Crack growth in single-crystal silicon

Crack growth in single-crystal silicon at room temperature in air was evaluated by double torsion (DT) load-relaxation method and monitored by acoustic emission (AE) technique. Both DT and AE methods indicated lack of subcritical crack growth in silicon. At the critical stress intensity factor, the crack front was found to be jumping several times in a 'mirror' region and then followed by fast crack growth in a 'hackle' region. Hackle marks were found to be associated with plastic deformation at the tip of the fast moving crack. No dislocation etch pits were found in the 'mirror' region, in which crack growth may result from interatomic bonds broken at the crack tip under stress without any plastic deformation. Acoustic emission appears to be spontaneously generated from both interatomic bonds broken and dislocation generation at the moving crack tip during the crack growth in single-crystal silicon.

Chen, C. P.↗

Design, Processing, and Properties of WTaCrV-Hf Multi-principal Element Alloys

Refractory multi-principal element alloys are candidates for high-temperature structural components due, in part, to their high strength and high melting points. Single-phase materials are initially preferred for isotropic material properties as a function of time and temperature in service conditions. This work outlines a computational rank-ordering and experimental validation methodology for single-phase body-centered-cubic phase stability in WTaCrV-Hf alloys using order–disorder transition temperature. Eight compositions were fabricated by arc-melting and heat-treated at 1400 °C for 24 hrs. X-ray diffraction, energy-dispersive x-ray spectroscopy, and Vickers hardness testing showed alloys with order–disorder transition temperatures below 600 °C formed a single-phase body-centered-cubic structure during solidification and remained single-phase after heat-treatment. The sample possessing the lowest order–disorder transition temperature exhibited slip traces suggestive of room-temperature plastic deformation under Vickers indentation, with both heat-treated single-phase samples exhibiting hardnesses over 800 HV with little cracking compared to tungsten. These results establish order–disorder transition temperature as a viable predictive parameter for multi-principal element alloy phase stability. The methodology outlined in this work provides a framework for future design, fabrication, and characterization of high-temperature structural multi-principal element alloys.

CALPHAD↗

Analysis of fatigue, fatique-crack propagation, and fracture data

Analytical methods have been developed for consolidation of fatigue, fatigue-crack propagation, and fracture data for use in design of metallic aerospace structural components. To evaluate these methods, a comprehensive file of data on 2024 and 7075 aluminums, Ti-6A1-4V, and 300M and D6Ac steels was established. Data were obtained from both published literature and unpublished reports furnished by aerospace companies. Fatigue and fatigue-crack-propagation analyses were restricted to information obtained from constant-amplitude load or strain cycling of specimens in air at room temperature. Fracture toughness data were from tests of center-cracked tension panels, part-through crack specimens, and compact-tension specimens.

Jaske, C. E.↗

Insulation Resistance and Leakage Currents in Low-Voltage Ceramic Capacitors with Cracks

Measurement of insulation resistance (IR) in multilayer ceramic capacitors (MLCCs) is considered a screening technique that ensures the dielectric is defect-free. This work analyzes the effectiveness of this technique for revealing cracks in ceramic capacitors. It is shown that absorption currents prevail over the intrinsic leakage currents during standard IR measurements at room temperature. Absorption currents, and consequently IR, have a weak temperature dependence, increase linearly with voltage (before saturation), and are not sensitive to the presence of mechanical defects. In contrary, intrinsic leakage currents increase super-linearly with voltage and exponentially with temperature (activation energy is in the range from 0.6 eV to 1.1 eV). Leakage currents associated with the presence of cracks have a weaker dependence on temperature and voltage compared to the intrinsic leakage currents. For this reason, intrinsic leakage currents prevail at high temperatures and voltages, thus masking the presence of defects.

testing↗

Durability and Design Issues of Thermal/environmental Barrier Coatings on Sic/sic Ceramic Matrix Composites Under 1650 C Test Conditions

Ceramic thermal/environmental barrier coatings for SiC-based ceramics will play an increasingly important role in future gas turbine engines because of their ability to effectively protect the engine components and further raise engine temperatures. However, the coating durability remains a major concern with the ever-increasing temperature requirements. Currently, advanced T/EBC systems, which typically include a high temperature capable zirconia- (or hahia-) based oxide top coat (thermal barrier) on a less temperature capable mullite/barium-strontium-aluminosilicate (BSAS)/Si inner coat (environmental barrier), are being developed and tested for higher temperature capability Sic combustor applications. In this paper, durability of several thermal/environmental barrier coating systems on SiC/SiC ceramic matrix composites was investigated under laser simulated engine thermal gradient cyclic, and 1650 C (3000 F) test conditions. The coating cracking and delamination processes were monitored and evaluated. The effects of temperature gradients and coating configurations on the ceramic coating crack initiation and propagation were analyzed using finite element analysis (FEA) models based on the observed failure mechanisms, in conjunction with mechanical testing results. The environmental effects on the coating durability will be discussed. The coating design approach will also be presented.

Zhu, Dong-Ming↗

"Ultra"-Fast Fracture Strength of Advanced Structural Ceramic Materials Studied at Elevated Temperatures

The accurate determination of inert strength is important in reliable life prediction of structural ceramic components. At ambient temperature, the inert strength of a brittle material is typically regarded as free of the effects of slow crack growth due to stress corrosion. Therefore, the inert strength can be determined either by eliminating active species, especially moisture, with an appropriate inert medium, or by using a very high test rate. However, at elevated temperatures, the concept or definition of the inert strength of brittle ceramic materials is not clear, since temperature itself is a degrading environment, resulting in strength degradation through slow crack growth and/or creep. Since the mechanism to control strength is rate-dependent viscous flow, the only conceivable way to determine the inert strength at elevated temperatures is to utilize a very fast test rate that either minimizes the time for or eliminates slow crack growth. Few experimental studies have measured the elevated-temperature, inert (or "ultra"-fast fracture) strength of advanced ceramics. At the NASA Lewis Research Center, an experimental study was initiated to better understand the "ultra"-fast fracture strength behavior of advanced ceramics at elevated temperatures. Fourteen advanced ceramics - one alumina, eleven silicon nitrides, and two silicon carbides - have been tested using constant stress-rate (dynamic fatigue) testing in flexure with a series of stress rates including the "ultra"-fast stress rate of 33 000 MPa/sec with digitally controlled test frames. The results for these 14 advanced ceramics indicate that, notwithstanding possible changes in flaw populations as well as flaw configurations because of elevated temperatures, the strength at 33 000 MPa/sec approached the room-temperature strength or reached a higher value than that determined at the conventional test rate of 30 MPa/sec. On the basis of the experimental data, it can be stated that the elevated-temperature, inert strength of an advanced ceramic material can be defined as the strength where no slow crack growth takes place at the temperature.

Choi, Sung R.↗

Grain-boundary fracture mechanisms in Li 7 La 3 Zr 2 O 12 (LLZO) solid electrolytes: When phase transformation acts as a temperature-dependent toughening mechanism

Garnet-type, solid electrolytes, such as Li 7 La 3 Zr 2 O 12 (LLZO), are a promising alternative to liquid electrolytes for lithium-metal batteries. However, such solid-electrolyte materials frequently exhibit undesirable lithium (Li) metal plating and fracture along grain boundaries. In this work, we employ atomistic simulations to investigate the mechanisms and key fracture properties associated with intergranular fracture along one such boundary. Our results show that, in the case of a Σ5 (310) grain boundary, this boundary exhibits brittle fracture behavior, i.e. the absence of dislocation activity ahead of the propagating crack tip, accompanied with a decrease in work of separation, peak stress, and maximum stress intensity factor as the temperature increases from 300 K to 1500 K. As the crack propagates, we predict two temperature-dependent Li clustering regimes. For temperatures at or below 900 K, Li tends to cluster in the bulk region away from the crack plane driven by a void-coalescence mechanism concomitant a simultaneous cubic-to-tetragonal phase transition. The tetragonalization of LLZO in this temperature regime acts as an emerging toughening mechanism. At higher temperatures, this phase transition mechanism is suppressed leading to a more uniform distribution of Li throughout the grain-boundary system and lower fracture properties as compared to lower temperatures.

36 MATERIALS SCIENCE↗

Solid rocket motor nozzles

The steps in the nozzle design process are examined. The nozzle designer's role in defining design requirements and constraints is included along with discussions of each of the three basic phases of the nozzle design process itself: (1) aerodynamic design, in which the gas-contacting surfaces are configured to produce the required performance within the envelope limits; (2) thermal design, in which termal liners and thermal insulators are selected and configured to maintain the surfaces as closely as practical against effects of erosion and to limit the structure temperature to acceptable levels; and (3) structural design, in which materials are selected and configured to support the thermal components and to sustain the predicted loads. Analytical techniques that are used to establish thermal and structural design integrity and to predict nozzle performance are discussed along with methods for nozzle quality assurance. Emphasis is placed on nozzle design and materials for modern high-temperature aluminized propellants. Recurring nozzle design problems of graphite cracking and ejection, differential erosion at material interfaces, lack of sufficient proven nondestructive testing (NDT) techniques, the uncertainty of adhesive bonding, and inadequate definition of material properties, particularly at high temperatures are considered.

Ellis, R. A.↗

Thermal High- and Low-Cycle Fatigue Behavior of Thick Thermal Barrier Coating Systems

Ceramic thermal barrier coatings have received increasing attention for advanced gas turbine and diesel engine applications because of their ability to provide thermal insulation to engine components. However, the durability of these coatings under the severe thermal cycling conditions encountered in a diesel engine (ref. 1) still remains a major issue. In this research at the NASA Lewis Research Center, a high-power laser was used to investigate the thermal fatigue behavior of a yttria-stabilized zirconia coating system under simulated diesel engine conditions. The mechanisms of fatigue crack initiation and propagation, and of coating failure under complex thermal low-cycle fatigue (LCF, representing stop/start cycles) and thermal high-cycle fatigue (HCF, representing operation at 1300 rpm) are described. Continuous wave and pulse laser modes were used to simulate pure LCF and combined LCF/HCF, respectively (ref. 2). The LCF mechanism was found to be closely related to the coating sintering and creep at high temperatures. These creep strains in the ceramic coating led to a tensile stress state during cooling, thus providing the major driving force for crack growth under LCF conditions. The combined LCF/HCF tests induced more severe coating surface cracking, microspallation, and accelerated crack growth than did the pure LCF test. HCF thermal loads also facilitated lateral crack branching and ceramic/bond coat interface delaminations. HCF is associated with the cyclic stresses originating from the high-frequency temperature fluctuation at the ceramic coating surface. The HCF thermal loads act on the crack by a wedging mechanism (ref. 1), resulting in continuous crack growth at temperature. The HCF stress intensity factor amplitude increases with the interaction depth and temperature swing, and decreases with the crack depth. HCF damage also increases with the thermal expansion coefficient and the Young's modulus of the ceramic coating (refs. 1 and 3).

Miller, Robert A.↗

Frequency effect on the fatigue life of a laminated composite

Effects of load frequency on the fatigue behavior of notched (+ or - 45 deg)2s laminated graphite/epoxy composites are investigated. Experimental results are obtained using four frequencies at three load levels. Temperature rises near the center hole are also measured. It is found that when temperature increase during the fatigue test is small, fatigue life increases as the load frequency increases. However, an increase in the near hole temperature results in a reduction in fatigue life. A theoretical model based upon crack propagation in viscoelastic media is presented. The model is modified to account for the temperature effect.

Sun, C. T.↗

A FEASIBILITY STUDY ON CRACK REPAIR IN AUSTENITIC STAINLESS STEEL DRY STORAGE CANISTERS USING ISOTHERMAL FRICTION STIR WELDING

In recent time, solid state crack repair techniques in spent nuclear fuel dry storage canisters (SNF-DSC) have garnered significant interest. Plates of austenitic stainless steels are usually arc welded to fabricate the cylindrical canisters which are prone to chloride-induced stress corrosion cracking. Friction stir welding (FSW) is considered to be a potential candidate for damage repair. In this work, electrical discharge machining was used to simulate cracks in 304L stainless steel plates of 12.7 mm thickness. Subsequently, isothermal FSW was carried out at two different temperatures (725 and 825°C) in order to repair the simulated crack. Microstructure-mechanical property correlations in FSWed plates were studied in detail. Significant grain refinement observed in the stir zone (SZ) was attributed to dynamic recrystallization occurring during FSW. A comparison of Vickers microhardness showed higher hardness and homogeneity in the 725°C SZ than its 825°C counterpart. The fraction of S3 boundary is found to be low in the SZ as compared to base metal (BM). Yield strength of the joints was found to be approximately 100 MPa higher than that of the BM accompanied by a drop in ductility by a factor of 2. Residual stress profile across 825°C weld was measured using x-ray diffraction.

Bhattacharyya, Madhumanti↗

Damage Accumulation in SiC/SiC Composites with 3D Architecture

Matrix cracking in Sic fiber reinforced, melt-infiltrated Sic composites with 3D orthogonal architectures was determined for specimens tested in tension at room temperature. Acoustic emission (AE) was used to monitor the matrix cracking activity and was later confirmed by microscopic examination of specimens that had failed. Exact location of AE demonstrated that initial cracking occurred in the matrix rich regions when a large z-direction fiber bundle was used. For specimens with large z-direction fiber tows, the earliest matrix cracking could occur at half the stress for standard 2D woven composites with similar constituents.

Yun, Hee-Mann↗

Use of Slow Strain Rate Tensile Testing to Assess the Ability of Several Superalloys to Resist Environmentally-Assisted Intergranular Cracking

Intergranular fatigue crack initiation and growth due to environmental degradation, especially at notched features, can often limit the fatigue life of disk superalloys at high temperatures. For clear comparisons, the effects of alloy composition on cracking in air needs to be understood and compared separately from variables associated with notches and cracks such as effective stress concentration, plastic flow, stress relaxation, and stress redistribution. The objective of this study was to attempt using simple tensile tests of specimens with uniform gage sections to compare the effects of varied alloy composition on environment-assisted cracking of several powder metal and cast and wrought superalloys including ME3, LSHR, Udimet 720(TradeMark) ATI 718Plus(Registered TradeMark) alloy, Haynes 282(Trademark), and Inconel 740(TradeMark) Slow and fast strain-rate tensile tests were found to be a useful tool to compare propensities for intergranular surface crack initiation and growth. The effects of composition and heat treatment on tensile fracture strain and associated failure modes were compared. Environment interactions were determined to often limit ductility, by promoting intergranular surface cracking. The response of various superalloys and heat treatments to slow strain rate tensile testing varied substantially, showing that composition and microstructure can significantly influence environmental resistance to cracking.

fatigue(materials)↗

Slow Strain Rate Tensile Testing to Assess the Ability of Superalloys to Resist Environment-Assisted Intergranular Cracking

Intergranular fatigue crack initiation and growth due to environmental degradation, especially at notched features, can often limit the fatigue life of disk superalloys at high temperatures. For clear comparisons, the effects of alloy composition on cracking in air needs to be understood and compared separately from variables associated with notches and cracks such as effective stress concentration, plastic flow, stress relaxation, and stress redistribution. The objective of this study was to attempt using simple tensile tests of specimens with uniform gage sections to compare the effects of varied alloy composition on environment-assisted cracking of several powder metal and cast and wrought superalloys including ME3, LSHR, Udimet 720, ATI 718Plus alloy, Haynes 282, and Inconel 740. Slow and fast strain-rate tensile tests were found to be a useful tool to compare propensities for intergranular surface crack initiation and growth. The effects of composition and heat treatment on tensile fracture strain and associated failure modes were compared. Environment interactions were determined to often limit ductility, by promoting intergranular surface cracking. The response of various superalloys and heat treatments to slow strain rate tensile testing varied substantially, showing that composition and microstructure can significantly influence environmental resistance to cracking.

Heat resistant alloys↗

Modeling brittle fracture due to anisotropic thermal expansion in polycrystalline materials

Here, this work investigated brittle fracture of polycrystalline materials due to thermal stresses arising from anisotropic thermal expansion. We used phase-field fracture simulations with the properties of alpha-uranium (α-U) and assumed a linear elastic mechanical response. Three-dimensional simulations were used to predict fracture for various conditions and crystallographic textures. We found that fracture was more pronounced during cooling than during heating because the anisotropy increased with temperature. We also found that the total crack surface area increased with increasing average misorientation, while the net shape change of the material decreased with increasing misorientation. Two-dimensional simulations in which one crystallographic coefficient of thermal expansion (CTE) was set to zero indicated that the expansion behavior in the crystallographic direction with the smallest CTE was the primary cause of fracture.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

A defect-resistant Co–Ni superalloy for 3D printing

Abstract Additive manufacturing promises a major transformation of the production of high economic value metallic materials, enabling innovative, geometrically complex designs with minimal material waste. The overarching challenge is to design alloys that are compatible with the unique additive processing conditions while maintaining material properties sufficient for the challenging environments encountered in energy, space, and nuclear applications. Here we describe a class of high strength, defect-resistant 3D printable superalloys containing approximately equal parts of Co and Ni along with Al, Cr, Ta and W that possess strengths in excess of 1.1 GPa in as-printed and post-processed forms and tensile ductilities of greater than 13% at room temperature. These alloys are amenable to crack-free 3D printing via electron beam melting (EBM) with preheat as well as selective laser melting (SLM) with limited preheat. Alloy design principles are described along with the structure and properties of EBM and SLM CoNi-base materials.

36 MATERIALS SCIENCE↗

Demonstrate new plasticity models for doped UO 2 that capture dislocation mechanisms

In light water reactors, fuel vendors are investigating the use of dopants to modify the properties of UO 2 pellets, with the goal of improving pellet-cladding mechanical interactions during operation. Dopants are expected to ‘soften’ the pellets; that is, the doped pellets have higher plastic deformation than conventional UO 2 . This leads to a reduction in the severity of mechanical pellet-cladding interactions, helping to reduce the hoop strain on the cladding. By minimizing the strain exerted by the pellet on the cladding, it is anticipated that cladding performance under accident conditions can be enhanced (i.e., lowering the risk of burst during a LOCA). Dopants such as chromium (Cr) promote grain growth during pellet fabrication, leading to larger grains; therefore, understanding the link between chemistry, microstructure and mechanical deformation (enhanced creep rates) behavior of UO 2 is critical to helping operators further substantiate the benefits of doping UO 2 . Historically, the nuclear energy industry has relied on empirical models to make assessments of performance. Compared to empirical models, mechanistic physics-based models provide benefits, such as, fewer data points for validation and better extrapolation where experimental data is scarce or non-existent. In this report, Bayesian inference techniques have been applied to a previously developed lower length-scale-informed diffusional creep model. The objective is to i) infer lower-length-scale parameter distributions from available experiment and then ii) determine the uncertainties in the measurable quantity (in this case creep rates) after propagating the inferred lower length scale parameter uncertainties. The approach requires many evaluations of the model, which becomes computationally insurmountable; therefore, a neural-network model is trained to data obtained by sampling the full model over the most important parameters. This neural-network is then used in the Bayesian inference approach to determine probability distributions in the parameter values that represent the uncertainty in the model given what is known from the experiments (posterior). A significant reduction compared to conservative initial (prior) uncertainties is achieved through inference against the experimental data, demonstrating the efficacy of this approach. Furthermore, by accounting for uncertainties in the experimental conditions and sample non-stoichiometry, it is possible to resolve apparent discrepancies in experimental measurements within a self-consistent grain boundary (Coble) creep model that is sensitive to chemistry. This work has been written up and submitted to Nuclear Technology for a special issue on accelerated fuel qualification (AFQ). This uncertainty quantification (UQ) work not only improves the diffusional model, while accounting for uncertainty, but also establishes a framework which can readily be applied to the mechanistic models of dislocation deformation developed in this study. The most likely values from the Bayesian analysis are incorporated into our UO 2 diffusional creep model and a lower length scale-informed irradiation UO 2 creep mechanistic model to generate a dataset. This dataset has been provided to our INL collaborators for training an artificial neural network surrogate model, which will be implemented in the BISON fuel performance code to assess how the results differ from those currently obtained using a fully empirical model and that of using the nominal (uncalibrated) atomic scale parameters in our mechanistic model. Plastic deformation (creep and glide) in UO 2 is a complex phenomenon, governed by multiple underlying processes such as local defect concentrations, applied stresses, and microstructural characteristics. Consequently, there is a need for a meso-scale model with polycrystalline resolution capable of extrapolating to large grain sizes applicable to doped UO 2 , where data is limited and the model can help bridge the knowledge gap. By integrating atomistic data into the polycrystal LApx code, it becomes possible to predict dislocation climb and glide plasticity that simple analytical models cannot accurately represent. The application of atomic-scale data within LApx demonstrated the importance of climb and glide mechanisms in reproducing high-stress UO 2 behavior. Behaviors such as this are crucial to capture and implement in BISON, as parts of the fuel pellet can reach temperatures where glide can occur before pellet cracking. This model which captures dislocation based mechanisms for UO 2 is then used to stand up the doped model accounting for larger grain sizes. It was found that larger grain sizes can lead to enhanced deformation rates in the glide regime, and therefore can help with the pellet cladding mechanical interaction. Therefore if the fuel pellet reaches conditions (stress/temperature) where glide is active, the enhanced creep rates for larger grains in the glide regime (doped UO 2 ) can help with pellet cladding mechanical interactions. Plastic deformation in UO 2 involves multiple mechanisms, including diffusional creep, dislocation climb, and glide. This milestone contains two parts: (1) UQ of a pre-existing lower length scale informed mechanistic diffusional creep model, and (2) development of a new LApx based model for dislocation-mediated creep mechanisms in UO 2 , with application to large-grain doped UO 2 .

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗