Through-thickness fracture behavior of neutron-irradiated nuclear graphite NBG-17 Using X-ray micro-CT
Achieving precise control over crack propagation in nuclear graphite and conducting quantitative analysis remain challenging. In this study, the through-thickness fracture behavior of pristine and neutron-irradiated (700 °C, ∼7 dpa) NBG-17 nuclear graphite was investigated using split-disc testing coupled with micro-computed tomography (micro-CT). A notably lower number of micropores was observed in the neutron-irradiated specimen. The fracture toughness of neutron-irradiated NBG-17 was measured to be 1.45 MPa√m, compared to 1.17 ± 0.05 MPa√m for the pristine specimen. In both materials, cracks were found to initiate at the filler–binder interface, and often correlated with microstructural features such as pores and thermal cracks. Crack bridging and deflections emerged as the primary toughening mechanisms in both unirradiated and irradiated NBG-17. However, compared with the pristine specimen, the cracks in the neutron-irradiated specimen were more likely to grow trans granularly, resulting in less deflected crack paths. The reduced micro-porosity and strengthened filler–binder boundaries were considered to be the cause of the observed differences in crack morphologies. In conclusion, this study provides a qualitative analysis of the fracture behavior of neutron-irradiated nuclear graphite in the absence of radiolytic oxidation.
Sulphate resistance of low‐clinker engineered cementitious composites examined by MicroXRF imaging
Abstract Engineered cementitious composites (ECC) are a class of high‐performing fibre‐reinforced cementitious materials recognised for their increased ductility and durability compared to conventional cement‐based materials, owing to their autogenously controlled tight crack widths, even when subjected to high strains. To reduce ECC's environmental impact, this research examines the use of a low‐clinker binder − limestone‐calcined clay cement (LC3) − as an alternative to portland cement (PC), along with fly ash to further reduce the clinker proportion and the embodied CO 2 of the formulations. In conventional concrete, LC3 hydrates to a denser microstructure resulting from the synergistic reaction between limestone and calcined clay. At the lower water contents typical of ECC and with the presence of fly ash, the influence of the binder composition on the microstructure is difficult to anticipate. To examine the influence of these compositional variables on microstructure, permeability and durability, the sulphate resistance of LC3‐based ECC is explored. Specifically, the ECC‐LC3 blends are designed with high clinker replacement rate of 75% by mass of binder and contain either conventional fly ash or reclaimed fly ash at 50% by mass of binder. Expansion of ECC‐LC3 samples subjected to standard sodium sulphate test conditions was measured up to 12 months and the depth of penetration of sulphates into the ECC‐LC3 of varying compositions was quantified using micro‐X‐Ray Fluorescence (microXRF) imaging and modelling. The expansion results show that the ECC‐LC3 formulations performed better than the PC samples and can provide adequate resistance to external sulphate attack, even when reclaimed fly ashes are used in place of the conventional ash. In addition, the shallow penetration of sulphate into these cementitious composites demonstrates the low diffusion coefficients values that were determined using the quantitative data from MicroXRF imaging.
Effect of Engineered Cracks in Catalyst Layers on PEMFC Catalyst Layer Durability
Proton exchange membrane fuel cells (PEMFCs) are expected to play a pivotal role in decarbonizing the transportation sector, and particularly heavy-duty vehicles (HDVs). However, improvements in durability are needed for PEMFCs to compete with state-of-the-art power sources for HDVs. Here, we examine how catalyst layer (CL) cracks that are engineered affect the CL durability by using patterned silicon templates to control the CL crack density at the micrometer scale. Electrochemical analyses show that the initial PEMFC performance is relatively unaffected by crack density, but the performance after durability testing was strongly affected. Specifically, CLs with high crack density showed higher performance relative to CLs without cracks after application of a carbon corrosion accelerated stress test. Electrochemical analyses coupled with X-ray computed tomography and scanning transmission electron microscopy with energy dispersive X-ray spectroscopy showed that the cracks provide shorter oxygen diffusion pathways to reaction sites, leading to decreased oxygen transport resistance. Additionally, we observed that the catalyst durability is unaffected by cracks. Our results provide a mechanistic explanation of the role of cracks in CL durability.
Intermediate Principal Stress Effects on the 3D Cracking Behavior of Flawed Rocks Under True Triaxial Compression
Crack initiation, growth, and coalescence in flawed rocks have been extensively studied for 2D (planar, penetrating) flaws under uniaxial/biaxial compression. However, little is known as to the mechanisms and processes of cracking from 3D flaws under true triaxial compression, where the intermediate principal stress (σ 2 ) is distinguished from the major and minor principal stresses. In this work, we systematically investigate the effects of σ 2 on the 3D cracking behavior of rock specimens with preexisting flaws, through the use of mechanistic simulations of mixed-mode fracture in rocks. We explore how two characteristics of σ 2 , namely, (i) its orientation with respect to the flaw and (ii) its magnitude, affect two aspects of the cracking behavior, namely, (i) the cracking pattern and (ii) the peak stress. Results show that the orientation of σ 2 exerts more control over the cracking pattern than the flaw inclination angle. The peak stress becomes highest when σ 1 is parallel to the flaw, whereas it becomes lowest when σ 2 is parallel to the flaw. Also, the effects of σ 2 magnitude are more significant when σ 2 becomes more oblique to the flaw plane. On the basis of our observations, we propose mechanisms underlying the cracking behavior of 3D flawed rocks under true triaxial compression.
Atomic force microscopy monitoring of subcritical slow crack growth in soda lime silicate glass
Prediction of brittle fracture in silicate glasses requires a fundamental understanding of slow crack growth rates, far below the critical stress intensity (K IC ) of the material. Here, in this study, atomic force microscopy (AFM) was used to characterize slow crack propagation in soda lime silicate glasses. Using large-sample AFM systems with specialized tips and scanners, fractures less than 20 nm wide were measured as a function of relative humidity (RH). The results were found to be sensitive to the type of AFM tip used and to the dryness of the surface. Continuous scanning and image capture over several days allowed the determination of the crack tip velocity. The dependance of crack tip velocity on RH was measured by enclosing the sample and AFM head in a humidity-controlled chamber. The crack tip velocity was measured as low 4.0×10 -12 m/s at 15 % RH and as high as 3.7×10 -10 m/s at 40 % RH. Overall crack growth was smooth during the AFM scan. Additionally, recession of the crack tip was noted as the sample dried, indicating crack tip closure may be occurring. Further studies on alternative compositions will provide details on subcritical fracture processes in a range of different environmental conditions.
Nanomechanical investigation of the interplay between pore morphology and crack orientation of amorphous silica
Porous amorphous silica (a-SiO 2 ) is of both fundamental and practical interests, as they exhibit a large specific surface area and tunable porous network. However, the brittle nature of a-SiO 2 and the presence of pre-existing cracks at both micro- and nano-scales lead to complex mechanical behavior. Here, we systematically investigate the effects of pre-existing crack and its orientation on the mechanical properties of a-SiO 2 with varying pore shapes using reactive molecular dynamics simulations. We demonstrate that pore shape will primarily influence the Young’s modulus (E) and critical energy release rate (G IC ). We further investigate the impact of pore shape and crack orientation by local characterization of the structural parameters. By defining the high stress and inter-mediate regions, the overall mechanical properties are found to be greatly influenced by the pore shape which can be reflected through the spatial distribution of von Mises stress. Overall, G IC is found to increase with the increase of ligament length (also known as pore wall thickness). Meanwhile, the effect of the pre-existing crack on the crack propagation process is confirmed by analyzing the density distribution evolution. These results highlight the interplay between pore morphology and crack orientation in controlling the fracture behaviors in brittle porous materials.
Enhanced composites via selective interfacial modification
A laminate comprising a first ply, a second ply, and a third ply which sandwiching the second ply between the first ply and the third ply. The laminate further includes a first plurality of interfacial modifiers arranged between opposing faces of the first ply and the second ply. The first plurality of interfacial modifiers are arranged in a first pattern. The laminate includes a second plurality of interfacial modifiers arranged between opposing faces of the second ply and the third ply such that the first plurality of interfacial modifiers and the second plurality of interfacial modifiers are arranged on opposite faces of the second ply. The second plurality of interfacial modifiers are arranged in a second pattern. The first pattern and the second pattern are configured to increase crack growth resistance of the laminate by selectively toughening portions of the laminate to control propagation of interfacial cracks within the laminate.
Repairing High γ’ Hot Section Gas Turbine Components Using Advanced Manufacturing
This article describes the ability to use laser-blown powder deposition to repair high γ' IN-100 superalloy gas turbine components. The influence of various process conditions on the ability to make crack-free IN-100 deposits over surrogate high γ' alloys was investigated to identify cracking mechanisms in the deposit and heat-affected zones (HAZs). The various crack formation mechanisms, such as solidification cracking and liquation cracking, were evaluated using multiscale characterization and numerical simulation. The cracking in the deposit region was predominantly solidification cracking, while those observed in the HAZ were liquation cracking. The results showed that controlling thermally induced residual stresses is the key to eliminating cracking, and the optimum preheat temperature was determined. In conclusion, the results were then contrasted with those in published literature and an approach to effectively repair hot section parts was presented.
Impact of polymer additives on crack mitigation of rod-coated fuel cell cathode catalyst layers
Cracks in catalyst layers (CLs) are a potential source of long-term failure in a fuel cell membrane electrode assembly (MEA). While modifications to the CL ink formulation can affect the degree of cracking, these changes may lead to lower initial performance than their cracked analogues due to the established link between formulation and performance. In this work, we explored the use of polymeric additives to mitigate CL cracks. Small quantities of poly (acrylic acid), poly (ethylene oxide), poly (methyl methacrylate), or poly (vinyl alcohol) - 5 wt% relative to ionomer mass - were added to the ink prior to its final mixing. Poly (vinyl alcohol) resulted in crack-free CLs, whereas the other polymers resulted in CLs with similar crack percentages as the control CL. Through a combination of transmission electron microscopy, X-ray computed tomography, and infrared spectroscopy, we ascribed the crack-mitigating mechanism of poly (vinyl alcohol) to its ability to hydrogen-bond with Nafion, the ion conducting polymer binder in the catalyst ink. Initial performance of this non-cracked electrode exhibited nearly identical electrochemical behavior to its cracked counterpart, demonstrating that PVA additives successfully reduce cracks while maintaining cell initial performance.
Kink bands promote exceptional fracture resistance in a NbTaTiHf refractory medium-entropy alloy
Single-phase body-centered cubic (bcc) refractory medium- or high-entropy alloys can retain compressive strength at elevated temperatures but suffer from extremely low tensile ductility and fracture toughness. We examined the strength and fracture toughness of a bcc refractory alloy, NbTaTiHf, from 77 to 1473 kelvin. This alloy’s behavior differed from that of comparable systems by having fracture toughness over 253 MPa·m 1/2 , which we attribute to a dynamic competition between screw and edge dislocations in controlling the plasticity at a crack tip. Whereas the glide and intersection of screw and mixed dislocations promotes strain hardening controlling uniform deformation, the coordinated slip of <111> edge dislocations with {110} and {112} glide planes prolongs nonuniform strain through formation of kink bands. These bands suppress strain hardening by reorienting microscale bands of the crystal along directions of higher resolved shear stress and continually nucleate to accommodate localized strain and distribute damage away from a crack tip.
Multiscale modeling of hydrogenolysis of ethane and propane on Ru(0001): Implications for plastics recycling
Plastic waste presents an environmental threat. Chemical recycling via hydrogenolysis can convert plastic waste into waxes, lubricants, and fuels. Among catalysts, Ru stands out for its superior activity and selectivity. The chemistry of light alkane hydrogenolysis can help understanding plastics deconstruction. Here, we perform first-principles calculations, develop descriptor-based relations, and conduct microkinetic modeling and analysis on ethane and propane. Predictions are in excellent agreement with experimental data. We identify a similar cracking pattern for both hydrocarbons entailing a deeply dehydrogenated species with the removal of four hydrogen atoms: CHCH*+* → 2CH* for ethane and CH 3 CCH*+2* → CH 3 C* + CH* for propane. We find that the rate-determining step is the C-C cracking for ethane and the first dehydrogenation from the terminal carbon (CH 3 CH 2 CH 3 *+* → CH 3 CH 2 CH 2 *+H*) for propane. The vinyl species CH 2 CH* produced from propane cracking is responsible for whether a single or multiple cracking events occur and effectively controls the selectivity. Specifically, ethane formation in propane hydrogenolysis is suppressed at elevated temperatures due to over-cracking via multiple (two here) cracking events being preferred over hydrogenation and desorption of ethane from the catalyst. Our workflow and models provide a baseline for future studies on heavier hydrocarbons. Insights into recent experimental studies of polyethylene over Ru-based catalysts are discussed.
Crack Catcher AI – Enabling smart fracture mechanics approaches for damage control of thin silicon cells or wafers
Not Available
AdditiveFOAM: A Continuum Multiphysics Code for Additive Manufacturing
AdditiveFOAM is a computational framework that simulates transport phenomena in Additive Manufacturing (AM) processes. It is built on OpenFOAM (Weller et al., 1998), the leading free, open-source software package for computational fluid dynamics (CFD). OpenFOAM offers an extensible platform for solving complex multiphysics problems using state-of-the-art finite volume methods. AdditiveFOAM leverages these capabilities to develop specialized tools aimed at addressing challenges in AM processing. Metal additive manufacturing, also known as metal 3D printing, is an advanced manufacturing technique that creates physical parts from a three-dimensional (3D) digital model by melting metal powder or wire feedstock. A significant area of research in metal AM focuses on process planning to mitigate anomalous features during printing that are deleterious to part performance (e.g., porosity and cracking), as well as controlling localized microstructure and material properties. Given the high costs and substantial time requirements associated with experimental methods for qualifying new materials and processes, there is a compelling incentive for researchers to utilize advanced computational simulations. In this context, AdditiveFOAM offers a simulation framework to better understand undesirable features in printing, thereby enhancing process planning and reducing the reliance on labor-intensive experimental campaigns.
Chloride and Hydride Transfer as Keys to Catalytic Upcycling of Polyethylene into Liquid Alkanes
Abstract Transforming polyolefin waste into liquid alkanes through tandem cracking‐alkylation reactions catalyzed by Lewis‐acid chlorides offers an efficient route for single‐step plastic upcycling. Lewis acids in dichloromethane establish a polar environment that stabilizes carbenium ion intermediates and catalyzes hydride transfer, enabling breaking of polyethylene C−C bonds and forming C−C bonds in alkylation. Here, we show that efficient and selective deconstruction of low‐density polyethylene (LDPE) to liquid alkanes is achieved with anhydrous aluminum chloride (AlCl 3 ) and gallium chloride (GaCl 3 ). Already at 60 °C, complete LDPE conversion was achieved, while maintaining the selectivity for gasoline‐range liquid alkanes over 70 %. AlCl 3 showed an exceptional conversion rate of 5000 , surpassing other Lewis acid catalysts by two orders of magnitude. Through kinetic and mechanistic studies, we show that the rates of LDPE conversion do not correlate directly with the intrinsic strength of the Lewis acids or steric constraints that may limit the polymer to access the Lewis acid sites. Instead, the rates for the tandem processes of cracking and alkylation are primarily governed by the rates of initiation of carbenium ions and the subsequent intermolecular hydride transfer. Both jointly control the relative rates of cracking and alkylation, thereby determining the overall conversion and selectivity.
Chloride and Hydride Transfer as Keys to Catalytic Upcycling of Polyethylene into Liquid Alkanes
Abstract Transforming polyolefin waste into liquid alkanes through tandem cracking‐alkylation reactions catalyzed by Lewis‐acid chlorides offers an efficient route for single‐step plastic upcycling. Lewis acids in dichloromethane establish a polar environment that stabilizes carbenium ion intermediates and catalyzes hydride transfer, enabling breaking of polyethylene C−C bonds and forming C−C bonds in alkylation. Here, we show that efficient and selective deconstruction of low‐density polyethylene (LDPE) to liquid alkanes is achieved with anhydrous aluminum chloride (AlCl 3 ) and gallium chloride (GaCl 3 ). Already at 60 °C, complete LDPE conversion was achieved, while maintaining the selectivity for gasoline‐range liquid alkanes over 70 %. AlCl 3 showed an exceptional conversion rate of 5000 , surpassing other Lewis acid catalysts by two orders of magnitude. Through kinetic and mechanistic studies, we show that the rates of LDPE conversion do not correlate directly with the intrinsic strength of the Lewis acids or steric constraints that may limit the polymer to access the Lewis acid sites. Instead, the rates for the tandem processes of cracking and alkylation are primarily governed by the rates of initiation of carbenium ions and the subsequent intermolecular hydride transfer. Both jointly control the relative rates of cracking and alkylation, thereby determining the overall conversion and selectivity.
FY23 Simulation of Elastic-Plastic Failure Propagation
This memo summarizes the simulation of ductile failure propagation work conducted under the ASC project “V&V of Ductile Failure” conducted during FY 23. Physically, the failure propagation consists of crack propagation in the material. In the numerical setting—specifically in a finite element model—propagation can be accomplished through element death when critical conditions occur locally at an element that is then deleted from the simulation. The validation of the finite element models is evaluated by direct comparison between the experimental and simulation results regarding the rate of crack growth and its influence on the load-deflection response of the specimens tested. This work considers two geometries that display stable crack propagation under displacement-controlled conditions. The first geometry consists of hat specimens loaded in compression with nominally identical geometries but made with three different materials: Steel A286, Al 7075-T651 and 304L stainless steel. The three materials represent a range of ductility values that affect the response and crack propagation within the specimen. The crack induced propagates under an essentially mode-II type of deformation. The second geometry consists of a pre-cracked 304L stainless steel compact tension test specimen loaded so as to induce a mode-I deformation at the crack.
Unified cohesive zone model (UCZM) for fracturing and fragmenting solids
Here, a Unified Cohesive Zone Model (UCZM), which inherits most of the advantages while overcoming the shortcomings of existing Cohesive Zone Models (CZMs), is proposed. Similar to the traditional extrinsic CZM approach, UCZM dynamically inserts the cohesive elements into the system based on local material states (e.g., stress, strain). However, the transition from continua to discontinua is smoothly achieved, thereby eliminating the “time-discontinuous” issue seen in the extrinsic CZM. Moreover, within the novel UCZM framework, the point of transition from continua to discontinua is controllable through the introduction of crack initialization criteria. As a result, the UCZM allows any material models (e.g., elastic, plastic, damage models) for continuum solids and for discrete fracture behavior to work together. In essence, both an enhanced extrinsic cohesive zone model and an intrinsic cohesive zone model can be represented by the proposed unified model. The proposed UCZM has been verified through different numerical examples. The work demonstrates that the UCZM is a highly effective approach for modeling fracture and fragmentation processes in solids.