DOE OSTI2024

Highly efficient La/Ni co-doped strontium titanate catalyst for co-production of propylene and hydrogen from propane in protonic ceramic electrochemical cells

A highly efficient La/Ni co-doped strontium titanate (LSNT) perovskite catalyst is developed and integrated in a protonic ceramic electrochemical cell for co-production of propylene and high-purity hydrogen from commercial propane feedstock. Propane conversion and hydrogen production rate can be effectively enhanced under an applied current due to the electrochemical promotion effect and/or shifted reaction equilibrium induced by rapid separation of hydrogen product. Water vapor in the feed gas could significantly improve the catalyst stability by suppressing the coke formation. The propane conversion could reach up to 53% at 600 °C under a current density of 90 mA cm −2 . The LSNT catalyst also shows excellent tolerance for the sulfur contaminant in commercial propane gas. Finally, the excellent performance of the LSNT catalyst is attributed to the highly active and selective Ni species at the interface with the perovskite substrate, which are formed in situ via reduction-induced exsolution under reaction conditions.

interfacial active sites↗
DOE OSTI2021

CFD analysis of a solid pin-fueled small modular fluoride salt-cooled reactor

A computational fluid dynamics (CFD) study is performed for the pre-conceptual solid pin-fueled small modular fluoride salt-cooled reactor developed by the Oak Ridge National Laboratory (ORNL). The solid and fluid regions in a 1/12th section of a fuel assembly are modeled. The solid region includes fuel and non-fuel pins, with heat generation in the active region of the fuel pins. Two different power profiles, uniform and center-peaked, are considered. The FLiBe coolant flows from the bottom to the top of the core, parallel to the bank of fuel and non-fuel pins. The k-ω shear-stress transport (SST) model is chosen as the baseline turbulence model. The effects of grid refinement, inlet turbulence specification, and turbulence models on the temperature and pressure drop predictions are studied. Turbulence model sensitivity is investigated by comparing the results from the k-ω SST model with other two-equation models (k-ω baseline or BSL and k-ε realizable) as well as with anisotropic Reynolds stress transport models (linear pressure-strain and stress-BSL). Here the results show that the choice of turbulence model has a significant impact on the pin temperature and bundle pressure drop predictions. The results from the baseline turbulence model show good agreement between the fuel pin temperatures and bundle pressure drop values predicted using a subchannel model previously developed by the authors of the present study.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2020

Abnormally Low Activation Energy in Cubic Na3SbS4 Superionic Conductor

Inorganic Na-ion superionic conductors play a vital role in all-solid-state Na batteries that operate at room temperature. Sodium thioantimonate (Na3SbS4), a popular sulfide-based solid electrolyte, has attracted serious attention due to its advantages of high ionic conductivity at room temperature and impressive chemical stability under ambient conditions. Much research detailing Na3SbS4 focused on its synthetic approaches and interfacial stability against Na metal, yet, there is limited information elucidating a fundamental understanding of the Na- ion diffusion mechanisms in Na3SbS4 with different crystal structures (e.g., tetragonal and cubic). Herein, we combine real-time electrochemical impedance measurements with theoretical simulations based on density functional theory and in situ quasi-elastic neutron scattering to study the Na-ion conductive properties of Na3SbS4 during its phase transition from a tetragonal to cubic structure. Although there is a slight change in the lattice parameters, the energy barrier for Na-ion diffusion in the tetragonal structure was determined to be much larger (5-10 times) than that in the cubic structure from both theoretical and experimental perspectives. The high degree of symmetry in cubic Na3SbS4 leads to less interatomic correlations between Na and S(Sb) atoms, a shorter jump distance (2.85 angstrom), and a larger diffusion coefficient. This research provides insight into understanding the Na-ion diffusion in solid electrolytes with phase transitions and provides fundamental guidance for designing novel solid-state Na-ion conductors.

Zhang, Qian↗
DOE OSTI2020

Solid Electrolytes for Li–S Batteries: Solid Solutions of Poly(ethylene oxide) with Li x PON- and Li x SiPON-Based Polymers

We report here efforts to synthesize free-standing, dry polymer electrolytes that exhibit superior ionic conductivities at ambient for Li–S batteries. Co-dissolution of poly(ethylene oxide) (PEO) (M n 900k) with Li x PON and Li x SiPON polymer systems at a ratio of approximately 3:2 followed by casting provides transparent, solid-solution films 25–50 μm thick, lowering PEO crystallinity, and providing measured impedance values of 0.1–2.8 × 10 –3 S/cm at ambient. These values are much higher than simple PEO/Li + salt systems. These solid-solution polymer electrolytes (PEs) are (1) thermally stable to 100 °C; (2) offer activation energies of 0.2–0.5 eV; (3) suppress dendrite formation; and (4) enable the use of lithium anodes at current densities as high as 3.5 mAh/cm 2 . Here, galvanostatic cycling of SPAN/PEs/Li cell (SPAN = sulfurized, carbonized polyacrylonitrile) shows discharge capacities of 1000 mAh/g sulfur at 0.25C and 800 mAh/g sulfur at 1C with high coulumbic efficiency over 100 cycles.

25 ENERGY STORAGE↗
DOE OSTI2022

Generalized scaling of spin qubit coherence in over 12,000 host materials

Significance Atomic defects in solid-state materials are promising candidates as quantum bits, or qubits. New materials are actively being investigated as hosts for new defect qubits; however, there are no unifying guidelines that can quantitatively predict qubit performance in a new material. One of the most critical property of qubits is their quantum coherence. While cluster correlation expansion (CCE) techniques are useful to simulate the coherence of electron spins in defects, they are computationally expensive to investigate broad classes of stable materials. Using CCE simulations, we reveal a general scaling relation between the electron spin coherence time and the properties of qubit host materials that enables rapid and quantitative exploration of new materials hosting spin defects.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗
DOE OSTI2023

Three New Spiral Galaxies with Active Nuclei Producing Double Radio Lobes

Abstract Double radio lobes are generally believed to be produced by active nuclei of elliptical galaxies. However, several double-lobed radio sources have been solidly found to be associated with spiral galaxies. By cross-matching ∼9 × 10 5 spiral galaxies selected from the Sloan Digital Sky Survey DR8 data with the full 1.4 GHz radio source catalogs of NRAO VLA Sky Survey and Faint Images of the Radio Sky at Twenty-centimeters, we identify three new spiral galaxies: J0326−0623, J1110+0321 and J1134+3046 that produce double radio lobes, and five double-lobed spirals previously known. By combining the newly discovered and all the other known cases in literature, we confirm the relation that more massive spiral galaxies could produce more powerful radio lobes. We find that most of these spiral galaxies are located in a galaxy group or a poor cluster, in which the environment is denser than in the field, and about half of them are the central brightest galaxies in their parent system. We therefore suggest that the environment is one of the key factors for a spiral to produce double radio lobes.

Astronomy & Astrophysics↗
DOE OSTI2024

Metal-Organic Frameworks: Structure, Function and Design via Hyperpolarized NMR Spectroscopy: Collaborative Proposal (Final Technical Report)

Nuclear magnetic resonance is a powerful tool to shed light on the properties of a vast range of materials but its use is affected by detection sensitivity. Throughout this work, we investigated new routes to dynamic nuclear spin polarization with an eye on applications to the study of metal-organic frameworks (MOFs). Work at the Meriles group focused on extending our understanding of the mechanisms governing the optical generation of spin order via photo-active electronic spin species and the subsequent transfer of spin polarization throughout the solid-state host.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Computational Fluid Dynamics Simulations of Glass Vitrification Refractory Coupon Tests

The Waste Treatment and Immobilization Plant (WTP) at the Hanford site is nearing the start of the Direct-Feed Low-Activity Waste (DFLAW) operations. DFLAW is destined to convert a pretreated low activity waste portion of the 56 million gallons of tank waste into a stable solid glass. In the subsequent decade completion of the high-level waste (HLW) facility is anticipated. Sustained operational missions of both LAW and HLW melter facilities are expected over multiple decades. In high-temperature glass melters, the refractory lining corrodes over time, which could potentially be an issue for longer term operations, this refractory corrosion is higher at the level of the glass-air interface due to surface tension driven flow. The glass viscosity, melt pool temperature, and glass chemical composition can impact the rate at which the refractory corrodes. This rate is important to quantify for the various waste glasses to be produced at the WTP since the integrity of the refractory should not be a limiting factor affecting the lifetime of the melter. To this end, a series of glasses representative of the first batches of waste glass produced by the WTP will be melted in small-scale crucibles with Monofrax® K-3 coupons inserted. The corrosion of the K-3 will be measured in the melt and at the meltline (or neckline). A model for the corrosion rate will be constructed and implemented into a previously developed framework for a computational fluid dynamics (CFD) model of the full-scale WTP. To assist with experimental design and validate the implementation of the model in the full-scale melter, CFD simulations of the small-scale crucible tests were performed. The bubbling that occurs in the small-scale crucible is initially validated here with a model that uses silicone oil at room temperature. The viscosity of the oil ranges from 1 to 100 Pa•s, which corresponds to operating glass pool temperatures near 1150 °C down to idling temperatures near 950 °C. The simulation results show good agreement with the bubble sizes that form during experiments. CFD modeling of the crucible setup was used to determine bubbling characteristics to match the range of near-wall velocities expected in the full-scale WTP. This study presents the initial CFD modeling results, corrosion testing plan, and some preliminary corrosion samples with an outline for the next steps for the development of the corrosion model.

Abboud, Alexander W. [Idaho National Lab]↗
DOE OSTI2024

Fuel‐Driven π‐Conjugated Superstructures to Form Transient Conductive Hydrogels

Despite advances in creating dissipative materials with transient properties, such as hydrogels and active droplets, their application remains confined to temporal changes in structural properties. Developing out-of-equilibrium materials whose electronic functions are parameterized by a chemical reaction cycle is challenging. Yet, this class of materials is required to construct biomimetic materials. In contrast to traditional chemical reaction cycles that exploit molecularly dissolved building blocks at thermodynamic equilibrium, we show that fiber structures derived from reactive naphthalene diimide (NDI) building blocks can be used as resting states to form far-from-equilibrium conductive hydrogels after the addition of chemical fuels. Upon fueling the NDI-derived fibers, a dual-component activation and deactivation pathway is deduced by kinetic analysis and is absent when using a molecularly dissolved resting state. Investigating the solid-state morphologies of the structures formed throughout the fuel-driven reaction cycle using cryo-EM reveals that the resting thermodynamic fibers evolve to transient thicker fibrils and layered superstructures. We show that the transient redox-active hydrogels exhibit a nearly threefold increase in electrical conductivity upon fuel consumption before reverting to their original value over hours. In conclusion, these far-from-equilibrium materials are potential candidates in applications such as programmable biorobotics and chemical computing.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

Characterization of Tank 11H samples from tank closure cesium removal (TCCR) Batch 3 - intermediate and final samples

Savannah River Remediation (SRR) is currently operating the Tank Closure Cesium Removal (TCCR) process to remove 137 Cs from tank waste supernate using an ion exchange process. The TCCR unit processes dissolved salt from Tank 10H through a series of ion exchange columns containing crystalline silicotitanate (CST) and the effluent is then discharged to Tank 11H. Four interim samples pulled from Tank 11H during and just after the completion of processing of Batch 3 through the TCCR process have been analyzed for 137 Cs activity and density. The 137 Cs activity was found to decrease with each subsequent sample, which is consistent with the addition of decontaminated solution to Tank 11H. When compared to the expected composition from mixing the Tank 10H Batch 3 feed with the material already present in Tank 11H, the bulk chemical composition was as expected. A corrosion control sample collected from Tank 11H in June 2020 showed changes in the chemical composition and 137 Cs activity when compared to the composition measured at the end of Batch 2 processing. As there were no additions made to the tank during this period, these changes were attributed to leaching of the solids present in Tank 11H. Revision 1 of this report contains additional analyses of the fourth interim sample including inductively coupled plasma – mass spectrometry (ICP-MS) results and activities of other radionuclides. These results are consistent with the previously reported results, showing leaching from the Tank 11H heel. Notably, the 90 Sr activity was about 2.7x higher than calculated from a mixture of the original Tank 11H supernate and the Tank 10H supernate as treated by TCCR, suggesting additional leaching of Sr from the Tank 11H heel solids. In addition, Revision 1 includes analysis results for the Batch 3 Post-Production surface and variable depth samples collected in October of 2020. The Post-Production surface sample was similar in composition to the fourth interim surface sample, except for the increased Cs-137 and oxalate concentrations that were presumably associated with leaching of the Tank 11H heel solids.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2021

Molecular dynamics simulation of vacancy and void effects on strain-induced martensitic transformations in Fe-50 at.% Ni model concentrated solid solution alloy

Strain-induced martensitic transformations can improve the strength and ductility of some face centered cubic (FCC) metals and alloys. Irradiation-induced defects such as vacancies, dislocation loops, and voids activate martensitic transformations over a wider range of mechanical loading conditions than in pristine material. Furthermore, the mechanisms underlying irradiation-enabled martensite transformations remain unclear. In this work, we use molecular dynamics simulations to study the effect of vacancies and voids on strain-induced martensitic transformations in a model concentrated solid solution alloy Fe-50 at.% Ni. It has been found that single vacancies have no resolvable effect on the transformation because they reduce the stacking fault energy by a relatively insignificant margin and do so only if the vacancy is located on the stacking fault plane. Voids, however, activate the martensite transformation through shear strain accumulation around the void due to dislocation pileup. The larger the void, the more pronounced this effect.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Techno-economic and environmental life cycle assessment of next-generation fiber-encapsulated nanoscale hybrid materials for direct air carbon capture

A techno-economic and environmental life cycle assessment was conducted for manufacturing two novel types of solid sorbents used for direct air CO 2 capture (DAC). One type of solid sorbent comprised Polyacrylonitrile (PAN)/Organopolysilizane (OPSZ)/nanoscale organic hybrid materials (NOHM)(, and the other comprised polymers of intrinsic microporosity (PIM)/NOHM. These solid sorbents were assumed to be manufactured via an unconventional route: electrospinning as fibers. Economic analyses revealed that manufacturing costs for a 0.73 MT/year capacity plant was $\$$831 and $\$$1398/kg of electrospun fiber in the case ofPAN/OPSZ/NOHM and PIM/NOHM, respectively. The costs were higher for PIM/NOHM owing to high raw material prices (Spirobisindane and tetrafluoroterephthalonitrile), that are used only in manufacturing PIM. Scaling up the plant capacity from 0.73 to 30 MT/year plant decreased the manufacturing cost by nearly half from $\$$831 to $\$$379 in the case of PAN/OPSZ/NOHM, depicting the economies of scale of effect. An LCA of both types of solid sorbent was performed using OpenLCA software, the Ecoinvent v 3.5 database, and the TRACI LCI assessment method. The Global Warming Potential (GWP) ofPAN/OPSZ/NOHM and PIM/NOHM was observed to be 151 × 10 -3 and 166 × 10 -3 kg CO 2 per kg CO 2 captured in the DAC plant, respectively. In conclusion, these GWP values were nearly five times as high as those observed for other solid sorbents existing in the literature such as PEI on silica gel, carbonate on silica, and carbonate on activated carbon owing to large amounts of electricity used in electrospinning unit operation.

36 MATERIALS SCIENCE↗
DOE OSTI2026

Abiotic manganese oxide formation induced by light and copper-driven Fenton chemistry

Redox-active transition metals such as manganese (Mn) and copper (Cu) frequently coexist in surface water systems, where their interactions can significantly influence contaminant fate and water quality. It is widely known that the oxidation of Mn 2+ (aq) to Mn(IV) oxide solids is driven mainly by biotic processes in which Cu 2+ serves as an inhibitor of Mn oxidation. However, Cu 2+ can also trigger Fenton reactions to produce reactive oxygen species (ROS) capable of promoting the abiotic Mn oxidation (i.e., without the involvement of biological organisms), through an alternative natural pathway that remains overlooked in water. In this study, we found that the abiotic oxidation of Mn 2+ can be facilitated by the co-existence of sunlight and Cu 2+ . By contrasting Cu 2+ with other divalent cations, such as Ca 2+ , Mg 2+ , and Zn 2+ , this investigation highlights the distinct role of Cu 2+ in promoting Mn oxidation. Moreover, the study elucidated how light induces ROS to trigger Cu-driven photo-Fenton reactions and identified the roles of ROS in Mn oxidation. Chemical-Fenton reactions (i.e., the interaction between Cu and H 2 O 2 in the absence of light) were also examined for their contribution to the Cu-driven Mn photo-oxidation, supporting the involvement of Fenton chemistry in Mn oxidation. By elucidating the novel photochemical mechanism of Mn oxide formation, our findings advance the understanding of heavy metal interactions in aqueous environments and highlight the intricate roles of Cu 2+ in affecting elemental cycling and the evaluation of heavy metal contamination in water resources. This discovery also underscores the critical contribution of co-existing Fenton-active metals in forming Mn oxide solids.

Abiotic Mn oxidation↗
DOE OSTI2020

LiAlO 2 /LiAl 5 O 8 Membranes Derived from Flame-Synthesized Nanopowders as a Potential Electrolyte and Coating Material for All-Solid-State Batteries

Recently, γ-LiAlO 2 has attracted considerable attention as a coating in Li-ion battery electrodes. However, its potential as a Li + ceramic electrolyte is limited due to its poor ionic conductivity (<10 –10 S cm –1 ). Here, we demonstrate an effective method of processing LiAlO 2 membranes (<50 μm) using nanopowders (NPs) produced via liquid-feed flame spray pyrolysis (LF-FSP). Here, membranes consisting of selected mixtures of lithium aluminate polymorphs and Li contents were processed by conventional tape casting of NPs followed by thermocompression of the green films (100 °C/10 kpsi/10 min). The sintered green films (1100 °C/2 h/air) present a mixture of LiAlO 2 (~72 wt %) and LiAl 5 O 8 (~27 wt %) phases, offering ionic conductivities (>10 –6 S cm –1 ) at ambient with an activation energy of 0.5 eV. This greatly increases their potential utility as ceramic electrolytes for all-solid-state batteries, which could simplify battery designs, significantly reduce costs, and increase their safety. Furthermore, a solid-state Li/Li 3.1 AlO 2 /Li symmetric cell was assembled and galvanostatically cycled at 0.375 mA cm –2 current density, exhibiting a transference number ≈ 1.

25 ENERGY STORAGE↗
DOE OSTI2020

Significance of a Solid Electrolyte Interphase on Separation of Anode and Cathode Materials from Spent Li-Ion Batteries by Froth Flotation

The separation of electrode active materials from spent Li-ion batteries (LIBs) by froth flotation is challenging due to the changes in surface properties of electrode active materials from cycling as well as the presence of organic binders. In this work, the froth flotation separation of aged anode and cathode composite materials from spent LIBs was systematically investigated after the materials were heat treated. The results show that aged anode and cathode materials from spent LIBs can be well separated from each other after a heating process in air at 400 degrees C and at which some of the PVDF binder remains intact. The underlying mechanism was investigated by X-ray photoelectron spectroscopy (XPS), contact angle measurements, and scanning transmission electron microscopy (STEM) coupled with energy-dispersive X-ray spectroscopy (EDX). The results from the XPS and contact angle measurements show that there is a hydrophilic and oxygen-rich layer on the surface of aged anode materials. This hydrophilic surface, associated with the solid electrolyte interface (SEI) layer, impacts the froth flotation process significantly. The results also show that both the SEI layers and PVDF binder residues on the surface are removed at 400 degrees C for an hour, restoring the hydrophobicity of the anode materials, which, in turn, benefits the separation of anode and cathode materials. The STEM/EDX elemental analysis data confirms that there are 20 nm-thick oxygen-rich SEI layers on the surfaces, which can be removed after a heating process. The present result illustrates the significance of the SEI layers in flotation separation of electrode materials and sheds new lights into the future development of the recycling processes for the separation of anode and cathode composite materials from spent Li-ion batteries.

25 ENERGY STORAGE↗
DOE OSTI2024

4 V Na Solid State Batteries Enabled by a Scalable Sodium Metal Oxyhalide Solid Electrolyte

All-solid-state sodium batteries (ASSSBs) are viable candidates for large scale energy storage that could vie with lithium. Ductile solid catholytes for such cells that can be prepared without extensive ball milling and directly paired with high voltage sodium cathodes are lacking, however. We report a new amorphous fast Na-ion conducting metal oxychloride that meets these criteria, synthesized through a scalable and low-cost route based on a spontaneous solid-state reaction with simple short mixing and 100 °C annealing. It has an ionic conductivity of 1.2 mS·cm–1 and low activation energy of 0.31 eV. Due to its dual O2–/Cl– framework, it exhibits a high anodic potential of 4 V vs Na+/Na and good chemical/electrochemical compatibility with high voltage sodium cathode materials. ASSSBs consisting of the oxychloride solid electrolyte paired with a high voltage P2–Na2/3Ni1/3Mn2/3O2 cathode showed stable long-term cycling with a 4.0 V vs Na3Sn cutoff potential and even to 4.3 V.

solid-state electrolyte, solid-state batteries, Nu↗
DOE OSTI2020

B‐MWW Zeolite: The Case Against Single‐Site Catalysis

Abstract Boron‐containing materials have recently been identified as highly selective catalysts for the oxidative dehydrogenation (ODH) of alkanes to olefins. It has previously been demonstrated by several spectroscopic characterization techniques that the surface of these boron‐containing ODH catalysts oxidize and hydrolyze under reaction conditions, forming an amorphous B 2 (OH) x O (3− x /2) ( x= 0–6) layer. Yet, the precise nature of the active site(s) remains elusive. In this Communication, we provide a detailed characterization of zeolite MCM‐22 isomorphously substituted with boron (B‐MWW). Using 11 B solid‐state NMR spectroscopy, we show that the majority of boron species in B‐MWW exist as isolated BO 3 units, fully incorporated into the zeolite framework. However, this material shows no catalytic activity for ODH of propane to propene. The catalytic inactivity of B‐MWW for ODH of propane falsifies the hypothesis that site‐isolated BO 3 units are the active site in boron‐based catalysts. This observation is at odds with other traditionally studied catalysts like vanadium‐based catalysts and provides an important piece of the mechanistic puzzle.

Altvater, Natalie R.↗
DOE OSTI2021

Crystal Structure and Preparation of Li7La3Zr2O12 (LLZO) Solid-State Electrolyte and Doping Impacts on the Conductivity: An Overview

As an essential part of solid-state lithium-ion batteries, solid electrolytes are receiving increasing interest. Among all solid electrolytes, garnet-type Li7La3Zr2O12 (LLZO) has proven to be one of the most promising electrolytes because of its high ionic conductivity at room temperature, low activation energy, good chemical and electrochemical stability, and wide potential window. Since the first report of LLZO, extensive research has been done in both experimental investigations and theoretical simulations aiming to improve its performance and make LLZO a feasible solid electrolyte. These include developing different methods for the synthesis of LLZO, using different crucibles and different sintering temperatures to stabilize the crystal structure, and adopting different methods of cation doping to achieve more stable LLZO with a higher ionic conductivity and lower activation energy. It also includes intensive efforts made to reveal the mechanism of Li ion movement and understand its determination of the ionic conductivity of the material through molecular dynamic simulations. Nonetheless, more insightful study is expected in order to obtain LLZO with a higher ionic conductivity at room temperature and further improve chemical and electrochemical stability, while optimal multiple doping is thought to be a feasible and promising route. This review summarizes recent progress in the investigations of crystal structure and preparation of LLZO, and the impacts of doping on the lithium ionic conductivity of LLZO.

Raju, Md Mozammal (ORCID:0000000319040523)↗