Evaluation of Technologies to Mitigate the Presence of Gaseous Elemental Mercury in Waste Disposal Containers
A study was conducted to evaluate sorbent technologies that can mitigate the presence of elemental mercury (Hg⁰) in waste containers for mercury-contaminated debris (MCD). Decontamination and demolition (D&D) activities at the Y-12 National Security Complex (Y-12) and other U.S. Department of Energy (DOE) Oak Ridge Reservation (ORR) facilities generate MCD requiring offsite disposal. The debris is packaged in appropriate waste containers and may be temporarily stored onsite prior to transport for treatment and/or disposal. During transportation of loads that had no visible liquid Hg at the point of origin, temperature changes can cause Hg⁰ to evaporate, condense, and form droplets on container walls. Furthermore, vibration during transportation could cause beads of Hg to be released from the debris, container walls, and ceiling, resulting in pools of liquid Hg⁰ on the container floor. Waste acceptance criteria (WAC) limitations for commercial disposal facilities, the Nevada National Security Site (NNSS), and ORR mixed low-level waste landfills prohibit the presence of any free liquids in containers identified as a solid waste form. Potential solutions to mitigate the presence of residual liquids that could be formed through vapor condensation include the use of sorbents or similar materials to capture and stabilize volatile Hg⁰ vapors and thus ensure compliance with landfill WAC requirements. This report summarizes data from small-scale laboratory experiments conducted to evaluate sorbent materials for Hg⁰ vapor suppression and sorption of liquid Hg⁰ that could form under relevant transportation and disposal conditions. A series of experiments was conducted to evaluate commercial sorbent materials and their effectiveness for Hg⁰ sorption across a temperature range from 19.4°C to 60°C. The impact of residual moisture on sorption was investigated under relevant conditions, and leaching tests were performed to assess the stability of Hg⁰ captured sorbent materials. The results provide estimates for sorbent quantities needed for a given Hg⁰ mass loading based on experimental results exposing sorbents to gaseous and liquid Hg⁰ at various mass ratios. Overall, sorbents that were most effective for Hg⁰ vapor suppression were brominated activated carbons, mackinawite-based sorbents coated on vermiculite, and sulfur-modified granular activated carbon. Elevated temperatures and moisture conditions did not result in significant increases of Hg⁰ headspace concentrations, and the materials also demonstrated high sorption capacities for the sorption of liquid Hg⁰.