Mechanical behavior in boron-microalloyed CoCrNi medium-entropy alloy studied by in situ high-energy X-ray diffraction
Abstract not provided
Shi, Yajuan↗
SEARCH · Engineering Papers
Results for “Medium-entropy alloy”
Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.
Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.
Deformation and failure of the CrCoNi medium-entropy alloy subjected to extreme shock loading
The extraordinary work hardening ability and fracture toughness of the face-centered cubic (fcc) high-entropy alloys render them ideal candidates for many structural applications. Here, the deformation and failure mechanisms of an equiatomic CrCoNi medium-entropyalloy (MEA) were investigated by powerful laser-driven shock experiments. Multiscale characterization demonstrates that profuse planar defects including stacking faults, nanotwins, and hexagonal nanolamella were generated during shock compression, forming a three-dimensional network. During shock release, the MEA fractured by strong tensile deformation and numerous voids was observed in the vicinity of the fracture plane. High defect populations, nanorecrystallization, and amorphization were found adjacent to these areas of localized deformation. Molecular dynamics simulations corroborate the experimental results and suggest that deformation-induced defects formed before void nucleation govern the geometry of void growth and delay their coalescence. Our results indicate that the CrCoNi-based alloys are impact resistant, damage tolerant, and potentially suitable in applications under extreme conditions.
36 MATERIALS SCIENCE↗
Kink bands promote exceptional fracture resistance in a NbTaTiHf refractory medium-entropy alloy
Single-phase body-centered cubic (bcc) refractory medium- or high-entropy alloys can retain compressive strength at elevated temperatures but suffer from extremely low tensile ductility and fracture toughness. We examined the strength and fracture toughness of a bcc refractory alloy, NbTaTiHf, from 77 to 1473 kelvin. This alloy’s behavior differed from that of comparable systems by having fracture toughness over 253 MPa·m 1/2 , which we attribute to a dynamic competition between screw and edge dislocations in controlling the plasticity at a crack tip. Whereas the glide and intersection of screw and mixed dislocations promotes strain hardening controlling uniform deformation, the coordinated slip of <111> edge dislocations with {110} and {112} glide planes prolongs nonuniform strain through formation of kink bands. These bands suppress strain hardening by reorienting microscale bands of the crystal along directions of higher resolved shear stress and continually nucleate to accommodate localized strain and distribute damage away from a crack tip.
36 MATERIALS SCIENCE↗
Effects of cryogenic temperature and grain size on fatigue-crack propagation in the medium-entropy CrCoNi alloy
CrCoNi-based high-entropy alloys have demonstrated outstanding mechanical properties, particularly at cryogenic temperatures. Here we investigate the fatigue-crack propagation properties of the equiatomic, single-phase, face-centered cubic, medium-entropy alloy (MEA), CrCoNi, that displays exceptional strength, ductility and toughness, all of which are enhanced at cryogenic temperatures. Fatigue-crack growth is examined, at a load ratio of 0.1 over a wide range of growth rates, from ~10 –11 to >10 –7 m/cycle, at room (293 K) and cryogenic (198 K, 77 K) temperatures for two grain sizes (~7 and 68 µm), with emphasis on near-threshold behavior. We find that the ΔK th fatigue thresholds are increased with decreasing temperature and increasing grain size: from 5.7 MPa√m at 293 K to 8 MPa√m at 77 K in the fine-grained alloy, and from 9.4 MPa√m at 293 K to 13.7 MPa√m at 77 K in the coarse-grained alloy. Mechanistically, transgranular cracking at 293 K transitions to a mixture of intergranular and transgranular at cryogenic temperatures, where the increased propensity of nano-twins appears to inhibit growth rates by deflecting the crack path. However, the main factor affecting near-threshold behavior is roughness-induced crack closure from interference between the crack flanks, which is enhanced by the rougher fracture surfaces at low temperatures, particularly in the coarser-grained microstructure. Here, fatigue-crack propagation behavior in CrCoNi is comparable to nickel-based superalloys but is superior to that of the high-entropy CrMnFeCoNi (Cantor) alloy and many high-strength steels, making the CrCoNi alloy an excellent candidate material for safety-critical applications, particularly involving low temperatures.
36 MATERIALS SCIENCE↗
An atomistic study connecting underlying dislocation behavior with superior mechanical properties of NiCoCr medium entropy alloy
NiCoCr-based medium-entropy alloy (MEA) with a simple face-centered cubic crystal phase exhibits excellent mechanical properties, often attributed to the synergy of multiple deformation mechanisms. However, the atomistic origin of their outstanding mechanical response, including microstructural evolution and dislocation behavior under varying strain-rates and orientation, remains unclear. In this work, we employ large-scale molecular dynamics (MD) simulations to investigate the changes in deformation mechanisms along three distinct orientations ([110], [111], [100]) under varying strain rates (1 ×10 8 /sec, 1 ×10 10 /sec, 1 ×10 12 /sec) in the NiCoCr MEA. The presence of the stair-rod and the Shockley partial dislocations under uniaxial tensile strain are found to play a key role in the formation of deformation twinning and ε-martensite, which positively correlates with strain-rate dependent dislocation analysis. These findings further establish the role of the dislocations in controlling the superior mechanical response and excellent fracture toughness of the NiCoCr MEA. Systematic transmission-electron microscopy tests performed on the [111]-oriented crystals, deformed at different strain levels, at room temperature provide clear evidence of both the extended stacking-fault and the stair rods, confirming the predicted microstructural features. Finally, this study offers key insights into the complex nucleation mechanisms of deformation twinning and ε-martensite, such as twinning – and transformation–induced plasticity (TWIP-TRIP), providing valuable guidelines for studying similar material classes.
36 MATERIALS SCIENCE↗
Three-dimensional atomic structure and local chemical order of medium- and high-entropy nanoalloys
Medium- and high-entropy alloys (M/HEAs) mix several principal elements with near-equiatomic composition and represent a model-shift strategy for designing previously unknown materials in metallurgy, catalysis and other fields. One of the core hypotheses of M/HEAs is lattice distortion, which has been investigated by different numerical and experimental techniques. However, determining the three-dimensional (3D) lattice distortion in M/HEAs remains a challenge. Moreover, the presumed random elemental mixing in M/HEAs has been questioned by X-ray and neutron studies, atomistic simulations, energy dispersive spectroscopy and electron diffraction, which suggest the existence of local chemical order in M/HEAs. However, direct experimental observation of the 3D local chemical order has been difficult because energy dispersive spectroscopy integrates the composition of atomic columns along the zone axes and diffuse electron reflections may originate from planar defects instead of local chemical order. Here, in this work, we determine the 3D atomic positions of M/HEA nanoparticles using atomic electron tomography and quantitatively characterize the local lattice distortion, strain tensor, twin boundaries, dislocation cores and chemical short-range order (CSRO). We find that the high-entropy alloys have larger local lattice distortion and more heterogeneous strain than the medium-entropy alloys and that strain is correlated to CSRO. We also observe CSRO-mediated twinning in the medium-entropy alloys, that is, twinning occurs in energetically unfavoured CSRO regions but not in energetically favoured CSRO ones, which represents, to our knowledge, the first experimental observation of correlating local chemical order with structural defects in any material. We expect that this work will not only expand our fundamental understanding of this important class of materials but also provide the foundation for tailoring M/HEA properties through engineering lattice distortion and local chemical order.
36 MATERIALS SCIENCE↗
Martensitic Transformation in Fe x Mn 80-x Co 10 Cr 10 High-Entropy Alloy
High-entropy alloys and even medium-entropy alloys are an intriguing class of materials in that structure and property relations can be controlled via alloying and chemical disorder over wide ranges in the composition space. Employing density-functional theory combined with the coherent-potential approximation to average over all chemical configurations, we tune free energies between face-centered-cubic and hexagonal-close-packed phases in Fe x Mn 80 - x Co 10 Cr 10 systems. Within Fe-Mn-based alloys, we show that the martensitic transformation and chemical short-range order directly correlate with the face-centered-cubic and hexagonal-close-packed energy difference and stacking-fault energies, which are in quantitative agreement with recent observation of two phase region (face-centered cubic and hexagonal closed pack) in a polycrystalline high-entropy alloy sample at x = 40 at.%. Our predictions are further confirmed by single-crystal measurements on a x = 40 at.% using transmission-electron microscopy, selective-area diffraction, and electron-backscattered-diffraction mapping. The results herein offer an understanding of transformation-induced or twinning-induced plasticity in this class of high-entropy alloys and a design guide for controlling the physics at the electronic level.
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
Microstructural, Oxidation, and Mechanical Behavior of NbTi-Based Refractory Alloys with 5 to 10 Pct Co, Cr, and Ni Additions
NbTi-based refractory alloys with additions of Co, Cr, and Ni represent an interesting medium-entropy alloy system with potential for protective oxide film formation, high strength, and ductility. This study investigates the microstructural evolution, oxidation behavior, and mechanical properties of NbTi-based alloys containing 5 to 10 at. pct Co, Cr, and Ni. CALPHAD predictions suggest that this composition range can be heat treated to obtain a predominantly body-centered cubic matrix phase. Mechanical properties, including microhardness, yield strength, maximum strength, and specific strength are evaluated through isothermal compression tests conducted between room temperature and 800 °C. The oxidation kinetics of these alloys are assessed through discontinuous oxidation tests. Parabolic oxidation kinetics were observed for NbTi–10Ni and NbTi–5Co, while linear oxidation kinetics were found for NbTi–10Cr and NbTi–10(CoCrNi). Microstructures and oxide layers are characterized using X-ray diffraction, electron backscatter diffraction, energy-dispersive X-ray spectroscopy, and scanning electron microscopy. All alloys exhibit significant mechanical softening between room temperature and 800 °C, with elastic-perfectly plastic flow observed at 800 °C. The addition of 10 pct Cr to NbTi resulted in two BCC phases up to 1050 °C, conflicting with CALPHAD predictions of a single-phase solid solution at this temperature, and resulting in higher flow stress at 800 °C. NbTi–10(CoCrNi) exhibited the lowest flow stress at 800 °C despite having more ‘cocktail effect’ potential and insufficient molar fractions of Co, Cr, or Ni to form a desirable protective oxide film.
36 MATERIALS SCIENCE↗
Medium-Entropy Engineering of Magnetism in Layered Antiferromagnet Cu x Ni 2(1- x ) Cr x P 2 S 6
Antiferromagnetic van der Waals-type M 2 P 2 X 6 compounds provide a versatile material platform for studying 2D magnetism and relevant phenomena. Establishing ferromagnetism in 2D materials is technologically valuable. Though magnetism is generally tunable via a chemical way, it is challenging to induce ferromagnetism with isovalent chalcogen and bimetallic substitutions in M 2 P 2 X 6 . Here, we report co-substitution of Cu 1+ and Cr 3+ for Ni 2+ in Ni 2 P 2 S 6 , creating Cu x Ni 2(1-x) Cr x P 2 S 6 medium-entropy alloys spanning a full substitution range (x = 0 to 1). Such substitution strategy leads to a unique evolution in crystal structure and magnetic phases that are distinct from traditional isovalent bimetallic doping, with Cu and Cr co-substitution enhancing ferromagnetic correlations and generating a weak ferromagnetic phase in intermediate compositions. This aliovalent substitution strategy offers a universal approach for tuning layered magnetism in antiferromagnetic systems, which along with the potential for light-matter interaction and high-temperature ferroelectricity, can enable multifunctional device applications.
2D magnetism↗
A theoretical study of solid solution strengthening in the refractory medium entropy alloy Nb 45 Ta 25 Ti 15 Hf 15
The refractory medium-entropy alloy (RMEA) Nb 45 Ta 25 Ti 15 Hf 15 exhibits exceptional tensile ductility and fracture toughness at ambient temperature, but its engineering applications are limited by a lack of high temperature strength. Using a machine-learning interatomic potential (MLIP) with near-density functional theory (DFT) accuracy, we conducted molecular dynamics (MD) and statics simulations of the behavior of dislocations with both screw and edge characters. We also analyze experimentally measured yield strengths using the Rao-Suzuki model and the Maresca-Curtin model modified to include a temperature-dependent shear modulus and a bulk modulus-dependent misfit volume, thereby uncovering the mechanisms underlying the yielding of this RMEA. Compared with the published experimental yield strength, the models parameterized by the MLIP effectively reproduce the experimental results over a wide temperature range. The models and MD simulations indicate that yielding is governed by screw dislocations, with dipole dragging as the dominant mechanism. In MD simulations, we observed a potential softening mechanism not considered by the Rao-Suzuki screw model: slow migration of interstitial jogs along the dislocation core, which could lead to the annihilation of vacancy and interstitial jog pairs by their combination.
BCC complex concentrated alloys↗
Neural-network model for force prediction in multi-principal-element alloys
Atomistic simulations can provide useful insights into the physical properties of multi-principal-element alloys. However, classical potentials mostly fail to capture key quantum (electronic-structure) effects. Here we present a deep 3D convolutional neural network (3D CNN) based framework combined with a voxelization technique to design interatomic potentials for chemically complex alloys. We highlight the performance of the 3D CNN model and its efficacy in computing potentials using the medium-entropy alloy TaNbMo. In order to provide insights into the effect of voxel resolution, we implemented two approaches based on the inner and outer bounding boxes. An efficient 3D CNN model, which is as accurate as the density-functional theory (DFT) approach, for calculating potentials will provide a promising schema for accurate atomistic simulations of structure and dynamics of general multi-principle element alloys.
36 MATERIALS SCIENCE↗
Quantifying the atomic neighbourhoods in complex concentrated alloys
Here is presented that atom probe tomography unlocks the potential to precisely analyse the short-range ordering in a CoCrNi medium-entropy alloy.
36 MATERIALS SCIENCE↗
Deciphering the multiple deformation mechanisms responsible for sustained work hardening in a FeCrCoNi medium entropy alloy
Two important and desirable properties of materials for most structural applications are high tensile strength and ductility, which typically require high work hardening to delay necking. Here, in this work, we designed and tensile tested a face-centered cubic (fcc) Fe-Cr-Co-Ni medium-entropy alloy in which multiple deformation mechanisms are triggered during tensile loading at different temperatures to induce sustained work hardening. Our strategy involved control of the relative stabilities of the fcc, hcp (hexagonal close-packed), and bcc (body-centered cubic) phases in this quaternary system via high-throughput thermodynamic calculations. This alloy not only exhibits extensive deformation-induced nanotwinning at room temperature, but also displays a two-step sequential phase transformation [γ (fcc) → ε (hcp) martensite → α’ (bcc) martensite] at 77 K, which contrasts with the single-step phase transformation [γ → ε martensite] observed in many other fcc high/medium entropy alloys with a low stacking fault energy. The sequence of phase transformation at 77K was supported by first-principles density functional theory calculations. This work provides new templates for the design of alloys capable of multiple deformation mechanisms for sustained work hardening.
36 MATERIALS SCIENCE↗
Tensile and compressive plastic deformation behavior of medium-entropy Cr-Co-Ni single crystals from cryogenic to elevated temperatures
The equiatomic Cr-Co-Ni medium-entropy alloy has the face-centered cubic (FCC) structure. Bulk single crystals of this alloy were grown and tested in tension and compression between 14 K and 1373 K with the loading axis parallel to [23]. At room temperature, the critical resolved shear stress (CRSS) for {111}<10> slip is 65 ± 5 MPa and does not exhibit a tension-compression asymmetry. It does, however, increase significantly as the test temperature decreases. A dulling of this temperature dependence occurs below 50 K, which may be due to the inertia effect. When the measured values above 50 K are extrapolated to lower temperatures, a value of 225 MPa is estimated for the CRSS at 0 K. This is larger than that (168 MPa) previously determined for the equiatomic Cr-Mn-Fe-Co-Ni high-entropy alloy using a similar procedure. The stacking fault energy of the present Cr-Co-Ni is estimated to be about 14 mJm-2, which is sufficiently low to account for deformation twinning both at 77 K and room temperature. Twinning at 77 K occurs on conjugate (1) planes at an onset shear stress of 482 MPa after primary slip and propagates in the form of Lüders deformation. At room temperature, twinning occurs uniformly throughout the gauge section on primary (111) planes at an onset shear stress of 381 MPa after primary and subsequent conjugate slip. Thin layers with the hexagonal close-packed stacking are observed in association with twinning both at 77 K and room temperature.
36 MATERIALS SCIENCE↗
Solid state welding of medium-entropy CrCoNi with heterogeneous, partially recrystallized microstructures
We report that heterogeneous, partially recrystallized (PRX) microstructures have recently been used to improve strength-ductility combinations in high-entropy alloys. However, these microstructures are incompatible with conventional joining processes that require melting or prolonged exposure to elevated temperatures. This work presents an initial exploration of solid state joining in this challenging condition using vaporizing foil actuator welding (VFAW) applied to PRX equiatomic alloy CrCoNi.
36 MATERIALS SCIENCE↗
Guided Design of Alloys, Strengthened via Precipitation
Using theoretical and computational guidance, we are designing stronger middle and high-entropy alloys and superalloys for the airspace applications. We focus on improving mechanical properties of materials at cryogenic and elevated temperatures. Here we discuss basic science and fundamental theory that are being used for guided design of next-generation alloys. As examples, we consider the medium-entropy NiCoCr alloy and precipitated superalloys with a local phase transformation strengthening. This research is funded by NASA’s Aeronautics Research Mission Directorate (ARMD) via Transformational Tools and Technologies (TTT) Project.
Alloys↗
Development of interatomic potential and effect of ordering on defect properties in CrMnV
Developing materials that can withstand extreme environments, such as high radiation doses and elevated temperatures, is crucial for next-generation particle accelerators, including the 2.4 MW Long-Baseline Neutrino Facility. High-Entropy Alloys have emerged as promising candidates for beam window materials due to their superior mechanical strength, corrosion resistance, and radiation tolerance. In this study, we focus on the Cr–Mn–V alloy system, developing and employing machine-learning interatomic potentials (MLIPs) to investigate the formation of an ordered phase and its influence on defect properties. Using hybrid Monte Carlo-Molecular Dynamics simulations, we observe the formation of a B2-ordered phase at lower temperatures, consistent with Density Functional Theory (DFT) predictions. Ordered structures display a bimodal distribution of migration energies and reduced mean square displacement values, indicating suppressed vacancy diffusion. Our results also show that the migration energy barrier varies based on the atomic species, with Mn and V exhibiting the highest and lowest average barriers, respectively. These findings suggest that atomic ordering inhibits defect mobility, potentially enhancing the radiation resistance of CrMnV alloys. The validated MLIP provides a reliable framework for simulations that are faster than traditional DFT while maintaining the accuracy required to study defect and ordering properties.
36 MATERIALS SCIENCE↗
Additive manufacturing of an ultrastrong, deformable Al alloy with nanoscale intermetallics
Abstract Light-weight, high-strength, aluminum (Al) alloys have widespread industrial applications. However, most commercially available high-strength Al alloys, like AA 7075, are not suitable for additive manufacturing due to their high susceptibility to solidification cracking. In this work, a custom Al alloy Al 92 Ti 2 Fe 2 Co 2 Ni 2 is fabricated by selective laser melting. Heterogeneous nanoscale medium-entropy intermetallic lamella form in the as-printed Al alloy. Macroscale compression tests reveal a combination of high strength, over 700 MPa, and prominent plastic deformability. Micropillar compression tests display significant back stress in all regions, and certain regions have flow stresses exceeding 900 MPa. Post-deformation analyses reveal that, in addition to abundant dislocation activities in Al matrix, complex dislocation structures and stacking faults form in monoclinic Al 9 Co 2 type brittle intermetallics. This study shows that proper introduction of heterogeneous microstructures and nanoscale medium entropy intermetallics offer an alternative solution to the design of ultrastrong, deformable Al alloys via additive manufacturing.
Science & Technology - Other Topics↗