Surface hardening of steel by boriding in a cold rf plasma

Scanning electron spectroscopy, X-ray diffractometry, Auger electron spectroscopy, and microhardness measurements, are used to study the surfaces of 4340-steel samples that have been borided in a cold RF plasma which had been initiated in a gas mixture of 2.7 percent diborane in Ar. As a result of the dislocation of the diborane in the plasma, boron is deposited on the surface of the steel substrate and two crystalline phases, tetragonal Fe2B and orthorhombic FeB, are formed. The formation of boride phases then increases the surface microhardness from 2650 MPa to a maximum value of 7740 MPa.

Finberg, I.↗

Radiation Hardening of Computers

Single-event upsets reduced by use of oversize transistors. Computers made less susceptible to ionizing radiation by replacing bipolar integrated circuits with properly designed, complementary metaloxide-semiconductor (CMOS) circuits. CMOS circuit chips made highly resistant to single-event upset (SEU), especially when certain feedback resistors are incorporated. Redesigned chips also consume less power than original chips.

Nichols, D. K.↗

Chemistry of MOS-LSI radiation hardening

The objective of this task was to obtain chemical information on MOS test samples. Toward this end, high resolution X-ray photoemission spectroscopy (XPS) has been the primary techniques used to characterize the chemistry and structure of the SiO2/Si interface for a variety of MOS structures with differing degrees of susceptibility to damage by ionizing radiation. The major accomplishments of this program are: (1) the identification of a structurally distinct region of SiO2 in the near-interfacial region of thermal SiO2 on Si; (2) the identification in the near-interfacial region of SiO2 structural differences between radiation hard and soft gate oxides; (3) the direct observation of radiation-induced damage sites in thermal SiO2 with XPS using in situ electron stress; (4) the correlation of suboxide state distributions at the SiO2/Si interface with processing parameters and radiation susceptibility; (5) the development of a chemical mechanism for radiation-induced interface state generation in SiO2/Si structures; and (6) the development benign chemical profiling techniques which permit the investigation of oxide/semiconductor structures using surface sensitive electron spectroscopic techniques.

Grunthaner, P.↗

Radiation hardening design of nuclear powered spacecraft

The design and operation of space systems utilizing nuclear fueled power systems must consider the radiation environment from the earliest stages of their design. A range of nuclear systems are being considered for present and future satellite systems capable of supplying tens of kilowatts to multimegawatt and generating a corresponding range of radiation environments. The effects of these radiations on electronics and materials can be minimized by implementing early design considerations which maximize the design efficiency and minimize the impact on system mass. Space systems design considerations for the radiation environment must include all sources in addition to the self induced gamma ray and neutron radiation. These include the orbital dependent environment from the high energy electron and protons encountered in natural space. The system trades which the designer must consider in the development of space platforms which utilize nuclear reactor power supplies are discussed.

Schmidt, R. E.↗

Surface fatigue life of carburized and hardened M50NiL and AISI 9310 spur gears and rolling-contact test bars

Spur gear endurance tests and rolling-element surface tests were conducted to investigate vacuum-induction-melted, vacuum-arc-melted (VIM-VAR) M50NiL steel for use as a gear steel in advanced aircraft applications, to determine its endurance characteristics, and to compare the results with those for standard VAR and VIM-VAR AISI 9310 gear material. Tests were conducted with spur gears and rolling-contact bars manufactured from VIM-VAR M50NiL and VAR and VIM-VAR AISI 9310. The gear pitch diameter was 8.9 cm (3.5 in.). Gear test conditions were an inlet oil temperature of 320 K (116 F), and outlet oil temperature of 350 K (170 F), a maximum Hertz stress of 1.71 GPa (248 ksi), and a speed of 10,000 rpm. Bench rolling-element fatigue tests were conducted at ambient temperatures with a bar speed of 12,500 rpm and a maximum Hertz stress of 4.83 GPA (700 ksi). The VIM-VAR M50NiL gears had a surface fatigue life that was 4.5 and 11.5 times that for VIM-VAR and VAR AISI 9310 gears, respectively. The surface fatigue life of the VIM-VAR M50NiL rolling-contact bars was 13.2 and 21.6 times that for the VIM-VAR and VAR AISI 9310, respectively. The VIM-VAR M50NiL material was shown to have good resistance to fracture through a fatigue spall and to have fatigue life far superior to that of both VIM-VAR and VAR AISI 9310 gears and rolling-contact bars.

Townsend, Dennis P.↗

Dispersion strengthening of precipitation hardened Al-Cu-Mg alloys prepared by rapid solidification and mechanical alloying

Several Al-4Cu-1Mg-1.5Fe-0.75Ce alloys have been processed from either rapidly solidified or mechanically alloyed powder using various vacuum degassing parameters and consolidation techniques. Strengthening by the fine subgrains, grains, and the dispersoids individually or in combination is more effective when the alloys contain shearable precipitates; consequently, the strength of the alloys is higher in the naturally aged rather than the artificially aged condition. The strengths of the mechanically alloyed variants are greater than those produced from prealloyed powder. Properties and microstructural features of these dispersion strengthened alloys are discussed in regards to their processing histories.

Gilman, P. S.↗

Diamond films for laser hardening

Laser-damage experiments were performed on free-standing polycrystalline diamond films prepared by plasma-enhanced CVD. The high laser-induced stress resistance found for this material makes it useful for thin-film coatings for laser optics. Results for diamond-coated silicon substrates demonstrate the enhanced damage threshold imparted by diamond thin-film coatings to materials susceptible to laser damage.

Albin, S.↗

Surface fatigue life of carburized and hardened M50NiL and AISI 9310 spur gears and rolling-contact test bars

Spur gear endurance tests and rolling-element surface tests were conducted to investigate vacuum-induction-melted, vacuum-arc-melted (VIM-VAR) M50NiL steel for use as a gear steel in advanced aircraft applications, to determine its endurance characteristics, and to compare the results with those for standard VAR and VIM-VAR AISI 9310 gear material. Tests were conducted with spur gears and rolling-contact bars manufactured from VIM-VAR M50NiL and VAR and VIM-VAR AISI 9310. The gear pitch diameter was 8.9 cm (3.5 in.). Gear test conditions were an inlet oil temperature of 320 K (116 F), and outlet oil temperature of 350 K (170 F), a maximum Hertz stress of 1.71 GPa (248 ksi), and a speed of 10,000 rpm. Bench rolling-element fatigue tests were conducted at ambient temperatures with a bar speed of 12,500 rpm and a maximum Hertz stress of 4.83 GPA (700 ksi). The VIM-VAR M50NiL gears had a surface fatigue life that was 4.5 and 11.5 times that for VIM-VAR and VAR AISI 9310 gears, respectively. The surface fatigue life of the VIM-VAR M50NiL rolling-contact bars was 13.2 and 21.6 times that for the VIM-VAR and VAR AISI 9310, respectively. The VIM-VAR M50NiL material was shown to have good resistance to fracture through a fatigue spall and to have fatigue life far superior to that of both VIM-VAR and VAR AISI 9310 gears and rolling-contact bars.

Townsend, Dennis P.↗

Be-Cu precipitation hardening experiment

The following is a laboratory experiment designed to further a student's understanding of materials science. The student performing this experiment should have a knowledge of binary phase diagrams. The objectives of this experiment are as follows: (1) to give the student a hands-on approach to changing materials properties through heat treatment of a specimen; (2) to quantify the amount of strengthening obtained in the specimen; and (3) to encourage the student to speculate about the structural changes that have occurred in the material to cause the changes in strength.

Cowan, Richard L.↗

The theory of plasticity in the case of simple loading accompanied by strain-hardening

The author has previously shown that a deformation theory of plasticity is entirely adequate when the loading is simple; that is, when all the applied forces grow in proportion to a single parameter. The author now shows how a general plasticitytheory for any complex loading may be constructed by successively adding quantities of the nature of correction terms to the deformation theory. All of the theories of plasticity so far suggested for the complex loading condition are shown to be special cases of this general theory.

THEORIES - PLASTICITY↗