Evidence for I 2 loss from the perovskite–gas interface upon light-induced halide segregation
Sunlight-induced halide segregation in (CH 3 NH 3 )Pb(Br x I 1−x ) 3 (1 > x > 0.2), which limits obtainable voltages from solar cells with these perovskite absorbers, reverses upon resting in the dark. However, sustained illumination at ca. 1 sun opens a new decomposition pathway, leading to irreversible I 2 loss in an open system. We conclusively show I 2 off-gassing from halide-segregated (CH 3 NH 3 )Pb(Br 0.75 I 0.25 ) 3 by trapping gaseous I 2 and tracking the electronic conductivity of the perovskite, which increases from electron-doping as iodides are oxidized to iodine. Importantly, we show that this reaction occurs across the perovskite-air solid–gas interface, without confounding effects from solvent or reactive solid interfaces. This characterization was conducted under a nitrogen atmosphere, avoiding vacuum- and oxygen-driven I 2 loss pathways. Consistent observations of I 2 loss upon light-soaking CsPb(Br 0.75 I 0.25 ) 3 films show that this reaction is intrinsic to the inorganic framework. We propose that the disruption of iodide-rich domains in the halide-segregated films through I 2 loss can masquerade as a light-induced healing or apparent remixing of the segregated film, when in fact it leads to irreversible decomposition. Although I 2 off-gassing is less likely in bromide-rich solid solutions, light-induced halide segregation brings the iodides into proximity and forms electronic states that are energetically poised to trap and accumulate holes, providing a driving force for I 2 loss. Thus, even bromide-rich mixed-halide perovskite absorbers will benefit from I 2 -impermeable encapsulation for long-term stability.