple-phase Al 10 Cr 12 Fe 35 Mn 23 Ni 20 high entropy alloy: Process optimization and microstructural evolution

A high-strength Co-free triple-phase Al 10 Cr 12 Fe 35 Mn 23 Ni 20 high-entropy alloy (HEA) was successfully fabricated using Friction Surface Layer Deposition (FSLD), a bulk manufacturing method. Multiple single-layer deposits were produced by varying forging force (F) and traverse speeds (T r ) to optimize the process parameters. The optimized conditions (F = 40 kN & T r = 200 mm/min) were then applied to manufacture a scaled-up multi-layer specimen. The initial microstructure of the HEA consisted of coarse grains of the soft FCC-phase, long columnar dendrites of the hard BCC-phase, and small precipitates of the harder B2-phase within the BCC-dendrites. During FSLD, the FCC-matrix underwent continuous dynamic recrystallization due to high-temperature severe plastic deformation, forming finer equiaxed grains. Simultaneously, the BCC-dendrites fractured into smaller fragments, some of which experienced partial growth and coarsening under applied stress, resulting in an hourglass morphology. In contrast, the small B2-precipitates within the BCC-fragments dissolved during the elevated temperatures of FSLD and reprecipitated as substantially finer precipitates during continuous cooling post-FSLD. Additionally, the orientation relationships between the FCC and BCC/B2 phases were completely destroyed by the severe thermoplastic deformation inherent to FSLD. The microstructural refinements led to a substantial improvement in hardness from 177 HV to 283 HV, driven by Hall-Petch strengthening. The increased number of interfaces, including coherent BCC-B2 interfaces, potentially enhances the sink strength and radiation tolerance of the HEA, making it a promising candidate for nuclear applications. In conclusion, this study also highlights FSLD as a versatile technique for achieving tunable properties in HEAs, with detailed schematics illustrating the complex mechanisms of phase transformations during processing.

Additive Manufacturing↗

DOE OSTI2025

Design of Silicide-Strengthened Nb–Si–Cr–(Mo) alloys for additive manufacturing

Three high–intermetallic volume Nb–Si–Cr–(Mo) alloys were designed using CALPHAD modeling with the goal of identifying high–specific strength, oxidation-resistant alloys that can be additively manufactured using powder bed fusion. The silicides Nb 5 Si 3 and Nb 9 Si 2 Cr3 were targeted as the primary strengthening phases, and the addition of Cr promoted the NbCr 2 phase. These alloys were cast and surface-processed with electron beam welding at different speeds to simulate additive manufacturing, and the phases and microstructures of both cast and welded regions were characterized. The weld processing was found to produce fine-grained microstructures in each alloy with fine-scale intermetallics uniformly distributed among a body-centered cubic Nb matrix. Microstructural refinement and hardness were found to increase with weld velocity; one alloy reached its highest hardness of approximately 16 GPa before the brittleness at higher velocities became detrimental. One alloy was found to be qualitatively the least brittle while also attaining a hardness of 13 GPa and was therefore identified as a good candidate for additive manufacturing.

36 MATERIALS SCIENCE↗

DOE OSTI2025

Boron Nitride-Driven Strengthening of Aluminum Composites via Friction Stir Processing

Friction stir welding and processing (FSW/P) has emerged as an effective solid-state joining technique for fabricating metal matrix composites (MMCs), offering improved mechanical properties through refined microstructural evolution. In this study, an aluminum-boron nitride nanoparticle (Al-BNNP) composite was synthesized via FSW, and its indentation-based mechanical properties were systematically evaluated. Microhardness mapping across the weld cross-section revealed a progressive increase in hardness toward the stir zone (SZ), attributed to severe plastic deformation, dynamic recrystallization (DRX), and the reinforcing effect of BNNPs. Profilometry-based indentation plastometry (PIP) inferred yield strength (YS) demonstrates a 47.8% increase compared to the base metal (BM) and a 75% improvement compared to FSP pure aluminum reported in literature. This enhancement is attributed to strengthening mechanisms, including grain boundary pinning, load transfer, and increased dislocation density. The strain rate sensitivity (SRS) measurements at the nanoscale demonstrated a substantial decrease in the SZ, correlated with ultrafine grain structures and strong BNNP-matrix interactions. Activation volume analysis revealed a significant reduction in the SZ, suggesting that dislocation motion is increasingly restricted by dislocation-dislocation and dislocation-particle interactions. These findings suggest that incorporating BNNPs in FSW/P enables tailoring the microstructure without thermal degradation of the secondary particles, thereby significantly enhancing the mechanical performance of aluminum composites, particularly for structural applications in aerospace and automotive industries.

Aluminum↗

DOE OSTI2025

Ultrafast Oxygen Conduction in Sillén Oxychlorides

Oxygen ion conductors are crucial for enhancing the efficiency of various clean energy technologies, including fuel cells, solid oxide air batteries, electrolyzers, membranes, sensors, and more. In this study, a structure-similarity analysis of ≈62k oxygen-containing compounds identified the MBi 2 O 4 X (M = rare-earth element, X = halogen element) family as promising candidates for fast oxygen transport. Among these, LaBi 2 O 4 Cl is found as an ultrafast oxygen conductor with an ultralow migration barrier of 0.1 eV based on ab initio studies. Its 2D layered structure, featuring a “triple fluorite” layer, supports diffusion of both oxygen vacancies and interstitials. In addition to vacancy diffusion with a 0.1 eV barrier, ab initio studies show interstitial diffusion exhibits a modest barrier of 0.6–0.8 eV. Frenkel pairs are found to be the dominant defects in intrinsic LaBi 2 O 4 Cl, facilitating significant vacancy-mediated oxygen diffusion at elevated temperatures. With 2.8% oxygen vacancies, LaBi 2 O 4 Cl is predicted to achieve a conductivity of 0.3 S/cm at 25 °C in a single crystal. Experimental synthesis and characterization of polycrystalline LaBi 2 O 4 Cl and Sr-doped LaBi 2 O 4 Cl revealed conductivity exceeding that of YSZ and LSGM below 400 °C, with lower activation energies, achieving a total conductivity of 0.1−0.2 mS/cm at 300 °C. Here, while these results confirm its potential of fast oxygen transport, we suggest further experimental optimization of LaBi 2 O 4 Cl, including aliovalent doping and microstructure refinement, could significantly enhance its performance, facilitating fast oxygen conduction approaching room temperature.

Defects↗

DOE OSTI2026

Role of Si substitution in modulating the coercivity and magnetic anisotropy in Fe3CoB2 nanocrystallites

In this work, we report the impact of Si substitution on the structural and magnetic properties of Fe3CoB2 nanocrystallites as a rare-earth-free hard-magnet candidate. X-ray diffraction confirmed the formation of the tetragonal phase with an average crystallite size of ∼40 nm, while the transmission electron microscopy image revealed nanosized crystallites embedded in an amorphous matrix. Room-temperature Mössbauer spectra exhibited two sextets and two doublets, indicating magnetically ordered Fe sites in the tetragonal phase along with high-spin paramagnetic FeIII species in disordered regions. ZFC–FC magnetization curves displayed field-dependent blocking behavior, consistent with paramagnetic Fe species. Singular point detection measurements revealed a high anisotropy field of ∼10.7 kOe in the pristine Fe3CoB2, and systematically decreased with Si substitution. Magnetization measurements revealed a monotonic decrease in saturation magnetization with Si content, while coercivity was observed to increase, likely due to microstructural refinement. These results establish Fe3CoB2 as a rare-earth-free material with strong magnetic anisotropy, ideal for hard magnets.

Abbas, Hur [Department of Physics, University of T↗

DOE OSTI2025

Improving high temperature resilience of fiber sensor embedded smart components through laser shock peening

This study explores the use of laser shock peening (LSP) to enhance material properties and high-temperature performance of fiber-sensor-fused smart parts fabricated by additive manufacturing (AM) methods. Using embedded fiber sensors as distributed strain gauges, the study demonstrates that LSP can induce compressive strains of up to 130 µε on fiber embedded 1-mm below metal surfaces. The electron backscatter diffraction (EBSD) analysis shows that, with optimized LSP parameters, the metallic matrix undergoes substantial microstructural refinement, resulting in denser structures. Thermal cycling tests showed that the LSP process can increase fiber slippage temperatures by more than 50 °C. This work shows that the LSP process is an effective room-temperature process for enhancing both surface quality and increasing fiber slippage threshold under both thermal and mechanical stress.

Zhong, Shuda [University of Pittsburgh, PA (United↗

DOE OSTI2024

High Strength Aluminum Additive Manufacturing

High-strength aluminum alloys for elevated temperature applications are desirable to replace heavier and more expensive titanium alloys. However, most aluminum alloys lose a large fraction of their strength at temperatures above approximately 200°C. ORNL has designed DuAlumin-3D, an alloy with nominal composition Al-9Ce-4Ni-0.5Mn-1Zr (wt.%), which utilizes the high cooling rates in additive manufacturing (AM) to achieve a refined microstructure, and thermally stable mechanical properties. DuAlumin-3D was fabricated by laser powder bed fusion and tested for its tensile mechanical properties across a range of temperature, and for its room temperature high-cycle fatigue resistance. The alloy was tested in both the as-printed and heat treated conditions, and both parallel and perpendicular to the AM build direction. The alloy was found to have anisotropic mechanical behavior in the as-printed state, but the anisotropy significantly decreased (both for tensile and fatigue properties) following heat treatment. The tensile properties significantly out-performed benchmark wrought 2219-T61 across a wide temperature range. The room temperature fatigue performance was approximately similar to 2219-T61.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Materials Characterization, Prediction, and Control Project: Summary Report on Material Characterization, Part 1

The Pacific Northwest National Laboratory (PNNL) undertook the Materials Characterization, Prediction, and Control (MCPC) Laboratory Directed Research and Development Project to advance understanding of nuclear material processing and enable multifold acceleration in the development and qualification of new material systems in national security and advanced energy applications (Smith 2021). The MCPC Project executed research across three scientific vertices—material characterization, predictive modeling, and data analytics—with extensive support by a data curation and management team. The central technical objective in the MCPC Project was to improve the prediction and characterization of the process-structure-property relationships within the microstructurally refined region of stainless-steel samples prepared utilizing friction stir processing (FSP). Application of the FSP technique is well established at PNNL within the Solid Phase Processing capability through many years of investment across a range of materials and applications (PNNL 2024). Three distinct rounds of FSP experiments were performed by the experimental team, producing replicate samples utilizing across different nominal processing conditions (Condition IDs) listed in Table 1. The starting material on which FSP was applied was commercially available unprocessed stainless-steel type 316L material. Chosen processing conditions were very diverse, and some were intentionally chosen to produce defects. Several samples experienced tool breakage during experimentation, so a full set of three replicates was not produced for every nominal processing condition.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Materials Characterization, Prediction, and Control Project: Summary Report on Material Characterization, Part 2

The Pacific Northwest National Laboratory (PNNL) undertook the Materials Characterization, Prediction, and Control (MCPC) Laboratory Directed Research and Development Project to advance understanding of nuclear material processing and enable multifold acceleration in the development and qualification of new material systems in national security and advanced energy applications (Smith 2021). The MCPC Project executed research across three scientific vertices—material characterization, predictive modeling, and data analytics—with extensive support by a data curation and management team. The central technical objective in the MCPC Project was to improve the prediction and characterization of the process-structure-property relationships within the microstructurally refined region of stainless-steel samples prepared utilizing friction stir processing (FSP). Application of the FSP technique is well established at PNNL within the Solid Phase Processing capability through many years of investment across a range of materials and applications (PNNL 2024).

36 MATERIALS SCIENCE↗

DOE OSTI2024

Materials Characterization, Prediction, and Control Project: Summary Report on Material Characterization, Part 3

The Pacific Northwest National Laboratory (PNNL) undertook the Materials Characterization, Prediction, and Control (MCPC) Laboratory Directed Research and Development Project to advance understanding of nuclear material processing and enable multifold acceleration in the development and qualification of new material systems in national security and advanced energy applications (Smith 2021). The MCPC Project executed research across three scientific vertices—material characterization, predictive modeling, and data analytics—with extensive support by a data curation and management team. The central technical objective in the MCPC Project was to improve the prediction and characterization of the process-structure-property relationships within the microstructurally refined region of stainless-steel samples prepared utilizing friction stir processing (FSP). Application of the FSP technique is well established at PNNL within the Solid Phase Processing capability through many years of investment across a range of materials and applications (PNNL 2024).

36 MATERIALS SCIENCE↗

DOE OSTI2024

Materials Characterization, Prediction, and Control Project: Summary Report on Material Characterization, Part 4

The Pacific Northwest National Laboratory (PNNL) undertook the Materials Characterization, Prediction, and Control (MCPC) Laboratory Directed Research and Development Project to advance understanding of nuclear material processing and enable multifold acceleration in the development and qualification of new material systems in national security and advanced energy applications (Smith 2021). The MCPC Project executed research across three scientific vertices—material characterization, predictive modeling, and data analytics—with extensive support by a data curation and management team. The central technical objective in the MCPC Project was to improve the prediction and characterization of the process-structure-property relationships within the microstructurally refined region of stainless-steel samples prepared utilizing friction stir processing (FSP). Application of the FSP technique is well established at PNNL within the Solid Phase Processing capability through many years of investment across a range of materials and applications (PNNL 2024).

36 MATERIALS SCIENCE↗

DOE OSTI2025

An Additively Manufactured Fe-3Si Stator for a High-Performance Electrical Motor

Additive manufacturing (AM) has the potential to produce novel high-performance electrical machines, enabling the direct printing of complex shapes and the simultaneous processing of multiple feedstocks in a single build. We examined the properties and functional performance of Fe-3 wt.% Si materials that were printed via selective laser melting, machined down to thin laminates, and stacked to form a stator core of a prototype brushless permanent-magnet electrical motor. Big Area Additive Manufacturing of Nd2Fe14B (NdFeB)–polyphenylene sulfide (PPS) bonded magnets was performed, with them then being magnetized and used for the rotor. The magnetic, mechanical, and electrical properties of the as-printed and various heat-treated thin laminates and the back electromotive force (EMF) of the electrical motors at different rotational speeds were measured. The thin laminates exhibit a maximum relative permeability of 7494 at an applied field of 0.8 Oe and a core loss of about 20 W/lb at 60 Hz with the maximum induction of 15 kg. In addition to the demonstration of AM printing, motor assembly, and complete characterization of printed Fe-3 wt.% Si, this report highlights the areas of improvement needed in printing technologies to achieve AM built electrical motors and the need for isotropic microstructure refinements to make the laminates appropriate for high-mechanical-strength and low-loss rotational electrical devices.

36 MATERIALS SCIENCE↗