Experimental Technetium Release from Simulated Salt-stone Cementitious Waste Form - 18419
Experiments are being conducted to evaluate the early release of technetium (Tc) from fresh salt-stone waste forms using dynamic flow-through tests. Salt-stone is a chemically reducing, grout-based waste form used by the U.S. Department of Energy (DOE) to dispose of low-activity salt solutions arising from high-level radioactive waste tank closure activities at the Savannah River Site (SRS). A key safety function of salt-stone is maintaining a low-flow, chemically reducing environment that will attenuate the release of redox-sensitive radioelements such as Tc. Salt-stone also provides a physical barrier due to its low intrinsic permeability, which limits both water and oxygen ingress. These release experiments, conducted to support the U.S. Nuclear Regulatory Commission's monitoring role during tank closure, are designed to provide independent information on how well salt-stone will perform its safety function. The dynamic leach tests were conducted in a Hassler-type core-holder permeameter system that allows an accelerated flow rate of simulated SRS groundwater through an intact cylinder of salt-stone spiked with Tc-99 at a concentration of approximately 2,100 Bq/g (3 ppm). The first salt-stone specimen to be tested (Specimen 2) was prepared with Grade 100 ground granulated blast-furnace slag and aged for 119 days in a temperature-controlled, low-oxygen, high-humidity environment. Before test completion, 9.5 pore volumes (PV) of simulated SRS groundwater were passed through the salt-stone cylinder. After a few PV, apparent saturated hydraulic conductivity (K{sub sat}) values calculated from flow data reached a steady-state value of approximately 1.0 x 10{sup -9} cm/s, which is within the range of previously reported data. Tc-99 concentrations in leachate peaked early during the leach test at 2.0 x 10{sup -7} M and then declined to approximately 4 x 10{sup -8} M after 9.5 PV. The leachate Tc-99 concentration after elution of 9.5 PV is broadly consistent with a Tc solution concentration controlled by the solubility of reduced Tc solids. The range of Tc-99 concentrations is similar to the range reported for a column test that was sponsored by DOE, but the time pattern of release differs. The second salt-stone specimen tested (Specimen 3) was aged for 372 days and it further differed from the first specimen in that its Grade 100 slag component had been finely ground using a mortar and pestle in an attempt to make it more reactive. This second test yielded Tc release behavior broadly similar to that observed during the first test, except that the early Tc peak (at 1.2 x 10{sup -6} M) was six times higher and the concentration after 6.7 PV (8.8 x 10{sup -8} M) was approximately two times higher than in the first test. In addition, the steady-state K{sub sat} was an order of magnitude lower than that of the first specimen. During the second test, the injection pump was intentionally turned off for a period of 11 days (i.e., approximate residence time for 1 PV) and a Tc spike was observed when pumping resumed, suggesting that longer residence times may promote higher Tc effluent concentrations. During a second intentional shut-down of the pump for 25 days (approximate residence time for 2 PV), another Tc spike was observed. An unplanned excursion to higher confining pressure physically affected the specimen, temporarily lowering the apparent K{sub sat} followed by a subsequent increase in both K{sub sat} and Tc effluent concentration. One hypothesis is that the transient spike in confining pressure and resulting salt-stone compression and later decompression may have induced Tc release from otherwise inactive pores. (authors)