DOE OSTI2025

Directed energy deposition of radially functionally graded nickel based superalloys IN625 and IN738: Microstructure and mechanical properties

This study investigates the microstructure and mechanical properties of radially functionally graded (RFG) materials fabricated from nickel-based superalloys IN625 and IN738 using directed energy deposition (DED). RFG cylindrical deposits with radial gradients of IN625-IN738 and IN738-IN625 were successfully fabricated and confirmed to be crack-free through tailored composition grading, scan strategy and process parameters that minimized thermal gradients and solidification velocities. Microstructural analysis revealed distinct variations across the gradient, characterized by differences in dendrite arm spacing, microsegregation, and the formation of distinct γ' precipitates and carbide/boride phases (MC, M 6 C, M 2 C, and MB 2 ) in as-deposited (AD) conditions, which evolved into M 23 C 6 and M 2 B upon subsequent heat treatment (HT). EBSD showed predominant columnar grains with a [100] texture, while microhardness profiles demonstrated consistent variation across the gradients. Mechanical testing highlighted the synergy of the graded structure, combining IN738's strength with IN625's ductility, resulting in enhanced properties such as a yield strength of 1131 MPa, ultimate tensile strength of 1382 MPa, and elongation of 12 % for HT IN625-IN738 grading. Numerical simulations employing CALPHAD thermodynamic calculations and finite element thermal modeling are used to establish phase evolution and microstructural feature correlation with thermal profiles, aiding in the optimization of process-structure-property relationship.

Additive manufacturing↗
DOE OSTI2025

Probing the shear-induced microstructure of a smectite clay aqueous suspensions using rheo-USANS and rheo-SIPLI measurements

Hypothesis: The static microstructure of aqueous sodium-montmorillonite (Na-Mt) suspensions at low ionic strengths (where Particle Size/Debye Length ≈1) exhibits both the particle–particle ordering as well as aggregation with repulsive ordered domains having characteristic optical birefringence and attractive aggregated entities larger than 20 µm resulting in ever-increasing yield stresses also known as physical aging-rejuvenation behavior. We hypothesize that the attractive particle–particle aggregation is the underlying cause behind the physical aging-rejuvenation behavior observed in Na-Mt suspensions with no contribution from structural dynamics driven by repulsive particle–particle ordering or jamming. Experiments: We investigate the shear-induced microstructure of aqueous Na-Mt suspensions in the sol and gel state using rheo-ultra-small angle neutron scattering (rheo-USANS) experiments at shear rates of 1, 50, 500, and 2000 s −1 . We also perform rheo-shear-induced polarization light imaging (rheo-SIPLI) experiments to relate ordering with shearing and aging. Findings: Shearing the suspensions at low to moderate shear rates induces particle–particle aggregation and shearing at high shear rates induces the breakage of particle–particle aggregation in the sol and gel states, suggesting the microstructural aggregation in the sol and gel state is shear sensitive and a full rejuvenation or breakage of particle–particle aggregation is only achieved at a minimum critical shear rate. The rheo-SIPLI experiments reveal that the sol and gel state exhibited strong Maltese cross patterns at a shear rate of 1000 s −1 , indicating particle–particle ordering. Post shearing, the gel exhibited temporal evolution of storage modulus without any noticeable influence on the appearance of the Maltese cross pattern indicating physical aging and particle ordering are distinct length scale phenomena in Na-Mt suspensions and the physical aging-rejuvenation behaviour is a feature of particle–particle aggregation as opposed to ordering.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Effect of powder layer thickness on the microstructural development of additively manufactured SS316

By Increasing the powder layer thickness we could increase material deposition rates and reduce build times during laser powder bed fusion (LPBF). However, increasing the powder layer thickness could also negatively affect the local melting and subsequent microstructure of the printed material. This study systematically investigated, for the first time, the defect evolution and microstructural changes of LPBF stainless steel 316 (SS316) processed by using various powder layer thicknesses of 40, 80, and 120 μm while also varying the laser dwell time for the pulsed laser. Through image analysis, the pore density was found to increase with increasing powder layer thickness, particularly when the dwell time was too high or too low. The maximum achievable density (>99%) was found over a wide processing window when using the smallest powder layer thickness of 40 μm between dwell times of 60 and 100 μs. Increasing the powder layer thicknesses to 80 and 120 μm resulted in maximum densities of 98.7 and 96.8%, respectively, but the window for acceptable laser dwell times that could achieve these densities narrowed considerably. A microstructural analysis of the melt pools was performed to measure the melt pool depths and widths, both of which increased with increasing dwell time. However, increasing the powder layer thickness did not affect the melt pool depth and only minorly affected the width. A sub-grain cellular structure distinguished the melt pool boundaries. The cell size increased with increasing dwell time and decreasing powder layer thickness. Moreover, the cell size was used to calculate a cooling rate that had a magnitude of 10 7 K/s and increased with increasing powder layer thickness.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Toughening Sm–Co sintered magnets via microstructure modification with additives

We report the mechanical properties of the brittle Smsingle bondCo permanent magnets are of great practical significance. However, studies on the magnets have mostly focused on their magnetic properties. This paper reports the modified microstructure and refined unimodal grain size, enhanced flexural strength, and magnetic properties of Sm 2 (Co,Fe,Cu,Zr) 17 sintered magnets doped with La 2 O 3 , MgO, and CaF 2 fine particulates. The correlations between microstructure, phase composition, and mechanical and magnetic properties were studied. Doping of a small amount (e.g., 0.5–3 wt%) of La 2 O 3 , MgO, or CaF 2 fine particulates could significantly refine the unimodal grain sizes of the Smsingle bondCo magnets via the Zener pinning effect. Moreover, doping significantly improved the flexural strengths σ of the magnets. For example, the σ values of the magnets with 0.5 wt% MgO, 1 wt% La 2 O 3 , and 1 wt% CaF 2 were approximately 65%, 63%, and 42% higher than that of the reference magnet, respectively. Micromechanical simulations revealed that the fine particles of La 2 O 3 could deflect crack growth, while the CaF 2 particles could attract or arrest cracks during the fracture process. The mechanical strengthening effect was mainly due to grain size refinement. The Smsingle bondCo magnets with 0.5–1.5 wt% CaF2 and 0.5 wt% La 2 O 3 exhibited excellent magnetic properties while doping 1–3 wt% La2O3 and 0.5–3 wt% MgO deteriorated magnetic performance. The rational design of CaF 2 - or La 2 O 3 -doped microstructure can be an economical and effective method for producing toughened Sm–Co sintered magnets with high magnetic performance.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Effect of nitriding on mechanical and microstructural properties of Direct Metal Laser Sintered 17-4PH stainless steel

In this work, the effect of the nitriding process on microstructure and mechanical properties of additively manufactured (AM) 17-4PH stainless steel is investigated. The nitriding was performed at 530 °C, 560 °C, and 580 °C for 2 h. The nitriding process improves the hardness and surface roughness of the AM 17-4PH steel. Detailed microstructural characterizations of both as-built and nitride samples are performed using an optical microscope, scanning electron microscope (SEM) equipped with energy-dispersive X-ray spectroscopy (EDS), and X-ray diffraction technique. It reveals that the nitride layer thickness increases with nitriding temperature. A distinct transition layer between the substrate and nitride layer is observed in the 560 °C and 580 °C nitride samples. The nitriding process develops almost equiaxed grain microstructure with new secondary phase precipitates, whereas in the as-built material, the grains are primarily columnar along the AM process build direction. Specifically, the nitriding process introduces γ-Fe4N, ε-Fe3N, CrN, and Ni3N precipitates. The increase in Ni- and Cu-rich precipitates with the nitriding temperature explains the observed improvement in the hardness and surface roughness. Furthermore, the nitriding process does not alter the substrate's initial weak crystallographic texture.

17-4PH steel↗
DOE OSTI2021

Quantifying the effect of hydride microstructure on zirconium alloys embrittlement using image analysis

Since hydride microstructure can significantly influence Zr alloy nuclear fuel cladding’s ductility, a new metric has been developed to quantify hydride microstructure in 2D micrographs and relate it to crack propagation. As cladding failure usually results from a hoop stress, this new metric, called the Radial Hydride Continuous Path (RHCP), is based on quantifying the continuity of brittle hydride particles along the radial direction of the cladding tube. Compared to previous metrics, this approach more closely relates to the propensity of a crack to propagate radially through the cladding tube thickness. The RHCP takes into account hydride length, orientation, and connectivity to choose the optimal path for crack propagation through the cladding thickness. The RHCP can therefore be more closely linked to hydride embrittlement of the Zr alloy material, thus creating a relationship between material structure, properties, and performance. The new definition, along with previously proposed metrics such as the Radial Hydride Fraction (RHF), the Hydride Continuity Coefficient (HCC), and the Radial Hydride Continuity Factor (RHCF), have been implemented and automated in MATLAB. These codes are made available with this publication as supplementary materials. These metrics were verified by comparing their predictions of hydride morphology against expected values in simple cases, and the implementation of the new metric was validated by comparing its predictions with manual measurements of hydride microstructure performed on ImageJ. The RHCP was also validated against experimental measurements of fracture behavior and it was shown to correlate with cladding failure better than previous metrics. The information provided by these metrics will help accurately assess cladding integrity during operation, transportation, and storage.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Microstructure-process relationships in monolithic U-10Mo fuel foil single-pass rolling: A parametric simulation study

In this work, a previously validated coupling of Kinetic Monte Carlo (KMC) Potts Model and finite element method (FEM) simulations was implemented to investigate the effects of microstructural features in as-cast and homogenized monolithic U-10Mo foils on the emergent microstructure after rolling and reheating. Parameters that could potentially affect recrystallization behavior of the rolled U-10Mo foils were considered: grain size distribution, uranium carbide (UC) size distribution, UC volume fraction, spatial distribution of UC, and rolling reduction magnitude. Grain structure and the magnitude of rolling reduction have the strongest influence on recrystallization kinetics and the fabricated grain size distribution. The UC distribution had only a weak effect on the recrystallization kinetics and final microstructures. While particle-stimulated nucleation (PSN) occurred in simulation more frequently as grain size increased, its incidence did not appear to considerably affect the recrystallization kinetics or grain size distribution.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Microstructure and phase evolution in the U-10Zr fuel investigated by in situ TEM heating experiments

The development of U-Zr metallic nuclear fuel for fast spectrum reactors is impacted by a lack of mechanistic understanding of the fuel behavior evolution under thermal irradiation conditions, despite previous works providing substantial fuel performance data. This work uses in-situ transmission electron microscopy heating experiments to study phase and microstructural evolution in several unirradiated U-10Zr specimens during rapid heating ramps (from room temperature to 1000 °C). The starting a-U + bcc-(Zr, U) eutectic microstructure began to decompose above 600 °C. The decomposition initiated from the bcc (U,Zr) phase. Similar results were observed for all specimens even when fabricated by different routes (e.g., cold rolled or annealed). As a result, the impact of observed microstructure and phase evolutions at high temperatures on fuel fabrication and in-pile fuel transient test was also discussed.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Irradiation creep measurement and microstructural analysis of chromium nitride–coated zirconium alloy using pressurized tubes

Environmental barrier coatings for Zr-based materials are currently under development to reduce oxidation and embrittlement in light-water reactors. Chromium nitride is one such candidate for this application, particularly as accident-tolerant fuel cladding. However, quantifying the impact of coatings on the irradiation-induced creep of zircaloy (Zry) is critical as this mechanism often exceeds thermal creep rates under light-water reactor operating conditions and can be a limiting design characteristic. Additionally, examining irradiation effects in the microstructure at the coating interface is key to understanding the compatibility of the material system. Here, to accelerate the experimental measurement of irradiation creep and microstructure evolution in CrN-Zry, compact, pressurized creep tubes were fabricated and irradiated in the High Flux Isotope Reactor (HFIR) at Oak Ridge National Laboratory. Miniature, thin-walled rodlets fabricated from annealed Zr-Sn barstock were coated with CrN using physical vapor deposition (PVD) to nominal thicknesses of 4 and 8 μm. Coated and uncoated rodlet specimens were internally pressurized and welded, generating nominal circumferential hoop stresses of 0, 90, or 180 MPa under 300°C irradiation conditions. Twelve specimens were measured diametrically prior to irradiation using a low-cost, automated, contactless laser profilometer developed for this work. Specimens were irradiated in sealed capsules for one 25-day HFIR cycle, accumulating approximately 1.8 $\times$ 10 21 n/cm 2 fast fluence (E n > 10 MeV). The irradiated samples were retrieved and remeasured using the same profilometry system in a shielded hot cell facility. Irradiation creep between specimens was compared using standard statistical tests and showed that both thicknesses of CrN coating had a negligible effect on the irradiation creep strain of the Zry material. Microstructure characterization of pre- and post-irradiated CrN-Zry specimens showed minimal changes due to irradiation but did show a substantial O-rich region at the Zry-CrN interface.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Correlating microstructure and mechanical properties of harvested high dose Zorita light water reactor internals

Here, in this study, microstructural studies and micro-mechanical testing of an ex-plant material harvested from the decommissioned pressurized water reactor (PWR) is carried out. Irradiated 304 stainless steel (SS) components were harvested by the Electric Power Research Institute, U.S. Nuclear Regulatory Commission, and members of the José Cabrera Nuclear Power Station (Zorita) in Spain. The bi-crystalline micro-tensile specimens, atom probe tomography (APT) tips, and transmission electron microscopy (TEM) lamellae were fabricated from the baffle plate materials irradiated to 0.05, 15 and 50 dpa to elucidate microstructural, microchemical, and local mechanical properties changes as a function of dose. TEM and APT studies reveal radiation induced Ni, Cr, and Si rich precipitates in the 15 dpa sample that become smaller and partially redissolve into the matrix of the 50 dpa sample (decreasing size and number density). Dislocation loop and cavity number density and size were quantified as a function of dose as well as swelling. Intergranular Ni and Si enrichments with concomitant Fe and Cr depletion were observed in the 15 dpa sample and were more pronounced in the 50 dpa sample. Micro-tensile testing performed in the scanning electron microscope (SEM) at room temperature and 300 °C shows that the material's local yield strength and ultimate tensile strength decreases with increased dose and elevated test temperature and provides further insights via localized strain mapping. Current and previous mechanical data was compared with calculated values using the dispersed barrier hardening model with inputs of dislocation loops, precipitates, and cavities from microstructural characterization.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Correlative electron and ion beam analysis of the electrochemical performances of LiV 3 O 8 cathode films as a function of microstructures

Degradation mechanisms in LiV 3 O 8 cathode films (~500 nm) with different initial microstructures i.e., globular nanocrystals in amorphous matrix and needle-like nanocrystals, synthesized by annealing the cathodes at 150 °C and 300 °C for 6 h are studied by Transmission Electron Microscopy (TEM) and Auger Electron Spectroscopy (AES). In addition, a unique in-situ combination of TEM and Secondary Ion Mass Spectrometry (SIMS) imaging techniques, namely Parallel Ion and Electron beam Spectrometry (PIES) is carried out to measure the 3D distribution of V and Li with nanoscale resolution. These characterization studies focus on correlating the pre- and post-cycling microstructure to observed electrochemical performance. The LiV 3 O 8 cathode film with needle-like nanocrystals (300 °C) shows a higher initial capacity but it degrades rapidly compared to the film with globular nanocrystals embedded in amorphous matrix (150 °C). We observed that LiV 3 O 8 films with needle-like nanocrystals are more susceptible to cathode decohesion and vanadium dissolution than the films with globular nanocrystals embedded in amorphous matrix, explaining the differences in their electrochemical performance. The findings from this study have relevance to the development of thin film electrode microstructures for high capacity and cyclic stability.

25 ENERGY STORAGE↗
DOE OSTI2025

High spatial resolution neutron imaging of lithium-ion batteries: Correlating microstructure and lithium transport

Thick electrodes for lithium-ion batteries can increase the overall energy density, but increasing the electrode thickness introduces charge transport limitations. These limitations may be mitigated through proper electrode structuring. Here, high spatial resolution neutron imaging was used to understand the correlation between microstructure and lithium transport in lithium-ion anodes. Batteries with distinct graphite anode microstructures were produced and studied with high spatial resolution in operando neutron radiography to observe the effects of structure on transport. High spatial resolution neutron computed tomography was performed following in operando neutron radiography. X-ray computed tomography and scanning electron microscopy were used to observe the finer scale anode structure to complement neutron imaging. Solvent-free anodes containing a tightly-packed layered structure confined lithium movement close to the separator. This structure limited capacity, but supported better rate capability. Conversely, a more open pore structure in the wet cast anodes yielded higher capacity with reduced rate capability. Together, these results show that lithium distributions can be controlled by the macroscopic structure of the electrodes, the microstructural pore network, and the microscale active areas that support electrochemical reactions. Furthermore, multimodal imaging applying the complementary strengths of neutron and X-ray methods is shown as a tool for advancing battery design.

25 ENERGY STORAGE↗
DOE OSTI2022

Local residual stresses and microstructure within recrystallizing grains in iron

The intragranular strains and the microstructure within recrystallizing grains in single phase pure iron have been systematically studied in 3D using synchrotron micro-diffraction. In contradiction to common knowledge we observe that residual elastic strains of up to 1–2 × 10 –3 are present in the recrystallizing grains. The local strain variations within individual grains can be similar in magnitude to those between different grains. The effects of processing parameters, including rolling reduction, recrystallized volume fraction, and cooling rate, as well as microstructural parameters, including grain size, orientation and internal misorientation, on the development of local residual elastic strains and microstructure have been quantified. It is suggested that the difference in local defect density between recrystallized grains and the surrounding deformed matrix, as well as the redistribution of medium to long-range residual stresses in the deformed grains, are the main reasons for the development of such strains in the recrystallized grains. The local residual stress levels are calculated and their possible impact on the mechanical properties and recrystallization processes are discussed.

36 MATERIALS SCIENCE↗
DOE OSTI2026

Influence of fabrication on microstructure and heat affected zone width in weldments of nuclear reactor pressure vessel steel

Advanced manufacturing routes such as electron beam welding and powder metallurgy with hot isostatic pressing are increasingly used across energy and aerospace industries, where the reliable prediction of weld behavior and heat affected zone (HAZ) evolution is critical. This study examines how fabrication routes and post-weld heat treatments influence phase distribution, crystallite size, microstrain, and dislocation density in nuclear reactor pressure vessel steels using synchrotron X-ray diffraction (SXRD). Retained austenite occurs only in samples that did not undergo austenitization, whereas an austenitizing heat treatment fully eliminates retained austenite and produces a more uniform microstructure across the weldment in terms of phase fraction, dislocation density, and microstrain. The Rosenthal solution underestimates the HAZ width for powder metallurgy samples. A newly proposed modified Rosenthal solution, reducing density by accounting for porosity, matches the SXRD-measured HAZ width with a 0.65% error. Structure–property correlations reveal that dislocation density correlates strongly with nanohardness in homogenous microstructures, while in heterogenous weldments nanohardness is further influenced by the presence of dissimilar phase boundaries. These findings provide new insight into the thermal and microstructural response of powder metallurgy fabricated steels and offer a framework for optimizing welding procedures and heat treatments in advanced manufacturing applications.

73 NUCLEAR PHYSICS AND RADIATION PHYSICS↗
DOE OSTI2026

Controlling homogenization length scales and microstructure in additively manufactured Ti-Ta functionally graded materials

Materials with smooth compositional gradients or functionally grade materials (FGMs) produced via additive manufacturing (AM), enables joining dissimilar materials and optimizing multiple properties in advanced engineering applications. However, as-printed AM microstructures exhibit micro-segregation and solidification defects which, when combined with controlling macroscale gradient properties, complicates necessary post-processing. Here, we use CALPHAD-informed diffusion modelling to design post-processing heat treatments for lightweight to refractory FGMs. Ti-Ta (0 to 85 at. % Ta) FGMs were fabricated using laser-based directed energy deposition AM. Post-processing heat treatments at 1000° C and 1500° C were designed to promote homogenization across specific length scales and experimentally validated. Investigation of chemical segregation and microstructures demonstrated that the length scale of homogenization is controlled as a function of time, temperature, and local composition. Ta-rich regions exhibited incomplete homogenization compared to Ti-rich layers. Unmelted Ta particles were found to completely dissolve at 1500 °C. By controlling cooling rate (200 °C/min), martensitic structures were produced between 14–36 at. % Ta, consistent with martensite-start temperatures calculations, while furnace cooling (2 °C/min) produced α+β morphologies. This work establishes a validated predictive framework for designing post-processing to tailor microstructure and chemical architecture in AM FGMs, facilitating their deployment in demanding environments.

Materials science↗
DOE OSTI2023

Heterogeneous microstructural evolution during hydrodynamic penetration of a high-velocity copper microparticle impacting copper

Microparticle hydrodynamic penetration (HDP) may be associated with the erosion regime in cold spray processing and other high-velocity impact events. Here, in an experimental approach where we can individually launch particles and study the impact sites, we explore copper microparticles impacted on copper substrates at velocities above 900 m/s where HDP begins. We lift cross-sectional lamellae from the impact sites with a focused-ion beam for further microstructural characterization using electron backscatter diffraction and scanning transmission electron microscopy. Due to the gradients of strain, strain rate, and temperature associated with HDP, heterogeneous microstructures result. The structural evolution processes observed include deformation twinning and multiple dislocation-mediated grain recrystallization mechanisms—geometric dynamic recrystallization (gDRX), discontinuous DRX (dDRX), and meta DRX (mDRX). The higher strains at the interface lead to the most significant structural changes and complex mechanisms. In contrast, there is a gradient to more conventional dislocation plasticity away from the interface (on either the particle or substrate side). Here, these microstructural observations are consistent with the deformation map for copper and extend the observations of impact-induced recrystallization across new regimes of behavior.

Cold spray process↗
DOE OSTI2022

Microstructural evolution and strengthening mechanisms in a heat-treated additively manufactured Al–Cu–Mn–Zr alloy

In this report the microstructural and strength evolution of an additively manufactured Al-8.6Cu-0.5Mn-0.9Zr alloy upon aging at 300, 350, and 400 °C is investigated. The strengthening phases of the alloy evolve significantly upon aging, with breakdown and spheroidization of the interconnected θ-Al 2 Cu network, dissolution of metastable θ'-Al 2 Cu precipitates, and precipitation of nanometric L1 2 -Al 3 Zr from a matrix supersaturated in Zr. In the peak-aged states, the alloy displays a favorable combination of strength and ductility, with a room-temperature yield strength of 314–341 MPa and ductility of 11–13%. The measured yield strengths for microstructures with different aging treatments are compared to predictions of yield strengths from grain boundary, solid solution, and particle strengthening contributions. The observed strain hardening behavior is related to fundamental precipitate and dislocation interactions. Comparison between predicted and measured strength values indicates a continued need for strengthening models specifically developed for the heterogeneous microstructures of additively manufactured alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2022

The effects of microstructure on deformation twinning in Mg WE43

The interplay between microstructure and deformation twinning in a WE43-T6 Mg alloy under uniaxial compression was investigated using a combination of scanning electron microscopy with digital image correlation (SEM-DIC) and crystal plasticity finite element (CPFE) simulation. To improve understanding of the statistical characteristics of deformation twin formation, microstructural effects were characterized in over 1000 grains through metrics including the nominal Schmid Factor, grain size, geometric compatibility factor (m'), residual Burgers vector, and the strain accommodated by neighboring grains. There was a strong correlation between the nominal Schmid Factor and both twin activation and variant selection, but this was not fully deterministic. Deformation twinning also exhibited a strong dependence on existing slip and twinning in the neighboring grain and on the m' value. Within the range of grain sizes present in this condition, grain size was determined to have minimal effect on deformation twinning. Finally, statistical analysis of CPFE simulations was used to further investigate microstructural effects on twinning, and qualitatively captured the effect of the nominal Schmid Factor.

36 MATERIALS SCIENCE↗