pCAM precursor produced from electroextraction technology and its application in synthesis of NMC 811 cathode material
The synthesis and characterization of LiNi 0.8 Co 0.1 Mn 0.1 O 2 (LNMC811) cathodes produced from recycled hydroxide precursors obtained from spent lithium-ion batteries is evaluated. Two precursor batches (Sample 1 and Sample 2) are prepared using modified recycling processes to examine how residual impurities and processing conditions influence the properties of the regenerated materials. Structural and compositional characterization by X-ray diffraction, ICP and SEM shows that the recycled precursors exhibit layered hydroxide structures containing both α Ni(OH) 2 and β Ni(OH) 2 phases. Trace impurities including sodium, boron, and aluminum are detected and partially mitigated during processing, with boron found to play a beneficial role in electrochemical behavior. Following lithiation with lithium carbonate and lithium hydroxide at 800 °C under an oxygen rich atmosphere, the resulting LNMC811 materials show electrochemical performance comparable to conventionally synthesized cathodes. Sample 2, which contains higher boron levels and improved cation ordering, delivers an initial discharge capacity of 174 mAh g -1 and retains more than 93 percent of its capacity after 50 cycles. The stable cycling behavior and structural integrity of these materials demonstrate that recycled precursors can be converted into high performance layered cathodes and support recycling as a practical and sustainable route for lithium-ion battery manufacturing.