Burst behavior of nuclear grade FeCrAl and Zircaloy-2 fuel cladding under simulated cyclic dryout conditions

A novel experiment to simulate cyclic dryout in boiling water reactors has been developed to better understand the performance of nuclear grade FeCrAl cladding in a BWR during dryout conditions caused by an Anticipated Operational Occurrence or Anticipated Transient Without SCRAM - both of which are Design Basis Accidents. Internally pressurized C26 M FeCrAl alloy cladding and Zircaloy-2 cladding were subjected to rapid 300°-650 °C thermal cycling in a steam environment; actual maximum temperatures were found to vary between materials but were always above 650 °C. In the range of 32–55 MPa hoop stress, Zircaloy-2 cladding burst within 1–16 cycles (about 100 s of dryout duration above 600 °C), while at 76 MPa hoop stress, C26 M cladding remained virtually undeformed after completing 54 cycles (over 1000 s of dryout duration above 600 °C). Higher temperature 300°-700 °C and 300°C–800 °C cycling experiments had to be performed to induce C26 M burst – failure occurred after 20 cycles in the former and during the first cycle in the latter. Zircaloy-2 and C26 M failure criteria were used to generate hoop stress specific dryout lifetimes. Overall, the simulated cyclic dryout experiments show that nuclear grade C26 M cladding has significantly enhanced survivability under dryout conditions relative to Zircaloy-2.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

Interface stability of ultrasonic additively manufactured Zircaloy-4 during hydrothermal corrosion

Simulated pressurized water reactor conditions (330 °C, 15.6 MPa, ~20 ppb oxygen) without irradiation were used to investigate the hydrothermal corrosion behavior of ultrasonic additively manufactured Zircaloy-4 up to 1000 h. X-ray computed tomography allowed for visualization of defects from processing and their progression after corrosion experiments. The specimens were found to have clear variability in the mass change data, compared to typical wrought Zircaloy-4 specimens. The variation in the mass change after exposure was attributed to weld defects connected to the specimen surface which allowed ingress of oxidant into the samples. Defects visualized by computed tomography were found via metallography and characterized. In conclusion, ultrasonic additively manufactured Zircaloy-4 was found to have comparable corrosion behavior as wrought Zircaloy-4 for specimens which did not have clear surface defects along weld interfaces.

36 MATERIALS SCIENCE↗

Second group of irradiation capsules: property data of irradiated welded stainless steel 347 and irradiated, welded, and hydrogen charged Zircaloy-4 for SHINE

Zircaloy-4 and AISI 347 stainless steel were irradiated to low doses (10 20 and 10 21 n/cm 2 ) at low temperature (~60°C) in the High Flux Isotope Reactor (HFIR) at Oak Ridge National Laboratory (ORNL). These materials were under consideration for some of the structural components of the medical isotope production facility developed by SHINE Technologies. Zircaloy-4 base metal, as welded, welded and post-weld heat treated (PWHT), and hydrogen charged samples were irradiated. AISI 347 base metal from Sandmeyer Steel, Penn Stainless, and Rolled Alloys suppliers were irradiated. AISI 347 gas tungsten arc welding (GTAW) and flux-cored arc welding (FCAW) samples of Penn Stainless and Rolled Alloys were also irradiated. The irradiated materials were tested with microhardness and tensile tests at room temperature in air. The AISI 347 materials had more elongation after irradiation than the Zircaloy-4 materials. In fact, the Zircaloy-4 welded without PWHT and with H charging had the lowest elongation of any of the materials. This report is the final in a series of reports on this project.

36 MATERIALS SCIENCE↗

First-Principles Studies of Tritium Species Dissociability & Diffusivity Across the Interface of Nickel-Plated Zircaloy-4

Zirconium (Zr) and its alloys (Zircaloy-4) are widely used in nuclear reactors due to their low neutron adsorption cross-section and excellent corrosion resistance. In tritium-producing burnable absorber rods (TPBARs), the metal getter tube located between the cladding and the γ-LiAlO 2 pellets is composed of nickel (Ni)-plated Zircaloy-4, which is used to capture tritium ( 3 H) species (mainly 3 H 2 and 3 H 2 O) generated from γ-LiAlO 2 pellets during irradiation. The 3 H-related products transfer to the surface of metal Ni upon adsorption and dissociation to form new 3 H species and diffuse into the Zircaloy-4 getters to form metal hydrides (Zr 3 H x ). Therefore, exploring 3 H species ( 3 H 2 , 3 H 2 O) dissociation on the surface of Ni and diffusion across the interface of Ni-plated Zircaloy-4 getters can provide a better understanding of 3H species formation and transport from pellets into the getters.

36 MATERIALS SCIENCE↗

A study on texture stability and the biaxial creep behavior of as-hydrided CWSR Zircaloy-4 cladding at the effective stresses from 55 MPa to 65 MPa and temperatures from 300°C to 400°C

The creep rupture of high burnup used nuclear fuel (> 45 GWD/MTU) cladding is regarded as one of the failure mechanisms during long-term dry storage. A high amount of zirconium hydride in the cladding matrix would degrade the mechanical properties of the cladding especially leading to delayed hydride cracking. To better understand the influence of zirconium hydride on the biaxial thermal creep performance and the crystalline texture stability of Zircaloy-4 cladding, the pressurized tube technique is applied to test the durability of the as-hydrided material. Tests were performed on as-received Zircaloy-4 tubular specimens as well as-hydrided ones with targeted 300 wt parts per million (wppm) or 750 wppm hydrogen. The biaxial creep experiments were conducted at temperatures from 300 degrees C to 400 degrees C and at equivalent stresses at mid-wall from 55 MPa to 65 MPa. The hydridation process prior to creep tests induces the formation of FCC delta-hydride platelets along the circumferential direction of the tube. This alignment and phase structure of hydride show no significant change after biaxial creep tests. The creep strain-rate negatively depends on the hydrogen content. The synchrotron wide-angle X-ray diffraction (WAXD) technique and electron backscatter diffraction (EBSD) analysis were applied for the study of the crystallographic orientation relationship. zirconium-to-hydride grain orientation follows Shoji-Nishiyama crystallographic relationship. This relationship is stable before and after creep deformation. These results of creep performance and texture stability of Zircaloy-4 claddings can help support the design basis of interim and long-term dry storage facilities.

creep↗

The impact of chromium coatings on Zircaloy cladding deformation behavior under reactivity-initiated accident-like mechanical loading conditions

A reactivity-initiated accident (RIA) occurs when a control rod ejection or control blade drop causes an increase in the fission rate. The injection of energy results in an increase in fuel temperature which in turn causes rapid thermal expansion of the fuel pellet. This thermal expansion may result in pellet-cladding mechanical interaction (PCMI) in which the fuel imparts a mechanical strain to the cladding. PCMI may cause the cladding to fail, and thus, the mechanical response of cladding due to PCMI must be investigated when characterizing new cladding materials. Chromium-coated Zircaloy-4 is a near-term accident-tolerant fuel cladding that exhibits improved high-temperature oxidation resistance. Modified burst testing was utilized to experimentally simulate the effects of PCMI on both uncoated and chromium-coated Zircaloy cladding samples at hot zero power conditions. Samples were coated using either cold spraying or physical vapor deposition to understand the differences in behavior that the coating application method may cause. Digital image correlation was used to analyze images of the deforming specimens to extract the in-situ strain behavior of the cladding. The uncoated specimens burst at hoop strains ranging from 8.8 % to 17.2 %. The cold-spray chromium-coated Zircaloy specimens burst at hoop strains of 7.0 % to 11.0 %. The physical vapor deposition coated tubes burst at hoop strains of 9.1 % to 11.5 %. These results indicate that the chromium coating causes a loss in the ductility of the cladding. Furthermore, the higher burst hoop strains of the physical vapor deposition-coated samples relative to the cold-spray samples indicate that the cold-spraying technique causes more of a loss in ductility than physical vapor deposition. All samples burst at higher hoop strains than those expected to occur in an RIA for fresh cladding.

Accident-tolerant fuel↗

Hydrogen embrittlement of Zircaloy-4 fabricated by ultrasonic additive manufacturing

Ultrasonic additive manufacturing (UAM) was successfully applied to the zirconium material system to create a planar geometry. Following fabrication, SS-J3 type tensile specimens of the UAM and wrought Zircaloy-4 with a nominal gage section of 5×1.2×0.75 mm were machined for hydriding studies and mechanical testing. The SS-J3 type tensile specimens were gas-charged with hydrogen using a custom system that precisely controls hydrogen gas flow rate, hydrogen partial pressure, and temperature. To avoid altering the UAM material, the maximum process temperature was limited to 550°C. Using different initial hydrogen gas pressures and flow rates, various hydrogen contents (70–1755 wppm) were achieved for Zircaloy-4 specimens. Tensile testing shows that, regardless of hydrogen content, all UAM specimens measured yield strengths in the range of 557±16 MPa and ultimate tensile strengths of 660±4MPa. However, total elongation clearly decreased as a function of increasing hydrogen content. Further, at the lowest hydrogen content, the total plastic elongation measured 21.5%, and this value decreased to less than 2% when the hydrogen content was increased to 1000 wppm. Cross-sectional optical microscopy images revealed that the hydride distributions are randomly oriented. For the low hydrogen content specimen, these randomly distributed hydrides are isolated from each other. A sandwiched structure, consisting of high-density and low-density layers, was also observed for the specimens with hydrogen content between 200 and 400 wppm. As the hydrogen content increases, the hydrides diffuse into the low-density hydride layers to form a network across the whole specimen. Although the tensile properties of UAM and wrought Zircaloy-4 exhibit the same behavior with increasing hydrogen content, the distinctions in grain orientations led to differences in the hydride orientations at low and intermediate hydrogen concentrations.

36 MATERIALS SCIENCE↗

Evaluation of Hydrogen Gettering Rates Correlated to Surface Composition and Texture of Nickel-Plated Zircaloy Getters of Different Heat Treatment Procedures

Coatings of metal specimens are known to have an impact on hydrogen gettering (hydrogen absorption). The coating can have one or more functions, such as enhancing gettering, preventing gettering and/or preventing oxidation of the metal substrate. It is known that contaminants and surface texture can impact hydrogen gettering/absorption performance, but has not previously been thoroughly explored. This study evaluated the role of different post-plating heat treatments of nickel-plated zircaloy-4 getters (NPGs) and the role of the heat treatments on gettering rates, surface composition and texture. Nickel plating is applied to prevent oxidation of the Zircaloy-4 surface and also enhances gettering. The nickel plating must be heat treated before desirable gettering can occur. Our NPG getters with historically known satisfying performance were pre-heat treated in air followed by activation heat treatment in a vacuum at a higher temperature. In this study, we were interested in finding out if both heat treatment steps were necessary to obtain a desirable gettering performance, or if one step could be omitted. XPS analysis showed that if the nickel surface is not heat treated before bonding the nickel to the zirconium in the activation step, there will be carbon contaminants on the surface, which significantly reduces gettering. We studied the texture of Zircaloy-4 using SEM/EBSD to compare NPGs with both heat treatment steps with NPGs that had no post-plating heat treatment to learn if the degree of cold work could be impacted by the heat treatment steps. We did not observe any differences in texture between them. We measured gettering rates of both pretreated and activated NPGs and NPGs that had been activated without first being pre-heat treated. We found that the NPGs without the first post-plating heating step had up to a seven times slower gettering rate and obtained higher plateau pressures due to the contaminated surface. Thus, the pre-heat treatment in air before activation is necessary to avoid slower gettering rates and higher plateau pressures.

36 MATERIALS SCIENCE↗

Critical heat flux on zircaloy and accident tolerant fuel cladding under prototypical conditions of pressurized and boiling water reactors

First of a kind high spatial and temporal resolution temperature measurements of Pressurized Water Reactor and Boiling Water Reactor simulated fuel pins (high heat flux cosine profile heaters) in annular rod type geometry during nucleate boiling, departure from nucleate boiling and re-wetting has been performed. Distributed fiber optic measurements of the cladding axial temperature with spatial resolutions down to 2.5 mm axially at up to three equally spaced azimuthal locations per rod have demonstrated the similarities and differences of the different accident tolerant fuel cladding materials. These experiments show the performance of accident tolerant cladding with a precise measurement of the location and evolution of dryout followed by the re-wetting phenomena (see supplementary time history of a critical heat flux event). Experimental parameters varied coolant mass fluxes from 1695 to 2712 kg/m 2 s, pressures from 10 to 20 MPa, and inlet subcooling from 10 to 55 °C. It was found that the coatings and different material have little effect on the value of the critical heat flux. Any discrepancies between the local critical heat flux verified among the cladding material are attributed to different departure from nucleate boiling phenomena captured during the experiment with the high-resolution optical fiber temperature data. Substantial differences in the performance of the different cladding material to survive a critical heat flux event were however observed by post-test X-ray and optical inspection. External evident damage and internal cracks to the simulated fuel pin having the bare zircaloy cladding were observed in regions associated with the occurrence of the critical heat flux for longer periods. Such damages were associated with zirconium oxidation, and not noticed on the Cr coated zircaloy or FeCrAl claddings. These results indicate that the use of FeCrAl or a Cr coated zircaloy as cladding in Pressurized Water Reactor and Boiling Water Reactor may increase the survivability of the cladding material for short transients.

32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATI↗

Determining failure properties of as-received and hydrided unirradiated Zircaloy-4 from ring compression tests

An integrated experimental and computational approach was developed to determine the plastic strain at fracture and to investigate the fracture energy of as-received and hydrided unirradiated Zircaloy-4 nuclear cladding tubes in the hoop direction at room temperature from ring compression testing (RCT). This work builds on previous methods in the literature that were developed to obtain the mechanical properties of nuclear cladding before fracture (Young’s modulus, yield stress, and strain-hardening parameters) from experimental RCT results and extends the characterization of this material class to include material failure properties. Furthermore, a ductile damage approach was developed and implemented in a validated finite element model to predict material failure, evaluate fracture energy, and quantify the plastic strain at fracture initiation. The hydrogen content of the Zircaloy-4 specimens was varied up to 610 wppm when the failure became brittle. As expected, increasing hydrogen content caused embrittlement of the Zircaloy-4 samples tested and the plastic strain at fracture and fracture energy to decrease.

36 MATERIALS SCIENCE↗

Mechanical properties, strain hardening, and fracture behavior of ultrasonic additively manufactured Zircaloy-4 after low-temperature neutron irradiation

Ultrasonic additive manufacturing (UAM) is a solid-state, layer-by-layer advanced manufacturing process that has the potential to create custom spatially controlled composites with embedded wires and sensors for nuclear component manufacture. For this work, to assess the feasibility of using UAM for nuclear-relevant materials research, the technique was used to produce a 3.5-mm-thick Zircaloy-4 plate for irradiation testing. The UAM Zircaloy-4 specimens were irradiated in the High Flux Isotope Reactor at a target irradiation temperature of 117 °C to 2.9 displacements per atom (dpa) to assess differences in irradiation-hardening behavior as a function of alloy processing path. The UAM and reference baseplate (BP) materials increased in yield strength by 372±27 MPa and 346±21 MPa, respectively, and both suffered significant reductions in uniform and total elongation attributed to irradiation hardening at low-temperature. Although the materials had similar nanoscale defect structures, including nanoscale black dot/loop features and strain-induced dislocation channels, the UAM material’s processing-related defects resulted in accelerated strain localization and failure as demonstrated by lower post-irradiation uniform elongation of UAM specimens (0.5 %) compared to BP (1.5 %) material. The UAM material also showed considerable anisotropy in mechanical response due to crack propagation along weld boundaries, resulting in differences in strength & ductility when tested parallel and perpendicular to the prior UAM build orientation. Therefore, although the fundamental irradiation response of UAM-processed Zircaloy-4 was phenomenologically comparable to that of BP reference material, additional optimization of the UAM processing is needed to produce irradiation-resistant and nuclear-relevant materials.

Digital image correlation↗

Fundamental Studies of Tritium Formation and Diffusivity in Pure and Defective Zircaloy-4 Getters

Zirconium (Zr) and its alloys are used as fuel cladding in nuclear reactors. These materials have their low absorption cross-section for thermal neutrons and have good mechanical and thermal properties. In addition, they are used as tritium getters in tritium-producing burnable absorber rods (TPBARs), in the form of nickel-plated Zircaloy-4 tubes. To produce 3 H, the breading blankets such as lithium aluminate are irradiated in pressurized water. 3 H produced in this process is captured by the getter and 3 H reacts chemically with Zr to form metal hydride (ZrTx). The precipitation of metal hydride results in not only the volume increase and hydrogen embrittlement of zircaloy but also changes in getter’s chemical properties. This degrades the getter’s performance. Therefore, understanding the behavior of 3 H (such as diffusion and solubility) in zircaloy is important to understand getter performance.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

Mechanical creep testing and characterization of Cr coated Zircaloy

Zirconium based cladding has been developed for use in light water reactor fuel applications due to the material’s desirable low neutron scattering cross section. To help improve corrosion resistance in accident conditions, such as a loss of coolant accident (LOCA), a chromium coating can be applied to the outer diameter of the Zircaloy tube. Cladding strength at reactor relevant temperatures is important for the structural performance. Stress relaxation creep testing was performed on Cr coated Zircaloy-4 to measure strain rate as a function of stress for 350 and 650°C. These were performed at both 5 ± 1 % and 7.5 ± 1 % strain. The lower temperature provides results near normal operating temperature, while the higher temperature provides results relevant to off-normal conditions where recrystallization will take place. Characterization was also performed to analyze the structure of the Cr coating and Zircaloy-4 as well as the interface between the two.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

BISON capability and validation for U3Si2, Cr2O3-doped UO2, FeCrAl, and Cr-coated Zircaloy ATF concepts

Development, implementation, and validation of material and behavior models for accident tolerant fuel (ATF) concepts in the BISON fuel performance code began in 2014 in response to the events that occurred at the Fukushima Daichii nuclear power plant in March 2011. Early on, the focus was on U3Si2 fuel and FeCrAl cladding as part of a high-impact problem through the Nuclear Energy and Advanced Model- ing Simulation program [1]. Then, developments for Cr2O3- doped UO2 fuel, as well as SiC-SiC and Cr-coated Zircaloy cladding began based upon industry interests. Near the end of fiscal year 2018 the Consortium for Advanced Simulation of Light Water Reactors took over further Accident Tolerant Fuel (ATF) work in BISON in support of Nuclear Regulatory Commission (NRC) engagement. Discussions with the NRC clarified their list of priority fuel and cladding concepts, which included Cr2O3-doped UO2 and U3Si2 fuels, as well as Cr-coated Zircaloy and FeCrAl claddings. Further, reports similar in form to NUREG/CR-7024 [2] that was developed for traditional light water reactor (LWR) materials, UO2 fuel with Zircaloy claddings were created for the priority fuel and cladding concepts. In this paper select details from the reports entitled "ATF material model development and validation for priority fuel concepts" [3] and "ATF material model development and validation for priority cladding concepts" [4] are presented. First, a brief overview of the available models and their associated uncertainty are provided for the priority fuel and cladding concepts. Then, for the concepts with experimental data, comparisons between simulation and experiment are shown taking into account forward uncertainty quantification (UQ) techniques. For the concepts without publicly available experimental data, parametric studies incorporating forward UQ are completed to verify claims made about the materials’ behavior.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

Length scale effects of micro- and meso-scale tensile tests of unirradiated and irradiated Zircaloy-4 cladding

Zircaloy-4 is an essential material for cladding structures within fission-based reactors. To explore the changes in properties measured on differing length scales, FIB-machined micro-scale tensile tests were performed on both irradiated and control groups of Zircaloy-4. This was correlated with tensile testing on femtosecond laser-machined meso-scale specimens. Pronounced size effects were found when varying specimen geometry. Increases in tensile geometry size were associated with a reduction in measured yield stress for both irradiated and unirradiated samples. Here, meso-scale testing found strength and strain values similar to that of bulk-scale testing.

36 MATERIALS SCIENCE↗

BISON analysis of FeCrAl and Zircaloy cladding deformation during simulated BWR cyclic dryout conditions

The BISON fuel performance analysis code has been used to study FeCrAl and Zircaloy cladding performance to better understand cladding deformation behavior in boiling water reactors during conditions caused by anticipated operational occurrences (AOOs) or by anticipated transients without scram (ATWS). BISON models of novel separate effects tests simulating ATWS events predicted mechanical responses to thermal cycling boundary conditions. Here, we assessed FeCrAl and Zircaloy deformation and burst models to determine those best suited for cyclic dryout event analysis. In addition, we compared diametral strain profiles of the post-experiment claddings to simulation results. The capability of the BISON code for modeling BWR AOO or ATWS events is promising.

36 MATERIALS SCIENCE↗

Discerning the effect of various irradiation modes on the corrosion of Zircaloy-4

Using proton irradiation, this study investigates the individual influence of several factors on the corrosion kinetics of Zircaloy-4 in a hydrogenated water environment simulating a Pressurized Water Reactor (PWR). Using both simultaneous irradiation-corrosion and autoclave corrosion, we separately examine: (i) the effect of pre-irradiation on modifying the structure of the material, (ii) the impact of irradiation on creating defects in the growing oxide layer during corrosion, and (iii) the influence of irradiation on increasing the corrosion potential through radiolysis during corrosion. To replicate neutron-irradiated microstructure, two proton pre-irradiation schedules were employed: Schedule 1 (isothermal irradiation at 350 °C to 5 dpa) to simulate high-temperature PWR conditions, and Schedule 2 (two-step process: irradiation to 2.5 dpa at -10 °C followed by 2.5 dpa at 350 °C) to simulate lower temperature PWR and Boiling Water Reactor (BWR) conditions. Long-term autoclave corrosion testing over 360 days at 320 °C revealed no significant difference between unirradiated samples and those pre-irradiated according to either schedule, with all samples exhibiting sub-cubic kinetics within the pre-transition regime. Irradiated samples underwent Simultaneous Irradiation Corrosion (SIC) tests, corroding in 320 °C water while being irradiated with protons. Corrosion was found to accelerate in all SIC-tested samples relative to autoclave conditions, with the greatest increase observed in non-pre-irradiated samples. Pre-irradiation with either schedule resulted in a slower corrosion rate compared to non-pre-irradiated regions under SIC conditions. The degree of radiolysis observed in the SIC tests surpassed typical PWR conditions, approaching levels found in BWRs. Radiolysis products were identified as the primary contributors to accelerated corrosion, corroborated by radiolysis bar tests. Furthermore, these findings underscore the intricate interactions between irradiation, corrosion, and water chemistry in determining Zircaloy-4 corrosion kinetics within nuclear reactor environments.

Pressurized Water Reactor↗

Structure evolution and tin redistribution during oxidation of Zircaloy-4 at 500°C

Zirconium (Zr) alloys are widely used as fuel cladding in nuclear power reactors due to their thermal stability, mechanical durability, corrosion resistance, and low neutron absorption cross-section. However, their performance is challenged by oxidation in reactor environments, making the study of Zr alloy corrosion behavior crucial for ensuring the safety, longevity, and economic viability of nuclear power systems. While the oxidation behavior of Zr-based cladding materials has been extensively studied since the 1950s, a mechanistic understanding into the relationship between structure evolution, solute element redistribution, and properties remains elusive. Valuable insights may be obtained through advanced experimental methods, such as in-situ and high resolution microscopy techniques. Here, in this study, the oxidation behavior of Zircaloy-4 at 500 °C in O 2 is characterized using a multimodal advanced characterization approach. Using in-situ X-ray diffraction, the phase evolution from metastable to stable oxides is tracked in real time. Complementary high-resolution techniques, including electron microscopy and atom probe tomography, reveal nanoscale insights into the microstructural changes and solute redistribution across the oxide/metal interface. Nanohardness mapping across the oxide/metal interface highlights localized mechanical property variations that may be linked to changes in microstructure and crystal structure within the oxide layer. These findings offer valuable insights into the microstructure and property evolution of Zircaloy-4 during oxidation, contributing to a better understanding of microstructural changes in Zr-based alloys under oxidative environments.

APT↗