A viewgraph presentation outlines the Earth Radiation Budget Satellite (ERBS) power system and battery history. ERBS spacecraft and battery cell failures are listed with the reasons for failure. The battery management decision and stabilization of the batteries is discussed. Present battery operations are shown to be successful.
Factors influencing cyclic life of nickel cadmium batteries - tabulated test results
As the energy storage devices continue to "pack" more energy in a small space, any damage, battery component failure, manufacturing defect, or electrically abusing the battery can lead to catastrophic thermal runaway events. A catastrophic thermal event in a cell leads to high temperature, in some instances spewing of battery materials due to gas development from side reactions initiated due to high internal temperatures. Also, a thermal runaway event can propagate from a single "failed" cell to the pack in a battery pack, leading to a more significant event. Mitigating a thermal runaway event is important in the commercial and automotive sectors. However, preventing such events in an electric aircraft (or air taxis) is paramount due to the lack of alternatives in the event of a failure. Battery prognostics algorithms allow the prediction of state-of-charge (SOC) and end-of-life (EOL) of a Li-ion battery in a UAV (unmanned air vehicle) [1]. For this presentation, we will extend this two-level battery predictive algorithm to predict SOC, EOL, and estimated maximum temperature during a simulated flight. The model is extended by integrating a lumped physics-driven thermal model for high current densities [2]. The parameters used to control SOC and EOL are maximum storable charge, time constant for Li-ion diffusivity in the carbon particles, and internal cell resistance. Cycling leads to an increase in the heat generated by an aged Li-ion cell with a LiyCoO2 (LCO) cathode and a LixC6 (MCMB) anode. The aging of a cell leads to increase in SEI layer thickness, the diffusion time for the lithium ions inside the electrodes, and the local reaction rates, in addition to the thermodynamic abuse caused by fixed cycling voltages controlled by a Battery Management System. As the battery ages, the cell resistance increases, while the onset temperature of the thermal runaway decreases (depends on the cell chemistry and cell abuse history). Any large deviation of the cell temperature from the estimated (expected) value can identify a faulty cell. Since SEI decomposition has the lowest onset temperature in the series of reactions leading to thermal runaway, the model considers the self-heating rate of the SEI decomposition as onset temperature (similar to Ref. [3]). The parameters in the Arrhenius equation for the SEI heating rate depend on the number of cycles, the cell's operating temperature, and the cell's abuse history [4,5]. Coupling the electrochemical, thermal, and aging model allow the prognostic algorithm to estimate a typical cell voltage and temperature as a function of age (cycling and calendar), whose departure from measured values from the BMS is used to identify a safety event. In addition, we will present the results from two simulated flight scenarios for a UAV: typical and extreme, since the power requirements vary significantly during take-off, landing, and changing altitudes, while the power requirements remain low during the cruise. For this presentation, the power requirement for a battery pack in a UAV is scaled to a single cell. This cell is cycled through a simulated profile, and the data is collected and used to predict a safety event.
Explore the source record for details and available documents.
A model has been developed to describe failure in electrochemical batteries. The model is based on the concept of the existence and subsequent growth of flaws which ultimately lead to battery failure. This model provides, in a natural way, for the statistical variability of lifetime data. The model as applied to the Crane data indicates that when the effects of temperature and depth of discharge are taken into account, the observed variability in lifetime data is due almost entirely to statistical variability inherent in the battery itself.
The TERRA spacecraft was launched in December 1999 from Vandenberg Air Force Base, becoming the flagship of NASA's Earth Observing System program to gather data on how the planet's processes create climate. Originally planned as a 5 year mission, it still provides valuable science data after nearly 10 years on orbit. On October 13th, 2009 at 16:23z following a routine inclination maneuver, TERRA experienced a battery cell failure and a simultaneous failure of several battery heater control circuits used to maintain cell temperatures and gradients within the battery. With several cells nearing the minimum survival temperature, preventing the electrolyte from freezing was the first priority. After several reset attempts and power cycling of the control electronics failed to reestablish control authority on the primary side of the controller, it was switched to the redundant side, but anomalous performance again prevented full heater control of the battery cells. As the investigation into the cause of the anomaly and corrective action continued, a battery thermal model was developed to be used in determining the control ability remaining and to simulate and assess corrective actions. Although no thermal model or detailed reference data of the battery was available, sufficient information was found to allow a simplified model to be constructed, correlated against pre-anomaly telemetry, and used to simulate the thermal behavior at several points after the anomaly. It was then used to simulate subsequent corrective actions to assess their impact on cell temperatures. This paper describes the rapid development of this thermal model, including correlation to flight data before and after the anomaly., along with a comparative assessment of the analysis results used to interpret the telemetry to determine the extent of damage to the thermal control hardware, with near-term corrective actions and long-term operations plan to overcome the anomaly.
A review was made of failures and irregularities experienced on nickel cadmium batteries for 31 spacecraft. Only rarely did batteries fail completely. In many cases, poorly performing batteries were compensated for by a reduction in loads or by continuing to operate in spite of out-of-voltage conditions. Low discharge voltage was the most common problem observed in flight spacecraft (42%). Spacecraft batteries are often designed to protect against cell shorts, but cell shorts accounted for only 16% of the failures. Other causes of problems were high charge voltage (16%), battery problems caused by other elements of the spacecraft (10%), and open circuit failures (6%). Problems of miscellaneous or unknown causes occurred in 10% of the cases.
As the energy storage devices continue to "pack" more energy in a small space, any damage, battery component failure, manufacturing defect, or electrically abusing the battery can lead to catastrophic thermal runaway events. A catastrophic thermal event in a cell leads to high temperature, in some instances to spewing of battery materials due to gas development from side reactions initiated due to high internal temperatures. Moreover, a thermal runaway can propagate from a single "failed" cell to a whole battery pack, resulting in a more serious event. The commercial and automotive sectors need to mitigate thermal runaway events. An electric aircraft (or air taxi) has no alternative in the event of a failure, so preventing such events is paramount. Currently, battery prognostics algorithms only predict the state-of-charge (SOC) and end-of-life (EOL) of a Li-ion battery in a UAV (unmanned air vehicle), but do not predict the maximum temperature during a flight or the likelihood of thermal runaway. Our current work focuses on adding the thermal model (based on Birkl's OCV model, in Ref. [1]) to the existing hybrid electrochemical model (single-particle model with lumped parameters as in Ref. [2]) to determine end-of-discharge, end-of-life, and maximum temperature during discharge.
Cells operating at five degrees Celsius or less, and going to 60 to 65 percent depth of discharge, were studied as to whether they could achieve a useful working life of 7.5 years in a GPS orbit. The characteristics of various orbits were compared and it is noted that the GPS orbit experiences only 220 cycles a year and must be treated as a geosynchronous rather than a low Earth orbit. Cell degradation is considered to be the result of both trickle-charge degradation and degradation due to cycling. Time-to-failure values are presented for selected temperatures and depth of discharges.
An analysis of reliability data on Nickel-Cadmium (NiCd) batteries (for use in spacecraft) is presented. The data were collected by Gates Aerospace and represent a substantial reliability database. The data were taken from the performance of 183 satellites which were in operation from between .1 and 22 years, for a total of 278 million cell-hours of operation.
Ground handling of flight as well as engineering batteries at test facilities and launch-site facilities is a safety critical process. Test equipment interfacing with the batteries should have the required controls to prevent a hazardous failure of the batteries. Test equipment failures should not induce catastrophic failures on the batteries. Transportation requirements for batteries should also be taken into consideration for safe transportation. This viewgraph presentation includes information on the safe handling of batteries for ground processing at test facilities as well as launch-site facilities.
Two batteries containing 18 cells have been cycling in a simulated synchronous (24-hour) orbit for over a year at 40% depth of discharge at 22 C. One battery is under individual cell monitoring and control and the other battery is controlled at the battery level. The battery with individual cell monitoring and protection has performed over 350 cycles with no sign of failure. The battery without individual cell protection failed at 270 cycles from failure to remain above the specified minimum discharge voltage. A significant conclusion is that the sealed Ag-Zn cells manufactured with the inorganic separator material have demonstrated their capability to cycle at a fairly high depth of discharge and are worthy of consideration in short life synchronous orbit applications.
Flight data for 17,000 orbital cycles are reviewed and summarized. The nickel cadmium battery system operated without failure or abnormality. Battery trend analysis used in determining the feasibility of extending mission life is discussed. The life test data for 20% depth of discharge indicates design life requirements would be reached even at a deeper depth of discharge.
Cryptanalytic technique for evaluating nickel- cadmium battery cell failure characteristic data
Results are discussed for a Ni-Cd battery test over a period of 8 years, 2 months and 44,213 simulated low Earth orbits. The battery cells were protected against overdischarge and reversal at discharge rates up to 25 amperes (1.25C) by a battery protection and reconditioning circuit. The circuit performed flawlessly during the test, and proved its value, both as a battery reconditioner and a cell protection device. Battery cell failures are also discussed. The test demonstrated the viability of using Ni-Cd batteries at depth-of-discharge up to 25 percent for over 5 years in a low Earth orbit.
The development of a long life Li/SO2 battery (one that could operate continuously for periods of at least five years) is discussed. The causes of premature failures in battery concepts are defined and solutions to these problems are described. In particular the corrosion of the glass in a glass-to-metal seal and a spot welded positive lead are addressed.
This investigation describes the capacitor failures and to identify the cause of the failure mechanism. Early failures were thought to have happened because of age and/or abuse since the failed capacitors were dated 1967. It is shown that all 1967 capacitors were replaced with 1972 capacitors.
The Solid Rocket Booster Range Safety System (SRBRSS) uses a lithium/poly-carbon monofluoride primary battery as a source of electrical power. After cell fabrication and activation, some battery cells have shown self discharge. One possible source of this cell discharge has been suggested to be the formation and growth of a conducting crystallized chemical compound across the glass bead insulator, electrically shorting the glass bead to the casing. This laboratory has begun an analysis of this compound, the glass seal holding the cathode into place, and the cell electrolyte, using Fast Fourier Transform Infrared (FFTIR) Analysis, Rutherford Backscattering Spectroscopy (RBS), and Nuclear Reaction Microanalysis. Preliminary measurements have confirmed the existence of lithium, nitrogen, fluorine, and oxygen on a reddish-brown deposit covering parts of the glass seal holding the positive electrode in place. Cells using Li metal electrodes, have many advantages over conventional primary batteries. One principal disadvantage of using Li batteries on a commercial basis would be the environmental impact of the fluorocarbon material. Another would be the relatively high expense of (CF)n.