Improved damage tolerance of titanium by adhesive lamination

Basic damage tolerance properties of Ti-6A1-4V titanium plate can be improved by laminating thin sheets of titanium with adhesives. Compact tension and center cracked tension specimens made from thick plate, thin sheet, and laminated plate (six plies of thin sheet) were tested. The fracture toughness of the laminated plate was 39 percent higher than the monolithic plate. The laminated plate's through the thickness crack growth rate was about 20 percent less than that of the monolithic plate. The damage tolerance life of the surface cracked laminate was 6 to over 15 times the life of a monolithic specimen. A simple method of predicting crack growth in a crack ply of a laminate is presented.

Johnson, W. S.↗

Damage tolerance evaluation of adhesively laminated titanium

Basic damage tolerance properties of Ti-6A1-4V titanium plate can be improved by laminating thin sheets of titanium with adhesives. Compact tension and center cracked tension specimens made from thick plate, thin sheet, and laminated plate (six plies of thin sheet) were tested. The fracture toughness of the laminated plate was 39 percent higher than the monolithic plate. The laminated plate's through the thickness crack growth rate was about 20 percent less than that of the monolithic plate. The damage tolerance life of the surface cracked laminate was 6 to over 15 times the life of a monolithic specimen. A simple method of predicting crack growth in a crack ply of a laminate is presented. Previously announced in STAR as N82-33737

Johnson, W. S.↗

Triboluminescent Materials for Smart Optical Damage Sensors for Space Applications

Triboluminescence is light that is produced by pressure, friction or mechanical shock. New composite materials are constantly being reengi neered in an effort to make lightweight spacecrafts for various NASA missions. For these materials there is interest in monitoring the con dition of the composite in real time to detect any delamination or cr acking due to damage, fatigue or external forces. Methods of periodic inspection of composite structures for mechanical damage such as ult rasonic testing are rather mature. However, there is a need to develop a new technique of damage detection for composites, which could dete ct cracking or delamination from any desired location within a materi al structure in real time. This could provide a valuable tool in the confident use of composite materials for various space applications. Recently, triboluminnescent materials have been proposed as smart sen sors of structural damage. To sense the damage, these materials can b e epoxy bonded or coated in a polymer matrix or embedded in a composi te host structure. When the damage or fracture takes place in the hos t structure, it will lead to the fracture of triboluminescent crystal s resulting in a light emission. This will warn, in real time, that a structural damage has occurred. The triboluminescent emission of the candidate phosphor has to be sufficiently bright, so that the light signal reaching from the point of fracture to the detector through a fiber optic cable is sufficiently strong to be detected. There are a large number of triboluminescent materials, but few satisfy the above criterion. Authors have synthesized a Eu based organic material know n as Europium tetrakis (dibenzoylmethide) triethylammonium .(EuD(sub 4)TEA), one of the bright triboluminescent materials, which is a pote ntial candidate for application as a damage sensor and could be made into a wireless sensor with the addition of microchip, antenna and el ectronics. Preliminary results on the synthesis and characterization of this material shall be presented.

Aggarwal, Mohan D.↗

Experimental and analytical study of fatigue damage in notched graphite/epoxy laminates

Fatigue damage development in notched graphite/epoxy laminates is investigated in both compression and tension, with tested specimens being examined for damage type and location using light microscopy, scanning electron microscopy, ultrasonic C-scans, and X-radiography. Delamination and ply cracking were found to be the dominant types of fatigue damage. Comparison of observed delamination locations with finite element calculations indicates that both interlaminar shear and peel stresses must be considered when predicting delamination. Fatigue loading generally caused only small stiffness losses, and residual strengths were in all cases greater than, or equal to, the virgin strengths.

Whitcomb, J. D.↗

Analysis of the progressive failure of brittle matrix composites

This report investigates two of the most common modes of localized failures, namely, periodic fiber-bridged matrix cracks and transverse matrix cracks. A modification of Daniels' bundle theory is combined with Weibull's weakest link theory to model the statistical distribution of the periodic matrix cracking strength for an individual layer. Results of the model predictions are compared with experimental data from the open literature. Extensions to the model are made to account for possible imperfections within the layer (i.e., nonuniform fiber lengths, irregular crack spacing, and degraded in-situ fiber properties), and the results of these studies are presented. A generalized shear-lag analysis is derived which is capable of modeling the development of transverse matrix cracks in material systems having a general multilayer configuration and under states of full in-plane load. A method for computing the effective elastic properties for the damaged layer at the global level is detailed based upon the solution for the effects of the damage at the local level. This methodology is general in nature and is therefore also applicable to (0(sub m)/90(sub n))(sub s) systems. The characteristic stress-strain response for more general cases is shown to be qualitatively correct (experimental data is not available for a quantitative evaluation), and the damage evolution is recorded in terms of the matrix crack density as a function of the applied strain. Probabilistic effects are introduced to account for the statistical nature of the material strengths, thus allowing cumulative distribution curves for the probability of failure to be generated for each of the example laminates. Additionally, Oh and Finney's classic work on fracture location in brittle materials is extended and combined with the shear-lag analysis. The result is an analytical form for predicting the probability density function for the location of the next transverse crack occurrence within a crack bounded region. The results of this study verified qualitatively the validity of assuming a uniform crack spacing (as was done in the shear-lag model).

Thomas, David J.↗

Multi-Layer Laminated Thin Films for Inflatable Structures

Special-purpose balloons and other inflatable structures would be constructed as flexible laminates of multiple thin polymeric films interspersed with layers of adhesive, according to a proposal. In the original intended application, the laminate would serve as the envelope of the Titan Aerobot a proposed robotic airship for exploring Titan (one of the moons of Saturn). Potential terrestrial applications for such flexible laminates could include blimps and sails. In the original application, the multi-layered laminate would contain six layers of 0.14-mil (0.0036-mm)-thick Mylar (or equivalent) polyethylene terephthalate film with a layer of adhesive between each layer of Mylar . The overall thickness and areal density of this laminate would be nearly the same as those of 1-mil (0.0254-mm)-thick monolayer polyethylene terephthalate sheet. However, the laminate would offer several advantages over the monolayer sheet, especially with respect to interrelated considerations of flexing properties, formation of pinholes, and difficulty or ease of handling, as discussed next. Most of the damage during flexing of the laminate would be localized in the outermost layers, where the radii of bending in a given bend would be the largest and, hence, the bending stress would be the greatest. The adverse effects of formation of pinholes would be nearly completely mitigated in the laminate because a pinhole in a given layer would not propagate to adjacent layers. Hence, the laminate would tend to remain effective as a barrier to retain gas. Similar arguments can be made regarding cracks: While a crack could form as a result of stress or a defect in the film material, a crack would not propagate into adjacent layers, and the adjacent layer(s) would even arrest propagation of the crack. In the case of the monolayer sheet, surface damage (scratches, dents, permanent folds, pinholes, and the like) caused by handling would constitute or give rise to defects that could propagate through the thickness as cracks or pinholes that would render the sheet less effective or ineffective as a barrier. In contrast, because damage incurred during handling of the laminate would ordinarily be limited to the outermost layers, the barrier properties of the laminate would be less likely to be adversely affected. Therefore, handling of the laminate would be easier because there would be less of a need to exercise care to ensure against surface damage.

Yavrouian, Andre↗

Crack Development in Cross-Ply Laminates Under Uniaxial Tension

This study addresses matrix-dominated failures in carbon fiber/polymer matrix composite laminates in a cross-ply lay-up. The events of interest are interlaminar fracture in the form of transverse cracks in the 90' plies and longitudinal splitting in the 0 deg plies and interlaminar fracture in the form of 0/90 delamination. These events were observed using various nondestructive evaluation (NDE) techniques during static tensile tests. Acoustic emission (AE) x radiography, and edge view microscopy were the principal ones utilized in a real-time environment. A comparison of the NDE results with an analytical model based on the classical linear fracture mechanics concept of strain energy release rate as a criterion for crack growth was performed. The virtual crack closure theory was incorporated with a finite element model to generate strain energy release rate curves for the analytical case. Celion carbon fiber/polyimide matrix (G30-500/PMR-15) was the material tested with cross-ply lay-ups of (0(2)/90(6))s and (0(4)/90(4))s. The test specimens contained thermally induced cracks caused by the high-temperature processing. The analytical model was updated to compensate for the initial damage and to study further accumulation by taking into account the crack interactions. By correlating the experimental and analytical data, the critical energy release rates were found for the observable events of interest.

Gyekenyesi, Andrew L.↗

Probability of failure prediction for step-stress fatigue under sine or random stress

A previously proposed cumulative fatigue damage law is extended to predict the probability of failure or fatigue life for structural materials with S-N fatigue curves represented as a scatterband of failure points. The proposed law applies to structures subjected to sinusoidal or random stresses and includes the effect of initial crack (i.e., flaw) sizes. The corrected cycle ratio damage function is shown to have physical significance.

Lambert, R. G.↗

On-Orbit Teflon FEP Degradation

During the Hubble Space Telescope (HST) Second Servicing Mission (SM2), degradation of unsupported Teflon' FEP (fluorinated ethylene propylene), used as the outer layer of the multi-layer insulation (MLI) blankets, was evident as large cracks on the telescope light shield. A sample of the degraded outer layer was retrieved during the mission and returned to Earth for ground testing and evaluation. The results of the Teflon FEP sample evaluation and additional testing of pristine Teflon FEP led the investigative team to theorize that the HST damage was caused by thermal cycling with deep-layer damage from electron and proton radiation which allowed the propagation of cracks along stress concentrations, and that the damage increased with the combined total dose of electrons, protons, LTV and x-rays along with thermal cycling. This paper discusses the testing and evaluation of the Teflon FEP.

Townsend, Jacqueline A.↗

On-Orbit Teflon(trademark) FEP Degradation

During the Hubble Space Telescope (HST) Second Servicing Mission (SM2), degradation of unsupported Teflon(trademark) FEP (fluorinated ethylene propylene), used as the outer layer of the multi-layer insulation (MLI) blankets, was evident as large cracks on the telescope light shield. A sample of the degraded outer layer was retrieved during the mission and returned to Earth for ground testing and evaluation. The results of the Teflon(trademark) FEP sample evaluation and additional testing of pristine Teflon FEP led the investigative team to theorize that the HST damage was caused by thermal cycling with deep-layer damage from electron and proton radiation which allowed the propagation of cracks along stress concentrations, and that the damage increased with the combined total dose of electrons, protons, UV and x-rays along with thermal cycling. This paper discusses the testing and evaluation of the Teflon(trademark) FEP.

Townsend, Jacqueline↗

On-Orbit Teflon(trademark) FEP Degradation

During the Hubble Space Telescope (HST) Second Servicing Mission (SM2), degradation of unsupported Teflon(trademark) FEP (fluorinated ethylene propylene), used as the outer layer of the multi-layer insulation (MLI) blankets, was evident as large cracks on the telescope light shield. A sample of the degraded outer layer was retrieved during the mission and returned to Earth for ground testing and evaluation. The results of the Teflon(trademark) FEP sample evaluation and additional testing of pristine Teflon(trademark) FEP led the investigative team to theorize that the HST damage was caused by thermal cycling with deep-layer damage from electron and proton radiation which allowed the propagation of cracks along stress concentrations, and that the damage increased with the combined total dose of electrons, protons, UV and x-rays along with thermal cycling. This paper discusses the testing and evaluation of the Teflon(trademark) FEP.

Townsend, Jacqueline A.↗

On-Orbit Teflon(R) FEP Degradation

During the Hubble Space Telescope (HST) Second Servicing Mission (SM2), degradation of unsupported Teflon(R) FEP (fluorinated ethylene propylene), used as the outer layer of the multi-layer insulation (MLI) blankets, was evident as large cracks on the telescope light shield. A sample of the degraded outer layer was retrieved during the mission and returned to Earth for ground testing and evaluation. The results of the Teflon(R) FEP sample evaluation and additional testing of pristine Teflon(R) FEP led the investigative team to theorize that the HST damage was caused by thermal cycling with deep-layer damage from electron and proton radiation which allowed the propagation of cracks along stress concentrations, and that the damage increased with the combined total dose of electrons, protons, UV and x-rays along with thermal cycling. This paper discusses the testing and evaluation of the Teflon(R) FEP.

Townsend, Jacqueline A.↗

Oxidation Microstructure Studies of Reinforced Carbon/Carbon

Laboratory oxidation studies of reinforced carbon/carbon (RCC) are discussed with particular emphasis on the resulting microstructures. This study involves laboratory furnace (500-1500 C deg) and arc-jet exposures (1538 C deg) on various forms of RCC. RCC without oxidation protection oxidized at 800 and 1100 C deg exhibits pointed and reduced diameter fibers, due to preferential attack along the fiber edges. RCC with a SiC conversion coating exhibits limited attack of the carbon substrate at 500, 700 and 1500 C deg. However samples oxidized at 900, 1100, and 1300 C deg show small oxidation cavities at the SiC/carbon interface below through-thickness cracks in the SiC coating. These cavities have rough edges with denuded fibers and can be easily distinguished from cavities created in processing. Arc-jet tests at 1538 C deg show limited oxidation attack when the SiC coating and glass sealants are intact. When the SiC/sealant protection system is damaged, attack is extensive and proceeds through matrix cracks, creating denuded fibers on the edges of the cracks. Even at 1538 C deg, where diffusion control dominates, attack is non-uniform with fiber edges oxidizing in preference to the bulk fiber and matrix.

Jacobson, Nathan S.↗

Hubble Space Telescope Metallized Teflon(registered trademark) FEP Thermal Control Materials: On-Orbit Degradation and Post-Retrieval Analysis

During the Hubble Space Telescope (HST) Second Servicing Mission (SM2), degradation of unsupported Teflon(Registered Trademark) FEP (fluorinated ethylene propylene), used as the outer layer of the multilayer insulation (MLI) blankets, was evident as large cracks on the telescope light shield. A sample of the degraded outer layer was retrieved during the mission and returned to Earth for ground testing and evaluation. The results of the Teflon(Registered Trademark) FEP sample evaluation and additional testing of pristine Teflon(Registered Trademark) FEP led the investigative team to theorize that the HST damage was caused by thermal cycling with deep-layer damage from electron and proton radiation which allowed the propagation of cracks along stress concentrations , and that the damage increased with the combined total dose of electrons, protons, UV and x-rays along with thermal cycling. This paper discusses the testing and evaluation of the retrieved Teflon(Registered Trademark) FEP.

Townsend, Jacqueline A.↗

Structural analysis demonstration of constitutive and life models

The overall objective of this program is to demonstrate the applicability of NASA-developed advanced constitutive and life damage models for calculating cyclic structural response and crack initiation in selected components of reusable space propulsion systems. The computer model resulting from this program will enable the user to produce an accurate life prediction of hot gas path, life limiting components of propulsion systems such as the space shuttle main engine (SSME). Previously developed computer models addressing constitutive modeling and life damage will be combined in an advanced finite element analysis to generate a sophisticated baseline life prediction program. A material data base will be established for the constitutive and life models parametrically involving temperature, strain range, strain rate, mean strain/stress, and dwell time. The verified computer program will be used to accomplish the life predictions of three SSME critical components as evidence of the model functionality.

Bechtel, G.↗

Response of thick, notched laminates subjected to tension-compression cyclic loads

The fatigue response of a (0/24/90/-45)s4 T300-5208 graphite-epoxy laminate with a drilled centerhole subjected to fully reversed tension-compression (R=-1, T-C) constant amplitude loading was investigated. Damage evaluation techniques such as stiffness monitoring, penetrant-enchanced X-ray radiography, C-scan, laminate deeply and residual strength were used to establish the mechanisms of damage development as well as the relations between this damage and the stiffness, strength and life of the laminate. Damage initiated at the hole as matrix cracking parallel to the fibers in all plies. Matrix cracks had a significant effect on delamination initiation and growth. Delaminations initiated near the surface in the densely cracked region at the hole and grew along major matrix cracks. Compressive properties degraded more rapidly than tensile properties. At the stress levels used, residual tensile strength increased early in the fatigue life and remained approximately constant to near the end of life, when failure was precipitated by excessive laminate instability during the compressive portion of the loading.

Bakis, C. E.↗

Response of thick, notched laminates subjected to tension-compression cyclic loads

The fatigue response of a (0/24/90/-45)s4 T300-5208 graphite-epoxy laminate with a drilled centerhole subjected to fully reversed tension-compression (R=-1, T-C) constant amplitude loading was investigated. Damage evaluation techniques such as stiffness monitoring, penetrant-enhanced X-ray radiography, C-scan, laminate deply and residual strength were used to establish the mechanisms of damage development as well as the relations between this damage and the stiffness, strength and life of the laminate. Damage initiated at the hole as matrix cracking parallel to the fibers in all plies. Matrix cracks had a significant effect on delamination initiation and growth. Delaminations initiated near the surface in the densely cracked region at the hole and grew along major matrix cracks. Compressive properties degraded more rapidly than tensile properties. At the stress levels used, residual tensile strength increased early in the fatigue life and remained approximately constant to near the end of life, when failure was precipitated by excessive laminate instability during the compressive portion of the loading.

Bakis, C. E.↗

Structural fatigue in the 34-meter HA-Dec antennas

Structural modifications to the 34-m hour-angle-declination antennas, coupled with the use of the antennas beyond their intended lifespans, have led to structural fatigue, as evidenced by damage to the declination drive gear and cracks on the structural members and gussets. An analysis and simulation were made of the main antenna structural members. The analysis showed that the total stress to the antenna structure substantially exceeds the maximum levels recommended by the American Institute of Steel Construction (AISC). Although each of the separate static conditions of stress is only 50 percent of the total stress and does not reach the AISC reduced yield limit, fatigue can and did occur, causing the material to crack in the weakest places.

Vanhek, R. A.↗