DOE OSTI2022

Effects of chemical segregation on ductility-anisotropy in high strength Fe-Mn-Al-C lightweight austenitic steels

Ductile Fe-Mn-Al-C lightweight steels offer great potential as high specific strength materials for weight critical applications. In the present work, very high yield (~1 GPa) and ultimate tensile strength levels (~1.5 GPa) were obtained along the rolling and transverse directions of Fe-30Mn-8.5Al-0.9Si-0.9C-0.5Mo (wt.%), with high tensile elongation to failure of ~35%. This excellent mechanical behavior was attributed to the nanoscale, ordered κ-carbide precipitates formed during aging after rolling. However, tensile ductility was not isotropic through all directions of the rolled plate. In particular, the ductility was consistently lower than 5% true strain along the normal direction. Upon detailed microstructural investigations, micro-scale lamellar chemical micro-segregation bands were detected, which caused the observed anisotropic embrittlement along certain plate directions. These bands resulted in low failure strains along the normal direction since it is oriented perpendicular to these chemical segregation bands, resulting in a failure type reminiscent of delamination-induced cleavage fracture. Chemical segregation causes an inhomogeneous κ-carbide precipitate distribution upon aging, producing more pronounced mechanical anisotropy after peak-aging as compared to the solution heat treated samples. Surprisingly, deformation twinning was observed after tensile deformation of solution-heat treated specimens via electron-backscatter diffraction experiments, which is anomalous for a high stacking faulty energy (SFE) material. Further, it was proposed that chemical micro-segregation promotes locally different SFE regions, leading to deformation twinning in this nominally high SFE material. Overall, this work demonstrates the effects of chemical segregation on mechanical properties and microstructural evolution in a high performance, lightweight Fe-Mn-Al-C steel.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Deformation behavior of CP-titanium under strain path changes: Experiment and crystal plasticity modeling

The deformation behavior of commercially pure rolled titanium subjected to strain path changes is studied using experiments and a crystal plasticity model. Four different loading combinations are performed at room temperature to study the activation of slip, twinning, de-twinning and double-twinning in hexagonal closed packed titanium. The strain paths considered are: rolling direction compression (RDC) followed by normal direction compression (NDC), RDC followed by transverse direction compression (TDC), NDC followed by RDC, and NDC followed by TDC. An EBSD-based analysis of the distribution of boundary misorientation angles before and after reload was developed to analyze the evolution of {$10\bar{1}2$} tensile and {$11\bar{2}2$} compression twins. This analysis supports the model results concerning the treatment of twin reorientation. A de-twinning and double-twinning model accounting for back stress effects, an important feature of strain path changes, is implemented within the framework of the visco-plastic self-consistent (VPSC) model along with a dislocation density (DD) based hardening scheme. In the model, plasticity is accommodated by prismatic $\langle$a$\rangle$, basal $\langle$a$\rangle$ and pyramidal $\langle$c+a$\rangle$ slip modes, and {$10\bar{1}2$} tensile and {$11\bar{2}2$} compression twinning modes. The VPSC model predicts the evolution of twinning, de-twinning and double-twinning processes for both tensile and compression twinning modes under strain path change. The model predicts macroscopic stress-strain response, texture evolution, and twin volume fraction that are in agreement with experimental observations. The evolution of texture is investigated in detail by separately analyzing the twinned domains, rather than the evolution of the global texture.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Metallic components with enhanced mechanical strength through surface mechanical grinding

A method of strengthening a component made of a metallic material. The method includes subjecting the component to a mechanical grinding process incorporating a relative motion between a tool and the component forming a gradient structure on the surface of the component, resulting in increased tensile strength of the component. A method of strengthening a component made of a TWIP steel. The method includes subjecting the component made of TWIP steel to a mechanical grinding process incorporating a relative motion between a tool and the component forming a gradient structure containing a surface nanolaminate layer, a shear band layer, and an inner deformation twinned layer, resulting in increased tensile strength of the component. A component made of a TWIP steel containing a gradient structure with a surface nanolaminate layer, a shear band layer, and a deformation twinned layer.

Ding, Jie↗
DOE OSTI2023

Metallic components with enhanced mechanical strength through surface mechanical grinding

A method of strengthening a component made of a metallic material. The method includes subjecting the component to a mechanical grinding process incorporating a relative motion between a tool and the component forming a gradient structure on the surface of the component, resulting in increased tensile strength of the component. A method of strengthening a component made of a TWIP steel. The method includes subjecting the component made of TWIP steel to a mechanical grinding process incorporating a relative motion between a tool and the component forming a gradient structure containing a surface nanolaminate layer, a shear band layer, and an inner deformation twinned layer, resulting in increased tensile strength of the component. A component made of a TWIP steel containing a gradient structure with a surface nanolaminate layer, a shear band layer, and a deformation twinned layer.

Ding, Jie↗
DOE OSTI2021

Columnar Grain-driven Plasticity and Cracking in Nanotwinned FCC Metals

The mechanisms of strengthening and plasticity in columnar-grained metals with preferentially oriented nano-sized twins have been examined traditionally by considering dislocation processes, but rarely from the perspective of grain boundary (GB) deformation. Here, the effects of GB strain accommodation on plastic deformation in four different columnar-grained nanocrystalline nanotwinned (nt) face-centered-cubic metals (Cu, Ag, Al, and Ni) were studied by large-scale molecular dynamics simulations. It is observed that in tensile deformation parallel to coherent twin boundaries (CTBs), the dislocation mechanisms in each metal are identical and associated with GB emissions of jog and threading dislocations at small and large CTB spacings, respectively. However, CTB strengthening effects are increasingly more pronounced in columnar-grained nt metals as their shear modulus increases, which is rationalized by the dependence of GB stress concentrations on twin size, metal type and strain rate. Also, while flow stresses in nt-Cu, nt-Ag, and nt-Al metals increase linearly with decreasing CTB spacing, a maximum strength limit is reached in nt-Ni below a critical CTB spacing of 6 nm. The strength limit in nt-Ni results from columnar GB cracking induced by prominent GB sliding. For columnar-grained microstructures, GB sliding is equivalent in nt-Ag and nt-Al and slightly lower in nt-Cu but markedly higher in nt-Ni. These findings underscore the importance of new GB deformation mechanisms on plasticity and fracture in columnar-grained nt metals and enrich our understanding of CTB strengthening in fcc metals synthesized in the literature.

36 MATERIALS SCIENCE↗
DOE OSTI2023

A spall and diffraction study of nanosecond pressure release across the iron ε-α phase boundary

The extreme response of polycrystalline iron at high pressures and high strain rates is revealed by means of high-power laser pulses. The compression portion of the pulse coupled with x-ray diffraction identifies the expected body-centered cubic (α) to hexagonal close packed (ε) displacive transformation. Upon release, observation shows that the complete reverse transformation takes approximately 8 ns and that the structure returns to its initial microstructural configuration, in a reversible transformation path. This is in good agreement with molecular dynamics (MD) simulations which predict an inverse dependence between transformation time and strain rate. The grain size is reduced from μm to nm range during compression and begins increasing back to the original grain size on decompression. The kinetics of the transition is dictated by heterogenous nucleation as it follows the Johnson-Mehl-Avrami-Kolmogorov equation with the appropriate time exponent of ~1. This is confirmed by MD simulations which also identify profuse twinning and dislocation generation. Here, the tensile pulse generated upon reflection at the free surface is captured by time-resolved free surface velocity measurements from which a peak tensile stress of 7 GPa is obtained, in stark contrast with its quasi-static value of ~200 MPa. At these strain rates, the strength of grain interiors, which is determined by twinning and slip exceeds the strength of the boundaries, and failure initiates preferentially in the latter.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Plastic deformation of single crystals of the equiatomic Cr-Mn-Fe-Co-Ni high-entropy alloy in tension and compression from 10 K to 1273 K

In this report the plastic deformation behavior of single crystals of the quinary, equiatomic Cr-Mn-Fe-Co-Ni high-entropy alloy (HEA) with the face-centered cubic structure has been investigated in tension and compression as a function of crystal orientation and temperature from 10 K to 1373 K. The critical resolved shear stress (CRSS) for {111}<110> slip at room temperature is 42-45 MPa. It does not depend much on crystal orientation (i.e., the Schmid law holds true) and the sense (tension vs. compression) of the applied load. The CRSS for {111}<110> slip increases with the decrease in temperature, without showing any significant inertia effects at cryogenic temperatures below 77 K. Extrapolation from the measured yield stresses down to 10 K yields a CRSS value at 0 K of 168 MPa. At cryogenic temperatures, the measured strain-rate sensitivity of flow stress is consistent with a very small activation volume. The concept of stress equivalence holds true both for the temperature dependence of CRSS and the stress dependence of activation volume, indicating that solid-solution hardening is the major strengthening mechanism. Deformation twinning occurs at 77 K but not at room temperature, resulting in higher tensile elongation to failure at 77 K than at room temperature. Deformation twinning at 77 K occurs at a shear stress of 378 MPa on conjugate ($\bar1\bar11$) planes in the form of Lüders deformation after large plastic strain (about 85%) achieved by the stage I (easy glide) and stage II (linear work-hardening) deformation.

36 MATERIALS SCIENCE↗
DOE OSTI2025

A novel microstructural approach for TRIP/TWIP β-Ti alloys using intermetallic precipitation

Interest in metastable β-Ti has grown, due to the exceptional work hardening caused by TRansformation and TWinning Induced Plasticity (TRIP/TWIP). A current challenge is increasing the yield strength, while maintaining the benefits of TRIP/TWIP. This study presents the first report of TRIP/TWIP in a metastable β-Ti alloy containing intermetallic compounds, specifically Ti silicide precipitates. Silicon (Si) additions enable the formation of silicide particles, which can be precipitated, dissolved, and controlled through tailored heat treatments. In-situ synchrotron x-ray diffraction during tensile testing reveals primary {332}<113> twinning activates first, followed by TRIP, leading to extensive work hardening and uniform elongation in the solutionized state. In conclusion, these findings open a novel microstructural approach to the design of multiphase TRIP/TWIP titanium alloys, relying on intermetallic precipitation rather than allotropes such as α or ω phase, and lay the groundwork for future studies on intermetallic precipitation strengthening.

Materials science↗
DOE OSTI2024

Uneven Strain Distribution Induces Consecutive Dislocation Slipping, Plane Gliding, and Subsequent Detwinning of Penta-Twinned Nanoparticles

Twin structures possess distinct physical and chemical properties by virtue of their specific twin configuration. However, twinning and detwinning processes are not fully understood on the atomic scale. Integrating in situ high resolution transmission electron microscopy and molecular dynamic simulations, here, we find tensile strain in the asymmetrical 5-fold twins of Au nanoparticles leads to twin boundary migration through dislocation sliding (slipping of an atomic layer) along twin boundaries and dislocation reactions at the 5-fold axis under an electron beam. Migration of one or two layers of twin planes is governed by energy barriers, but overall, the total energy, including surface, lattice strain, and twin boundary energy, is relaxed after consecutive twin boundary migration, leading to a detwinning process. In addition, surface rearrangement of 5-fold twinned nanoparticles can aid in the detwinning process.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Microstructure and high temperature tensile properties of 316L fabricated by laser powder-bed fusion

316L stainless steel fabricated by laser powder-bed fusion (LPBF) has attracted significant attention due to a unique combination of strength and ductility at room temperature. Understanding of high temperature tensile properties of LPBF fabricated 316L is, however, limited. In the present investigation, tensile testing was conducted at 20–700ºC on LPBF 316L in as printed condition and after annealing for 5 h at 500–800ºC. Room temperature data confirmed the excellent ductility of the LPBF-processed 316L steel due to the cellular structure with high dislocation density. However, a significant decrease in ductility was observed at temperatures above 200ºC. These results are consistent with a change of deformation mechanisms observed in wrought 316L, with twinning playing a key role at room temperature. Finally, microstructure characterization and tensile testing revealed that the cellular structure is stable up to 500ºC, but a decrease of yield strength was observed at temperatures above 600ºC likely due to a decrease in dislocation density via annealing.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Highly deformable Mg–Al–Ca alloy with Al 2 Ca precipitates

Magnesium (Mg) is the lightest structural metal. However, the poor formability of Mg alloys to great extent limits their applications in making structural parts. Formability is strongly correlated to both high tensile elongation and large work hardening capacity. In this work, we report a new Mg-Al-Ca alloy in which a majority of deformable Al 2 Ca precipitates form while the formation of Laves phases of Mg 17 Al 12 and Mg 2 Ca seems suppressed. Al 2 Ca precipitates imped dislocation motion, leading to large work hardening. Then, Al 2 Ca precipitates deform with dislocations and stacking faults under the enhanced flow stress, which relieve local stress concentration and improve tensile elongation. In addition, solutes Al and Ca suppress twin nucleation while promoting non-basal dislocations in Mg. Our Mg-Al-Ca alloy demonstrates one of the highest combinations of tensile elongation and work hardening capacity among existing Mg alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Polypropylene Composites Reinforced With Recycled Waste Cellulosic Fiber/Fine Mixture: The Impact of Cellulose Sieving on Performance

This study explores how a sieving step of waste cellulosic fiber and fine (WCFF) mixture affects the performance of WCFF‐loaded polypropylene (PP) composites and whether the separation of fines from fibers offers an added benefit. The WCFF samples were downsized, and four different filler size ranges were sieved using a series of mesh sizes from 4 to 0.85 mm. The WCFF/PP composites were then compounded at 20 wt.% loading of WCFF using a twin‐screw extruder. Incorporating WCFF increased the tensile strength to 41.28 MPa and the modulus to 3207 MPa, accounting for 28% and 38% enhancements, respectively. Interestingly, the greatest improvements were associated with the nonsieved WCFF case, and the sieved WCFF fibers provided only marginal enhancements over virgin PP. The outperformance of nonsieved WCFF was attributed to the synergistic reinforcement of hybrid fibers and fines as well as the maintenance of longer fibers in the system. However, the strain at break and impact strength of PP decreased after introducing WCFF. Moreover, the complex viscosity and storage modulus increased with an increase in the filler size, due to the formation of a more effective percolative network. The PP's crystallinity exhibited a relatively strong dependency on the sieving, where WCFF samples with short‐aspect‐ratio fillers promoted the crystallinity significantly. It was also found that the WCFF degradation onset temperature increased once it was incorporated into PP. This study suggests that waste cellulosic feedstocks can be utilized as a reinforcement without additional sieving to manufacture high‐performance and cost‐effective composites.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Investigating the dislocation reactions on Σ3{111} twin boundary during deformation twin nucleation process in an ultrafine-grained high-manganese steel

Abstract Some of ultrafine-grained (UFG) metals including UFG twinning induced plasticity (TWIP) steels have been found to overcome the paradox of strength and ductility in metals benefiting from their unique deformation modes. Here, this study provides insights into the atomistic process of deformation twin nucleation at Σ3{111} twin boundaries, the dominant type of grain boundary in this UFG high manganese TWIP steel. In response to the applied tensile stresses, grain boundary sliding takes place which changes the structure of coherent Σ3{111} twin boundary from atomistically smooth to partly defective. High resolution transmission electron microscopy demonstrates that the formation of disconnection on Σ3{111} twin boundaries is associated with the motion of Shockley partial dislocations on the boundaries. The twin boundary disconnections act as preferential nucleation sites for deformation twin that is a characteristic difference from the coarse-grained counterpart, and is likely correlated with the lethargy of grain interior dislocation activities, frequently seen in UFG metals. The deformation twin nucleation behavior will be discussed based on in-situ TEM deformation experiments and nanoscale strain distribution analyses results.

36 MATERIALS SCIENCE↗
NASA NTRS1975

Hot tensile properties and deformation response of a gamma/Ni/-gamma prime/Ni3Al/-delta/Ni3Nb/ eutectic composite

Three distinct regions of tensile, deformation and fracture behavior were observed in a 2.5 wt. per cent Al gamma/gamma prime-delta eutectic alloy as the testing temperature was varied. The major finding was an extraordinary ductility maximum at about 550 C. It was shown that this phenomenon is caused by the deflection of transverse cracks at the eutectic grain boundaries when yielding occurs. This delamination between eutectics grains caused by fracture of a gamma prime eutectic grain boundary film leads to a distinctly different 'wood-like' fracture surface morphology. Above 690 C to 926 C, yield and tensile strength values decrease while ductility increase slightly. Cooperative twinning of both phases develops giving rise to block-like deformation of the microstructure quite in parallel to the behavior observed previously in the gamma-delta system.

Bertorello, H. R.↗
DOE OSTI2023

Orientation dependence of the effect of short-range ordering on the plastic deformation of a medium entropy alloy

Multi-principal-element alloys (also known as medium and high entropy alloys) offer a much larger and richer design space than conventional alloys, providing opportunities for discovering new functionalities and their governing physics. Some of these alloys exhibit an outstanding combination of high strength and ductility, linked to the activation of various deformation modes triggered by low-energy stacking faults. However, a pressing question remains: Is the plasticity of medium- and high-entropy alloys governed only by stacking fault energy, or does atomic short-range order (SRO) play a role? Here, to answer this, we investigated how SRO affects the deformation in single-crystalline NiCoCr, with previous contradictory findings. First, we established unique experimental evidence for SRO formation in bulk single crystals using high-energy synchrotron transmission X-Ray Diffraction. By tuning the degree of SRO by aging at high temperatures, twinning density and strain-induced martensitic phase transformation can be significantly increased in the [110] and [111] orientations under tension, increasing the tensile ductility; yet, no increase was observed along the [001] orientation due to lack of TWinning-Induced Plasticity (TWIP) or TRansformation-Induced Plasticity (TRIP), indicating a strong crystallographic orientation dependence. Our first-principles thermodynamic calculations unequivocally show SRO exists and governs the observed microstructural evolution and deformation hardening behavior. Here we find direct proof that SRO triggers a simultaneous TWIP and TRIP in NiCoCr, a rare microstructural evolution path. Our findings establish that the interplay of SRO and plasticity could be exploited to alter deformation modes and yield unprecedented mechanical response in medium- and high-entropy alloys.

36 MATERIALS SCIENCE↗