Effects of Wire Diameter and Filament Size on the Processing Window of Bi-2212 Round Wire
High engineering critical current density (J E of 1300 A/mm 2 at 4.2 K and 15 T) in Bi-2212 round wire has been achieved through a partial melt, overpressure heat treatment process. J E varies strongly with processing conditions, particularly the maximum heat treatment temperature (T max ). Increasing T max results in longer time in the melt (defined as the time between when Bi-2212 melts on heating and when Bi-2212 begins to form on cooling), more bridging between the filaments, lower J E , and higher ac losses. A wide processing window with a large range of T max that has a nearly constant J E is desired for processing large coils with large thermal mass and significant thermal time constants that may make precise control over the desired temperature – time profiles uncertain. Accordingly, we wanted to explore broadening the T max window by controlling the Bi-2212 powder melting or wire architecture design. In this work, we report on studies of the performance variation with T max for two production wires with a filling factor of about 20% and 85 × 18 filaments where filament size was varied by changing the wire diameter, a process which also shortens the distance between filaments. We found that wires with smaller filament diameter (9 to 11 μm) showed a peak J E at the low end of T max and also a J E that was more sensitive to T max . A J E – T max plot showed a plateau J E (4.2 K, 5 T) of ~1100 A/mm 2 between T max of 886 and 894 °C for 1.0 and 1.2 mm wires, where J E is less sensitive to the wire diameter and T max . This J E plateau range is a preferred processing window for achieving high J E in coils.