Fractography of composite delamination
The microdamage that occurs for Mode 1 and Mode 2 delamination was examined by potting delaminated specimens in a clear epoxy, sectioning through the damage, polishing the cut sections and examining using light microscopy. For Mode 1 delamination of unidirectional carbon fiber reinforced plastic (CFRP) composites, the major observation was fiber bridging including large ligaments of fiber bundles. The Mode 2 delamination of unidirectional laminates revealed a very narrow crack opening with only occasional fiber bridging. Impact testing by repetitive impacts with increasing energy was studied and it was found that this technique does not discern changes in the type of damage with increasing cumulative impact energy. Instead, the changes in the impact response, notably stiffness, are the result of changes in the extent of damage. For laminates with a brittle thermoplastic matrix, 3501-6, there were distinct changes in stiffness that corresponded to the development of through the thickness damage and then to the extension of the damage to the specimen edges. For PEEK and polycarbonate, the changes in stiffness were not as abrupt as for the thermoset. None the less, the damage progressed in the same manner.