DOE OSTI2022
Understanding of the high temperature durability of particles and the materials that contain them is critical to next generation of concentrating solar power (CSP) technology. Here we studied the durability of particles and their containment materials under extreme UV cycling, thermal cycling, and in low-speed high temperature mechanical wear situations. The optical stability of seven candidate particles has been determined following exposure to the high temperature conditions present in a generation 3 particle-based CSP technology. Particle solar weighted absorptance and emittance measured periodically during 10,000 high solar irradiance exposure cycles and up to 400 hours of isothermal aging has been documented. The particle aging due to repeated exposure to concentrated solar flux represented the 30-year lifetime of a power plant. Models were fit to the absorptivity and emissivity data following the isothermal aging provides the projected optical degradation of the particles as a function of temperature. Mechanical wear was studied through the use of custom developed wear testing facilities for measuring high temperature impact wear, abrasion wear, and particle attrition. Additionally, a novel technique for measuring the high temperature mechanical properties of single particles was developed. Through these tests it was observed that high nickel alloys generally showed lower wear than comparable iron based steels, particularly at elevated temperatures of 800°C. Mechanical wear at these temperatures is a highly complex phenomenon combining both mechanical wear and oxidation. Additionally, the containment materials wear rates are influenced by the particles (both hardness and roundness), making the wear mechanisms complex. The initial wear test conducted in the abrasion test rig revealed a substantial amount of oxide materials in the particle bed after testing (in relative to later tests), and substantially more wear, likely indicating a need for concern in startup operation of particle facilities to not incur high wear from the presence of oxides. Particle attrition experiments have only been conducted for a single material but increase size distribution, reduction in circularity, and particle diameter is observed. Efforts to develop predictive models was limited due to a testing campaign that prioritized testing materials for particle pathway developers over building a comprehensive design of experiments. The results discussed in this report inform future CSP developers and researchers further de risking the technology and assisting in its future development. ParticleBased CSP development provides a path to dispatchable solar power generation with storage at a price competitive in the current energy market. Lowering the cost of CSP technology provides a carbon free power generation solution that can assist in the transition from fossil fuels to renewable sources of electricity.