SEARCH · Engineering Papers

Results for “CTE”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

SourceResearch connectionFrom yearThrough year

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 55 records · Page 3

All sources NASA NTRS DOE OSTI

NASA NTRS2000

The Charge Transfer Efficiency and Calibration of WFPC2

A new determination of WFPC2 photometric corrections is presented, using HSTphot reduction of the WFPC2 Omega Centauri and NGC 2419 observations from January 1994 through March 2000 and a comparison with ground-based photometry. No evidence is seen for any position-independent photometric offsets (the "long-short anomaly"); all systematic errors appear to be corrected with the CTE and zero point solution. The CTE loss time dependence is determined to be very significant in the Y direction, causing time-independent CTE solutions to be valid only for a small range of times. On average, the present solution produces corrections similar to Whitmore, Heyer, & Casertano, although with an improved functional form that produces less scatter in the residuals and determined with roughly a year of additional data. In addition to the CTE loss characterization, zero point corrections are also determined as functions of chip, gain, filter, and temperature. Of interest, there are chip-to-chip differences of order 0.01 - 0.02 magnitudes relative to the Holtzman et al. calibrations, and the present study provides empirical zero point determinations for the non-standard filters such as the frequently-used F450W, F606W, and F702W.

Dolphin, Andrew E.↗

NASA NTRS2002

Thermophysical ESEM Characterization of Carbon Fibers

Coefficients of thermal expansion (CTE) of carbon fibers create residual stresses in aggressive manufacturing and service environments. In this effort, environmental scanning electron microscope (ESEM) is used for in situ observations of a carbon fiber cross-section up to 1000 C in order to evaluate the much neglected transverse CTE. The perimeter of fiber cross-section is calculated with the Scion image processing program from images that were taken at every 100 C increments. CTE values are calculated by linear regression of the strain data based on the perimeter changes. Furthermore, through SEM, WDS and TEM observations, we are in the process of bringing an interactive rationale between CTE, crystallinity and surface roughness of carbon fibers.

Sue, Jiwoong↗

NASA NTRS2003

High-Temperature Oxidation-Resistant and Low Coefficient of Thermal Expansion NiAl-Base Bond Coat Developed for a Turbine Blade Application

Many critical gas turbine engine components are currently made from Ni-base superalloys that are coated with a thermal barrier coating (TBC). The TBC consists of a ZrO2-based top coat and a bond coat that is used to enhance the bonding between the superalloy substrate and the top coat. MCrAlY alloys (CoCrAlY and NiCrAlY) are currently used as bond coats and are chosen for their very good oxidation resistance. TBC life is frequently limited by the oxidation resistance of the bond coat, along with a thermal expansion mismatch between the metallic bond coat and the ceramic top coat. The aim of this investigation at the NASA Glenn Research Center was to develop a new longer life, higher temperature bond coat by improving both the oxidation resistance and the thermal expansion characteristics of the bond coat. Nickel aluminide (NiAl) has excellent high-temperature oxidation resistance and can sustain a protective Al2O3 scale to longer times and higher temperatures in comparison to MCrAlY alloys. Cryomilling of NiAl results in aluminum nitride (AlN) formation that reduces the coefficient of thermal expansion (CTE) of the alloy and enhances creep strength. Thus, additions of cryomilled NiAl-AlN to CoCrAlY were examined as a potential bond coat. In this work, the composite alloy was investigated as a stand-alone substrate to demonstrate its feasibility prior to actual use as a coating. About 85 percent of prealloyed NiAl and 15 percent of standard commercial CoCrAlY alloys were mixed and cryomilled in an attritor with stainless steel balls used as grinding media. The milling was carried out in the presence of liquid nitrogen. The milled powder was consolidated by hot extrusion or by hot isostatic pressing. From the consolidated material, oxidation coupons, four-point bend, CTE, and tensile specimens were machined. The CTE measurements were made between room temperature and 1000 C in an argon atmosphere. It is shown that the CTE of the NiAl-AlN-CoCrAlY composite bond coat is lower than that of the commercially used coating alloy 16-6. To examine the potential of NiAl-AlN-CoCrAlY as a bond coat, we subjected two samples to cyclic furnace testing. The furnace cycle consisted of 45 min at 1163 C (2125 F ) followed by 15 min of cooling out of the furnace. The current NASA baseline TBC is a NiCrAlY bond coat below the 7YSZ top coat. The average TBC life for this baseline coating on Ren N5 is 188 plus or minus 19 cycles. NiAl-AlN-CoCrAlY specimens coated with the same 7YSZ top coat were still intact even after 1000 cycles. Therefore, the NiAl-AlN-CoCrAlY as a bulk substrate material, exhibits more than 5 times the life of the current state-of-the-art material. The next step is to evaluate this material as a coating on the same superalloy substrate.

Source record↗

NASA NTRS2011

Mount Protects Thin-Walled Glass or Ceramic Tubes from Large Thermal and Vibration Loads

The design allows for the low-stress mounting of fragile objects, like thin walled glass, by using particular ways of compensating, isolating, or releasing the coefficient of thermal expansion (CTE) differences between the mounted object and the mount itself. This mount profile is lower than true full kinematic mounting. Also, this approach enables accurate positioning of the component for electrical and optical interfaces. It avoids the higher and unpredictable stress issues that often result from potting the object. The mount has been built and tested to space-flight specifications, and has been used for fiber-optic, optical, and electrical interfaces for a spaceflight mission. This mount design is often metal and is slightly larger than the object to be mounted. The objects are optical or optical/electrical, and optical and/or electrical interfaces are required from the top and bottom. This requires the mount to be open at both ends, and for the object s position to be controlled. Thin inside inserts at the top and bottom contact the housing at defined lips, or edges, and hold the fragile object in the mount. The inserts can be customized to mimic the outer surface of the object, which further reduces stress. The inserts have the opposite CTE of the housing material, partially compensating for the CTE difference that causes thermal stress. A spring washer is inserted at one end to compensate for more CTE difference and to hold the object against the location edge of the mount for any optical position requirements. The spring also ensures that any fiber-optic or optic interface, which often requires some pressure to ensure a good interface, does not overstress the fragile object. The insert thickness, material, and spring washer size can be traded against each other to optimize the mount and stresses for various thermal and vibration load ranges and other mounting requirements. The alternate design uses two separate, unique features to reduce stress and hold the object. A release agent is applied to the inside surface of the mount just before the binding potting material is injected in the mount. This prevents the potting material from bonding to the mount, and thus prevents stress from being applied, at very low temperatures, to the fragile object being mounted. The potting material mixing and curing is temperature- and humidity-controlled. The mount has radial grooves cut in it that the potting material fills, thus controlling the vertical position of the mounted object. The design can easily be used for long and thin objects, short and wide objects, and any shape in between. The design s advantages are amplified for long and thin fragile objects. The general testing range was 45 to +45 C, but multiple mounts were successfully tested down to 60 and up to 50 C and the design can be adjusted for larger ranges.

Amato, Michael↗

NASA NTRS2019

Development of Composite Sandwich Bonded Longitudinal Joints for Space Launch Vehicle Structures

The NASA Composite Technology for Exploration (CTE) Project is developing and demonstrating critical composite technologies with a focus on composite bonded joints; incorporating materials, design/analysis, manufacturing, and tests that utilize NASA’s expertise and capabilities. The project has goals of advancing composite technologies and providing lightweight structures to support future NASA exploration missions. In particular, the CTE project will demonstrate weight-saving, performance-enhancing composite bonded joint technology for Space Launch System (SLS)-scale composite hardware. Advancements from the CTE project may be incorporated as future block upgrades for SLS structural components. This paper discusses the details of the development of a composite sandwich bonded longitudinal joint for a generic space launch vehicle structure called the CTE Point Design. The paper includes details of the design, analysis, materials, manufacturing, and testing of sub-element joint test articles to test the capability of the joint design. The test results show that the composite longitudinal bonded joint design significantly exceeds the design loads with a 2.0 factor of safety. Analysis pre-test failure predictions for all sub-element bonded joint test coupons were all within 10% of the average test coupon failure load. This testing and analysis provides confidence in the potential use of composite bonded joints for future launch vehicle structures.

Segal, Kenneth N.↗

NASA NTRS2019

Testing and Analysis Correlation of Composite Sandwich Longitudinal Bonded Joints for Space Launch Vehicle Structures

The NASA Composite Technology for Exploration (CTE) Project has been developing and demonstrating critical composite technologies with a focus on joints; incorporating materials, design/analysis, manufacturing, and tests that utilize NASA expertise and capabilities. The CTE project has focused on the development of composite longitudinal bonded joint technologies for conical structures such as the SLS Payload Attach Fitting (PAF) due to challenging joint geometries and loads compared to cylindrical jointed structures. The CTE team selected and designed a double-lap composite bonded joint as the most advantageous longitudinal joint to advance for the CTE project. This paper reports on the longitudinal bonded joint sub-element test articles that were fabricated and tested for several loading conditions to test the capability of the bonded joint design. Test and analysis correlation to the sub-element test articles are presented in the paper.

Sleight, David W.↗

NASA NTRSDate not supplied

Testing and Analysis Correlation of a Large-Scale Composite Sandwich Longitudinal Bonded Joint for Space Launch Vehicle Structures

The NASA Composite Technology for Exploration (CTE) Project is developing and demonstrating critical composite technologies with a focus on composite bonded joints; incorporating materials, design/analysis, manufacturing, and tests that utilize NASA’s expertise and capabilities. The project has goals of advancing composite technologies and providing lightweight structures to support future NASA exploration missions. In particular, the CTE project will demonstrate weight-saving, performance-enhancing composite bonded joint technology for Space Launch System (SLS)-scale composite hardware. Advancements from the CTE project may be incorporated as future block upgrades for SLS structural components. This paper discusses the details of the development of a composite sandwich bonded longitudinal joint for a generic space launch vehicle structure called the CTE Point Design. This paper reports on the large-scale longitudinal bonded joint test articles that were fabricated and tested under axial compressive loading conditions to test the capability of the bonded joint design for buckling and joint failure. Test and analysis correlation of an as-manufactured undamaged longitudinal bonded joint panel are presented in the paper for tests to the onset of buckling and panel failure. Analysis predictions for buckling initiation and panel failure were both within 10% of the longitudinal bonded joint panel test results. This testing and analysis provide confidence in the potential use of composite bonded joints for future launch vehicle structures.

David W Sleight↗

NASA NTRS2023

Influence of Cation Species on Thermal Expansion of Y2Si2O7–Gd2Si2O7 Solid Solutions

Mixtures of Y 2 Si 2 O 7 and Gd 2 Si 2 O 7 were synthesized by solid-state reaction at 1600°C and characterized via in situ x-ray diffraction (XRD) to determine their coefficients of thermal expansion (CTE). All solid solutions within the system exhibited the orthorhombic δ-RE 2 Si 2 O 7 (Pna2 1 ) structure. Thermal expansion measurements of Y 2 Si 2 O 7 and Gd 2 Si 2 O 7 correlated well with reported values in literature, and all synthesized solid solutions exhibited CTEs between Y 2 Si 2 O 7 and Gd 2 Si 2 O 7 . Generally, there was a slight decrease in CTE exhibited by the materials with increasing Gd 2 Si 2 O 7 content, with Gd 2 Si 2 O 7 having the lowest CTEs and Y 2 Si 2 O 7 the highest CTEs. The decrease in CTE was attributed to stronger bonds of Gd-O over Y-O, as determined by calculated crystal orbital Hamilton populations using density functional theory. However, such differences were very small and crystal structure was the dominating factor in CTE trends.

rare earth silicates↗

NASA NTRS1987

Electro-optical characterization of the Tektronix TK512M-011 charge-coupled device

An electrooptical characterization encompassing linearity, blooming, dark-count rate, charge-transfer efficiency (CTE), and quantum efficiency, is presented for a front/side-illuminated CCD with 512x512 format and 27x27-micron pixels. The detailed noise characteristics of the CCD-output FET are reported. While very good low light level CTE is obtained in the parallel-shift direction, CTE problems arise in the serial direction. The output FET noise is equivalent to 5-12 electrons, depending on FET operating conditions and system bandwidth.

Epperson, Patrick M.↗

NASA NTRS1990

Optimization of interface layers in the design of ceramic fiber reinforced metal matrix composites

The potential of using an interface layer to reduce thermal stresses in the matrix of composites with a mismatch in coefficients of thermal expansion (CTE) of fiber and matrix was investigated. It was found that the performance of the layer can be defined by the product of the CTE and the thickness, and that a compensating layer with a sufficiently high CTE can reduce the thermal stresses in the matrix significantly. A practical procedure offering a window of candidate layer materials is proposed.

Doghri, I.↗

NASA NTRS1991

A resistive-gate Al(0.3)Ga(0.7)As/GaAs 2DEG CCD with high charge-transfer efficiency at 1 GHz

The fabrication and performance of an Al(0.3)Ga(0.7)As/GaAs modulation-doped resistive-gate CCD are reported. The two-dimensional electron gas (2DEG) CCD, implemented as a 32-stage four-phase delay line, was tested at both low (1-13 MHz) and high (0.6-1.0 GHz) frequency. It exhibits a room-temperature charge-transfer efficiency (CTE) of better than 0.999 at clock frequencies from 10 MHz up to 1 GHz without a fat-zero signal and is limited by dark current below 10 MHz. The high-frequency test showed no CTE degradation up to 1-GHz operation. The CTE degraded at frequencies lower than approximately 5 MHz due to dark current. The charge-handling capability and minimum clock swing of the resistive-gate 2DEG CCD are calculated.

Song, J.-I.↗

NASA NTRS1992

Low coefficient of thermal expansion polyimides containing metal ion additives

Polyimides have become widely used as high performance polymers as a result of their excellent thermal stability and toughness. However, lowering their coefficient of thermal expansion (CTE) would increase their usefulness for aerospace and electronic applications where dimensional stability is a requirement. The incorporation of metal ion-containing additives into polyimides, resulting in significantly lowered CTE's, has been studied. Various metal ion additives have been added to both polyamic acid resins and soluble polyimide solutions in the concentration range of 4-23 weight percent. The incorporation of these metal ions has resulted in reductions in the CTE's of the control polyimides of 12 percent to over 100 percent depending on the choice of additive and its concentration.

Stoakley, D. M.↗

NASA NTRS1993

Temperature induced distortions in space telescope mirrors

In this paper, it is illustrated how measured instantaneous coefficients of thermal expansion (CTE) can be accurately taken into account when modeling the structural behavior of space based optical systems. In particular, the importance of including CTE spatial variations in the analysis of optical elements is emphasized. A comparison is made between the CTE's of three optical materials commonly used in the construction of space mirrors (ULE, Zerodur, and beryllium). The overall impact that selection of any one of these materials has on thermal distortions is briefly discussed. As an example of how temperature dependent spatial variations in thermal strain can be accurately incorporated in the thermo-structural analysis of a precision optical system, a finite element model is developed, which is used to estimate the thermally induced distortions in the Hubble Space Telescope's (HST) primary mirror. In addition to the structural analysis, the optical aberrations due to thermally induced distortions are also examined. These calculations indicate that thermal distortions in HST's primary mirror contribute mainly to defocus error with a relatively small contribution to spherical aberration.

Nied, H. F.↗

NASA NTRS1992

Materials and structures

Materials and structures technology covers a wide range of technical areas. Some of the most pertinent issues for the Astrotech 21 missions include dimensionally stable structural materials, advanced composites, dielectric coatings, optical metallic coatings for low scattered light applications, low scattered light surfaces, deployable and inflatable structures (including optical), support structures in 0-g and 1-g environments, cryogenic optics, optical blacks, contamination hardened surfaces, radiation hardened glasses and crystals, mono-metallic telescopes and instruments, and materials characterization. Some specific examples include low coefficients of thermal expansion (CTE) structures (0.01 ppm/K), lightweight thermally stable mirror materials, thermally stable optical assemblies, high reliability/accuracy (1 micron) deployable structures, and characterization of nanometer level behavior of materials/structures for interferometry concepts. Large filled-aperture concepts will require materials with CTE's of 10(exp 9) at 80 K, anti-contamination coatings, deployable and erectable structures, composite materials with CTE's less than 0.01 ppm/K and thermal hysteresis, 0.001 ppm/K. Gravitational detection systems such as LAGOS will require rigid/deployable structures, dimensionally stable components, lightweight materials with low conductivity, and high stability optics. The Materials and Structures panel addressed these issues and the relevance of the Astrotech 21 mission requirements by dividing materials and structures technology into five categories. These categories, the necessary development, and applicable mission/program development phasing are summarized. For each of these areas, technology assessments were made and development plans were defined.

Saito, Theodore T.↗

NASA NTRS1994

Thermomechanical Fatigue Damage/Failure Mechanisms in SCS-6/Timetal 21S [0/90](Sub S) Composite

The thermomechanical fatigue (TMF) deformation, damage, and life behaviors of SCS6/Timetal 21S (0/90)s were investigated under zero-tension conditions. In-phase (IP) and out-of-phase (OP) loadings were investigated with a temperature cycle from 150 to 650 deg C. An advanced TMF test technique was used to quantify mechanically damage progression. The technique incorporated explicit measurements of the macroscopic (1) isothermal static moduli at the temperature extremes of the TMF cycle and (2) coefficient of thermal expansion (CTE) as functions of the TMF cycles. The importance of thermal property degradation and its relevance to accurate post-test data analysis and interpretation is briefly addressed. Extensive fractography and metallography were conducted on specimens from failed and interrupted tests to characterize the extent of damage at the microstructure level. Fatigue life results indicated trends analogous to those established for similar unidirectional(0) reinforced titanium matrix composite systems. High stress IP and mid to low stress OP loading conditions were life-limiting in comparison to maximum temperature isothermal conditions. Dominant damage mechanisms changed with cycle type. Damage resulting from IP TMF conditions produced measurable decreases in static moduli but only minimal changes in the CTE. Metallography on interrupted and failed specimens revealed extensive (0) fiber cracking with sparse matrix damage. No surface initiated matrix cracks were present. Comparable OP TMF conditions initiated environment enhanced surface cracking and matrix cracking initiated at (90) fiber/matrix (F/M) interfaces. Notable static moduli and CTE degradations were measured. Fractography and metallography revealed that the transverse cracks originating from the surface and (90) F/M interfaces tended to converge and coalesce at the (0) fibers.

Castelli, Michael G.↗

NASA NTRS1995

Thermomechanical Fatigue Behavior of Three Cfcc's

The thermomechanical fatigue (TMF) behavior of three continuous-fiber ceramic composites (CFCC's) was examined. The three matrices consisted of two different glass-ceramics and silicon carbide, respectively. The matrices of some of the specimens with the silicon carbide matrix were enhanced to improve oxidation resistance. All three were reinforced with Nicalon fibers with various fiber architectures. The thermoelastic properties of the matrix relative to the fibers, the elastic moduli and coefficients of thermal expansion (CTE), were different in each composite, providing a comparison of the effects of these critical properties. The specimens were tested under in-phase (IP) and out-of-phase (OP) cyclic loadings with respect to thermal cycling between 600 C and 1100 C. One of the glass-ceramic composites had greatly increased TMF lives compared to the other glass-ceramic matrix composites. This was probably caused by the reversal of the CTE mismatch between the fibers and the matrices and caused by the different oxidation resistances of the composites. For the same TMF lives a cross-ply reinforced composite had a maximum cyclic stress half as great, as that of unidirectionally reinforced composite. This indicated that the (0 deg) ply fibers had a strong influence of TMF life. Both the glass ceramic matrix composites had shallow-slope stress-life plots that indicated sensitivity to damage and therefore low damage tolerance. The composites with an unenhanced silicon carbide matrix experienced the shortest TMF lives of all the CFCC's tested. However, the enhanced composite had the longest. Also, the enhanced composite demonstrated the best damage tolerance as evidenced by a stress-life curve that curves sharply upward to the left. In all the composites, out-of-phase cyclic loading was worse than in-phase cyclic loadings despite the CTE mismatch between fiber and matrix. A damage investigation and a preliminary analysis of the stresses in the fibers and matrices taking into account their respective thermoelastic properties provided insight into the relative behavior of the glass-ceramic matrix composites under IP and OP TMF.

Worthem, Dennis W.↗

NASA NTRS1995

The Dependence of the Change in the Coefficient of Thermal Expansion of Graphite Fiber Reinforced Polyimide IM7-K3B on Microcracking due to Thermal Cycling

Composite IM7-K3B was subjected to a simulated high speed aircraft thermal environment to determine the effects of microcracking on the change in CTE. IM7-K3B is a graphite fiber reinforced polyimide laminate, manufactured by Dupont. The lay-up for the material was (0.90((Sub 3)(Sub s))). The specimens were placed in a laser-interferometric dilatometer to obtain thermal expansion measurements and were then repeatedly cycled between -65 F and 350 F up to 1000 cycles. After cycling they were scanned for microcracks at a magnification of 400x. The material was expected not to crack and to have a near zero CTE. Some microcracking did occur in all specimens and extensive microcracking occurred in one specimen. Further testing is required to determine how closely the CTE and microcracking are related.

Stewart, Melissa C.↗

NASA NTRS1998

Development and Characterization of SiC)/ MoSi2-Si3N4(p) Hybrid Composites

Intermetallic compound MoSi2 has long been known as a high temperature material that has excellent oxidation resistance and electrical/thermal conductivity. Also its low cost, high melting point (2023 C), relatively low density (6.2 g/cu cm versus 9 g/cu cm for current engine materials), and ease of machining, make it an attractive structural material. However, the use of MoSi2 has been hindered due to its poor toughness at low temperatures, poor creep resistance at high temperatures, and accelerated oxidation (also known as 'pest' oxidation) at temperatures between approximately 450 and 550 C. Continuous fiber reinforcing is very effective means of improving both toughness and strength. Unfortunately, MoSi2 has a relatively high coefficient of thermal expansion (CTE) compared to potential reinforcing fibers such as SiC. The large CTE mismatch between the fiber and the matrix resulted in severe matrix cracking during thermal cycling. Addition of about 30 to 50 vol % of Si3N4 particulate to MoSi2 improved resistance to low temperature accelerated oxidation by forming a Si2ON2 protective scale and thereby eliminating catastrophic 'pest failure'. The Si3N4 addition also improved the high temperature creep strength by nearly five orders of magnitude, doubled the room temperature toughness and significantly lowered the CTE of the MoSi2 and eliminated matrix cracking in SCS-6 reinforced composites even after thermal cycling. The SCS-6 fiber reinforcement improved the room temperature fracture toughness by seven times and impact resistance by five times. The composite exhibited excellent strength and toughness improvement up to 1400 C. More recently, tape casting was adopted as the preferred processing of MoSi2-base composites for improved fiber spacing, ability to use small diameter fibers, and for lower cost. Good strength and toughness values were also obtained with fine diameter Hi-Nicalon tow fibers. This hybrid composite remains competitive with ceramic matrix composites as a replacement for Ni-base superalloys in aircraft engine applications.

Hebsur, Mohan G.↗