Effects of He Ion Irradiation in Simple Borosilicate Glasses for HLW Immobilisation - 20324
High-level radioactive waste (HLW) consists of fission products and minor actinides. Borosilicate glass is the host material of choice in most countries to safely immobilize HLW, followed by eventual geological disposal. HLW glasses will experience both self-heating and self-irradiation effects due to the decay of fission products and minor actinides present therein. During the first 500 years of geological disposal, beta-gamma decay will be the main source of radiation due to short half-lives of fission products, as compared to very long-lived actinides which will be responsible for irradiation over much longer timescales. High-energy alpha particles and alpha recoil nuclei can potentially have significant impact (stored energy, volume change, accumulated dose, chemical durability) on the performance of the wasteform over longer timescales. Thus, to ensure safe and economic disposal over geological periods (10{sup 4} - 10{sup 6} years), the assessment of performance and properties in terms of radiation effects becomes indispensable. This work aims to simulate the effects of alpha decay in radioactive waste glasses. Two international glasses, namely UK 'MW' lithium-sodium borosilicate and Indian sodium-barium borosilicate, which are being used as HLW immobilization matrices by the UK and India respectively, were prepared by a melt-quench method and annealed below their glass transition temperatures. Both glasses were irradiated with 650 KeV He{sup 2+} ions with doses ranging from 10{sup 15} to 10{sup 17} ions/cm{sup 2}. Structural analysis was carried out using electron paramagnetic resonance (EPR) and Raman spectroscopies. First derivative continuous wave EPR spectra were recorded for all pristine and irradiated glass monoliths at room temperature using an X-band (frequency 9.6 GHz) EPR Bruker spectrometer. Results from EPR analyses showed the formation of irradiation induced paramagnetic centers at g ∼ 2.00 in all irradiated glasses. Raman spectra of pristine and irradiated samples were acquired, and showed notable changes in glass structure post-irradiation, with the emergence of a broad Raman band at 1560 cm{sup -1} upon irradiation with high fluences. (authors)