Results for “porous ablator” — Page 2

NASA NTRS2019

Experimental Measurements of the High-Temperature Oxidation of Carbon Fibers

We carried out laboratory experiments to study the decomposition of carbon fibers at high temperature and studied the material used in charring carbon phenolic ablators for planetary probe heatshields. Porous plug samples were exposed to controlled rates of molecular oxygen, carbon dioxide, and carbon monoxide at furnace-heated flow-tube reactor temperatures between 700 and 1500 K and pressures between 2000 and 6200 Pa. We used calibrated mass spectroscopy to make time-resolved quantitative measurements of decomposition products of the gases downstream of the test sample. Absolute and differential pressure measurements were used to determine the high-temperature permeability of the material and to monitor changes during material decomposition, and we characterized the microstructure of the porous sample using scanning electron microscopy. We found substantial carbon fiber oxidation for O2 flows, resulting in increasing CO/CO2 production ratios with increasing temperature. The CO2 was shown to react with carbon fibers following a Boudouard reaction at temperatures above 1200 K.

Francesco Panerai↗

NASA NTRS1989

Analysis of internal ablation for the thermal control of aerospace vehicles

A new method of thermal protection for transatmospheric vehicles is introduced. The method involves the combination of radiation, ablation and transpiration cooling. By placing an ablating material behind a fixed-shape, porous outer shield, the effectiveness of transpiration cooling is made possible while retaining the simplicity of a passive mechanism. A simplified one-dimensional approach is used to derive the governing equations. Reduction of these equations to non-dimensional form yields two parameters which characterize the thermal protection effectiveness of the shield and ablator combination for a given trajectory. The non-dimensional equations are solved numerically for a sample trajectory corresponding to glide re-entry. Four typical ablators are tested and compared with results obtained by using the thermal properties of water. For the present level of analysis, the numerical computations adequately support the analytical model.

Camberos, Jose A.↗

NASA NTRS1996

PICA Forebody Heatshield Qualification for the Stardust Discovery Class Mission

This paper presents the qualification of the light weight Phenolic Impregnated Carbon Ablators (PICA) as the forebody heatshield for the Stardust Discovery Class Mission. The Stardust spacecraft will be launched in early 1999 and fly by Comet Wild-2 to collect cometary and interstellar dust and return them back to earth in the Sample Return Capsule (SRC). This earth re-entry will be the fastest to date, at 12.6 km/s, and therefore requires a heatshield that can withstand very high heating rates and stagnation pressures, as well as provide the necessary insulation to the vehicle structure. The PICA material was developed as part of the Lightweight Ceramic Ablators program at NASA Ames Research Center, and was baselined as the forebody heatshield because of its low density and superior ablation and thermal performance at severe aerothermodynamic conditions. Under a Small Business Innovative Research (SBIR) program with NASA Ames, Fiber Materials, Inc. developed a process to manufacture a single-piece PICA heatshield for the forebody of the SRC, along with witness material for the fabrication of the test models. The test models were fabricated and instrumented by the staff of Lockheed Martin Astronautics in Denver, Colorado. Full body preliminary aerothermal CFD calculations were performed at NASA Ames to determine the heating and stagnation pressure conditions. The Heat shield sizing was also performed at NASA Ames by using a new material response code that accounts for the highly porous characteristics of the PICA material. The ablation and thermal performance of PICA was qualified in the NASA Ames Interaction Heating Arc Jet Facility. A total of 24 models and four test conditions were used to qualify PICA at the predicted peak heat flux, heat load, shear, and stagnation pressure conditions. Surface and in-depth temperatures were measured using optical pyrometers and thermocouples. Surface recession was measured by using a template and a height gage. Several models were tested to evaluate repair procedures, and two models were cold soaked in liquid nitrogen, prior th testing, to investigate the effect of the cold space environment on the performance of the material. In addition, material cored from a demonstration single-piece heatshield was tested to verify that the PICA process can be successfully completed on a large, complex heatshield shape.

Tran, Huy K.↗

NASA NTRS2017

Tortuosity Computations of Porous Materials using the Direct Simulation Monte Carlo

Low-density carbon fiber preforms, used as thermal protection systems (TPS) materials for planetary entry systems, have permeable, highly porous microstructures consisting of interlaced fibers. Internal gas transport in TPS is important in modeling the penetration of hot boundary-layer gases and the in-depth transport of pyrolysis and ablation products. The gas effective diffusion coefficient of a porous material must be known before the gas transport can be modeled in material response solvers; however, there are very little available data for rigid fibrous insulators used in heritage TPS.The tortuosity factor, which reflects the efficiency of the percolation paths, can be computed from the effective diffusion coefficient of a gas inside a porous material and is based on the micro-structure of the material. It is well known, that the tortuosity factor is a strong function of the Knudsen number. Due to the small characteristic scales of porous media used in TPS applications (typical pore size of the order of 50 micron), the transport of gases can occur in the rarefied and transitional regimes, at Knudsen numbers above 1. A proper way to model the gas dynamics at these conditions consists in solving the Boltzmann equation using particle-based methods that account for movement and collisions of atoms and molecules.In this work we adopt, for the first time, the Direct Simulation Monte Carlo (DSMC) method to compute the tortuosity factor of fibrous media in the rarefied regime. To enable realistic simulations of the actual transport of gases in the porous medium, digitized computational grids are obtained from X-ray micro-tomography imaging of real TPS materials. The SPARTA DSMC solver is used for simulations. Effective diffusion coefficients and tortuosity factors are obtained by computing the mean-square displacement of diffusing particles.We first apply the method to compute the tortuosity factors as a function of the Knudsen number for computationally designed materials such as random cylindrical fibers and packed bed of spheres with prescribed porosity. Results are compared to literature values obtained using random walk methods in the rarefied and transitional regime and a finite-volume method for the continuum regime. We then compute tortuosity factors for a real carbon fiber material with a transverse isotropic structure (FiberForm), quantifying differences between through-thickness and in-plain tortuosities at various Knudsen regimes.

Tortuosity↗

NASA NTRS1977

Liquid rocket engine self-cooled combustion chambers

Self-cooled combustion chambers are chambers in which the chamber wall temperature is controlled by methods other than fluid flow within the chamber wall supplied from an external source. In such chambers, adiabatic wall temperature may be controlled by use of upstream fluid components such as the injector or a film-coolant ring, or by internal flow of self-contained materials; e.g. pyrolysis gas flow in charring ablators, and the flow of infiltrated liquid metals in porous matrices. Five types of self-cooled chambers are considered in this monograph. The name identifying the chamber is indicative of the method (mechanism) by which the chamber is cooled, as follows: ablative; radiation cooled; internally regenerative (Interegen); heat sink; adiabatic wall. Except for the Interegen and heat sink concepts, each chamber type is discussed separately. A separate and final section of the monograph deals with heat transfer to the chamber wall and treats Stanton number evaluation, film cooling, and film-coolant injection techniques, since these subjects are common to all chamber types. Techniques for analysis of gas film cooling and liquid film cooling are presented.

Source record↗

NASA NTRS2026

Development of a One-Domain Volume-Averaged Navier–Stokes Solver

The interaction between a high-enthalpy flow and a thermal protection material is inherently multiscale and multiphysics. In conventional aerothermal analyses, the external flow and material response are generally modeled using separate computational domains coupled through boundary conditions at the material surface. Although this approach has supported many practical applications, it requires assumptions about the location and behavior of the interface and may become difficult to apply when material decomposition, internal reactions, and surface recession substantially alter the porous structure. This report presents the development of a one-domain formulation in which the free-fluid and porous-material regions are represented within a single computational domain. The formulation is based on the volume-averaged Navier–Stokes (VANS) equations, derived from the governing equations for reacting, compressible flow and condensed material. Volume averaging transfers the influence of the unresolved material microstructure to the macroscale equations through effective transport properties, interfacial source terms, and dispersion fluxes. Particular attention is given to regions in which porosity and permeability vary rapidly, including the diffuse transition between a porous material and the surrounding fluid. The resulting equations are implemented in the Porous-material Analysis Toolbox based on OpenFOAM (PATO). The report describes the pressure–velocity coupling strategy used by the solver, examines spatial filtering techniques for deriving effective properties, and evaluates the influence of a smoothly varying interface permeability. Numerical demonstrations include canonical porous-flow configurations, a flow-tube configuration representative of FiberForm® permeability experiments, and the oxidation of a porous carbon material. The purpose of this work is to establish a mathematical and computational foundation for a unified treatment of flow and thermal protection material response. The present formulation is intended to support the progressive inclusion of additional physical processes, including multicomponent transport, finite-rate gas–surface chemistry, pyrolysis, internal oxidation, and material recession. It also provides a framework for connecting pore-scale simulations and microstructural characterization with macroscale aerothermal-response calculations. This report is intended for researchers and engineers working in computational fluid dynamics, porous-media transport, material response, and thermal protection system modeling. It documents both the theoretical development and the initial numerical assessment of the one-domain approach, while identifying the closure of effective and dispersion terms as an important subject for continued investigation.

Ablation↗

NASA NTRS1973

On the design and test of a liquid injection electric thruster

The design of the thruster described incorporates a coaxial four-segment trigger assembly to discharge a high-energy capacitor. The discharge ablates a waxy perfluorocarbon from the surface of porous annular metal ring, and the resulting plasma is electromagnetically accelerated to ambient producing thrust. Tests revealed a thruster performance well in excess of the major design goals.

Youmans, E. H.↗

NASA NTRS2026

Advances in Entry Systems Modeling: Modeling Summer Visit 2025 Technical Reports

This NASA Technical Memorandum presents the collective work carried out during the Modeling Summer Visit (MSV) 2025, a collaborative research program between NASA Ames Research Center and three leading European research institutions: the University of Bordeaux, the von Karman Institute (VKI), and Ecole Polytechnique. Held from July 7th to August 1st, 2025, the NASA ARC MSV program brought together 42 researchers from Europe to work alongside NASA staff on 22 projects in entry systems modeling. The program was organized by Bruno Dias, Sergio Fraile-Izquierdo, and Jeremie Meurisse from Analytical Mechanics Associates, Inc., in collaboration with Marc Massot (Ecole Polytechnique), Jean Lachaud (University of Bordeaux), and Thierry Magin (VKI). The MSV program traces its origins to an initiative started by Nagi N. Mansour in 2018, with this 2025 edition representing a consolidation and expansion of that original vision. The projects were organized into six thematic groups: Porous Media, Numerical Methods, Plasma/Rarefied Methods, Experimental Reconstruction, Flow and Material Coupling Methods, and Transition and High-Speed Flows. Throughout the four-week program, participants presented their work in three public presentations (July 7th, July 21st, and August 1st), allowing for continuous feedback and discussion of their evolving research.

Plasmas↗

NASA NTRS2019

Bayesian Inference and the Effects of Varying Uncertainty Models in Charring Ablator Calibration and Uncertainty Quantification Problems

The Mars Science Laboratory (MSL) vehicle utilized a heat shield constructed from NASA’s Phenolic-Impregnated Carbon Ablator (PICA) material to protect the main structure from the high enthalpy environment encountered during hypersonic atmospheric entry. During the vehicle’s descent through Martian atmosphere, multiple thermocouples embedded within the heat shield captured in-depth material temperature data that allow for studies to be conducted on current material response reconstruction tools. In the present work, material temperature data obtained from thermocouples within the MISP-4 plug (MEDLI (Mars Science Laboratory Entry, Descent, and Landing Instrument) Integrated Sensor Plug) are utilized in the calibration of Theoretical Ablative Composite for Open Testing (TACOT) model parameters in conjunction with NASA’s Porous material Analysis Toolbox (PATO) through Bayesian inference where uncertainty due to parametric, modeling, and experimental sources is simultaneously quantified. Prior to the study, a sensitivity analysis is performed through computation of the robust Sobol indices in an effort to study the relationship between input space and model response and to reduce the dimensionality of the statistical inverse problem. The Bayesian inference methodology necessitates an a-priori choice to be made for the uncertainty model for which numerous possibilities are available. Across most works, however, only basic additive or multiplicative models are utilized with pre-defined magnitudes of uncertainty based on a-priori knowledge or to-be-calibrated multipliers of static covariance matrix structures. The present effort explores the effects of informed uncertainty models, ones with temporal dependence that are simultaneously calibrated through Bayesian inference, on calibrated results for parameters that make up the uncertain input space.

Sensitivity Analysis↗

NASA NTRS2006

Carbon Nanotube-enhanced Carbon-phenolic Ablator Material

Phenolic impregnated carbon ablator (PICA) is a thermal protection system (TPS) material developed at NASA Ames Research Center in the mid-90 s for Discovery missions. It was used on the Stardust return capsule heat shield which successfully executed the highest speed Earth entry to date on January 15, 2006. PICA is a porous fibrous carbon insulation infiltrated with phenolic resin, and is an excellent ablator that is effective for heating rates up to 1000 W/sq cm. It is one of several candidate TPS materials for the next generation of crewed spacecraft for Lunar and Mars missions. We will describe an ongoing research effort at NASA to improve mechanical properties of the phenolic matrix with carbon nanotubes. The aim is two-fold: to increase overall TPS strength during reentry and to improve Micrometeoroid/Orbital Debris (MMOD) protection in space. The former requires at least a good dispersion of nanotubes in phenolic, while the latter also requires covalent bonding between them to couple and transfer impact energy effectively from matrix to nanotubes. We will discuss the required chemical functionalization of nanotubes, processing issues and test results.

Nikolaev, P.↗

NASA NTRSDate not supplied

Characterizing Porous and Nonporous Phenolic Resins from Molecular Dynamics Simulations

Phenolic resins are an important component of many ablative heat shield materials, which protect spacecrafts from the extreme temperatures reached during atmospheric entry. Examples include the high-density Heritage Carbon Phenolic (HCP) used in the Pioneer-Venus and Galileo missions, as well as the low-density Phenolic Impregnated Carbon Ablator (PICA) used in the Mars Science Laboratory and Mars 2020 missions. Additionally, recent developments within NASA have produced the mid-density Heatshield for Extreme Entry Environment Technology (HEEET) and its derivative 3D Woven Mid-Density Carbon Phenolic (3MDCP). Unlike the nonporous phenolic in HCP, PICA and HEEET/3MDCP are fabricated by infusing preforms with diluted phenolic formulations to obtain a lower density porous matrix. Despite the importance of the phenolic phase to the material response during entry, the variation in properties of porous and nonporous phenolic is not well understood. Here, we present an investigation of porous and nonporous phenolic resins using molecular dynamics (MD) simulations. Resin cure is mimicked in the simulations through the inclusion of representative reaction templates to generate accurate models of the complex crosslinked structures. To create porous models, explicit solvent molecules are included during the cure simulations. We observe nanoscale separation of the phenolic and solvent phases, which results in significant differences in the final structures of porous and nonporous models. In addition to a quantitative assessment of the network structure and porosity, we elucidate the effects of the phenolic formulation on the final material properties. These results are compared with experimental data as appropriate.

phenolic↗

NASA NTRSDate not supplied

Computational Investigation of Oxidative Etch Pitting in FiberForm and Its Impact on Material Properties

Oxidation-driven carbon erosion does not occur uniformly but rather through the development of localized etch pits at active surface sites. These active sites form due to atomic defects on the carbon surface, making them significantly more reactive than the surrounding, non-defective areas. As a result, these sites are the first to react during ablation, leading to their removal. This process creates new defects in neighboring atoms, increasing their reactivity and causing localized carbon removal around these active sites. In this way, the highly reactive defective areas serve as nucleation points for the formation and growth of etch pits, which can have adverse effects on structural integrity of FiberForm. To better understand how these etch pits impact the material properties of carbon fiber microstructures, we have developed a new capability within the direct simulation Monte Carlo (DSMC) framework to capture the etch pit formation process. This capability, integrated into the DSMC code SPARTA (Stochastic Parallel Rarefied-gas Time-accurate Analyzer), models material removal in the presence of active sites, leading to the formation of etch pits. The current work focuses on studying the effects of these etch pits on the material properties of FiberForm, a widely used base material in thermal protection systems (TPS). The microstructure of virgin FiberForm, obtained via X-ray microtomography, is imported into SPARTA to generate the ablated geometries with etch pits. These modified microstructures are then analyzed using the Porous Microstructure Analysis (PuMA) software to compute various material properties, including elasticity, thermal conductivity, and permeability. We investigate the variation of these properties due to the complex surface topology changes caused by etch pit formation. Additionally, we compare the effects of pitting with the conventional model of shrinking fibers, traditionally used to simulate the ablation of carbon structures. Significant differences emerge between the two approaches. Consequently, this physically realistic model of material removal through etch pit formation offers improved accuracy in predicting the degradation of carbon-based TPS during oxidation. It also provides insights into other mechanisms, such as spallation, where chunks of material are removed into the flow due to etch pit growth. Ultimately, this model enhances our understanding of failure modes in these materials during ablation.

PuMA↗

NASA NTRSDate not supplied

Computational Study of Oxidative Etch Pitting in FiberForm and the Effect on Its Material Properties

Erosion of carbon due to oxidation does not occur uniformly but through the formation of localized etch pits because of active surface sites. These active sites are formed due to the presence of atomic defects on the carbon surface, and have much higher reactivity compared to average non-defective sites. Thus, these active sites are first to react during ablation, resulting in their removal. This causes all the neighboring atoms to be defective and increase their reactivity, thus leading to the localized carbon removal around these “active” sites. In this manner, these highly reactive defective sites serve as nucleation sites for the formation and growth of etch pits with potentially detrimental effects on the structural integrity. In order to understand the influence of these etch pits on the material properties of carbon fiber microstructures, we have developed a new capability within direct simulation Monte Carlo (DSMC) to capture the etch pit formation process. This capability is developed within the DSMC code SPARTA (Stochastic PArallel Rarefied-gas Time-accurate Analyzer) and can model the material removal in presence of active sites leading to the formation of etch pits. The focus of the current work will be to study the effect of etch pits on the material properties of FiberForm, a commonly used base material within many thermal protection system materials (TPS). The microstructure of virgin FiberForm obtained directly from X-ray microtomography experiments is used within SPARTA to obtain the ablated geometries with etch pits. These pitted microstructures are then imported within the Porous Microstructure Analysis (PuMA) software and various material properties such as elasticity, thermal conductivity, and permeability are computed. The variation of these properties as a result of the complex evolution of the surface topology due to etch pit formation is studied and analyzed. Furthermore, the effect of pitting is compared to the case of shrinking fibers, which has been the standard for modelling ablation of carbon structures; and significant differences are observed. Thus, such a physically realistic modeling of material removal through the formation of etch pits will be helpful in predicting the degradation of carbon-based TPS more accurately during oxidation; as well as other mechanisms such as spallation, which involves the removal of chunks of material into the flow due to etch pit growth. This will ultimately improve our understanding of the failure modes in these materials due to ablation.

Carbon Ablators↗

NASA NTRSDate not supplied

Computational Study of Oxidative Etch Pitting in FiberForm and the Effect on Its Material Properties

Erosion of carbon due to oxidation does not occur uniformly but through the formation of localized etch pits because of active surface sites. These active sites are formed due to the presence of atomic defects on the carbon surface, and have much higher reactivity compared to average non-defective sites. Thus, these active sites are first to react during ablation, resulting in their removal. This causes all the neighboring atoms to be defective and increase their reactivity, thus leading to the localized carbon removal around these “active” sites. In this manner, these highly reactive defective sites serve as nucleation sites for the formation and growth of etch pits with potentially detrimental effects on the structural integrity. In order to understand the influence of these etch pits on the material properties of carbon fiber microstructures, we have developed a new capability within direct simulation Monte Carlo (DSMC) to capture the etch pit formation process. This capability is developed within the DSMC code SPARTA (Stochastic PArallel Rarefied-gas Time-accurate Analyzer) and can model the material removal in presence of active sites leading to the formation of etch pits. The focus of the current work will be to study the effect of etch pits on the material properties of FiberForm, a commonly used base material within many thermal protection system materials (TPS). The microstructure of virgin FiberForm obtained directly from X-ray microtomography experiments is used within SPARTA to obtain the ablated geometries with etch pits. These pitted microstructures are then imported within the Porous Microstructure Analysis (PuMA) software and various material properties such as elasticity, thermal conductivity, and permeability are computed. The variation of these properties as a result of the complex evolution of the surface topology due to etch pit formation is studied and analyzed. Furthermore, the effect of pitting is compared to the case of shrinking fibers, which has been the standard for modelling ablation of carbon structures; and significant differences are observed. Thus, such a physically realistic modeling of material removal through the formation of etch pits will be helpful in predicting the degradation of carbon-based TPS more accurately during oxidation; as well as other mechanisms such as spallation, which involves the removal of chunks of material into the flow due to etch pit growth. This will ultimately improve our understanding of the failure modes in these materials due to ablation.

Carbon Ablators↗

NASA NTRSDate not supplied

Simulation of Oxidative Etch Pit Formation and Growth on FiberForm

Erosion of carbon surfaces due to oxidation does not occur uniformly but through the formation of localized etch pits because of active surface sites. These active sites are formed due to the presence of atomic defects on the carbon surface and have much higher reactivity compared to average non-defective sites. Thus, these active sites are the first to react during ablation, resulting in their removal. This causes all the neighboring atoms to be defective, and increasing their reactivity, thus leading to localized carbon removal around these “active” sites. In this manner, these highly reactive defects serve as nucleation sites for the formation and growth of etch pits, with detrimental effects on the structural integrity. In order to understand the influence of these etch pits on the material properties of carbon fiber microstructures, we have developed a new capability within direct simulation Monte Carlo (DSMC) to capture the etch pit formation process. This capability is developed within the DSMC code SPARTA (Stochastic PArallel Rarefied-gas Time-accurate Analyzer) and can model the material removal in the presence of active sites leading to the formation of etch pits. The focus of the current work will be to study the effect of etch pits on the material properties of FiberForm, the precursor substrate of the PICA Thermal Protection System (TPS) material. The microstructure of virgin FiberForm obtained directly from X-ray microtomography scans is used within SPARTA to obtain the ablated geometries with etch pits. These pitted microstructures are then imported into the Porous Microstructure Analysis (PuMA) software and various material properties such as thermal conductivity, elasticity, and permeability are computed. The variation of these properties because of the complex evolution of the surface topology due to the formation of etch pits is studied and analyzed. Furthermore, the effect of pitting is compared to the case of uniform radial shrinking of fibers, which has been the standard for modelling ablation of carbon structures, and significant differences are observed. Thus, a physically realistic model of material removal through the formation of etch pits will be helpful in predicting the degradation of carbon-based TPS more accurately during oxidation; as well as other mechanisms such as spallation, which involves the removal of chunks of material into the flow due to the growth of etch pits. This will ultimately improve our understanding of the failure modes in these materials due to ablation.

DSMC↗

NASA NTRSDate not supplied

Simulation of Oxidative Etch Pit Formation and Growth on FiberForm

Erosion of carbon surfaces due to oxidation does not occur uniformly but through the formation of localized etch pits because of active surface sites. These active sites are formed due to the presence of atomic defects on the carbon surface and have much higher reactivity compared to average non-defective sites. Thus, these active sites are the first to react during ablation, resulting in their removal. This causes all the neighboring atoms to be defective, and increasing their reactivity, thus leading to localized carbon removal around these “active” sites. In this manner, these highly reactive defects serve as nucleation sites for the formation and growth of etch pits, with detrimental effects on the structural integrity. In order to understand the influence of these etch pits on the material properties of carbon fiber microstructures, we have developed a new capability within direct simulation Monte Carlo (DSMC) to capture the etch pit formation process. This capability is developed within the DSMC code SPARTA (Stochastic PArallel Rarefied-gas Time-accurate Analyzer) and can model the material removal in the presence of active sites leading to the formation of etch pits. The focus of the current work will be to study the effect of etch pits on the material properties of FiberForm, the precursor substrate of the PICA Thermal Protection System (TPS) material. The microstructure of virgin FiberForm obtained directly from X-ray microtomography scans is used within SPARTA to obtain the ablated geometries with etch pits. These pitted microstructures are then imported into the Porous Microstructure Analysis (PuMA) software and various material properties such as thermal conductivity, elasticity, and permeability are computed. The variation of these properties because of the complex evolution of the surface topology due to the formation of etch pits is studied and analyzed. Furthermore, the effect of pitting is compared to the case of uniform radial shrinking of fibers, which has been the standard for modelling ablation of carbon structures, and significant differences are observed. Thus, a physically realistic model of material removal through the formation of etch pits will be helpful in predicting the degradation of carbon-based TPS more accurately during oxidation; as well as other mechanisms such as spallation, which involves the removal of chunks of material into the flow due to the growth of etch pits. This will ultimately improve our understanding of the failure modes in these materials due to ablation.

DSMC↗

NASA NTRS1984

Melting, ablation, and vapor phase condensation during atmospheric passage of the Bjurbole meteorite

A detailed study of the Bjurbole fusion crust using scanning electron microscopy (SEM) and energy dispersive analysis (EDS) shows that filamentary crystals and ablation spheres may form on the meteoroid surface. Filamentary crystals, hollow spheres, and porous regions of the surface point to a period of intense vapor phase activity during atmospheric passage. Filamentary crystals can be divided into three categories on the basis of bulk composition and morphology. Two types of filamentary crystals are vapor phase condensation products formed during atmospheric entry of the meteoroid. The other type forms by the interaction of seawater with the fusion surface. The density and composition of ablation spheres varies with the flight orientation of the meteorite. The size range and composition of iron-nickel spheres on the surface of Bjurbole are similar to spheres collected in the stratosphere. A comparison of stratospheric dust collections with meteorite surfaces may provide further insight into the mechanisms of meteoroid entry into planetary atmospheres.

Rietmeijer, F. J. M.↗

NASA NTRS2007

One-Dimensional Ablation with Pyrolysis Gas Flow Using a Full Newton's Method and Finite Control Volume Procedure

The development and verification of a one-dimensional material thermal response code with ablation is presented. The implicit time integrator, control volume finite element spatial discretization, and Newton's method for nonlinear iteration on the entire system of residual equations have been implemented and verified for the thermochemical ablation of internally decomposing materials. This study is a continuation of the work presented in "One-Dimensional Ablation with Pyrolysis Gas Flow Using a Full Newton's Method and Finite Control Volume Procedure" (AIAA-2006-2910), which described the derivation, implementation, and verification of the constant density solid energy equation terms and boundary conditions. The present study extends the model to decomposing materials including decomposition kinetics, pyrolysis gas flow through the porous char layer, and a mixture (solid and gas) energy equation. Verification results are presented for the thermochemical ablation of a carbon-phenolic ablator which involves the solution of the entire system of governing equations.

Amar, Adam J.↗