NASA NTRS1994

The effects of embedded internal delaminations on composite laminate compression strength; an experimental review

Delaminations in laminated composite materials can degrade the compressive strength of these materials. Delaminations can form as a result of impact damage or processing flaws. In order to better understand the effects of these delaminations on the compressive behavior of laminated composite plates, programs have been conducted to assess the criticality of prescribed delaminations of known size, shape, and location on the compression strength of laminated composites. A review of these programs is presented along with highlights of pertinent findings from each.

Nettles, Alan T.↗
NASA NTRS1976

Effect of Low Velocity Impact Damage on the Compressive Strength of Graphite/Epoxy Hat-Stiffened Panels

Low velocity impact damage on the compressive strength of graphite/epoxy hat stiffened panels is studied. Fourteen panels, representative of minimum-mass designs for two compression load levels were tested. Eight panels were damaged by impact and the effect on compressive strength was evaluated by comparing the results with data for undamaged panels. The impact tests consisted of firing 1.27 cm diameter aluminum projectiles normal to the plane of the panel at a velocity of approximately 55 m/sec to simulate impact from runway debris. The results of this investigation indicate that impact damage in the panels designed for 0.53 MN/m was contained locally and the damaged panels were capable of carrying the design load. The panels designed for 1.58 MN/m failed between 50 and 58 percent of the design load due to impact damage in the high axial stiffness region. The extent of damage in the high axial stiffness region of both panel designs increased with the magnitude of applied axial load. Damage in this region was the most significant factor in reducing panel strength. Limited damage that was not visually detectable reduced ultimate strength as much as extensive visible damage.

Rhodes, M. D.↗
NASA NTRS1979

Effect of impact damage and holes on the compressive strength of a graphite/epoxy laminate

An experimental investigation has been conducted to determine the effect of low-velocity impact damage and unloaded circular holes on the compressive strength of a 48-ply orthotropic graphite/epoxy flat laminate. Specimens were impacted by a 1.27-cm-diameter aluminum sphere with speeds from 52 to 101 m/x to simulate momenta typical of low-velocity impact hazards that can occur in commercial aircraft service. It is shown that low-velocity impact damage can significantly degrade the static compressive strength of the laminate. Specimens that fail at axial strains above 0.008 in the undamaged condition can fail at strains as low as 0.0031 when impacted at 100 m/s. Circular holes also reduce the static compressive strength of the laminate. The failure strain decreases as the hole diameter increases.

Starnes, J. H., Jr.↗
NASA NTRS1992

Post impact compressive strength in composites

Presented in this paper are the plan, equipment, procedures, and findings of an experimental investigation of the tolerance to low velocity impact of a graphite epoxy (AS4/3501-6) and graphite bismaleimide (M6/CYCOM3100) advanced composites. The applied impacts were governed by the Air Force Guide Specification 87221. Specimens of each material system having a common nominal layup (10% 0 deg; 80% +/-45 deg; 10% 90 deg), a common 7 inch (17.78 cm) by 10 inch (25.40 cm) size, five different thicknesses (9, 26, 48, 74, and 96 plies), and ambient moisture content were impacted and strength tested at room temperature. Damaged areas and post impact compression strengths (PICS) were among the most significant findings obtained. While the undamaged per ply compression strength of both materials is a strong function of laminate thickness, the per ply PICS is not. The average difference in per ply PICS between the two material systems is about seven percent. Although a smaller percentage of the applied kinetic energy was absorbed by the Gr/BMI than by the Gr/Epoxy composites, larger damaged areas were produced in the Gr/BMI than in Gr/Epoxy. Within the limitations of this investigation, the Gr/BMI system seems to offer no advantage in damage tolerance over the Gr/Epoxy system examined.

Demuts, Edvins↗
NASA NTRS1933

Comparison of Three Methods for Calculating the Compressive Strength of Flat and Slightly Curved Sheet and Stiffener Combinations

This report gives a comparison of the accuracy of the three methods for calculating the compressive strength of flat sheet and stiffener combinations such as occur in stressed-skin or monocoque structures for aircraft. Of the three methods based upon various assumptions with regard to the interaction of sheet and stiffener, the method based upon mutual action of the stiffener and an effective width as a column gave the best agreement with the results of the tests. An investigation of the effect of small curvature resulted in the conclusion that the compressive strength of the curved panels is, for all practical purposes, equal to the strength of flat panels except for thick sheet where non-uniform curvature throughout the length may cause the strength of the curved panel to be 10 to 15 percent less than that of a corresponding flat panel.

STRESSED SKIN↗
NASA NTRS1994

Effects of fiber, matrix, and interphase on carbon fiber composite compression strength

The major goal of this project was to obtain basic information on compression failure properties of carbon fiber composites. To do this, we investigated fiber effects, matrix effects, and fiber/matrix interface effects. Using each of nine fiber types, we prepared embedded single-fiber specimens, single-ply specimens, and full laminates. From the single-fiber specimens, in addition to the standard fragmentation test analysis, we were able to use the low crack density data to provide information about the distribution of fiber flaws. The single-ply specimens provided evidence of a correlation between the size of kink band zones and the quality of the interface. Results of the laminate compression experiments mostly agreed with the results from single-ply experiments, although the ultimate compression strengths of laminates were higher. Generally, these experiments showed a strong effect of interfacial properties. Matrix effects were examined using laminates subjected to precracking under mixed-mode loading conditions. A large effect of precracking conditions on the mode 1 toughness of the laminates was found. In order to control the properties of the fiber/matrix interface, we prepared composites of carbon fiber and polycarbonate and subjected these to annealing. The changes in interfacial properties directly correlated with changes in compression strength.

Nairn, John A.↗
NASA NTRS1974

Compressive strength of fiber reinforced composite materials

Results of an experimental and analytical investigation of the compressive strength of unidirectional boron-epoxy composite material are presented. Observation of fiber coordinates in a boron-epoxy composite indicates that the fibers contain initial curvature. Combined axial compression and torsion tests were conducted on boron-epoxy tubes, and it was shown that the shear modulus is a function of axial compressive stress. An analytical model which includes initial curvature in the fibers and permits an estimate of the effect of curvature on compressive strength is proposed. Two modes of failure which may result from the application of axial compressive stress are analyzed, delamination and shear instability. Based on tests and analysis, failure of boron-epoxy under axial compressive load is due to shear instability.

Davis, J. G., Jr.↗
NASA NTRS1980

Graphite-epoxy panel compression strength reduction due to local impact

The effects of low velocity impact on the compressive strength of graphite/epoxy structures are reviewed. Extensive tests were conducted on sandwich beams, laminated plates and stiffened panels. Conditions for failures were investigated by impact tests on statically loaded test specimens. Lightly loaded graphite structures (such as aircraft secondary structure) were insensitive to impact damage. In more heavily loaded structures, (such as wing panels), appreciable reductions in compressive strength occurred. The implications of the tests for structural design are discussed by comparing panel masses for designs where ultimate strains were reduced due to impact considerations with the masses of designs with higher ultimate strains. Preliminary test data are presented to show the possibility of improvements in damage to tolerance achievable by using an alternate matrix material.

Card, M. F.↗
NASA NTRS1975

Compressive strength of fiber-reinforced composite materials

Results of an experimental and analytical investigation of the compressive strength of unidirectional boron-epoxy composite material are presented. Observation of fiber coordinates in a boron-epoxy composite indicates that the fibers contain initial curvature. Combined axial compression and torsion tests were conducted on boron-epoxy tubes and it was shown that the shear modulus is a function of axial compressive stress. An analytical model which includes initial curvature in the fibers and permits an estimate of the effect of curvature on compressive strength is proposed. Two modes of failure which may result from the application of axial compressive stress are analyzed - delamination and shear instability. Based on tests and analysis, failure of boron-epoxy under axial compressive load is due to shear instability.

Davis, J. G., Jr.↗
NASA NTRS1957

Investigation of the Compressive Strength and Creep Lifetime of 2024-T3 Aluminum-Alloy Plates at Elevated Temperatures

The results of elevated-temperature compressive strength and creep tests of 2024-t3 (formerly 24s-t3) aluminum alloy plates supported in v-grooves are presented. The strength-test results indicate that a relation previously developed for predicting plate compressive strength for plates of all materials at room temperature is also satisfactory for determining elevated-temperature strength. Creep-lifetime results are presented for plates in the form of master creep-lifetime curves by using a time-temperature parameter that is convenient for summarizing tensile creep-rupture data. A comparison is made between tensile and compressive creep lifetime for the plates and a method that made use of isochronous stress-strain curves for predicting plate-creep failure stresses is investigated.

Mathauser, Eldon E↗
NASA NTRS2013

A Unified Model for Predicting the Open Hole Tensile and Compressive Strengths of Composite Laminates for Aerospace Applications

The open hole tensile and compressive strengths are important design parameters in qualifying fiber reinforced laminates for a wide variety of structural applications in the aerospace industry. In this paper, we present a unified model that can be used for predicting both these strengths (tensile and compressive) using the same set of coupon level, material property data. As a prelude to the unified computational model that follows, simplified approaches, referred to as "zeroth order", "first order", etc. with increasing levels of fidelity are first presented. The results and methods presented are practical and validated against experimental data. They serve as an introductory step in establishing a virtual building block, bottom-up approach to designing future airframe structures with composite materials. The results are useful for aerospace design engineers, particularly those that deal with airframe design.

Davidson, Paul↗
NASA NTRS1992

Compressive strength of damaged and repaired composite plates

Tests were performed assessing the effectiveness of repair in restoring the mechanical properties of damaged, solid composite plates made either of Fiberite T300/976 graphite-epoxy, Fiberite IM7/977-2 graphite-toughened epoxy, or ICI APC-2 graphite-PEEK. The plate length, the layup and the amount of damage were also varied. Damage was introduced in the plates either by impacting them with a solid projectile or by applying a transverse static load. Some (75 percent) or all (100 percent) of the damaged zone was then cut out, and the plate was repaired by plugging and patching the hole. The effectiveness of the repair was evaluated by measuring the compressive strengths of undamaged plates, damaged plates with no cutout, damaged plates with a cutout, and repaired plates. The data at an intermediate stage of repair provide information on the effect of each repair step on the compressive strength. The results indicated that for the solid plates used in these tests, the repair methods used herein did not improve the compressive strength of already damaged plates.

Finn, Scott R.↗
NASA NTRS1955

Preliminary investigation of the compressive strength and creep lifetime of 2024-T3 (formerly 24S-T3) aluminum-alloy plates at elevated temperatures

The results of elevated-temperature compressive strength and creep tests of 2024-T3 (formerly 23S-T3) aluminum-alloy plates supported in V-grooves are presented. For determining elevated-temperature strength, where creep effects are negligible, a relation previously developed for predicting plate compressive strength at room temperature was satisfactory. Creep-lifetime results are presented for the plates in the form of master creep-lifetime curves by using a time-temperature parameter that is convenient for summarizing tensile creep-rupture data. A comparison is made between tensile and compressive creep lifetime for the plates, and the magnitude by which the design stress is decreased because of material creep and loss of strength due to exposure at elevated temperatures is indicated.

Mathauser, Eldon E↗