Mixing of two liquid metals on spar payload due to spin-up and spin-down

Unexpected results from SPAR experiments, directed at obtaining fine dispersions of metal systems that in a 1-g environment tend to segregate very rapidly, were considered. The physical processes occurring in fluid samples, such as the SPAR samples before solidification, were shown to be insufficient to produce a well mixed liquid by the time solidification was initiated. This would result in solidified samples with the type of segregation noted in the SPAR samples. Experimental evidence and analytical arguments are presented.

Schafer, C. F.↗
DOE OSTI2024

Liquid metal compatibility of pre-oxidized FeCrAl in flowing Sn

Here, a flowing Sn thermal convection loop (TCL) experiment was conducted in FeCrAlMo (Kanthal alloy APMT) tubing for 1000 h with a peak temperature of 400 °C. Oxide dispersion strengthened (ODS) Fe-(10–12)Cr-6Al and APMT specimens were exposed and all were pre-oxidized to form an external alumina scale. Unlike static exposures at 400° and 500 °C where pre-oxidation prevented dissolution, large mass losses were observed in the TCL hot leg after the specimens were cleaned in Li. The observed pitting suggests that localized failure of the pre-formed alumina surface oxide caused significant metal loss. Specimen mass gains were not observed on the cold leg implying that mass transfer did not occur and the small levels of Fe and Cr in the Sn after the experiment implies that Sn-rich phases may have formed. Post exposure room temperature tensile testing showed limited impact of the Sn exposure on the 12Cr ODS FeCrAl alloy, comparable to a 1000 h anneal in Ar at 400 °C. These results suggest that pre-oxidation is not sufficient to protect FeCrAl alloys in contact with flowing liquid Sn at 350°-400 °C.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗
DOE OSTI2023

Preface to the ISLA-7 Special Issue: Liquid Metals Applications for Fusion

Although most of the readers of this special issue of JoFE may already be familiar, briefly addressed in this work for completeness are some of the technical issues associated with the divertor which employs tungsten as the plasma-facing surface material brazed on a heat sink, perhaps made of copper alloys such as Glidcop, the thermal conductivity of which can be as high as ~365 W/mK.