NASA NTRS2020

Durability of YSZ coated Ti2AlC in 1300°C high velocity burner rig tests

A thermal barrier coating system survived 500 h in cyclic burner rig tests at 1300°C, exceeding the life of all previous systems. An yttria stabilized zirconia (7YSZ) thermal barrier coating (TBC) was plasma sprayed on the oxidation resistant Ti2AlC MAX phase and tested in a jet fuel burner. No coating spallation or recession was observed, only a 2.4 mg/sq.cm mass gain due to typical cubic Al2O3 oxidation kinetics. The modest weight gain contrasted with large TBC spallation or oxide volatility losses that might occur under cyclic, high velocity (~100 m/s) burner conditions. The coating surface exhibited colonies of [111]flourite fiber-textured columns separated by craze crack patterns, but with no visible moisture attack. The thickness of the alumina scale under the YSZ face was >20 μm, more than twice that formed on TBC/superalloy systems at failure. TiO2 nodules, initially formed on the uncoated backside, were then removed as volatile hydroxides formed in high temperature, high velocity water vapor (~10%). Overall, the test indicated the exceptional stability of the YSZ/Ti2AlC system under turbine conditions, due in large part to good thermal expansion matching.

alumina, MAX phases, thermal barrier coatings (TBC↗
NASA NTRS1984

An investigation of enhanced capability thermal barrier coating systems for diesel engine components

Material systems and processes for the development of effective and durable thermal barriers for heavy duty diesel engines were investigated. Seven coating systems were evaluated for thermal conductivity, erosion resistance, corrosion/oxidation resistance, and thermal shock resistance. An advanced coating system based on plasma sprayed particle yttria stabilized zirconia (PS/HYSZ) was judged superior in these tests. The measured thermal conductivity of the selected coating was 0.893 W/m C at 371 C. The PS/HYSZ coating system was applied to the piston crown, fire deck and valves of a single cylinder low heat rejection diesel engine. The coated engine components were tested for 24 hr at power levels from 0.83 MPa to 1.17 MPa brake mean effective pressure. The component coatings survived the engine tests with a minimum of distress. The measured fire deck temperatures decreased 86 C (155 F) on the intake side and 42 C (75 F) on the exhaust side with the coating applied.

Holtzman, R. L.↗
NASA NTRS1993

Thermal Barrier Coatings

In order to reduce heat transfer between a hot gas heat source and a metallic engine component, a thermal insulating layer of material is placed between them. This thermal barrier coating is applied by plasma spray processing the thin films. The coating has been successfully employed in aerospace applications for many years. Lewis Research Center, a leader in the development engine components coating technology, has assisted Caterpillar, Inc. in applying ceramic thermal barrier coatings on engines. Because these large engines use heavy fuels containing vanadium, engine valve life is sharply decreased. The barrier coating controls temperatures, extends valve life and reduces operating cost. Additional applications are currently under development.

Source record↗
NASA NTRS2023

Radiation Shielding Plasma Sprayed Coatings Heads to International Space Station for MISSE-17 Experiments

NASA's Artemis program aims to return to the moon in search of scientific discoveries and establish a habitat using in-situ resource utilization. However, the past lunar explorations presented challenges, such as thermal cycles, solar and intergalactic cosmic radiation, and severe abrasive interaction of sharp lunar regolith particles[1]–[4].Dust mitigation and radiation shielding have become the most important concerns for lunar structural components and rovers which can fail abruptly without a protective solution. To counter these threats, Plasma Forming Laboratory(PFL) at Florida International University (FIU), in collaboration with NASA, has developed a novel multi-functional coating to protect the components synergistically against abrasion, erosion ,and radiation. The titanium-boron nitride composite coatings were prepared using the atmospheric plasma spray technique from engineered composite powders [5], [6].The coatings were subjected to extensive characterization and tribological study with lunar mare simulant JSC-1A, which shows tremendous improvement in the wear performance. The coatings subjected to neutron radiation shielding experiments at NASA Langley Research Center exhibited significantly improved neutron attenuation capacity compared to the substrate. The coating is selected to undergo radiation exposure on the International Space Station as a part of MISSE-17 (Materials International Space Station Experiment).

Thermal Spray↗
NASA NTRS1986

Plasma-Sprayed Coatings on Porous Surfaces

Need for combining benefits of duplex thermal-barrier coatings with film cooling on gas-turbine vanes and blades stimulated development of improved method for plasma spraying these coatings. Method reduces blocking of holes by plasma-sprayed material and at same time reduces base-metal oxidation during coating operation. Features provide potential for increased engine efficiency and power, reduced fuel consumption, use of less costly materials or construction procedures, and extended life and durability.

Leibert, C. H.↗
NASA NTRS1983

Covering solid, film cooled surfaces with a duplex thermal barrier coating

Thermal barrier coating systems were applied to hardware having passageways in the walls connecting apertures in the surface to a gas supply for film cooling. An inert gas, such as argon, is discharged through the apertures during the application of the thermal barrier coating system by plasma spraying. This flow of inert gas reduces both blocking of the holes and base metal oxidation during the coating operation.

Liebert, C. H.↗
NASA NTRS1989

Nondestructive Inspection Of Foam And Multilayer Insulations

Techniques and equipment enable nondestructive inspection of sprayed-on foam and multilayer reflecting thermal insulations on metallic substrates. Technology is applied in factories and laboratories; to inspect insulation on cryogenic tanks and pipes. Equipment includes probe head, several electronic modules that take measurements via electromagnetic and electrostatic sensors in probe head, small computer to store and process signals from modules, and printer.

Krause, Dennis R.↗
NASA NTRS1992

Cryogenic testing of a foam-multilayer insulation concept in a simulated prelaunch environment

NASA-Marshall has devised an upper-stage vehicle-applicable reusable cryogenic insulation thermal-control system which employs spray-on foam insulation (SOFI) that is attached to the cryotank wall and covered by 17-sheet multilayer insulation composed of double-aluminized mylar and Dacron scrim. Four prelaunch test simulations have been conducted for the case of LH2 with gaseous N2 purge gas. Test results indicate that the SOFI surface temperature was sufficiently high to preclude atmospheric oxygen and nitrogen liquefaction.

Martin, James J.↗
NASA NTRS1995

Multivariate Quantitative Chemical Analysis

Technique of multivariate quantitative chemical analysis devised for use in determining relative proportions of two components mixed and sprayed together onto object to form thermally insulating foam. Potentially adaptable to other materials, especially in process-monitoring applications in which necessary to know and control critical properties of products via quantitative chemical analyses of products. In addition to chemical composition, also used to determine such physical properties as densities and strengths.

Kinchen, David G.↗
NASA NTRS2003

Strength, Fracture Toughness, Fatigue, and Standardization Issues of Free-standing Thermal Barrier Coatings

Strength, fracture toughness and fatigue behavior of free-standing thick thermal barrier coatings of plasma-sprayed ZrO2-8wt % Y2O3 were determined at ambient and elevated temperatures in an attempt to establish a database for design. Strength, in conjunction with deformation (stress-strain behavior), was evaluated in tension (uniaxial and trans-thickness), compression, and uniaxial and biaxial flexure; fracture toughness was determined in various load conditions including mode I, mode II, and mixed modes I and II; fatigue or slow crack growth behavior was estimated in cyclic tension and dynamic flexure loading. Effect of sintering was quantified through approaches using strength, fracture toughness, and modulus (constitutive relations) measurements. Standardization issues on test methodology also was presented with a special regard to material's unique constitutive relations.

Choi, Sung R.↗
NASA NTRS2011

Molecular Adsorber Coating

A document discusses a zeolite-based sprayable molecular adsorber coating that has been developed to alleviate the size and weight issues of current ceramic puck-based technology, while providing a configuration that more projects can use to protect against degradation from outgassed materials within a spacecraft, particularly contamination-sensitive instruments. This coating system demonstrates five times the adsorption capacity of previously developed adsorber coating slurries. The molecular adsorber formulation was developed and refined, and a procedure for spray application was developed. Samples were spray-coated and tested for capacity, thermal optical/radiative properties, coating adhesion, and thermal cycling. Work performed during this study indicates that the molecular adsorber formulation can be applied to aluminum, stainless steel, or other metal substrates that can accept silicate-based coatings. The coating can also function as a thermal- control coating. This adsorber will dramatically reduce the mass and volume restrictions, and is less expensive than the currently used molecular adsorber puck design.

Straka, Sharon↗
NASA NTRSDate not supplied

Solar White Thermal Coating for Cryogenic Propulsion Systems

NASA is currently conducting research into the potential of storing cryogenic fluid in low Earth orbit (LEO). Having cryogenic propellant readily available for high-performance propulsion systems can be very beneficial for deep space missions in the near future. One of the key challenges to storing cryogenic fluid in LEO is minimizing boil-off. To address the challenge, NASA is evaluating new concepts in thermal insulation. One recent experimental study evaluated the feasibility of using Yttrium Oxide (Y2O3), formed into tiles or spray coating that can potentially be used as a thermal coating for cryogenic propellant storage applications in deep space. Due to its temperature and wavelength dependent optical properties, this “solar white” material can reflect a vast majority of the Sun’s radiative energy while having a very high infrared emissivity for rejecting heat to deep space. As a part of the material development and proof of concept testing, multiple tests have been run at KSC and GRC to demonstrate the performance of the material. At GRC, the tests were run using the Deep Space Solar Simulator (DS3) which contains a thermal vacuum chamber in which the solar white sample was exposed to a deep space environment (< 10 K, optically dense walls) while under full illumination via solar lamp. In order to improve the use of the test results and apply them to spacecraft, there is a need to be able to model the material properties within NASA’s standard thermal modeling tools. As such, it was set out to verify a thermal model of one of the experiments using Thermal Desktop with Sinda. The thermal model of the DS3 test setup includes the solar white sample along with a solar lamp simulator capable of outputting heat at varying wavelengths. The model was developed in order to validate the test results and also to help predict results that will be obtained in future tests. This paper will review the modeling methods and thermal analysis results for various test cases that were run within the DS3 facility.

Cryogenic↗
DOE OSTI2021

Method of manufacturing a reinforced nuclear fuel cladding using an intermediate thermal deposition layer

A method is described that includes the steps of making a thin walled Zr alloy tube, loading nuclear fuel pellets into the tube, compressing the tube onto the fuel pellets to substantially reduce free space around the fuel pellets, positioning end plugs at each of two ends of the tube, filling the tube with a heat transferring gas, and coating the compressed tube with a corrosion resistant material using a thermal deposition process, such as cold spray, before inserting the tube into a pre-formed SiC composite cover having at least one closed end.

Lahoda, Edward J.↗
NASA NTRS1988

Vacuum application of thermal barrier plasma coatings

Coatings are presently applied to Space Shuttle Main Engine (SSME) turbine blades for protection against the harsh environment realized in the engine during lift off-to-orbit. High performance nickel, chromium, aluminum, and yttrium (NiCrAlY) alloy coatings, which are applied by atmospheric plasma spraying, crack and spall off because of the severe thermal shock experienced during start-up and shut-down of the engine. Ceramic coatings of yttria stabilized zirconia (ZrO2-Y2O3) were applied initially as a thermal barrier over coating to the NiCrAlY but were removed because of even greater spalling. Utilizing a vacuum plasma spraying process, bond coatings of NiCrAlY were applied in a low pressure atmosphere of argon/helium, producing significantly improved coating-to-blade bonding. The improved coatings showed no spalling after 40 MSFC burner rig thermal shock cycles, cycling between 1700 and -423 F. The current atmospheric plasma NiCrAlY coatings spalled during 25 test cycles. Subsequently, a process was developed for applying a durable thermal barrier coating of ZrO2-Y2O3 to the turbine blades of first stage high-pressure fuel turbopumps utilizing the vacuum plasma process. The improved thermal barrier coating has successfully passed 40 burner rig thermal shock cycles without spalling. Hot firing in an SSME turbine engine is scheduled for the blades. Tooling was installed in preparation for vacuum plasma spray coating other SSME hardware, e.g., the titanium main fuel valve housing (MFVH) and the fuel turbopump nozzle/stator.

Holmes, R. R.↗
NASA NTRS1972

Effective thermal conductivities of four metal ceramic composite coatings in hydrogen-oxygen rocket firings

An experimental investigation was conducted to determine the effective conductivities of four plasma-arc-sprayed, metal-ceramic gradated coatings on hydrogen-oxygen thrust chambers. The effective thermal conductivities were not a function of pressure or oxidant-to-fuel ratio. The various materials that made up these composites do not seem to affect the thermal conductivity values as much as the differences in the thermal conductivities of the parent materials would lead one to expect. Contact resistance evolving from the spraying process seems to be the controlling factor. The thermal conductivities of all the composites tested fell in the range of 0.75 to 7.5 watts per meter kelvin.

Schacht, R. L.↗
NASA NTRS1995

New generation of plasma-sprayed mullite coatings on silicon carbide

Mullite is promising as a protective coating for silicon-based ceramics in aggressive high-temperature environments. Conventionally plasma-sprayed mullite on SiC tends to crack and debond on thermal cycling. It is shown that this behavior is due to the presence of amorphous mullite in the conventionally sprayed mullite. Heating the SiC substrate during the plasma spraying eliminated the amorphous phase and produced coatings with dramatically improved properties. The new coating exhibits excellent adherence and crack resistance under thermal cycling between room temperature and 1000 to 1400 C. Preliminary tests showed good resistance to Na2CO3-induced hot corrosion.

Lee, Kang N.↗
NASA NTRS1980

Comparative evaluation of insulating properties of plasma-sprayed ceramic coatings

A simple method for evaluating the thermal insulating capability of ceramic coatings was devised. It is based on monitoring the temperature of the uncoated back surface of a thin superalloy disk while its front surface, coated with the ceramic material, is exposed to the high-temperature environment of an electric muffle furnace. The results obtained indicate that zirconia containing 8 wt% Y2O3 is a better thermal insulator than barium zirconate or calcium orthosilicate.

Zaplatynsky, I.↗