DOE OSTI2026

Graphitization of banana peel – synergistic effect of Ca and other elements of the biomass on carbon structure transformation

Recently, growing interest has been observed in using calcium as an effective catalyst for graphitizing disordered carbon materials derived from biomass and bioprecursors, such as cellulose and lignin, at relatively low tem peratures (<2000 °C). Herein, it is demonstrated that in the presence of elements such as calcium, silicon, sulfur, and potassium, which are abundant in banana peel composed of cellulose and lignin base, graphitization occurs much more effectively. The addition of external calcium source, in the form of calcium carbonate, to the banana peel-derived carbon and heat-treatment of the mixture under protective atmosphere up to 1750 °C results in a significant increase in the degree of the graphitization order and local formation of graphite crystals, whereas the same preparation and heat-treatment procedure applied to carbon material derived from pristine cellulose does not lead to such effective graphitization. It is indicated that the graphitization of banana peel carbon occurs due to the synergistic effect of the external Ca-based catalyst and the internal elements present in the raw biomass, supporting the transformation of the disordered graphene-like layers into graphitic structures. These findings are important for the future production of green graphite from biomass

09 BIOMASS FUELS↗
DOE OSTI2026

Computational modeling of graphite degradation in molten salt reactors: Role of infiltration

Molten salt reactors (MSRs) often employ graphite as a moderator and reflector. An important challenge for deploying graphite in these reactors is that, due to limited experimental data, our understanding of graphite’s structural integrity in molten salt environments remains incomplete. Here, this study addresses heat generation from fuel-bearing salt that has infiltrated open pores in the graphite, driven primarily by pressure differentials. This is one of multiple identified physical and chemical mechanisms through which molten salt could potentially degrade graphite. Thermally driven stresses are quantified using the Molten-Salt Reactor Experiment (MSRE) graphite moderator elements as a case study. Finite element simulations predict stress distributions at varying infiltration levels, indicating that thermal stresses increase with higher infiltration. Rare-event simulations using the parallel subset simulation framework identify the combinations and corresponding ranges of input parameters that lead to stresses above a specified threshold. In particular, combinations involving high infiltration amounts, high power density, and low thermal conductivity tend to induce the highest stresses. Under the inputs and assumptions considered in this work, the magnitudes of the thermally driven stresses are quite low, with a very low likelihood of causing failure due to exceeding the graphite’s tensile strength. Additionally, rare-event simulations were performed for two more scenarios: a scaled-up moderator geometry and a localized hotspot in the original geometry. Both cases resulted in increased susceptibility to failure, though not to a detrimental extent. Furthermore, the combined effects of irradiation and infiltration-induced thermal stresses were evaluated. The results showed that thermal stresses from infiltration were negligible compared to those caused by irradiation. The findings of such a study are inherently component-specific, but the methodology presented here could be used for similar assessments of salt-infiltration effects in other graphite components.

36 - MATERIALS SCIENCE↗
DOE OSTI2025

Summary of Graphite Data Stored within NDMAS

The Graphite Technology Development Project provides data to support the design of graphite core components within specific reactor service conditions of the next generation of high-temperature, gas-cooled nuclear reactors. Physical, mechanical, and thermal properties of nuclear grade graphite were characterized for specimens that were unirradiated, irradiated, and irradiated under various stress conditions. The material properties include diameter, length, mass, density, compressive strength, tensile strength, flexural strength, modulus, resistivity, thermal diffusivity, and thermal expansion coefficient. Baseline graphite specimens are unirradiated from different grades (2114, IG-110, NBG-17, NBG-18, and PCEA) and different types used in different characterization tests (compressive, flexural, tensile, one-inch cylinder, and quarter-inch cylinder). The Advanced Graphite Creep (AGC) irradiation specimens are from a much larger number of grades and cylinder types (creep, piggyback, and pencil). For baseline graphite, characterization data for 7,756 specimens extracted from thirteen graphite billets were captured to the NDMAS database. For AGC experiments, four irradiation campaigns have been completed: AGC-1, AGC-2, AGC-3, and AGC-4. The ongoing HDG-1 (High-Dose Graphite) experiment, which began irradiation with Cycle 168B on August 26, 2020, includes specimens previously irradiated in AGC-2 in addition to the specimens originally destined for AGC-5.. Besides the characterization data, the AGC data includes irradiation monitoring and physics data representing the irradiation conditions of AGC specimens. Currently, all data for AGC-1, AGC-2, and AGC-3 have been captured to the NDMAS database. Only AGC-4 pre-irradiation and irradiation monitoring data have been captured, and HDG-1 pre-irradiation data are in process of being captured for unirradiated specimens. To date, a total of 38,149 material property records have been captured into NDMAS database for baseline and AGC specimens. All characterization data are qualified for use according to their perspective data verification reports. For the AGC irradiation campaigns, a total of 41,502 qualified physics calculation records were added for AGC-1, AGC-2, and AGC-3. Finally, a total of 173,698,505 AGC irradiation monitoring data records (thermocouple temperature, gas flow rate, gas pressure, gas moisture, applied load, and specimen displacement) have been captured to NDMAS; the majority of those records (~94%) are qualified data records.

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
NASA NTRS1962

PYROLYTIC GRAPHITE ROCKET THRUST CHAMBER INVESTIGATION PROJECT. MONTHLY LETTER

This is the Monthly Letter Progress Report for the eighth month of a twelve month technical study directed toward the following objectives: A. Determining analytically and experimentally the feasibility and attractiveness of using free-standing pyrolytic graphite for a radiation cooled liquid rocket thrust chamber and exit nozzle for space application. B. Establishing through analysis and experimental demonstration, a set of design principles to facilitate the design of a reliable pyrolytic graphite thrust chamber assembly for a specific range of operating conditions. C. Demonstrate by means of test firings of complete thrust chamber assemblies, the validity of the design data and principles developed during the program. Preparations have been completed for test firing the two 100 lb. thrust Boron Pyralloy chambers at Marquardt during the first week in March 1962. These two chambers will first be static pressure checked with water to a pressure of 135 psig. The chambers will then be test fired with N204/N2H4-MMH propellants . Test samples of eleven different pyrolytic carbide and nitride materials have been ordered for high temperature oxidation tests and should be delivered by the end of March for evaluation in the plasma torch facility. The specific materials ordered in free- standing condition in thicknesses from 0.030 inch to 0.065 inch were as follows: (a) Pyrolytic graphite (on hand) (b) Pyrolytic graphite-boron alloy (on hand) (c) Pyrolytic graphite-tungsten alloy (d)Boron nitride (e) Titanium nitride (f) Silicon carbide (g) Titanium carbide (h) Zirconium carbide (i) Hafnium carbide (j) Niobium carbide (k) Tantalum carbide (l) High density (1 1-90) graphite (m) High density graphite (heat treated) These materials were ordered from Raytheon, HTM, and American Meta 1 Products . A summary of the available data on the oxidation rates of pyrolytic materials under slow air and rocket motor conditions is shown in Figure 1. High Temperature Materials, Inc. has been contacted relative to providing Pyrographite thrust chambers with extra-thick walls . They believe they can deliver chambers with substantially thicker walls than were possible a short time ago. Such a configuration, with acceptable residual stresses, would provide a longer firing life since it is ultimately limited by the oxidation rate of the chamber wall material. Stress and structural studies have continued. The analytical stress studies point out some of the problems associated with the experimental determination of the elastic constants of this highly anisotropic material. Further analysis may shed light on improved techniques for making these experimental determinations. The large potential weight saving available with the use of pyrolytic graphite as a thrust chamber wall material in a radiation cooled rocket motor has been calculated and is shown graphically in Figure 2. Figure A presents the program progress schedule and the actual expenditures as of 7 February 1962.

ROCKET ENGINE↗
DOE OSTI2024

ASME Design Code Rule Changes for Nuclear Graphite

The American Society of Mechanical Engineers Boiler Pressure and Vessel Code (ASME BPVC) Section III, Division 5, Article HHA-3000 outlines graphite core component and graphite core assembly design guidelines. Graphite core components are defined as ?components manufactured from graphite that are installed to form a graphite core assembly within the reactor pressure vessel of a high temperature, graphite moderated fission reactor.? (p. 413) Graphites? inherent defect distributions do not allow for deterministic material reliability. Rather, graphite has variable strength distributions which change by grade. Article HHA-3000 outlines two semi-probabilistic methods, the full and simplified assessments, which set design load limit targets for each of three component structural reliability classes. The Design Task Group was officially recognized as a specialized task group within ASME November of 2023, though we?ve been collaborating since 2022. The purpose of the Design Task Group is to correct, clarify, and make HHA-3000 function as intended. The Design Task Group will sunset once we?ve achieved our objectives. The Design Task Group was specifically told to not write new Code. While there may be more precise and more accurate methods to determine reliability targets, the current methods are conservative, relatively simple to implement, and have thus far been considered satisfactory for setting design reliability targets. Much of the ground-work to write proposal files and background documents for records to make the changes needed to achieve our objective have been completed. The Design Task Group has documented much of their work through papers, presentations, and memorandums. Three memorandums in which INL team members had substantial contributions are found in the Appendices: FEA Modeling for the Baseline Program, Evaluating the Effects on Margin of Updating the Threshold and Shape Parameters in the Full Assessment, and Interpretations of the Full and Simplified Assessments in ASME BPVC. Most of the on-going work to achieve the Design Task Group?s objective will be addressing comments on existing records and moving records through the balloting process. The Design Task Group met bi-weekly mostly through the end of FY2023. Since February 2024, the Design Task Group has mostly been completed with solving and documenting the technical issues associated with the assessments. Unless new tasks are identified, the remaining work of the Design Task Group will be political and editorial.

97 MATHEMATICS AND COMPUTING↗
DOE OSTI2025

HDG-1 Graphite Preirradiation Data Package Report

This report documents all pre-irradiation examination material-property measurement data for graphite specimens that are going to be used within the first high dose graphite (HDG) -1 irradiation capsule. The two new HDG capsules signify a major change to the AGC Experiment. HDG-1 and HDG-2 will replace the last two Advanced Graphite Creep (AGC) capsules (AGC-5 and AGC-6) which were designed to irradiate graphite at the extreme upper operational temperatures for a very-high-temperature reactor (VHTR) design, 1100°C. These very high temperature AGC-5 and AGC-6 capsules have been repurposed to re-irradiated specimens (from AGC-2, AGC-3, and AGC-4) at the lower temperatures of 600°C and 800°C. HDG-1 will be irradiated at 600°C and HDG-2 will be irradiated at 800°C. By re-irradiating the previous AGC specimens a total maximum neutron dose of around 15 dpa (displacements per atom) can be achieved for all major graphite grades at irradiation temperatures of 600°C and 800°C. Specimens in the HDG-1 capsule are made up of previously irradiated specimens from the AGC-2 capsule and unirradiated specimens prepared for the now discontinued AGC-5 capsule. Utilizing the irradiated specimens, a maximum neutron dose of around 15 dpa is anticipated. These new maximum dose levels will provide irradiated material property data over a total neutron dose range of 1-15 dpa at a temperature of 600°C when combined with the previous AGC-1 and AGC-2 irradiation data. This will provide quantitative data necessary for predicting the irradiation behavior and operating performance of new nuclear graphite grades for use within high temperature reactor designs. Similar to previous AGC test trains, HDG-1 includes the major graphite grades (IG-110, NBG-17, NBG-18, PCEA, and 2114) as well as adding the very fine-grain grade IG-430 which is of interest to the Molten Salt Reactor (MSR) designs. Also new to the HDG-1 capsule are 90 smaller geometry specimens designated as pencil specimens. These specimens take up only one third the space of a standard creep size specimen. This increased number of specimens will enhance property measurement statistics because they will provide 3 times the control specimen data at a position that would otherwise only have a single measurement.

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2025

Design of Critical Experiments Involving Graphite elements at the IPEN/MB-01 Plate-Type Core

A series of critical experiments were designed involving the use of characterized graphite elements in the new plate-type core of the IPEN/MB-01 reactor. Eleven configurations with different graphite quantities are considered, each producing distinct effects on neutron fluxes and offering opportunities to analyze varying sensitivities to k eff in the system. The analysis shows that the experiments can be performed with acceptably low k eff uncertainties considering an adequate characterization of the graphite elements to be used. The sensitivity results obtained using SCALE TSUNAMI calculations show that the experiments have a notable k eff sensitivity coefficient to graphite. In the configurations tested, the k eff sensitivity to graphite TSL is low. This experiment will be useful for criticality safety validation of applications using uranium fuel enriched to around 19.75 wt % 235 U, light water and graphite. It will also be useful to gain more insight into graphite material properties and their effect on k eff as a result of using the well-characterized graphite elements. The execution of the experiments is planned for the summer of 2025. The 11 designed configurations serve as a basis for the final design, and fewer configurations will be executed. Once executed, these critical experiments will be evaluated and submitted for publication in the International Criticality Safety Benchmark Evaluation Project Handbook, supporting the DOE/NRC Collaboration for Criticality Safety Support for Commercial-Scale HALEU for Fuel Cycles and Transportation project goal.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗
DOE OSTI2025

Friction and wear of nuclear graphite exposed to molten FLiNaK salt environment

This report formally documents the completion of the Advanced Reactor Technologies Level 3 Milestone (M3TG-25OR0501104), “Initiate graphite wear studies of graphite samples exposed to molten salt environment,” due August 1, 2025. The report summarizes the ongoing activities aimed at characterizing the friction and wear behavior of graphite in molten LiF–NaF–KF (FLiNaK) salt environment. The wear and friction behavior of self-mated ET-10 nuclear graphite were tested at varying temperatures (550°C and 650°C), contact loads (40 and 80 N) and sliding speeds (1 and 10 mm/s) in a controlled argon environment. The results were compared to the wear and friction behavior of the same graphite material in a dry argon environment. This report presents initial studies on the friction and wear behavior of graphite in sliding contact mode, with future work focused on investigating the graphite matrix materials, as well as rolling and impact contact modes. The outcomes of this report could provide insights into assessing the integrity of the graphitic components of pebble-bed fluoride salt–cooled high-temperature reactors (PB-FHRs) to enhance their safe operation.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2025

Understanding the Reaction of Nuclear Graphite with Molecular Oxygen

A thorough understanding of oxidation is important when considering the health and integrity of graphite components in graphite reactors. For the next generation of graphite reactors, HTGRs specifically, an unlikely air ingress has been deemed significant enough to have made its way into the licensing applications of many international licensing bodies. While a substantial body of literature exists on nuclear graphite oxidation in the presence of molecular oxygen and significant efforts have been made to characterize oxidation kinetics of various grades, the value of existing information is somewhat limited. Often, multiple competing processes, including reaction kinetics, mass transfer, and microstructural evolution, are lumped together into a single rate expression that limits the ability to translate this information to different conditions. This article reviews the reaction of graphite with molecular oxygen in terms of the reaction kinetics, gas transport, and microstructural evolution of graphite. It also presents the foundations of a model for the graphite-molecular oxygen reaction system that is kinetically independent of graphite grade, and is capable of describing both the bulk and local oxidation rates under a wide range of conditions applicable to air-ingress.

J. Kane, Joshua↗
NASA NTRS1972

The ablation of graphitic materials in the sublimation regime.

A large variety of graphitic materials have been tested in an arc heated air stream at a surface pressure of 4.3 atm and a nominal surface temperature of 3925 K. Included were commercial and developmental grades of artificial graphites, both two and three dimensional carbon-carbon composites, composites seeded with refractory compounds, and several special materials such as pyrolytic graphite, mesophase graphite, glassy carbon, and natural graphite. ATJ graphite was used as a control material. Except for the seeded materials which had poor performance, the mass loss rate for all the man-made graphitic materials fell within the range of 17 per cent less to 30 per cent more than the rate for ATJ. Thus it is concluded that wide variations in constituents, processing, fabrication and structure have relatively little effect on the ablation performance of graphitic materials, at least under the conditions of the present tests. Particulate mass loss was observed for all the materials tested and is the dominant mechanism for mass removal at the present test conditions. It is suggested that this mechanism results from physical failure, primarily by compressive thermal stress.

Lundell, J. H.↗
NASA NTRS1981

Dynamics of solid dispersions in oil during the lubrication of point contacts. Part 1: Graphite

A Hertzian contact was lubricated with dispersed graphite in mineral oils under boundary lubrication conditions. The contact was optically observed under pure rolling, combined rolling and sliding, and pure sliding conditions. The contact was formed with a steel ball on the flat surface of a glass disk. Photomicrographs are presented which show the distribution of the graphite in and around the contact. Friction and surface damage are also shown for conditions when the base oils are used alone and when graphite is added to the base oils. Under pure rolling and combined rolling and sliding conditions, it is found that, for low speeds, a graphite film can form which will separate the contacting surfaces. Under pure sliding conditions, graphite accumulates at the inlet and sweeps around the contact, but very little of the graphite passes through the contact. The accumulated graphite appears to act as a barrier which reduces the supply of oil available to the contact for boundary lubrication. Friction data show no clear short term beneficial or detrimental effect caused by addition of graphite to the base oil. However, during pure sliding, more abrasion occurs on the polished balls lubricated with the dispersion than on those lubricated with the base oil alone. All observations were for the special case of a highly-polished ball on a glass surface and may not be applicable to other geometries and materials, or to rougher surfaces.

Cusano, C.↗
NASA NTRS1985

Meteoritic evidence that graphite is rare in the interstellar medium

Carbonaceous material from several distinct astrophysical environments that has been identified in primitive meteorites is discussed. Most of this material is not well crystallized graphite, but ranges from kerogenlike macromolecular organic matter to poorly graphitized carbon. Of the small fraction of the carbonaceous material which is graphite, most may have resulted from the graphitization of macromolecular precursors in the solar nebula. Since graphite is more stable than those precursors, preexisting interstellar graphite should have survived in meteorites to at least the same extent as did other forms of carbon. It is concluded from this dearth of graphite that graphitic carbon was not a major component of the interstellar dust at the time of the formation of the solar system.

Nuth, J. A.↗
DOE OSTI2025

Highly Crystalline Graphite Synthesis from Coal with a Sustainable Process

Synthetic graphite is made predominantly from a petroleum-derived needle coke using the Acheson method. This involves heating the needle coke at elevated temperatures of ~ 3000 °C for more than 7 days. High-temperature heating is the most technically challenging, expensive, and energy-intensive aspect of graphite manufacturing. We will present a strategy for synthesizing high-quality graphite powder from coal using a low-temperature catalytic graphitization process. The use of a catalyst drops the processing temperatures to 1500 °C and processing times to a few hours. The graphite produced with this process has been characterized and has been shown to have comparable physical/chemical properties with commercially sourced graphite materials. We will also present a sustainable method to recover and reuse the catalyst and acid used to retrieve the catalyst. This overcomes a long-standing technical hurdle associated with using catalysts for manufacturing graphite.

crystalline graphite powder↗
DOE OSTI2024

Low-Temperature Production of Battery Grade Graphite from Coal with Recovery and Reuse of the Catalyst

Synthetic graphite is made predominantly from a petroleum-derived needle coke using the Acheson method. This involves heating the needle coke at elevated temperatures of ~ 3000 °C for more than 7 days. High-temperature heating is the most technically challenging, expensive, and energy-intensive aspect of graphite manufacturing. We will present a strategy for synthesizing high-quality battery-grade graphite powder from coal using a low-temperature catalytic graphitization process. The use of a catalyst drops the processing temperatures to 1500 °C and processing times to a few hours. The graphite produced with this process has been tested as a battery anode and has been shown to outperform anodes made with commercially sourced graphite materials. We will also present a sustainable method to recover and reuse the catalyst and acid used to retrieve the catalyst. This overcomes a long-standing technical hurdle associated with using catalysts for manufacturing graphite.

Kim, Ki-Joong↗
NASA NTRS1975

Friction and wear of carbon-graphite materials for high energy brakes

Caliper-type brakes simulation experiments were conducted on seven different carbon-graphite material formulations against a steel disk material and against a carbon-graphite disk material. The effects of binder level, boron carbide (B4C) additions, graphite fiber additions, and graphite cloth reinforcement on friction and wear behavior were investigated. Reductions in binder level and additions of B4C each resulted in increased wear. The wear rate was not affected by the addition of graphite fibers. Transition to severe wear and high friction was observed in the case of graphite-cloth-reinforced carbon sliding against a disk of similar composition. This transition was related to the disruption of a continuous graphite shear film that must form on the sliding surfaces if low wear is to occur. The exposure of the fiber structure of the cloth constituent is believed to play a role in the shear film disruption.

Bill, R. C.↗
NASA NTRS1978

Friction and wear of carbon-graphite materials for high-energy brakes

Caliper type brake simulation experiments were conducted on seven different carbon graphite materials formulations against a steel disk material and against a carbon graphite disk material. The effects of binder level, boron carbide (B4C) additions, SiC additions, graphite fiber additions, and graphite cloth reinforcement on friction and wear behavior were investigated. Reductions in binder level, additions of B4C, and additions of SiC each resulted in increased wear. The wear rate was not affected by the addition of graphite fibers. Transition to severe wear and high friction was observed in the case of graphite-cloth-reinforced carbon sliding against a disk of similar composition. The transition was related to the disruption of a continuous graphite shear film that must form on the sliding surfaces if low wear is to occur.

Bill, R. C.↗
NASA NTRS1987

Design, fabrication and performance of small, graphite electrode, multistage depressed collectors with 200-W, CW, 8- to 18-GHz traveling-wave tubes

Small multistage depressed collectors (MDC's) which used pyrolytic graphite, ion-beam-textured pyrolytic graphite, and isotropic graphite electrodes were designed, fabricated, and evaluated in conjuntion with 200-W, continuous wave (CW), 8- to 18-GHz traveling-wave tubes (TWT's). The design, construction, and performance of the MDC's are described. The bakeout performance of the collectors, in terms of gas evolution, was indistinguishable from that of typical production tubes with copper collectors. However, preliminary results indicate that some additional radiofrequency (RF) and dc beam processing time (and/or longer or higher temperature bakeouts) may be needed beyond that of typical copper electrode collectors. This is particularly true for pyrolytic graphite electrodes and for TWT's without appendage ion pumps. Extended testing indicated good long-term stability of the textured pyrolytic graphite and isotropic graphite electrode surfaces. The isotropic graphite in particular showed considerable promise as an MDC electrode material because of its high purity, low cost, simple construction, potential for very compact overall size, and relatively low secondary electron emission yield characteristics in the as-machined state. However, considerably more testing experience is required before definitive conclusions on its suitability for electronic countermeasure systems and space TWT's can be made.

Ebihara, Ben T.↗
NASA NTRS1987

Effects of sequential treatment with fluorine and bromine on graphite fibers

Three pitch based graphite fibers with different degrees of graphitization and one polyacryonitrile (PAN) based carbon fiber from Amoco Corporation were treated with 1 atm, room temperature fluorine gas for 90 hrs. Fluorination resulted in higher electrical conductivity for all pitch fibers. Further bromination after ambient condition defluorination resulted in further increases in electrical defluorination conductivity for less graphitized, less structurally ordered pitch fibers (P-55) which contain about 3% fluorine by weight before bromination. This product can be stable in 200 C air, or 100% humidity at 60 C. Due to its low cost, this less graphitized fiber may be useful for industrial application, such as airfoil deicer materials. The same bromination process, however, resulted in conductivity decreases for fluorine rich, more graphitized, structurally oriented pitch fibers (P-100 and P-75). Such decreases in electrical conductivity were partially reversed by heating the fibers at 185 C in air. Differential scanning calorimetric (DSC) data indicated that the more graphitized fibers (P-100) contained BrF3, whereas the less graphitized fibers (P-55) did not.

Hung, Ching-Cheh↗