In situ investigation of high-pressure hydrogen-induced swelling in elastomers and its correlation with material properties

The resistance of elastomeric materials to high-pressure hydrogen-induced damage is essential for ensuring the reliability of hydrogen infrastructure. Here, in this study, we systematically investigated the swelling behavior and hydrogen transport properties of four elastomer types – EPDM, NBR, FKM, and HNBR – using a custom in-situ view cell system capable of real-time monitoring during decompression from pressures up to 96.5 MPa. Each elastomer was formulated with and without fillers and plasticizers to assess the effects of formulation on swelling response. Thermal desorption analysis (TDA) was employed to determine equilibrium hydrogen content and diffusion coefficients, providing insight into gas uptake and mobility within each material. Correlation analyses using Pearson and Spearman coefficients revealed that the diffusion coefficient showed a stronger relationship with swelling behavior than hydrogen content, highlighting the dominant role of hydrogen mobility. Filled elastomers, particularly those with carbon black, consistently showed reduced swelling due to enhanced stiffness and reduced diffusivity. These results deepen our understanding of diffuso-mechanical interactions in elastomers and support the rational design of sealing materials for high-pressure hydrogen systems.

EPDM↗
DOE OSTI2022

Interfacial Effects on the Dielectric Properties of Elastomer Composites and Nanocomposites

Elastomer-based composites and nanocomposites are discussed, with the emphasis on the filler and interfacial effects on their dynamics, and the resulting manifestation in their macroscopic dielectric or mechanical response. Specifically, selected polydimethylsiloxane (PDMS)/barium-titanate and styrene-butadiene rubber (SBR)/graphene oxide nanocomposites are discussed, as examples where controlled spatial distribution of filler (structured composites) gives rise to significantly different dielectric and thermomechanical behaviors. Also, ethylene–propylene–diene (EPDM)/carbon black (CB) composites are presented, as examples of systems that exhibit an abnormal temperature dependence of dielectric relaxation; and this response is discussed in the context of CB cluster polarization and quantified through a simple scaling model of the same. Finally, multi-filler EPDM/CB/ceramic elastomer nanocomposites are discussed, as examples of systems with antagonistic interfacial effects between conductive and dielectric fillers, as well as with strong interphase responses that can overwhelm the dielectric contributions from the fillers; in these systems, interphasial responses result in counter-intuitive dielectric behaviors and in strong deviations from standard design principles typically employed in the design of dielectric composite systems.

Li, Bo↗
DOE OSTI2022

Coupled diffusion-deformation-damage model for polymers used in hydrogen infrastructure

The soft materials used in the infrastructure of hydrogen storage and distribution systems are vulnerable because exposure to high-pressure hydrogen can lead to mechanical damage and property degradation. Some materials, such as polymers, can undergo mechanical failure due to a phenomenon wherein hydrogen gas diffuses through the polymer chains and occupies preexisting cavities or voids inside the polymer material. If the hydrogen gas pressure is reduced more quickly than hydrogen can diffuse back out of the polymer which is necessary for some applications, the trapped hydrogen gas instead escapes by rupturing the material, causing surface blistering or permanent damage. In this study, a continuum mechanics-based fully coupled diffusion-deformation model with damage is developed to predict the stress distribution and damage propagation while the polymer undergoes rapid decompression failure. The hyperelastic material model, along with the maximum principal strain failure theory, was chosen for this study as it represents the nonlinear material response with brittle failure observed in uniaxial tensile tests perfectly. EPDM polymer was chosen for this study because of its commercial availability and common use in hydrogen storage and distribution system. It has superior mechanical properties, high and low temperature resistance, and certain compounds work well in hydrogen gas. This work is useful for design engineers to alter the parameters while manufacturing polymer composites to increase their performance in a high-pressure hydrogen environment.

Kulkarni, Shank S.↗
DOE OSTI2023

Investigation of desorption of hydrogen gas from polymer matrix using thermal desorption analysis and finite element modeling

Polymer materials are used widely as sealing materials and liners in hydrogen storage and transportation infrastructure. During operating conditions, polymers are exposed to high pressure hydrogen gas periodically. When in contact, the hydrogen gas diffuses through the polymer material with ease due to its smaller sized molecules compared to the polymer molecules. In the event of rapid decompression of outside hydrogen gas, the hydrogen molecules within the polymer diffuse out. This process is known as the desorption of polymer and can cause blisters or cracking causing permanent damage to the polymer. Here, we used a combined experimental and modeling approach to investigate the desorption of the hydrogen gas in the polymer. Thermal desorption analysis (TDA) experiments were performed on the polymer sample exposed to the high-pressure hydrogen gas to measure the diffusion coefficient and equilibrium hydrogen concentration. Experiments also provided the quantity of hydrogen within the polymer during the desorption process which followed Fick’s law. However, for higher pressurization values, some anomaly was observed in the quantity of hydrogen remaining in the polymer sample. A continuum mechanics based coupled diffusion–deformation-damage model was deployed to simulate the gas desorption process in the material using the finite element method to understand its effect on the material. It was found that the anomaly in TDA results were due to the blister formation on the polymer surface which resulted in longer hydrogen retention. Simulations also showed that blister formation can be affected by multiple parameters such as the addition of filler particles, and pre-existing cavity size.

36 MATERIALS SCIENCE↗