Embedding of Optical Fibers with Electric Field Assisted Sintering
The Electric Field Assisted Sintering (EFAS) technique was used for embedding the fibers, involving rapid heating via an electric current and pressure, reducing fiber exposure to high temperatures. Stainless steel guide tubes were inserted at the fiber-matrix junctions to prevent fiber breakage during the sintering process. The study varied key EFAS parameters—temperature (800°C to 980°C), pressure (40-50 MPa), and hold time (5-10 minutes)—to assess how they influenced fiber embedding. After embedding, the fibers were inspected using optical frequency domain reflectometry (OFDR) to evaluate optical losses and strain along the fiber length. The OFDR scans confirmed that the fibers remained intact, and subsequent transmission tests demonstrated no macroscopic fractures. The embedded samples were also analyzed using scanning electron microscopy (SEM) and X-ray computed tomography (CT) scans. These tests confirmed good bonding between the fiber and matrix with no cracking, though some porosity was present in samples fabricated at lower temperatures. At higher temperatures (980°C), the fiber-matrix bonding was continuous and defect-free, with metal coatings aiding in the bonding process. Elemental analysis showed interdiffusion between the fiber coatings and matrix materials, particularly between the gold coating and stainless steel. Helium leak tests revealed that lower sintering temperatures resulted in matrix porosity, causing leaks, but samples fabricated at 980°C were leak-tight.