Enhancing the Electrode Gravimetric Capacity of Li 1.2 Mn 0.4 Ti 0.4 O 2 Cathode Using Interfacial Carbon Deposition and Carbon Nanotube-Mediated Electrical Percolation
Mn-based cation disordered rocksalt oxides (Mn-DRX) are emerging as promising cathode materials for next-generation Li-ion batteries due to their high specific capacities and cobalt and nickel free characteristic. However, to reach the theoretical capacity, solid-state method synthesized Mn-DRX materials require activation via post-synthetic ball milling, typically incorporating more than 20 wt.% conductive carbon that adversely reduces the electrode level gravimetric capacity. To solve this issue, we firstly deposit amorphous carbon on the surface of the Li 1.2 Mn 0.4 Ti 0.4 O 2 (LMTO) particles to increase the electrical conductivity by a five order of magnitude. Although the cathode material gravimetric first charge capacity reaches 180 mAh/g, its highly irreversible behavior leads to a 70 mAh/g first discharge capacity. Subsequently, to ensure a good electrical percolation network, the LMTO material is ball milled with multi-wall carbon nanotube (CNT) to obtain a 78.7 wt.% LMTO active material loading in the cathode electrode (LMTO-CNT). As a result, a 210 mAh/g cathode electrode gravimetric first charge and 165 mAh/g first discharge capacity are obtained, compared to the respective capacity values of 222 mAh/g and 155 mAh/g for the LMTO ball milled with 20 wt.% SuperP C65 electrode (LMTO-SP). After 50 cycles, the LMTO-CNT delivers a 121 mAh/g electrode gravimetric discharge capacity, largely outperforming the 44 mAh/g value of the LMTO-SP. In conclusion, our study demonstrates that while ball milling is necessary to achieve the theoretical capacity of LMTO, a careful selection of the additive, such as CNT, effectively reduces the required carbon quantity to achieve a higher electrode gravimetric discharge capacity.