Extended Interfacial Stability through Simple Acid Rinsing in a Li-Rich Oxide Cathode Material
Layered Li-rich Ni, Mn, Co (NMC) oxide cathodes in Li-ion batteries provide high specific capacities (>250 mAh/g) via O-redox at high voltages. However, associated high-voltage interfacial degradation processes require strategies for effective electrode surface passivation. Here, we show that an acidic surface treatment of a Li-rich NMC layered oxide cathode material leads to a substantial suppression of CO 2 and O 2 evolution, ~90% and ~100% respectively, during the first charge up to 4.8 V vs. Li +/0 . CO 2 suppression is related to Li 2 CO 3 removal as well as effective surface passivation against electrolyte degradation. This treatment does not result in any loss of discharge capacity and provides superior long-term cycling and rate performance compared to as-received, untreated materials. We also quantify the extent of lattice oxygen participation in charge compensation (“O-redox”) during Li + removal by a novel ex-situ acid titration. Our results indicate that the peroxo-like species resulting from O-redox originate on the surface at least 300 mV earlier than the activation plateau region around 4.5 V. X-ray photoelectron spectra and Mn -L X-ray absorption spectra of the cathode powders reveal a Li + deficiency and a partial reduction of Mn ions on the surface of the acid-treated material. More interestingly, although the irreversible oxygen evolution is greatly suppressed through the surface treatment, our O K-edge resonant inelastic X-ray scattering shows the lattice O-redox behavior largely sustained. The acidic treatment, therefore, only optimizes the surface of the Li-rich material and almost eliminates the irreversible gas evolution, leading to improved cycling and rate performance. This work therefore presents a simple yet effective approach to passivate cathode surfaces against interfacial instabilities during high-voltage battery operation.