Laser-zone growth in a Ribbon-To-Ribbon (RTR) process. Silicon sheet growth development for the large area silicon sheet task of the low cost silicon solar array project

The Ribbon-to-Ribbon (RTR) approach to silicon ribbon growth is investigated. An existing RTR apparatus is to be upgraded to its full capabilities and operated routinely to investigate and optimize the effects of various growth parameters on growth results. A new RTR apparatus was constructed to incorporate increased capabilities and improvements over the first apparatus and to be capable of continuous growth. New high power lasers were implemented and this led to major improvements in growth velocity -- 4 inch/min. growth has been demonstrated. A major step in demonstration of the full feasibility of the RTR process is reported in the demonstration of RTR growth from CVD polyribbon rather than sliced polyribbon ingots. Average solar cell efficiencies of greater than 9% and a best cell efficiency of 11.7% are reported. Processing was shown to provide a substantial improvement in material minority carrier diffusion length. An economic analysis is reported which treats both the polyribbon fabrication and RTR processes.

Gurtler, R. W.↗

Development of advanced methods for continuous Czochralski growth. Silicon sheet growth development for the large area silicon sheet task of the low cost silicon solar array project

The three components required to modify the furnace for batch and continuous recharging with granular silicon were designed. The feasibility of extended growth cycles up to 40 hours long was demonstrated by a recharge simulation experiment; a 6 inch diameter crystal was pulled from a 20 kg charge, remelted, and pulled again for a total of four growth cycles, 59-1/8 inch of body length, and approximately 65 kg of calculated mass.

Wolfson, R. G.↗

Hot forming of silicon sheet, silicon sheet growth development for the large area silicon sheet task of the low cost silicon solar array project

The hot workability of polycrystalline silicon was studied. Uniaxail stress-strain curves are given for strain rates in the range of .0001 to .1/sec and temperatures from 1100 to 1380 C. At the highest strain rates at 1380 C axial strains in excess of 20% were easily obtainable without cracking. After deformations of 36%, recrystallization was completed within 0.1 hr at 1380 C. When the recrystallization was complete, there was still a small volume fraction of unrecyrstallized material which appeared very stable and may degrade the electronic properties of the bulk materials. Texture measurements showed that the as-produced vapor deposited polycrystalline rods have a 110 fiber texture with the 110 direction parallel to the growth direction and no preferred orientation about this axis. Upon axial compression perpendicular to the growth direction, the former 110 fiber axis changed to 111 and the compression axis became 110 . Recrystallization changed the texture to 110 along the former fiber axis and to 100 along the compression axis.

Graham, C. D., Jr.↗

Delayed fracture of silicon: Silicon sheet growth development for the large area silicon sheet task of the low cost silicon solar array project

Bar specimens were cut from ingots of single crystal silicon, and acid etched prior to testing. Artificial surface flaws were introduced in specimens by indentation with a Knoop hardness tester. The specimens were loaded in four-point bending to 95 percent of the nominal fracture stress, while keeping the surface area, containing the flaw, wet with test liquids. No evidence of delayed fracture, and, therefore stress corrosion, of single crystal silicon was observed for liquid environments including water, acetone, and aqueous solutions of NaCl, NH4OH, and HNO3, when tested with a flaw parallel to a (110) surface. The fracture toughness was calculated.

Chen, T. J.↗