SEARCH · Engineering Papers

Results for “Residual Stresses”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

SourceResearch connectionFrom yearThrough year

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 361 records · Page 20

All sources NASA NTRS DOE OSTI

NASA NTRS1990

Use of unbalanced laminates as a screening method for microcracking

State-of-the-art, high temperature polyimide matrix composites, reinforced with continuous graphite fibers are known to be susceptible to intraply cracking when thermally cycled over their useful service temperature range. It is believed that the transply cracking, in part, results from residual stresses caused by differences in coefficients of thermal expansion (CTE) between the polymer matrix and the reinforcement. Thermal cycling tests to investigate this phenomenon involve expensive time and energy consuming programs which are not economically feasible for use as a part of a materials screening process. As an alternative to thermal cycling studies, a study of unbalanced crossply graphite fiber reinforcement composites was conducted to assess the effect of the composite ply layup and surface condition on the residual stresses that remain after the processing of these materials. The residual stresses were assessed by measuring the radii of curvature of the types of laminates that were studied. The temperature at which stress-free conditions existed were determined and a dye penetrant method was used to observe surface damage resulting from excessive residual stress buildup. These results are compared with some published results of thermal cycling tests that were previously conducted on balanced polyimide composites.

Papadopoulos, Demetrios S.↗

NASA NTRS1977

Development of a plasma sprayed ceramic gas path seal for high pressure turbine applications

The plasma sprayed graded layered yittria stabilized zirconia (ZrO2)/metal(CoCrAlY) seal system for gas turbine blade tip applications up to 1589 K (2400 F) seal temperatures was studied. Abradability, erosion, and thermal fatigue characteristics of the graded layered system were evaluated by rig tests. Satisfactory abradability and erosion resistance was demonstrated. Encouraging thermal fatigue tolerance was shown. Initial properties for the plasma sprayed materials in the graded, layered seal system was obtained, and thermal stress analyses were performed. Sprayed residual stresses were determined. Thermal stability of the sprayed layer materials was evaluated at estimated maximum operating temperatures in each layer. Anisotropic behavior in the layer thickness direction was demonstrated by all layers. Residual stresses and thermal stability effects were not included in the analyses. Analytical results correlated reasonably well with results of the thermal fatigue tests. Analytical application of the seal system to a typical gas turbine engine application predicted performance similar to rig specimen thermal fatigue performance. A model for predicting crack propagation in the sprayed ZrO2/CoCrAlY seal system was proposed, and recommendations for improving thermal fatigue resistance were made. Seal system layer thicknesses were analytically optimized to minimize thermal stresses in the abradability specimen during thermal fatigue testing. Rig tests on the optimized seal configuration demonstrated some improvement in thermal fatigue characteristics.

Shiembob, L. T.↗

NASA NTRS1990

Micromechanical thermal analysis of interphase region in a titanium aluminide MMC

The high reactivity between the fiber and matrix in silicon carbide/titanium aluminide MMCs leads to the formation of brittle reaction products at the fiber/matrix (F/M) interface. Also, the high thermal expansion coefficient mismatch between the fiber and matrix leads to high tensile residual stresses at the F/M interface, and this can lead to premature cracking during cooldown. One solution to these problems is the use of a metallic fiber coating like Ta which acts as an F/M diffusion barrier and reacts with the matrix to form a beta stabilized compliant layer. A finite element micromechanics analysis was performed to study the effects of Ta and beta interphase layers on the thermal residual stresses during consolidation. A 5-micron-thick beta layer reduced cool-down stresses by 8 percent compared to a 2 percent reduction computed for a Ta layer of the same thickness. Plastic yielding in the Ta was not effective in reducing cool-down stresses. Compliant alpha-2 particles next to the stiffer gamma particles reduced stresses in the gamma particles by less than 2 percent. A simple closed form analysis was developed to calculate thermal residual stresses in a fiber/interphase/matrix system. A 2-micron-thick Ag interphase layer was found to reduce residual stresses by about 11 percent.

Naik, R. A.↗

NASA NTRS1981

Effects of environmental variables on the crack initiation stages of corrosion fatigue of high strength aluminum alloys

Fatigue initiation in six aluminum alloys used in the aircraft industry was investigated. Cyclic loading superimposed on a constant stress was alternated with atmospheric corrosion. Tests made at different stress levels revealed that a residual stress as low as 39% of the yield strength caused stress corrosion cracking in some of the alloys. An atmospheric corrosion rate meter developed to measure the corrosivity of the atmosphere is described. An easily duplicated hole in the square test specimen with a self-induced residual stress was developed.

Poteat, L. E.↗

NASA NTRS1998

Electroformed Nickel Mirrors for the Next Generation Space Telescope

This paper summarizes the work to date on a novel mirror fabrication technique being developed at the Marshall Space Flight Center for potential use on the Next Generation Space Telescope (NGST). This technique involves forming an extremely lightweight mirror by electroplating nickel and nickel based alloys onto a highly polished precision mandrel. The resulting mirror shell can then be backed up with or attached to a lightweight structure to produce a mirror element that is on the order of 15 kg/sq m areal density. Since the mirrors are fabricated from a mandrel (or master), subsequent mirrors can be made with very high economy; this technique is particularly suited to segmented mirrors schemes whereby large apertures are achieved through the deployment of smaller segments. Control of the electroplating process is the key element for producing high quality optics; bath chemistry and real time control of the plating current density yields uniform grained electroforms with zero residual stress. To accomplish this, a special electronic sensor was developed whereby the residual stress can be monitored as the nickel is electrolytically deposited. This information is used in a feedback loop to modulate current density which, in turn, directly governs the residual stress. Details pertaining to this and other aspects of the fabrication of a half meter mirror will be published along with test results and metrology data.

Redmon, John W.↗

DOE OSTI2024

Effect of Internal Structure on Warpage in a Large-Scale Additive Manufacturing Process With Bio-Derived Composites

Extrusion-based large-format additive manufacturing (LFAM) often results in unintended deformation and failures due to thermal residual stress between layers. This LFAM involves a hot molten polymer deposited on a previously deposited and cooled layer, generating a temperature mismatch between the layers. The temperature discrepancy causes a thermal contraction mismatch, generating thermal residual stress. Due to the residual stress, printed structures experience warpage and delamination Therefore, understanding the heat distribution behavior is essential to preventing undesired deformation and failures. The goal of this study is to investigate the effect of infill patterns on heat distribution and deformation in an LFAM system. Wood fiber-reinforced polylactic acid was used as a sustainable and low-cost reinforcement material. A numerical model was developed to predict the temperature and deformation field with thermo-mechanical properties, which were measured by a dynamic mechanical analysis and a thermal expansion test. Simulations were performed on a box geometry with three different infill patterns. The simulation model was verified with temperature data gathered from an infrared camera. The results show good agreement between predicted and measured temperature profiles. The developed simulation model was applied to a roof tray with different infill patterns for a case study. We found that the different thermal mass distributions resulting from the various infill patterns affected the heat distribution and deformation. These findings contribute to a better understanding of the thermal and mechanical behavior of LFAM.

Jo, Eonyeon↗

NASA NTRS1983

Experimental creep data for a built-up aluminum/titanium structure subjected to heating and loading

Experimental creep, temperature, and strain data resulting from a laboratory experiment on a built-up aluminum/titanium structure are presented. The structure and the experiment are described in detail. A heating and loading experiment lasting approximately six hours is conducted on a test structure. Considerable creep strain resulted from compressive stresses in the heated skin. Large residual stresses were found after the experiment was completed. The residual stresses in the substructure frames were large enough to preclude further cycles of creep experiments with this built-up structure because of concern that the frame webs would buckle.

Jenkins, J. M.↗

DOE OSTI2021

Additive manufacturing of cobalt-based alloy on tool steel by directed energy deposition

Cladding hard-surfacing alloys on tool steel is an effective approach to enhance the surface properties of tool steel. In this study, a Co-based alloy was deposited on tool steel by Directed Energy Deposition (DED) following a three-factor three-level design of experiment matrix with varied laser power, scan speed, and powder flow rate. The microstructure of the deposits was characterized using scanning electron microscopy (SEM). The residual stress on the surface of the samples was measured by the X-ray diffraction (XRD) sin2? technique. The parameters that produced promising deposits were used to fabricate samples for tensile test, four-point bending test, Charpy impact test, and hardness measurement. Our result reveals that the processing parameters have a significant role in the residual stress of the coatings. Residual stress reduces with the increase of laser energy density. Cracks were found at samples with energy density below a threshold. Tensile testing of the coating/substrate combined structure reveals fracture at the coatings with an ultimate tensile strength of 633.9 ± 54.7 MPa. The bi-material interface survived the tensile test, indicating a strong interfacial bond. The four-point bending test of coating/substrate laminates shows an ultimate flexure strength of 860.6 ± 36.9 MPa. Cracks initiated from the coatings ignored the interface and penetrated the substrate, suggesting a solid bi-material bond. Charpy impact test shows the absorbed energy of coating/substrate laminates is more than doubled that of the substrate.

36 MATERIALS SCIENCE↗

NASA NTRS2001

Evaluation of a Linear Cumulative Damage Failure Model for Epoxy Adhesive

Recently a significant amount of work has been conducted to provide more complex and accurate material models for use in the evaluation of adhesive bondlines. Some of this has been prompted by recent studies into the effects of residual stresses on the integrity of bondlines. Several techniques have been developed for the analysis of bondline residual stresses. Key to these analyses is the criterion that is used for predicting failure. Residual stress loading of an adhesive bondline can occur over the life of the component. For many bonded systems, this can be several years. It is impractical to directly characterize failure of adhesive bondlines under a constant load for several years. Therefore, alternative approaches for predictions of bondline failures are required. In the past, cumulative damage failure models have been developed. These models have ranged from very simple to very complex. This paper documents the generation and evaluation of some of the most simple linear damage accumulation tensile failure models for an epoxy adhesive. This paper shows how several variations on the failure model were generated and presents an evaluation of the accuracy of these failure models in predicting creep failure of the adhesive. The paper shows that a simple failure model can be generated from short-term failure data for accurate predictions of long-term adhesive performance.

Richardson, David E.↗

NASA NTRS1995

Stress In A Fiber During Curing Of Surrounding Matrix Resin

Experiments run to determine variation in tensile stress in single fiber during curing of matrix resin surrounding fiber. Study part of effort to understand physical mechanisms affecting residual stresses in matrix/fiber composites, with view toward optimizing curing cycles (in particular, optimizing temperature-vs.-time schedules of final cooldowns to ambient temperature) to minimize residual stresses. Results signify primary mechanisms affecting residual stress in fibers are thermal expansion and contraction and cure shrinkage of matrix material.

Bowles, Kenneth J.↗

DOE OSTI2021

Residual strain-stress in manganese steel railway crossing determined by synchrotron and laboratory X-rays

The residual stress within the nose of a worn manganese steel railway crossing was investigated. The macroscopic residual stress at the running surface was determined in areas with and without visual faults by laboratory X-rays. To get information about the penetration depth of the residual stress, synchrotron X-ray diffraction was used to map the distribution of local (within grain) residual strains below the running surface. The laboratory X-ray measurements revealed significant compressive stress on the rail running surface. The synchrotron measurements documented that local strains exist through the entire depth investigated. Relations between residual stress, plastic deformation, and crack formation are analysed, leading to a discussion on potentials/limitations of the two experimental methods for investigations of residual stress in large engineering components.

differentia aperture synchrotron diffraction↗

NASA NTRS1997

Fiber Contraction Approaches for Improving CMC Proportional Limit

The fact that the service life of ceramic matrix composites (CMC) decreases dramatically for stresses above the CMC proportional limit has triggered a variety of research activities to develop microstructural approaches that can significantly improve this limit. As discussed in a previous report, both local and global approaches exist for hindering the propagation of cracks through the CMC matrix, the physical source for the proportional limit. Local approaches include: (1) minimizing fiber diameter and matrix modulus; (2) maximizing fiber volume fraction, fiber modulus, and matrix toughness; and (3) optimizing fiber-matrix interfacial shear strength; all of which should reduce the stress concentration at the tip of cracks pre existing or created in the matrix during CMC service. Global approaches, as with pre-stressed concrete, center on seeking mechanisms for utilizing the reinforcing fiber to subject the matrix to in-situ compressive stresses which will remain stable during CMC service. Demonstrated CMC examples for the viability of this residual stress approach are based on strain mismatches between the fiber and matrix in their free states, such as, thermal expansion mismatch and creep mismatch. However, these particular mismatch approaches are application limited in that the residual stresses from expansion mismatch are optimum only at low CMC service temperatures and the residual stresses from creep mismatch are typically unidirectional and difficult to implement in complex-shaped CMC.

DiCarlo, James A.↗

DOE OSTI2022

Residual elastic strain evolution due to thermal cycling of a ceramic-metal composite (WC-Cu) via high energy X-ray diffraction and analytical modeling

Residual stress, when superimposed with in-service loading, can significantly reduce the lifetime and performance of a component. Ceramic-metal composites are susceptible to residual stresses due to the thermal expansion mismatch of the ceramic and metallic phases. The WC-Cu composite explored in the present study provides a promising combination of thermal conductivity and strength properties, while exhibiting counterintuitive improvements in strength and ductility after thermal cycling. Further, this work quantifies the evolution of the residual elastic strains as a result of processing and cyclic thermal loading in a co-continuous WC-Cu composite through experimental high energy X-ray diffraction and kinetics-based modeling. Both analyses indicate that processing-induced residual tensile stress in the copper phase is relieved upon subsequent thermal cycling, with kinetics modeling revealing the cyclic-dependent nature of the active power-law creep mechanisms. The results indicate that, through stress relaxation, this material system maintains structural stability during thermal cycling. The illustrated kinetics of relaxation can inform general material processors and designers of ceramic-metal composites to minimize detrimental residual stress and improve performance of these material systems.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Unveiling the origins of work-hardening enhancement and mechanical instability in laser shock peened titanium

Laser shock-peening (LSP) produces complex gradients in microstructures and residual stresses, which enables fabrication of metallic engineering components with superior mechanical properties. In this work, we use non-destructive and spatially resolved high-energy X-ray diffraction (HE-XRD) to investigate the influences of LSP on microstructure, surface topography, and residual stress for high purity titanium plates. LSP is found to produce large compressive in-plane residual stresses near the peened surface which monotonically decay to zero about 2.5 mm below the surface. These properties were also tracked during in-situ tensile loading, allowing stress partitioning and work-hardening rates to be measured as a function of depth. The surface region is found to have the highest work-hardening rate and remain mechanically stable up to sample failure. In addition, a crystal rigid rotation along a transversal axis of about 27 & nbsp; was observed at large applied strain near the surface region, which is attributed to the formation of denser dispersed shear bands. Furthermore, a sudden drop in tensile stress was observed at a depth of similar to 160 mu m from the LSP surface, indicating the formation of a localized mechanical instability zone (LMIZ). The origin of this LMIZ could be attributed to the increase in shear stress induced by a load transfer from LSP surface due to the formation of denser dispersed shear bands. These observations indicate a localized transition in deformation behavior has occurred from dispersed shear banding to LMIZ and homogeneous deformation.

36 MATERIALS SCIENCE↗

DOE OSTI2025

Simulation Tools for Characterizing Stress Distribution in Laser Welded Dissimilar Joints

This project focuses on developing a thermo-metallurgical-mechanical modeling method to accurately predict the microstructural evolution and residual stress in laser welding between dissimilar metals, such as HSLA steel and high carbon equivalent (CE) gear steel. The method leverages a comprehensive material database to model the temperature and rate dependent phase transformations, along with their associated effects on material properties, such as thermal expansion and flow stress, throughout the welding process. A key innovation is the incorporation of phase transformation and phase-specific properties, which enhances the accuracy of residual stress predictions. The mixture material in the fusion zone due to the dissimilar metals will also be addressed in the numerical model. This is especially critical in scenarios involving phase transformations in the fusion zone and heat-affected zone (HAZ), where the phase changes can induce substantial residual stress variations. The material database has been generated using JMatPro. The modeling approach is implemented through a custom User Material (UMAT) subroutine, executed with the commercial finite element software Abaqus.

36 MATERIALS SCIENCE↗

DOE OSTI2025

Simulation Tools for Characterizing Stress Distribution in Laser Welded Dissimilar Joints

36 MATERIALS SCIENCE↗

DOE OSTI2024

Failure Analysis for Molten Salt Thermal Energy Storage Tanks for In-Service CSP Plants

Thermal Energy Storage (TES) is a fundamental component in concentrating solar power (CSP) plants to increase the plant's dispatchability, capacity factor, while reducing the levelized cost of electricity. In central receivers CSP plants, nitrate molten salts have been used for several years for operation temperatures of up to 565 degrees C. Despite many efforts to advance nitrate salt to higher operation temperatures (even considering a replacement with molten chloride salts) to achieve higher energy conversion efficiencies, the 565 degrees C temperature is currently considered the state-of-the art. Although molten salt tanks have been broadly deployed in commercial CSP plants worldwide, several failures have been reported in these tanks after a few months or years of operation, causing significant economic loss and mistrust in CSP technologies. Most of these failures are associated with the infancy of the technology and multiple issues related to tank design, fabrication, commissioning, and aggressive operation. A technical standard dedicated to the design and fabrication of molten nitrate TES tanks does not exist today. Current in-service molten salt tanks have been generally designed based on the American Petroleum Institute's (API) 650 and ASME Section II standards. The API 650 code provides guidelines for dimensions and fabrication for oil storage tanks up to 260 degrees C. The ASME standard provides allowable stress values for various materials at a range of temperatures and conditions. Both standards seem to be limited for molten salt TES tanks where high temperatures, thermal cycling, and transient conditions are expected. In 2020, NREL released the Concentrating Solar Power Best Practices Study (NREL/TP-5500-75763) that summarized multiple issues in CSP plants, along with potential alternatives and recommendations to address those issues based on information collected from participants representing about 80% of operating CSP plants in the world. One of the recommendations from this study was the development of accurate and validated models to evaluate the plant's transient operation, capable of capturing the effect of short-term clouds and operator response, while being flexible in being adapted to various spatial and temporal resource data. The "Failure Analysis for Molten Salt Thermal Energy Tanks for In-Service CSP Plants" project was inspired on this recommendation and was focused on (1) the development and validation of a physics-based model for a representative, commercial-scale molten salt tank, (2) performing simulations to evaluate the behavior of the tank as a function of typical plant operation conditions, (3) understanding tank failures mechanisms, (4) determining the residual stress and distortion in the tank floor after welding fabrication and evaluating their impact in the stresses developed in the tank during operation, (5) assessing the impact of key operation parameters on the temperature and stress distribution, (6) conduct a preliminary evaluation of design features to reduce stress and improve tank's reliability, and (7) estimate the tank's service life based on the stress developed under diverse operation scenarios. From the analysis conducted in the project and presented in this report, it was found that maximum stresses surpassing the yield strength point of the stainless steel (SS) 347H are developed on the tank floor near the perimeter. These large stresses are strongly influenced by the initial residual stresses and distortion of the tank floor after welding fabrication. During operation, large stresses are developed in the tank floor at high operation temperatures with large salt inventory levels during transient operation. High stresses are also related to elevated temperature gradients in the tank floor that could be attributed to insufficient mixing within the salt inflow and the salt inventory. Based on the analysis, creep is the predominant failure mechanism. However, the large stress levels could favor the plastic deformation into buckles, and crack formation due to stress relaxation cracking during cycle operation. A lifetime below 3 years was estimated for the typical plant operation conditions and a specific initial residual stress and deformation distribution of the tank floor. The estimated life agrees with the service time to failure reported in several commercial molten salt tanks. Desing and operation guidelines can be extracted from the analysis presented in this report, which could be adopted by tank manufacturers and CSP operators to advance toward an ultimate solution for tank failures by reducing residual and operational stresses to achieve a tank service life of more than 30 years. Addressing failures in molten salt TES tanks is fundamental for the CSP industry's survivability, but it is also important for other industrial and power generation applications using this technology, including nuclear and concentrating solar thermal.

14 SOLAR ENERGY↗

DOE OSTI2024

Stress relaxation cracking susceptibility evaluation in 347H stainless steel welds

Abstract Stress relaxation cracking (SRC) has been reported as a dominant failure mechanism for 347H stainless steel welds at elevated service temperatures, occurring in either the heat-affected zone (HAZ) or fusion zone (FZ). In this study, SRC susceptibility of physically simulated HAZ and cross-welded E347-347H stainless steel welds was studied using a four-step accelerated SRC test with a thermomechanical physical simulator. The stress and temperature range studied represents weld-induced residual stress at 150–600 MPa and post-weld heat treatment temperatures between 800 and 1050 °C. For all temperature conditions, the cross-welded samples failed at a lower critical stress threshold than the simulated HAZ. A finite element model of a 50.8-mm-thick single-V groove weld was used to generate the residual stress maps induced by a 40-pass welding procedure, which in combination with the experimental threshold stress map predicted potential SRC failure locations. Postmortem microstructural evaluations were performed to identify contributing characteristics to SRC. It was found that HAZ samples exhibited a combination of creep void development, secondary cracks with intergranular fracture near grain boundary carbides, and eutectic phases. FZ samples showed brittle fracture with cracks propagating along straight, non-tortuous interdendritic grain boundaries.