NASA NTRS1998

Method Developed for the High-Temperature Nondestructive Evaluation of Fiber-Reinforced Silicon Carbide Ceramic Matrix Composites

Ceramic matrix composites have emerged as candidate materials to allow higher operating temperatures (1000 to 1400 C) in gas turbine engines. A need, therefore, exists to develop nondestructive methods to evaluate material integrity at the material operating temperature by monitoring thermal and mechanical fatigue. These methods would also have potential as quality inspection tools. The goal of this investigation at the NASA Lewis Research Center is to survey and correlate the temperature-dependent damping and stiffness of advanced ceramic composite materials with imposed thermal and stress histories that simulate in-service turbine engine conditions. A typical sample size of 100 by 4 by 2 cubic millimeters, along with the specified stiffness and density, placed the fundamental vibration frequencies between 100 and 2000 Hz. A modified Forster apparatus seemed most applicable to simultaneously measure both damping and stiffness. Testing in vacuum reduced the effects of air on the measurements. In this method, a single composite sample is vibrated at its fundamental tone; then suddenly, the mechanical excitation is removed so that the sample's motion freely decays with time. Typical results are illlustrated in this paper.

Goldsby, Jon C.↗
NASA NTRS2003

NASA Glenn/AADC-Rolls Royce Collaborated to Measure Erosion Resistance on Coated Polymer Matrix Composites

Polymer matrix composites (PMCs) are increasingly used in aerospace and automotive applications because of their light weight and high strength-to-weight ratio relative to metals. However, a major drawback of PMCs is poor abrasion resistance, which restricts their use, especially at high temperatures. Simply applying a hard coating on PMCs to improve abrasion and erosion resistance is not effective since coating durability is short lived (ref. 1). Generally, PMCs have higher coefficients of thermal expansion than metallic or ceramic coatings have, and coating adhesion suffers because of poor interfacial adhesion strength. One technique commonly used to improve coating adhesion or durability is the use of bond coats that are interleaved between a coating and a substrate with vastly different coefficients of thermal expansion. An example of this remedy is the use of bondcoats for ceramic thermal barrier coatings on metallic turbine components (ref. 2). Prior collaborative research between the NASA Glenn Research Center and the Allison Advanced Development Company (AADC) demonstrated that bond coats sandwiched between PMCs and high-quality plasma-sprayed, erosion-resistant coatings substantially improved the erosion resistance of PMCs (ref. 3). One unresolved problem in this earlier collaboration was that there was no easy, accurate way to measure the coating erosion wear scar. Coating wear was determined by both profilometry and optical microscopy. Both techniques are time consuming. Wear measurement by optical microscopy requires sample destruction and does not provide a comprehensive measure of the entire wear volume. An even more subtle, yet critical, problem is that these erosion coatings contain two or more materials with different densities. Therefore, simply measuring specimen mass loss before and after erosion will not provide an accurate gauge for coating and/or substrate volume loss. By using a noncontact technique called scanning optical interferometry, which was recently developed at Glenn, researchers can accurately determine the wear performance of erosion-coated PMCs while preserving the sample. An example of this interferometry technique is shown in the preceding figure for an erosion-coated inlet guide vane from a Rolls Royce AE3007 regional gas turbine jet engine. Erosion was conducted with coated and uncoated PMC vanes, with the abrasive material moving at a velocity of 229 m/s at impingement angles of 20 and 90 degrees. The coatings for PMCs remarkably reduced the erosion volume loss by a factor of approximately 10. Currently, several erosion coatings for PMCs are being compared and downselected for engine testing at Rolls Royce.

Miyoshi, Kazuhisa↗
DOE OSTI2025

Additive manufacturing of metal matrix composites

Although Metal matrix composites (MMCs) are superior to most sought-after metallic alloys, their challenging fabricability has limited their widespread use in bulk-form applications. Among the many advanced fabrication techniques, Additive Manufacturing (AM), owing to its unique capabilities to produce near-net shapes, has drawn significant traction in the past two decades, especially for materials that are difficult to process using traditional methods. However, unlike pure metal/alloy systems, MMCs are highly sensitive to the processing conditions prevailing in AM techniques due to factors such as the high melting point of reinforcement particles and the potential for in-situ reactions. Therefore, it may be a while before metal matrix composites are commercially produced via AM. This review will discuss the current state-of-the-art design, fabricability, and performance of various additively manufactured MMCs. A particular focus will be on microstructural evolution and microstructure-property relationships. The most employed AM techniques, such as directed energy deposition, powder bed fusion, binder jetting, sheet lamination, and solid-state friction stir processing, are fundamentally different in terms of thermo-kinetics, forming the perspective for this review. A detailed comparison of microstructural evolution and process parameter optimization, including feedstock preparation methods and the role of machine learning and modeling among the different AM processes, is also presented. Finally, a critical evaluation of emerging AM technologies for MMCs is also provided, highlighting their potential advantages and challenges.

36 - MATERIALS SCIENCE↗
NASA NTRS1994

Program For Analysis Of Metal-Matrix Composites

METCAN (METal matrix Composite ANalyzer) is computer program used to simulate computationally nonlinear behavior of high-temperature metal-matrix composite structural components in specific applications, providing comprehensive analyses of thermal and mechanical performances. Written in FORTRAN 77.

Murthy, P. L. N.↗
NASA NTRS1999

Design Tool Developed for Probabilistic Modeling of Ceramic Matrix Composite Strength

Ceramic matrix composites are being evaluated as candidate materials for many high temperature applications such as engine combustor liners for the High-Speed Civil Transport (HSCT). They are required to have an assured life of several thousand hours. Estimating the reliability of these components is quite a complex process and requires knowledge of the uncertainties that occur at various scales. The properties of ceramic matrix composites (CMC) are known to display a considerable amount of scatter due to variations in fiber/matrix properties, interphase/coating properties, bonding, amount of matrix voids, and many geometry- and fabrication-related parameters such as ply thickness and ply orientations. The objective of this research effort is to account for these uncertainties in a formal way by probabilistically analyzing both the stiffness- and strength related properties of CMC's. In current deterministic approaches, uncertainties are usually accounted for by safety factors. This approach often yields overly conservative designs, thereby reducing the potential of many advanced composite materials.

Murthy, Pappu L. N.↗
NASA NTRS1988

METCAN: The metal matrix composite analyzer

Metal matrix composites (MMC) are the subject of intensive study and are receiving serious consideration for critical structural applications in advanced aerospace systems. MMC structural analysis and design methodologies are studied. Predicting the mechanical and thermal behavior and the structural response of components fabricated from MMC requires the use of a variety of mathematical models. These models relate stresses to applied forces, stress intensities at the tips of cracks to nominal stresses, buckling resistance to applied force, or vibration response to excitation forces. The extensive research in computational mechanics methods for predicting the nonlinear behavior of MMC are described. This research has culminated in the development of the METCAN (METal Matrix Composite ANalyzer) computer code.

Hopkins, Dale A.↗
NASA NTRS2003

Stress-Dependent Matrix Cracking in 2D Woven SiC-Fiber Reinforced Melt-Infiltrated SiC Matrix Composites

The matrix cracking of a variety of SiC/SiC composites has been characterized for a wide range of constituent variation. These composites were fabricated by the 2-dimensional lay-up of 0/90 five-harness satin fabric consisting of Sylramic fiber tows that were then chemical vapor infiltrated (CVI) with BN, CVI with SiC, slurry infiltrated with SiC particles followed by molten infiltration of Si. The composites varied in number of plies, the number of tows per length, thickness, and the size of the tows. This resulted in composites with a fiber volume fraction in the loading direction that ranged from 0.12 to 0.20. Matrix cracking was monitored with modal acoustic emission in order to estimate the stress-dependent distribution of matrix cracks. It was found that the general matrix crack properties of this system could be fairly well characterized by assuming that no matrix cracks originated in the load-bearing fiber, interphase, chemical vapor infiltrated Sic tow-minicomposites, i.e., all matrix cracks originate in the 90 degree tow-minicomposites or the large unreinforced Sic-Si matrix regions. Also, it was determined that the larger tow size composites had a much narrower stress range for matrix cracking compared to the standard tow size composites.

Morscher, Gregory N.↗
NASA NTRS1982

A compliant, high failure strain, fibre-reinforced glass-matrix composite

A glass-matrix composite reinforced by discontinuous graphite fibers was produced by hot pressing glass-powder-impregnated two-dimensional arrays of in-plane randomly oriented graphite fibers held together by approximately 5-10% by weight of organic binder (generally polyester). The composite tensile behavior is characterized by a highly nonlinear stress-strain curve which differs markedly from that of either unreinforced glass or a similarly reinforced epoxy-matrix composite. By virtue of this nonlinearity, the composite is able to redistribute applied stresses to achieve a high load-carrying capacity. The fibrous microstructure and the low fiber-matrix bond provide a mechanism for achieving high fracture toughness and unusually high compliance. For a 96%-silica-matrix composite, the strength is retained to over 1000 C.

Prewo, K. M.↗
NASA NTRS1993

Analysis of thermal mechanical fatigue in titanium matrix composites

Titanium metal matrix composites are being evaluated for structural applications on advanced hypersonic vehicles. These composites are reinforced with ceramic fibers such as silicon carbide, SCS-6. This combination of matrix and fiber results in a high stiffness, high strength composite that has good retention of properties even at elevated temperatures. However, significant thermal stresses are developed within the composite between the fiber and the matrix due to the difference in their respective coefficients of thermal expansion. In addition to the internal stresses that are generated due to thermal cycling, the overall laminate will be subjected to considerable mechanical loads during the thermal cycling. In order to develop life prediction methodology, one must be able to predict the stresses and strains that occur in the composite's constituents during the complex loading. Thus the purpose is to describe such an analytical tool, VISCOPLY.

Johnson, W. Steven↗
NASA NTRS1989

A review of failure models for unidirectional ceramic matrix composites under monotonic loads

Ceramic matrix composites offer significant potential for improving the performance of turbine engines. In order to achieve their potential, however, improvements in design methodology are needed. In the past most components using structural ceramic matrix composites were designed by trial and error since the emphasis of feasibility demonstration minimized the development of mathematical models. To understand the key parameters controlling response and the mechanics of failure, the development of structural failure models is required. A review of short term failure models with potential for ceramic matrix composite laminates under monotonic loads is presented. Phenomenological, semi-empirical, shear-lag, fracture mechanics, damage mechanics, and statistical models for the fast fracture analysis of continuous fiber unidirectional ceramic matrix composites under monotonic loads are surveyed.

Tripp, David E.↗
DOE OSTI2023

An ICME Modeling Framework for Metal Matrix Composites Focusing on Ultrahigh Temperature Matrix Material and Tungsten Carbide Reinforcement Particulate (Final CRADA Report)

Ultra High Temperature Metal Matrix Composites (UHT-MMCs) are of interest to the due to their potential defense and aerospace applications. These materials consist of a metal matrix reinforced with a stiff ceramic or cermet. Based on a preliminary literature survey, this project will focused on a pure titanium (Ti) matrix reinforced with tungsten carbide-cobalt (WC-Co). UHT-MMC technology is still at a nascent stage of development and requires extensive experimental work to optimize the structure and resulting material properties of a particular UHT-MMC material system. An accurate and complete high-performance computing (HPC) model of the Ti/WC-Co material system could greatly accelerate the development and deployment Ti/WC-Co materials by connecting processing parameters to material properties. This type of model could then be used in an integrated computational materials engineering approach to optimize the material structure to achieve a targeted level of performance.

36 MATERIALS SCIENCE↗
NASA NTRS2011

Phase Stability and Thermal Conductivity of Composite Environmental Barrier Coatings on SiC/SiC Ceramic Matrix Composites

Advanced environmental barrier coatings are being developed to protect SiC/SiC ceramic matrix composites in harsh combustion environments. The current coating development emphasis has been placed on the significantly improved cyclic durability and combustion environment stability in high-heat-flux and high velocity gas turbine engine environments. Environmental barrier coating systems based on hafnia (HfO2) and ytterbium silicate, HfO2-Si nano-composite bond coat systems have been processed and their stability and thermal conductivity behavior have been evaluated in simulated turbine environments. The incorporation of Silicon Carbide Nanotubes (SiCNT) into high stability (HfO2) and/or HfO2-silicon composite bond coats, along with ZrO2, HfO2 and rare earth silicate composite top coat systems, showed promise as excellent environmental barriers to protect the SiC/SiC ceramic matrix composites.

Benkel, Samantha↗
NASA NTRS1997

Effects of Interface Modification on Mechanical Behavior of Hi-Nicalon Fiber-Reinforced Celsian Matrix Composites

Unidirectional celsian matrix composites having approx. 42 volume percent of uncoated or BN/SiC-coated Hi-Nicalon fibers were tested in three-point bend at room temperature. The uncoated fiber-reinforced composites showed catastrophic failure with strength of 210 +/- 35 MPa and a flat fracture surface. In contrast, composites reinforced with BN/SiC-coated fibers exhibited graceful failure with extensive fiber pullout. Values of first matrix cracking stress and strain were 435 +/- 35 MPa and 0.27 +/- 0.01 %, respectively, with ultimate strength as high as 960 MPa. The elastic Young's modulus of the uncoated and BN/SiC-coated fiber-reinforced composites were measured as 184 q 4 GPa and 165 +/- 5 GPa, respectively. Fiber push-through tests and microscopic examination indicated no chemical reaction at the uncoated or coated fiber-matrix interface. The low strength of the uncoated fiber-reinforced composite is probably due to degradation of the fibers from mechanical surface damage during processing. Because both the coated and uncoated fiber reinforced composites exhibited weak interfaces, the beneficial effect of the BN-SiC dual layer is primarily the protection of fibers from mechanical damage during processing.

Bansal, Narottam P.↗
DOE OSTI2023

Tailoring the Toughening Effects in Two-Dimensional Nanomaterial-Reinforced Ceramic Matrix Composites

Abstract Ceramic matrix composites (CMCs) reinforced by two-dimensional (2D) nanomaterials have shown extraordinary load-carrying capacities, even in the harsh environments required by emerging applications. Their exceptional mechanical performance, especially fracture toughness, primarily arises from their heterogeneous microstructures. The deliberate dispersion of 2D reinforcements enables toughening mechanisms that are extrinsic to the matrix and thus endows the composites with substantial resistance to catastrophic failure. However, the incomplete understanding of the fracture behavior of such nanocomposites, especially the complex energy dissipation process of the matrix/reinforcement interface, limits the development of stronger and tougher CMCs. To overcome these limitations, we investigate crack deflection and energy dissipation in nanocomposites using an extended cohesive shear-lag model. This new model accounts for interfacial debonding and friction, which critically control the toughening of nanocomposites. Our analysis provides mechanistic insights for optimizing the toughening effects of CMCs.

Mechanics↗
NASA NTRS1985

Thermal expansion of selected graphite reinforced polyimide-, epoxy-, and glass-matrix composite

The thermal expansion of three epoxy-matrix composites, a polyimide-matrix composite and a borosilicate glass-matrix composite, each reinforced with continuous carbon fibers, has been measured and compared. The expansion of a composite with a rubber toughened epoxy-matrix and P75S carbon fibers was very different from the expansion of two different single phase epoxy-matrix composites with P75S fibers although all three had the same stacking sequence. Reasonable agreement was obtained between measured thermal-expansion data and results from classical laminate theory. The thermal expansion of a material may change markedly as a result of thermal cycling. Microdamage, induced by 250 cycles between -156 C and 121 C in the graphite/polyimide laminate, caused a 53 percent decrease in the coefficient of thermal expansion. The thermal expansion of the graphite/glass laminate was not changed by 100 thermal cycles from -129 C to 38 C; however, a residual strain of about 10 x 10 to the minus 6 power was measured for the laminate tested.

Tompkins, S. S.↗
NASA NTRS1993

Considerations concerning fatigue life of metal matrix composites

Since metal matrix composites (MMC) are composed from two very distinct materials each having their own physical and mechanical properties, it is feasible that the fatigue resistance depends on the strength of the weaker constituent. Based on this assumption, isothermal fatigue lives of several MMC's were analyzed utilizing a fatigue life diagram approach. For each MMC, the fatigue life diagram was quantified using the mechanical properties of its constituents. The fatigue life regions controlled by fiber fracture and matrix were also quantitatively defined.

Radhakrishnan, V. M.↗