Results for “Powder” — Page 24

DOE OSTI2024

An experimental process parameter study on the identification of defects in additively fabricated Al6061 with laser powder bed fusion

Additively fabricated metal parts using laser powder bed fusion (L-PBF) possess sophisticated morphology due to the recurrent use of laser-induced metal powder melting and solidification. The surface and 3D morphology of these parts often include defects in the form of protrusions, depressions, pores, voids, keyholes, or cracks that are known to be influenced by laser scanning paths and layer-to-layer processing. Such inconsistent part quality hampers the extensive adoption of L-PBF. Pores and cracks are detrimental to the fatigue life of the parts and components. Quantifying and controlling part defects and optimizing processing and scanning strategy parameters adaptively in real-time through in situ monitoring systems are highly desired. This study investigates the optimization of experimental process parameters (power, scan velocity, and hatch spacing) and their effects on the cracking and porosity of Al6061 alloy using machine learning techniques. Multi-objective optimization is formulated and conducted to determine the L-PBF parameters that minimize both porosity and crack densities.

36 MATERIALS SCIENCE↗

NASA NTRSDate not supplied

Microstructural Characterization of Laser Powder Bed Fusion (L-PBF) Additively Manufactured Inconel 718 for Aerospace Application

Alloy 718 (Inconel 718) is used for aerospace applications because of its excellent corrosion resistance and mechanical properties. This alloy is particularly applicable in manufacturing components subjected to high temperatures in rocket engines, aero-engines, and gas turbines. Properties for this alloy when processing on systems from similar and different Laser Powder Bed Fusion (L-PBF) machines provide subtle differences due to process parameters, feedstock, and machine configurations. A series of sixteen L-PBF AM Inconel 718 geometric feature build plates have been evaluated for microstructure using optical microscopy. This study presents the details of the microstructure analysis concerning geometry and different machine platforms. Microstructural investigations of these samples included average grain width measurement for all the X-Y and Y-Z build layers and are accompanied by process parameters and powder characterization. The present work concludes with a discussion on the importance of captured differences among builds to understand the practical limitations among AM platforms.

Additive Manufacturing↗

DOE OSTI2020

ICME and In-Situ Process Monitoring for Rapid Qualification of Components Made by Laser-based Powder Bed Additive Manufacturing Processes for Nuclear Structural Applications

Additive manufacturing (AM) through selective powder bed melting of successive layers is being considered as disruptive technology for rapid production of low-cost nuclear reactor internal components with complex geometries. However, there is a potential for non-uniform distribution of physical features, such as porosity or microstructural differences, due to variations of temperature across a component build. These heterogeneities make the deployment of traditional material qualification and non-destructive evaluation of AM components difficult. This research project explored the feasibility of using in-situ process monitoring methods and integrated computational materials engineering (ICME) principles as an alternate qualification methodology and approach. This project included six individual tasks: (i) design of artifacts relevant to the nuclear power industry, (ii) evaluation of laser processing and in-situ measurements, (iii) computational modeling, (iv) ex-situ microstructural characterization, (v) evaluation of scaling the methodology for large-scale structures, and (vi) development of a data package to codes and standards organizations. As a part of this research, laser powder bed fusion of metals (316L, Alloy 718, and Ti6Al4V) was explored. This document provides an overview of the research performed over three years and serves as the final U.S. Department of Energy report for this project. In the third year, the project focused on the following activities: (a) in-situ infrared and optical imaging of each layer during processing of representative stainless steel geometries; (b) development of methodologies to analyze the data; and (c) application of ICME methodologies and other experiments to estimate the relevance of defects and microstructure to tensile properties.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗

DOE OSTI2020

ICME and In-Situ Process Monitoring for Rapid Qualification of Components Made by Laser-based Powder Bed Additive Manufacturing Processes for Nuclear Structural Applications

Additive manufacturing (AM) through selective powder bed melting of successive layers is being considered as disruptive technology for rapid production of low-cost nuclear reactor internal components with complex geometries. However, there is a potential for non-uniform distribution of physical features, such as porosity or microstructural differences, due to variations of temperature across a component build. These heterogeneities make the deployment of traditional material qualification and non-destructive evaluation of AM components difficult. This research project explored the feasibility of using in-situ process monitoring methods and integrated computational materials engineering (ICME) principles as an alternate qualification methodology and approach. This project included six individual tasks: (i) design of artifacts relevant to the nuclear power industry, (ii) evaluation of laser processing and in-situ measurements, (iii) computational modeling, (iv) ex-situ microstructural characterization, (v) evaluation of scaling the methodology for large-scale structures, and (vi) development of a data package to codes and standards organizations. As a part of this research, laser powder bed fusion of metals (316L, Alloy 718, and Ti6Al4V) was explored. This document provides an overview of the research performed over three years and serves as the final U.S. Department of Energy report for this project. In the third year, the project focused on the following activities: (a) in-situ infrared and optical imaging of each layer during processing of representative stainless steel geometries; (b) development of methodologies to analyze the data; and (c) application of ICME methodologies and other experiments to estimate the relevance of defects and microstructure to tensile properties.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗

DOE OSTI2020

ICME and In-Situ Process Monitoring for Rapid Qualification of Components Made by Laser-based Powder Bed Additive Manufacturing Processes for Nuclear Structural Applications

Additive manufacturing (AM) through selective powder bed melting of successive layers is being considered as disruptive technology for rapid production of low-cost nuclear reactor internal components with complex geometries. However, there is a potential for non-uniform distribution of physical features, such as porosity or microstructural differences, due to variations of temperature across a component build. These heterogeneities make the deployment of traditional material qualification and non-destructive evaluation of AM components difficult. This research project explored the feasibility of using in-situ process monitoring methods and integrated computational materials engineering (ICME) principles as an alternate qualification methodology and approach. This project included six individual tasks: (i) design of artifacts relevant to the nuclear power industry, (ii) evaluation of laser processing and in-situ measurements, (iii) computational modeling, (iv) ex-situ microstructural characterization, (v) evaluation of scaling the methodology for large-scale structures, and (vi) development of a data package to codes and standards organizations. As a part of this research, laser powder bed fusion of metals (316L, Alloy 718, and Ti6Al4V) was explored. This document provides an overview of the research performed over three years and serves as the final U.S. Department of Energy report for this project. In the third year, the project focused on the following activities: (a) in-situ infrared and optical imaging of each layer during processing of representative stainless steel geometries; (b) development of methodologies to analyze the data; and (c) application of ICME methodologies and other experiments to estimate the relevance of defects and microstructure to tensile properties.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗

DOE OSTI2020

ICME and In-Situ Process Monitoring for Rapid Qualification of Components Made by Laser-based Powder Bed Additive Manufacturing Processes for Nuclear Structural Applications

Additive manufacturing (AM) through selective powder bed melting of successive layers is being considered as disruptive technology for rapid production of low-cost nuclear reactor internal components with complex geometries. However, there is a potential for non-uniform distribution of physical features, such as porosity or microstructural differences, due to variations of temperature across a component build. These heterogenities make the deployment of traditional material qualification and non-destructive evaluation of AM components difficult. This research project explored the feasibility of using in-situ process monitoring methods and integrated computational materials engineering (ICME) principles as an alternate qualification methodology and approach. This project included six individual tasks: (i) design of artifacts relevant to the nuclear power industry, (ii) evaluation of laser processing and in-situ measurements, (iii) computational modeling, (iv) ex-situ microstructural characterization, (v) evaluation of scaling the methodology for large-scale structures, and (vi) development of a data package to codes and standards organizations. As a part of this research, laser powder bed fusion of metals (316L, Alloy 718, and Ti6Al4V) was explored. This document provides an overview of the research performed over three years and serves as the final U.S. Department of Energy report for this project. In the third year, the project focused on the following activities: (a) in-situ infrared and optical imaging of each layer during processing of representative stainless steel geometries; (b) development of methodologies to analyze the data; and (c) application of ICME methodologies and other experiments to estimate the relevance of defects and microstructure to tensile properties.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗

DOE OSTI2020

ICME and In-Situ Process Monitoring for Rapid Qualification of Components Made by Laser-based Powder Bed Additive Manufacturing Processes for Nuclear Structural Applications

Additive manufacturing (AM) through selective powder bed melting of successive layers is being considered as disruptive technology for rapid production of low-cost nuclear reactor internal components with complex geometries. However, there is a potential for non-uniform distribution of physical features, such as porosity or microstructural differences, due to variations of temperature across a component build. These heterogenities make the deployment of traditional material qualification and non-destructive evaluation of AM components difficult. This research project explored the feasibility of using in-situ process monitoring methods and integrated computational materials engineering (ICME) principles as an alternate qualification methodology and approach. This project included six individual tasks: (i) design of artifacts relevant to the nuclear power industry, (ii) evaluation of laser processing and in-situ measurements, (iii) computational modeling, (iv) ex-situ microstructural characterization, (v) evaluation of scaling the methodology for large-scale structures, and (vi) development of a data package to codes and standards organizations. As a part of this research, laser powder bed fusion of metals (316L, Alloy 718, and Ti6Al4V) was explored. This document provides an overview of the research performed over three years and serves as the final U.S. Department of Energy report for this project. In the third year, the project focused on the following activities: (a) in-situ infrared and optical imaging of each layer during processing of representative stainless steel geometries; (b) development of methodologies to analyze the data; and (c) application of ICME methodologies and other experiments to estimate the relevance of defects and microstructure to tensile properties.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2023

Evaluation of Nickel Alloys, Manufactured through Powder Bed Fusion, for Application for Advanced Nuclear Reactors

In collaboration with other laboratories, Idaho National Laboratory has investigated additively manufactured alloys for applications in advanced nuclear reactors. The primary focus has been on nickel alloys, as well as “other” alloys, which are alloys not considered steel nor nickel-based alloys, manufactured by laser powder bed fusion. Suitability of investigated alloys were considered against a matrix of properties of interest, developed jointly with the collaborating laboratories. For the nickel alloys, Alloys 282 and 625 are considered promising due to their properties, existing data, and availability of commercial powder feedstock. Haynes 244 is also of interest for its molten salt corrosion resistance, however there is no current feedstock supply chain, and no experience with this alloy as an additively manufactured material. Iron-chrome-aluminum alloys, titanium alloys, zirconium alloys, ceramics, and ceramic inclusions were all considered within the other alloys category. The results and discussions within this report will be compiled with the investigations from the other collaborating laboratories and compiled into a final report later this year (2023).

36 MATERIALS SCIENCE↗

DOE OSTI2024

Creep-Fatigue Properties of Additional 316H PM-HIP Materials Fabricated from Different Powder Compositions and Processing Routes

The process of powder metallurgy (PM) hot isostatic pressing (HIP) works by consolidating powdered materials at relatively high temperature and pressure to form near-net-shaped components. Ideally, PM-HIP production methods can reduce component lead time and improve designs for high-temperature reactors and/or microreactors. To introduce PM-HIP into Section III, Division 5 of the American Society of Mechanical Engineers Boiler and Pressure Vessel Code, it is necessary to show adequate material properties regarding creep, high-temperature low-cycle fatigue, and creep fatigue. However, prior work has shown that the creep-fatigue cycles to failure for PM-HIP 316H stainless steel are greatly reduced compared to the conventional, wrought product. This work continued creep-fatigue analysis on a 316H stainless steel with lower oxygen and nitrogen contents and at different HIP parameters than previously analyzed. The objective was to better understand what is causing the reduced PM-HIP 316H performance so improvements can be made PM-HIP 316H creep-fatigue lifetimes.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

Testing and Modeling of Functionally Graded Aluminum-Doped Zinc Oxide Using Spark Plasma Sintering and Discrete Powder Layers of Varying Composition

Functionally graded material (FGM) ZnO is made via spark plasma sintering/field-assisted sintering technique (SPS/FAST) by varying the Al dopant content along the z-axis or pressing direction. A wide range of Al content (0–5 wt%) is used by adding Al powder to nanosized ZnO powder. Thermoelectric (TE) measurements are done on the FGM and individual layers made separately. X-ray diffraction (XRD) shows two phases, ZnO and spinel phase (ZnAl 2 O 4 ). High-resolution Raman spectroscopy reveals doped ZnO and spinel phase (ZnAl 2 O 4 ) spatially and shows segregation in the layer with highest Al content. Electron backscatter diffraction (EBSD) reveals noticeable grain growth with decreasing Al content, and there is a common, random preferred orientation in all layers. The tested properties are used to simulate efficiency curves for a discretely graded, five-layer FGM as well as a homogenous material, where both graded structures provide an opportunity to widen the current density ranges and therefore the temperature range of useful energy conversion.

36 MATERIALS SCIENCE↗

DOE OSTI2025

Laser powder bed fusion parameter estimation with k-NN

Abstract Laser powder bed fusion (L-PBF) is a technique within additive manufacturing that uses a high power density laser to build parts from fused powdered metal alloy. This technology is well equipped to produce complex parts with otherwise impossible features, such as hidden voids or lattice structures. Alongside capability, reliability and quality are key characteristics considered when choosing a manufacturing method, and these are gaining attention as this method becomes more prevalent in industry. One main indicator of a stable L-PBF process is consistent melt pool geometry, and the properties of which are likely to determine the quality of the part produced. As computing power and sensing technologies become more advanced, this melt pool geometry could be studied in real time. This work addresses the challenge by leveraging a k-nearest neighbor (k-NN) model to identify key features within melt pool imagery and predict the energy density. The k-NN model was trained on data provided by the National Institute of Standards and Technology (NIST). Data preprocessing was performed on the images to extract features that were used in the k-NN model. This approach was used to accurately infer the energy density of unseen layers within the same part. The algorithm was subsequently tested with unique scan strategies and found to reasonably estimate the energy density of different parts. A fivefold cross validation found the algorithm to be consistently predicting the class of 91.4% of the in situ melt pool images.

Jung, Patrick (ORCID:0000000267890859)↗

DOE OSTI2021

Measurements of the emanation of 37Ar and 39Ar from irradiated rocks and powders

The emanation fraction of radionuclides has been highlighted as a known source of uncertainty in the estimation of radionuclide source signatures from underground nuclear tests and other nuclear activities, particularly in the case of activation products. A system was developed at Pacific Northwest National Laboratory to quantify the emanation fraction of argon from samples ranging in particle size from powder to small rocks. Seven materials, two powders and five rock types, were neutron irradiated and the emanation fraction of 37Ar was measured. Additional measurements were made of the 39Ar emanation for four of these materials.

Johnson, Christine M.↗

DOE OSTI2024

Characterization and Rationalization of Microstructural Evolution in GRCop-84 Processed by Laser-Powder Bed Fusion (L-PBF)

In this study, prismatic geometries of GRCop-84 [Cu-8Cr-4Nb (at. pct)] were built with laser-powder bed fusion (L-PBF) process. The samples were sectioned parallel or perpendicular to the build direction and characterized in the as-built and after post-processing with a hot-isostatically pressing (HIP) treatment. The microstructure and phase evolutions were evaluated with optical microscopy, scanning electron microscopy (SEM), electron backscattered diffraction (EBSD), and high-temperature X-ray diffraction (HTXRD) up to 1223 K. The samples in the as-built conditions exhibited predominantly columnar epitaxial and misoriented Cu-FCC grains. The microstructure evolutions are discussed based on locations within the overall build geometry, the dynamics of small melt pool shape and sectioning effects. The above grain structure did not change significantly during post-process HIP treatment. The stability of this FCC grain structure is attributed to the formation of primary stable Cr 2 Nb (Laves phase) during L-PBF, even before the emergence of FCC grains from liquid. The stability of Cr 2 Nb in both as-built and HIPed samples were evaluated using high-temperature X-ray diffraction measurements and compared with that of gas-atomized powder. The significance of these results is discussed with reference to aerospace applications.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Leveraging Solute Segregation in Laser Powder Bed Fusion to Achieve Superior Strength and Ductility Via Single-Step Heat Treatment in Ti-Free Grade 300 Maraging Steel

Maraging steels are Fe-Ni precipitation-strengthened steels that can be heat treated for achieving high strength with an accompanying loss in ductility, a trend common to most metals. Here, we show that the segregation of Ni during laser powder bed fusion, commonly considered a nuisance that is dealt with via solutionizing heat treatments, can be leveraged via direct aging to achieve higher strength and ductility simultaneously, compared to a solutionized and aged condition. The high dislocation density in combination with solute segregation in the as-fabricated material promotes the precipitation of Mo-rich intermetallic phases that are responsible for the high strength, and the Ni segregated regions facilitate austenite reversion during direct aging. The reverted austenite enhances the elongation via transformation-induced plasticity. While overcoming the strength–ductility conundrum, direct aging can significantly reduce the energy and emissions associated with multistep heat treatments, especially in the global tool and die industry, while laser powder bed fusion (LPBF) can enable tools with integrated cooling channels for increased downstream production efficiency.

36 MATERIALS SCIENCE↗

DOE OSTI2021

High-Throughput Statistical Interrogation of Mechanical Properties with Build Plate Location and Powder Reuse in AlSi10Mg

Abstract Additive manufacturing (AM) allows agile, rapid manufacturing of geometrically complex components that would otherwise be impossible through traditional manufacturing methods. With this maturing manufacturing technology comes the need to adopt testing methods that are commensurate with the speed of additive manufacturing and take advantage of its geometric flexibility. High-throughput tensile testing (HTT) is a technique that allows a large number of tensile bars to be tested in a short amount of time. In the present study, HTT is used to evaluate AM AlSi10Mg produced using powder bed fusion with a Renishaw AM250 machine. Three parameters were varied in this study: (1) powder reuse history, (2) location on the build plate, and (3) size of the tensile specimen. For all parameter combinations, at least 22 specimens were tested; in several cases, over 40 were tested. This large dataset, consisting of over 500 tensile tests, permits Weibull statistical analysis and provides sufficient fidelity to isolate subtle trends that would have likely been missed in smaller, traditional datasets. The observed trends are rationalized in terms of the role of porosity and surface crust on mechanical response.

Carroll, Jay D. (ORCID:0000000258184709)↗

DOE OSTI2024

Standardization Gaps in Powder Feedstock Characterization and Establishing Acceptability for Reuse in Additive Manufacturing

Characterization techniques for powder feedstocks used in additive manufacturing (AM) have long been relied upon to describe the inputs to an AM workflow. However, functional gaps remain between tests to measure intrinsic and extrinsic properties with the direct performance within AM equipment. Furthermore, the common practice of reusing powder through multiple build cycles introduces effects and changes to feedstock performance that are otherwise difficult to measure quantitatively. Here, standardization and the development of new test methods have not kept pace with the rapid evolution of the AM industry and its reliance on highly coupled process-structure–property-performance relationships.

Characterization and Analytical Technique↗

DOE OSTI2024

Manufacturing ODS Steels from GARS Powders by Friction Consolidation and Extrusion

Previous research suggested that friction-based processing is a promising method for fabricating oxide dispersion-strengthened (ODS) steel. In this study, we combined friction consolidation and friction extrusion to successfully manufacture ODS steel rods using precursor powder made with gas atomization reaction synthesis. We examined the microstructure evolution from the initial powder to the final extruded rod, which revealed the dispersion process of Y. Additionally, by comparing the microstructures of three rods extruded at different temperatures, we showed that low-temperature friction extrusion effectively enhanced microstructure uniformity and prevented grain coarsening, leading to improved mechanical properties. Furthermore, our findings provide practical guidelines for adjusting processing parameters in the production of ODS steel using friction-based processing.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Synthesis of precipitation-strengthened Al-Sc, Al-Zr and Al-Sc-Zr alloys via selective laser melting of elemental powder blends

Selective laser melting is used to create Al-1.5Sc, Al-1.5Zr and Al-0.75Sc-0.75Zr (at.%) alloys from blends of elemental Al, Sc, and Zr powders. This study investigates elemental alloying elements (Sc and Zr) which are high-melting and highly reactive, unlike previous work which focused on more concentrated elemental additions of lower-melting, lower-reactivity Cu and Si to aluminum. High-speed in situ synchrotron x-ray imaging and diffraction show that the 20–30 μm Al, Sc, and Zr powders fully melt and sufficiently mix in the molten state to create, on solidification, a homogeneous distribution of primary, micron-size L12 precipitates (Al 3 Sc, Al 3 Zr, and Al 3 (Sc,Zr), respectively) and nucleate micron-size Al matrix grains, as confirmed by SEM imaging of cross-sections. Here, a second laser pass, simulating a realistic additive-manufacturing build condition, fully remelts the initial volume which shows, after solidification, the same Al 3 (Sc,Zr) L1 2 primary micro-precipitates and very fine Al grains. After aging at 300–400°C, the alloys show large increases in hardness, consistent with an exceptionally high number density (1.4 × 10 24 m –3 ) and volume fraction (2.5%) of secondary Al 3 (Sc,Zr) nano-precipitates with a Sc-rich core and Zr-rich shell, as measured via atom-probe tomography.

36 MATERIALS SCIENCE↗