A Case History of Titanium Stress Corrosion in Nitrogen Tetroxide

An investigation of the incompatibility of titanium in certain grades of nitrogen tetroxide will be discussed as a case history. The methodology used in its resolution will point out some of the dangers associate with compatibility testing. The methodology also will present some of the difficulties associated with coordinating an investigation involving many contractors and U. S. Government agencies. The techniques employed in this investigation are described in considerable detail for the benefit of investigators with similar problems.

Johnson, Robert E.↗
NASA NTRS1970

Stress corrosion crack inhibiting method for titanium

Addition of oxyanions to liquid solvents in excess of the number of chloride, bromide, or iodide ions present prevents cracking of titanium-aluminum alloys under exposure to aqueous and other solvent environments. The molar concentration of oxyanion is set from 10 to 100 times higher than concentration of halide ions.

Beck, T. R.↗
NASA NTRS1971

Stress corrosion in titanium alloys and other metallic materials

Multiple physical and chemical techniques including mass spectroscopy, atomic absorption spectroscopy, gas chromatography, electron microscopy, optical microscopy, electronic spectroscopy for chemical analysis (ESCA), infrared spectroscopy, nuclear magnetic resonance (NMR), X-ray analysis, conductivity, and isotopic labeling were used in investigating the atomic interactions between organic environments and titanium and titanium oxide surfaces. Key anhydrous environments studied included alcohols, which contain hydrogen; carbon tetrachloride, which does not contain hydrogen; and mixtures of alcohols and halocarbons. Effects of dissolved salts in alcohols were also studied. This program emphasized experiments designed to delineate the conditions necessary rather than sufficient for initiation processes and for propagation processes in Ti SCC.

Harkins, C. G.↗
NASA NTRS1974

Relation between surface slip topography and stress corrosion cracking in Ti-8 wt % Al

The deformation behavior of Ti-8 wt % Al has been investigated in an inert environment (air), and an aggressive environment (salt water). Details of surface slip geometry were examined by high resolution surface replicas at various stages of deformation in both environments. Specimens aged to contain a fine dispersion of Ti3Al precipitates failed by subcritical crack growth in salt water, whereas specimens in the single phase condition showed no effects of environment on the yield or fracture characteristics. The Ti3Al precipitates produce little change in strength level or slip character compared to the single phase alloy, and there is no evidence of any effects of environment on the character of surface slip. Rather, the presence of trenches along slip bands on the surface of aged specimens suggest that the specific effect of the Ti3Al precipitates is to render the surface slip steps chemically active relative to the surrounding matrix by slip induced dissolution of the particles.

Boyd, J. D.↗
NASA NTRS1974

Stress corrosion cracking of a titanium alloy in chloride-containing liquid environments

Ti-8 Al-1 Mo-1 V was tested in solvents containing chloride, bromide or iodide ions. It was found that the region II plateau velocity could be correlated with the inverse of the viscosity for several solvents. It seems most likely that this reflects the influence of the viscosity on the diffusion coefficient of some species involved in a mass transfer process which limits the crack growth. Associated tests were performed in which the potential, pH and concentration of Cl- were varied, in some of the same solutions as used for the viscosity tests. It is concluded from these tests that the absence of cathodic protection against cracking in solutions of low pH arises from an ohmic effect which isolates the crack tip from external potential control.

Smyrl, W. H.↗