NASA NTRS1989

Fatigue crack growth in a unidirectional SCS-6/Ti-15-3 composite

An investigation was conducted to characterize and model the fatigue crack growth (FCG) behavior of a SCS-6/Ti-15-3 metal matrix composite. Part of the study was conducted using a fatigue loading stage mounted inside a scanning electron microscope (SEM). This unique facility allowed high magnification viewing of the composite fatigue processes and measurement of the near crack tip displacements. The unidirectional composite was tested in the (0)8 (i.e., longitudinal) and (90)8 (i.e., transverse) orientations. For comparison purposes unreinforced matrix material produced by the identical process as the reinforced material was also tested. The results of the study reveal that the fatigue crack growth behavior of the composite is a function of specimen geometry, fiber orientation and the interaction of local stress fields with the highly anisotropic composite. In the case of (0)8 oriented single edge notch (SEN) specimens and (90)8 oriented compact tension (CT) specimens, the crack growth was normal to the loading direction. However, for the (0)8 CT specimens the crack grew mostly parallel to the loading and the fiber direction. The unusual fatigue behavior of the (0)8 CT specimens was attributed to the specimen geometry and the associated high tensile bending stresses perpendicular to the fiber direction. These stresses resulted in preferential cracking in the weak interface region perpendicular to the fiber direction. The interface region, and in particular the carbon coating surrounding the fiber proved to be the composites weakest link. In the (0)8 SEN the crack growth was confined to the matrix leaving behind unbroken fibers which bridged the cracked surfaces. As the crack grew longer, more fibers bridged the crack resulting in a progressive decrease in the crack growth rates and eventual crack arrest. The actual near crack tip displacement measurements were used in a proposed formulation for a bridging-corrected effective crack driving force, delta K(sub eff). This parameter was able to account for most of the experienced bridging and correlated the (0)8 SEN fatigue crack growth data reasonably well.

Kantzos, Peter↗
NASA NTRS1990

Thermomechanical testing techniques for high-temparature composites: TMF behavior of SiC(SCS-6)/Ti-15-3

Thermomechanical testing techniques recently developed for monolithic structural alloys were successfully extended to continuous fiber reinforced composite materials in plate form. The success of this adaptation was verified on a model metal matrix composite (MMC) material, namely SiC(SCS-6)/Ti-15V-3Cr-3Al-3Sn. Effects of heating system type and specimen preparation are also addressed. Cyclic lives determined under full thermo-mechanical conditions were shown to be significantly reduced from those obtained under comparable isothermal and in-phase bi-thermal conditions. Fractography and metallography from specimens subjected to isothermal, out-of-phase and in-phase conditions reveal distinct differences in damage-failure modes. Isothermal metallography revealed extensive matrix cracking associated with fiber damage throughout the entire cross-section of the specimen. Out-of-phase metallography revealed extensive matrix damage associated with minimal (if any) fiber cracking. However, the damage was located exclusively at surface and near-surface locations. In-phase conditions produced extensive fiber cracking throughout the entire cross-section, associated with minimal (if any) matrix damage.

Castelli, Michael G.↗
NASA NTRS1990

Characterization of unnotched SCS-6/Ti-15-3 metal matrix composites at 650 C

Ti-15-3 reinforced with SCS-6 silicon carbide fibers, in five different layups, was tested at 650 C to determine monotonic and fatigue strengths, basic mechanical properties, and damage initiation and progression. The elevated temperature results were compared to those obtained at room temperature. Analytical predictions were made of the monotonic stress-strain response as well as cyclic stress-strain hysteresis. The fiber reinforcement was found to significantly increase the static and fatigue strengths of the laminates over that of the matrix material at elevated temperature while the increase was insignificant at room temperature. Initial damage, in either the fibers or the matrix, was partitioned as a function of the life and applied strain range in the constituents. High strains and short lives resulted in multiple fiber failure with no signs of matrix fatigue cracking. Low strains and long lives resulted in extensive matrix cracking and no fiber breaks away from the fracture surface. At 650 C the matrix was too weak to cause fiber-matrix interface failure prior to matrix yielding. Laminate fatigue lives were hypothesized to be a function of the 0 deg fiber stress. More scatter was found in the 0 deg fiber stress vs. high temperature fatigue life data than for the room temperature data. An initial unloading modulus that was greater than the initial loading modulus was observed in the elevated temperature fatigue tests.

Pollock, W. D.↗
NASA NTRS1990

Matrix fatigue crack development in a notched continuous fiber SCS-6/Ti-15-3 composite

In this study the extensive matrix fatigue cracking that has been observed in notched SCS-6/Ti-15-3 composites is investigated. Away from the notch a uniform spacing of the fatigue cracks develops. Closer to the notch, fiber-matrix debonding which occurs increases the crack spacing. Crack spacing and debond length determined from shear-lag cylinder models compare favorably with experimental observations. Scanning electron microscope (SEM) fractography showed that the principal fatigue crack initiation occurred around the zero degree fibers. Interface failure in the 90 degree plies does not lead to the development of the primary fatigue cracking.

Hillberry, B. M.↗
NASA NTRS1991

The microstructure of SCS-6 SiC fiber

A thorough investigation of the microstructure of single SCS-6 SiC fibers widely used as reinforcements in metal-matrix and ceramic-matrix composites has been made. Various techniques of EM including SEM, TEM, HREM parallel electron energy loss spectroscopy (PEELS), and SAM have been used to analyze and characterize the microstructure. The fiber is a complicated composite consisting of many different layers of SiC deposited on a carbon core and different carbonaceous coatings covering the SiC layers. The structural and chemical aspects of each layer are characterized and discussed.

Ning, X. J.↗
NASA NTRS1991

Prediction of matrix fatigue crack initiation in notched SCS-6/Ti-15-3 metal matrix composites

Several lay-ups of SCS-6/Ti-15-3 metal matrix composites were tested in either a center hole or a double edge notched geometry. At different cyclic strss levels, the number of cycles required to develop matrix fatigue cracks at the notches was recorded. A fatigue strat-life curve was developed for the Ti-15-3 matrix material. This modified parameter predicted the number of cycles required for matrix crack initiation at the notches. The predictions were in good agreement with the experimental data.

Hillberry, B. M.↗
NASA NTRS1992

The effects of uneven fiber spacing on thermal residual stresses in a unidirectional SCS-6Ti-15-3 laminate

High residual stresses develop in SCS-6/Ti-15-3 composites during cooldown from the fabrication temperature; these residual stresses can effect the mechanical and physical properties of the composite. Discrete fiber-matrix finite element models were used to study the residual stresses due to the temperature change during the fabrication process, including the effects of uneven fiber spacing, the free surface, and increased fiber volume fractions. To accurately model the effects of the free surface, it is only necessary to model one fiber through the thickness. Below the first ply, the analysis predicts stress distributions that are identical to the infinite array predictions. For uneven fiber space less then 0.042 mm in an interior ply, the maximum hoop stress was predicted to occur between fibers within a ply and to increase as the fiber spacing decreased. The maximum hoop stress correlated well with the observed radial cracking between fibers. For the case of touching fibers, the analysis predicted tensile radial stresses at the fiber-matrix debonding during the fabrication cooldown. Identical trends were predicted for uneven fiber spacing in surface plies with slightly greater values of maximum stresses. The analysis predicted matrix yielding to occur upon cooldown when the edge-to-edge fiber spacing was less than or equal to 0.022 mm. The stress distributions predicted for increasing fiber volume fractions were similar to those predicted for decreasing the fiber spacing for two adjacent fibers within a ply.

Bigelow, C. A.↗
NASA NTRS1991

Fatigue crack growth in a unidirectional SCS-6/Ti-15-3 composite

An investigation was conducted to characterize and model the fatigue crack growth (FCG) behavior of an SCS-6/Ti-15-3 metal matrix composite. Part of the study was conducted using a fatigue loading stage mounted inside a scanning electron microscope (SEM). The results of the study reveal that the fatigue crack growth behavior of the composite is a function of specimen geometry, fiber orientation, and interaction of local stress fields with the highly anisotropic composite. In the case of (0)8 oriented single edge notch specimens and (90)8 oriented compact tension (CT) specimens, the crack growth was normal to the loading direction. However, for the (0)8 CT specimens, the crack grew mostly parallel to the loading and the fiber direction. The unusual fatigue behavior of the (0)8 CT specimens is attributed to the specimen geometry and the associated high tensile bending stresses perpendicular to the fiber direction.

Kantzos, Peter↗
NASA NTRS1992

Thermomechanical testing of high-temperature composites - Thermomechanical fatigue (TMF) behavior of SiC(SCS-6)/Ti-15-3

Thermomechanical testing techniques recently developed for monolithic structural alloys were successfully extended to continuous fiber reinforced composite materials in plate form. The success of this adaptation was verified on a model metal matrix composite (MMC) material, namely SiC(SCS-6)/Ti-15V-3Cr-3Al-3Sn. Effects of heating system type and specimen preparation are also addressed. Cyclic lives determined under full thermomechanical conditions were shown to be significantly reduced from those obtained under comparable isothermal and in-phase bi-thermal conditions. Fractography and metallography from specimens subjected to isothermal, out-of-phase and in-phase conditions reveal distinct differences in damage-failure modes. Isothermal metallography revealed extensive matrix cracking associated with fiber damage throughout the entire cross-section of the specimen. Out-of-phase metallography revealed extensive matrix damage associated with minimal (if any) fiber cracking. However, the damage was located exclusively at surface and near-surface locations. In-phase conditions produced extensive fiber cracking throughout the entire cross-section, associated with minimal (if any) matrix damage.

Castelli, Michael G.↗
NASA NTRS1992

Characterization of unnotched SCS-6/Ti-15-3 metal matrix composites at 650 C

Ti-15-3 reinforced with SCS-6 silicon carbide fibers, in five different layups, was tested at 650 C to determine monotonic and fatigue strengths, basic mechanical properties, and damage initiation and progression. The elevated temperature results were compared to those obtained at room temperature. Analytical predictions were made of the monotonic stress-strain response as well as cyclic stress-strain hysteresis. The fiber reinforcement was found to significantly increase the static and fatigue strengths of the laminates over that of the matrix material at elevated temperature while the increase was insignificant at room temperature. Initial damage, in either the fibers or the matrix, was partitioned as a function of the life and applied strain range in the constituents. High strains and short lives resulted in multiple fiber failure with no signs of matrix fatigue cracking. Low strains and long lives resulted in extensive matrix cracking and no fiber breaks away from the fracture surface. At 650 C the matrix was too weak to cause fiber-matrix interface failure prior to matrix yielding. Laminate fatigue lives were hypothesized to be a function of the 0 deg fiber stress. More scatter was found in the 0 deg fiber stress vs. high temperature fatigue life data than for the room temperature data. An initial unloading modulus that was greater than the initial loading modulus was observed in the elevated temperature fatigue tests.

Pollock, William D.↗
NASA NTRS1990

Matrix fatigue crack development in a notched continuous fiber SCS-6/Ti-15-3 composite

In this study the extensive matrix fatigue cracking that has been observed in notched SCS-6/Ti-15-3 composites is investigated. Away from the notch uniform spacing of the fatigue cracks develops. Closer to the notch, fiber-matrix debonding which occurs increases the crack spacing. Crack spacing and debond length determined from shear-lag cylinder models compare favorably with experimental observations. Scanning electron microscope (SEM) fractography showed that the principal fatigue crack initiation occurred around the zero degree fibers. Interface failure in the 90 degree plies does not lead to the development of the primary fatigue cracking.

Hillberry, B. M.↗
NASA NTRS1992

The effects of uneven fiber spacing on thermal residual stresses in a unidirectional SCS-6/Ti-15-3 laminate

High residual stresses develop in SCS-6/Ti-15-3 composites during cooldown from the fabrication temperature; these residual stresses can effect the mechanical and physical properties of the composite. Discrete fiber-matrix finite element models were used to study the residual stresses due to the temperature change during the fabrication process, including the effects of uneven fiber spacing, the free surface, and increased fiber volume fractions. To accurately model the effects of the free surface, it is only necessary to model one fiber through the thickness. Below the first ply, the analysis predicts stress distributions that are identical to the infinite array predictions. For uneven fiber space less than 0.042 mm in an interior ply, the maximum hoop stress was predicted to occur between fibers within a ply and to increase as the fiber spacing decreased. The maximum hoop stress correlated well with the observed radial cracking between fibers. For the case of touching fibers, the analysis predicted tensile radial stresses at the fiber-matrix debonding during the fabrication cooldown. Identical trends were predicted for uneven fiber spacing in surface plies with slightly greater values of maximum stresses. The analysis predicted matrix yielding to occur upon cooldown when the edge-to-edge fiber spacing was less than or equal to 0.022 mm. The stress distributions preidcted for increasing fiber volume fractions were similar to those predicted for decreasing the fiber spacing for two adjacent fibers within a ply.

Bigelow, Catherine A.↗
NASA NTRS1992

Prediction of matrix fatigue crack initiation in notched SCS-6/Ti-15-3 metal matrix composites

Several lay-ups of SCS-6/Ti-15-3 metal matrix composites were tested in either a center hole or a double edge notched geometry. At different cyclic stress levels, the number of cycles required to develop matrix fatigue cracks at the notches was recorded. A fatigue strat-life curve was developed for the Ti-15-3 matrix material. This modified parameter predicted the number of cycles required for matrix crack initiation at the notches. The predictions were in good agreement with the experimental data.

Hillberry, Benjamin M.↗
NASA NTRS1992

Effect of high temperature annealing on the microstructure of SCS-6 SiC fibers

The effect of annealing the SCS-6 SiC fiber for one hour at 2000 C in an argon atmosphere is reported. The SiC grains in the fiber coarsen appreciably and the intergranular carbon films segregate to the grain junctions. It would appear that grain growth in the outer part of the fiber is primarily responsible for the loss in fiber strength and improvement in fiber creep resistance.

Ning, X. J.↗
NASA NTRS1993

Microchemical analysis of the SCS-6 silicon carbide fiber

A detailed quantitative study of the microstructural variation of chemical composition of chemically vapor-deposited commercial SiC SCS-6 fiber is presented. Chemical etching and various electron-optical techniques including SEM, TEM, scanning Auger microscopy, AES, and parallel electron energy loss spectroscopy are used to analyze the chemical composition of the as-received fiber. In addition, some results on stereology of the high-temperature annealed fiber are presented. The results show that the carbon-to-silicon atom ratio in the SiC layers decreases in a stepwise fashion from about 3:2 to about 1:1 in going from the innermost layer to the outermost layer.

Ning, Xian-Jie↗
NASA NTRS1993

A study of fiber volume fraction effects in notched unidirectional SCS-6/Ti-15V-3Cr-3Al-3Sn composite

Notched unidirectional SCS-6/Ti-15-3 composite of three different fiber volume fractions (vf = 0.15, 0.37, and 0.41) was investigated for various room temperature microstructural and material properties including: fatigue crack initiation, fatigue crack growth, and fracture toughness. While the matrix hardness is similar for all fiber volume fractions, the fiber/matrix interfacial shear strength and matrix residual stress increases with fiber volume fraction. The composite fatigue crack initiation stress is shown to be matrix controlled and occurs when the net maximum matrix stress approaches the endurance limit stress of the matrix. A model is presented which includes residual stresses and presents the composite initiation stress as a function of fiber volume fraction. This model predicts a maximum composite initiation stress at vf approximately 0.15 which agrees with the experimental data. The applied composite stress levels were increased as necessary for continued crack growth. The applied Delta(K) values at crack arrest increase with fiber volume fraction by an amount better approximated using an energy based formulation rather than when scaled linear with modulus. After crack arrest, the crack growth rate exponents for vf37 and vf41 were much lower and toughness much higher, when compared to the unreinforced matrix, because of the bridged region which parades with the propagating fatigue crack. However, the vf15 material exhibited a higher crack growth rate exponent and lower toughness than the unreinforced matrix because once the bridged fibers nearest the crack mouth broke, the stress redistribution broke all bridged fibers, leaving an unbridged crack. Degraded, unbridged behavior is modeled using the residual stress state in the matrix ahead of the crack tip. Plastic zone sizes were directly measured using a metallographic technique and allow prediction of an effective matrix stress intensity which agrees with the fiber pressure model if residual stresses are considered. The sophisticated macro/micro finite element models of the 0.15 and 0.37 fiber volume fractions presented show good agreement with experimental data and the fiber pressure model when an estimated effective fiber/matrix debond length is used.

Covey, Steven J.↗
NASA NTRS1994

Prediction of stress-strain response of SCS-6/Timetal-21S subjected to a hypersonic flight profile

Thermomechanical response of a cross-ply SCS-6/Timetal-21S composite subjected to a generic hypersonic flight profile with the temperature ranging from -130 C to 816 C was evaluated experimentally and analytically. A two dimensional micromechanical anlaysis, VISCOPLY, was used to predict the stress-strain response of the laminate and of the constituents in each ply during thermomechanical loading conditions. In the analysis, the fiber was modeled as elastic with transverse orthotropic and temperature dependent properties and the matrix was modeled using a thermoviscoplastic constitutive relation. The fiber transverse modulus was reduced in the analysis to simulate fiber-matrix interface failure. Reasonable agreement was found between measured and predicted laminate stress-strain response when fiber-matrix debonding was modeled.

Mirdamadi, Massoud↗
NASA NTRS1994

Isothermal Damage and Fatigue Behavior of SCS-6/Timetal 21S [0/90](Sub S) Composite at 650 Deg C

The isothermal fatigue damage and life behaviors of SCS-6/Timetal 21S (0/90)s were investigated at 650 C. Strain ratcheting and degradation of the composite's static elastic modulus were carefully monitored as functions of cycles to indicate damage progression. Extensive fractographic and metallographic analyses were conducted to determine damage/failure mechanisms. Resulting fatigue lives show considerable reductions in comparison to (0) reinforced titanium matrix composites subjected to comparable conditions. Notable stiffness degradations were found to occur after the first cycle of loading, even at relatively low maximum stress levels, where cyclic lives are greater than 25,000 cycles. This was attributed to the extremely weak fiber/matrix bond which fails under relatively low transverse loads. Stiffness degradations incurred on first cycle loadings and degradations thereafter were found to increase with increasing maximum stress. Environmental effects associated with oxidation of the (90) fiber interfaces clearly played a role in the damage mechanisms as fracture surfaces revealed environment assisted matrix cracking along the (90) fibers. Metallographic analysis indicated that all observable matrix fatigue cracks initiated at the (90) fiber/matrix interfaces. Global de-bonding in the loading direction was found along the (90) fibers. No surface initiated cracks were evident and minimal if any (0) fiber cracking was visible.

Castelli, Michael G.↗