Results for “Corrosion Protection”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 289 records · Page 16
All sourcesNASA NTRSDOE OSTI
NASA NTRS1990

Hot corrosion of silicon carbide and silicon nitride at 1000 C

The sodium sulfate hot corrosion of silicon-based ceramics at 1000 C has been extensively studied. Deposition of the sodium sulfate corrodant from combustion products is discussed in relation to sodium air impurity and sulfur fuel impurity content. Corrosion occurs by the combined processes of oxidation to form protective silica scales and dissolution of these scales to form nonprotective sodium silicates. The chemical corrosion mechanisms are presented in terms of acidic/basic dissolution of oxides in molten salts. The reactions are strongly influenced by the presence of free carbon in the ceramic. Strength reductions have been measured and are attributed to pitting in SiC and grain boundary attack in Si3N4. Initial results of burner corrosion of two ceramic matrix composites are consistent with the models developed for monolithic ceramics.

Fox, Dennis S.↗
NASA NTRS1990

Composite structural armor for combat vehicle applications

Several projects that have demonstrated the advantages of using thick composite armor technology for structural applications in armored combat vehicles are discussed. The first involved composite cargo doors for the Marine Corps LVTP-7 amphibious landing vehicle. Another was a demonstration composite turret that offered a weight reduction of 15.5 percent. The advantages of this composite armor compared to metallic armors used for combat vehicle hull and turret applications are reduced weight at equal ballistic protection; reduced back armor spall; excellent corrosion resistance; reduced production costs by parts consolidation; and inherent thermal and acoustic insulative properties. Based on the encouraging results of these past programs, the Demonstration Composite Hull Program was started in September 1986. To demonstrate this composite armor technology, the Army's newest infantry fighting vehicle, the Bradley Fighting Vehicle (BFV), was selected as a model. A composite infantry fighting vehicle, designated the CIFV for this program, has been designed and fabricated and is currently undergoing a 6000 mile field endurance test. The CIFV demonstration vehicle uses the BFV engine, transmission, suspension, track and other equipment.

Haskell, William E., III↗
NASA NTRS1995

Tests Of Protective Coats For Carbon Steel

Report describes laboratory and field tests of candidate paints (primers, tie coats, and topcoats) for use in protecting carbon-steel structures against corrosion in seaside environment at Kennedy Space Center. Coating materials selected because of utility in preventing corrosion, also on basis of legal requirements, imposed in several urban areas, for reduction of volatile organic contents.

Macdowell, Louis G., III↗
NASA NTRS1976

Space Paint

Developed at Goddard, this improved inorganic paint may help protect coastal bridges subject to extreme corrosion from seawater spray. Potassium silicate formulated into a thin waterbase binder that sprays easily, adheres readily, and can be heavily loaded with zinc particles to provide uniform coverage in a single coat. Stanford Research Institute has measured an annual market in excess of $2 billion in painting highway bridges, utility pipelines, nuclear reactors, and railcar hoppers. Other suitable markets include offshore drilling facilities, railroad bridges, and ships.

Source record↗
NASA NTRS2014

High Temperature Chemistry at NASA: Hot Topics

High Temperature issues in aircraft engines Hot section: Ni and Co based Superalloys Oxidation and Corrosion (Durability) at high temperatures. Thermal protection system (TPS) and RCC (Reinforced Carbon-Carbon) on the Space Shuttle Orbiter. High temperatures in other worlds: Planets close to their stars.

re-entry heat shields↗
NASA NTRS2017

Residual Stresses in a NiCrY-Coated Powder Metallurgy Disk Superalloy

Protective ductile coatings will be necessary to mitigate oxidation and corrosion attack on superalloy disks exposed to increasing operating temperatures in some turbine engine environments. However, such coatings must be resistant to harmful surface cracking during service. The objective of this study was to investigate how residual stresses evolve in such coatings. Cylindrical gage fatigue specimens of powder metallurgy-processed disk superalloy LSHR were coated with a NiCrY coating, shot peened, and then subjected to fatigue in air at room and high temperatures. The effects of shot peening and fatigue cycling on average residual stresses and other aspects of the coating were assessed. Shot peening did induce beneficial compressive residual stresses in the coating and substrate. However, these stresses became more tensile in the coating with subsequent heating and contributed to cracking of the coating in long intervals of cycling at 760 C. Substantial compressive residual stresses remained in the substrate adjacent to the coating, sufficient to suppress fatigue cracking. The coating continued to protect the substrate from hot corrosion pitting, even after fatigue cracks initiated in the coating.

superalloy↗
NASA NTRS1981

Silicon carbide as an oxidation-resistant high-temperature material. 1: Oxidation and heat corrosion behavior

The oxidation and corrosion behavior of SiC (in the form of a SiC powder) and hot-pressed and reaction-bound material were studied. The excellent stability of SiC in an oxidizing atmosphere is due to the development of protective SiO2 coatings. Any changes in these protective layers (e.g., due to impurities, reaction with corrosive media, high porosity of SiC, etc.) lead in most cases to increased rates of oxidation and thus restrict the field of SiC application.

Schlichting, J.↗
NASA NTRS2015

Alumina-Forming MAX Phases in Turbine Material Systems

Coatings for high temperature turbine components are based on low conductivity YSZ thermal barriers and protective NiAl, NiCoCrAlY bond coats. Good oxidation hot corrosion resistance, intermediate CTE, and strain tolerance of Ti2AlC and Cr2AlC MAX phases are thus of special interest. Their alumina scale growth follows a cubic law in accord with FeCrAlY alloys, with oxygen grain boundary diffusivity: Dgb 1.8 x 10-10 exp(-375 kJmole) m3s. Protective cubic kinetics are also found in high pressure burner rig (6 atm., 25 ms) and TGA tests of MAXthal 211Ti2AlC. The initial portion (0.1 hr) is dominated by fast TiO2 growth (with little evidence of scale volatility in high pressure water vapor, as found for SiO2 scales). Bulk Ti2AlC and Cr2AlC substrates show promise as potential bond coats for YSZ TBCs in 1000-1200 C furnace life (500 h) tests. Cr2AlC is proving to be very resistant to 700-900 C Na2SO4 hot corrosion and is of interest for disk alloys. Preliminary diffusion bonded Cr2AlC-superalloy hybrid couples have survived 1000 hr interrupted furnace tests at 800C with no indication of cracking or debonding. Diffusion zones of -NiAl+Cr7C3 were produced in these above 1000 C, but did not grow to any great extent after 1000 hr at 800 C. Processing as coatings presents challenges, however the basic properties of MAX phases provide novel opportunities for high temperature turbine components.

MAX phase↗
NASA NTRS1993

The impact of LDEF results on the space application of metal matrix composites

Over 200 graphite/aluminum and graphite/magnesium composites were flown on the leading and trailing edges of LDEF on the Advanced Composites Experiment. The performance of these composites was evaluated by performing scanning electron microscopy and x-ray photoelectron spectroscopy of exposed surfaces, optical microscopy of cross sections, and on-orbit and postflight thermal expansion measurements. Graphite/aluminum and graphite/magnesium were found to be superior to graphite/polymer matrix composites in that they are inherently resistant to atomic oxygen and are less susceptible to thermal cycling induced microcracking. The surface foils on graphite/aluminum and graphite/magnesium protect the graphite fibers from atomic oxygen and from impact damage from small micrometeoroid or space debris particles. However, the surface foils were found to be susceptible to thermal fatigue cracking arising from contamination embrittlement, surface oxidation, or stress risers. Thus, the experiment reinforced requirements for carefully protecting these composites from prelaunch oxidation or corrosion, avoiding spacecraft contamination, and designing composite structures to minimize stress concentrations. On-orbit strain measurements demonstrated the importance of through-thickness thermal conductivity in composites to minimize thermal distortions arising from thermal gradients. Because of the high thermal conductivity of aluminum, thermal distortions were greatly reduced in the LDEF thermal environment for graphite/aluminum as compared to graphite/magnesium and graphite/polymer composites. The thermal expansion behavior of graphite/aluminum and graphite/magnesium was stabilized by on-orbit thermal cycling in the same manner as observed in laboratory tests.

Steckel, Gary L.↗
NASA NTRS1994

New Trends in Coatings Developments for Turbine Blades: Materials Processing and Repair

Turbine engines for aeronautic applications now have to face strenuous requirements concerning not only operating performances but also reliability and repairability. This evolution of the specifications induces important consequences regarding the choice and the design of turbine blade protective coatings. This paper presents several key features concerning the deposition techniques and the real-life behavior of such coatings: (1) complex aluminides well suited to the protection against high temperature oxidation and hot corrosion of directionally solidified nickel-base superalloy turbine blades; (2) ceramic coatings used as thermal barriers - they have to exhibit both high resistance to thermomechanical fatigue and adequate smoothness; (3) processing techniques for thermal barriers, including plasma spraying, electron beam physical vapor deposition and plasma enhanced chemical vapor deposition; and (4) blades and coatings repair techniques.

S Alpérine↗
NASA NTRS1985

Internal stresses in wear and corrosion resistant amorphous metallic coatings of (W/0.6/Re/0.4/)76B24 and (Mo/0.6/Ru/0.4/)82B18

Hard protective coatings in the W-Re-B and Mo-Ru-B alloy systems have been deposited by magnetron sputtering onto soda-lime glass and heat-treated AISI 52100 steel substrates. X-ray diffraction has confirmed the amorphous nature of the as-deposited coatings, and their crystallization temperatures were determined by differential thermal analysis to be 1000 and 790 C for W-Re-B and Mo-Ru-B coatings, respectively. Both coatings exhibit high microhardness; Mo-Ru-B, in addition, has excellent corrosion resistance by comparison with pure Mo at high anodic potentials. Attention is given to the influence of internal stresses on the protective properties of the coatings deposited under different conditions.

Thakoor, A. P.↗
NASA NTRS1988

Hot corrosion of ceramic engine materials

A number of commercially available SiC and Si3N4 materials were exposed to 1000 C in a high velocity, pressurized burner rig as a simulation of a turbine engine environment. Sodium impurities added to the burner flame resulted in molten Na2SO4 deposition, attack of the SiC and Si4N4 and formation of substantial Na2O-x(SiO2) corrosion product. Room temperature strength of the materials decreased. This was a result of the formation of corrosion pits in SiC, and grain boundary dissolution and pitting in Si3N4. Corrosion regimes for such Si-based ceramics have been predicted using thermodynamics and verified in rig tests of SiO2 coupons. Protective mullite coatings are being investigated as a solution to the corrosion problem for SiC and Si3N4. Limited corrosion occurred to cordierite (Mg2Al4Si5O18) but some cracking of the substrate occurred.

Fox, Dennis S.↗
NASA NTRS2020

LCF Life of NiCr-Y Coated Disk Alloys After Shot Peening, Oxidation and Hot Corrosion

In a prior companion study (Ref. 1), three different Ni-Cr coating compositions (29, 35.5, 45 wt% Cr) were applied at two thicknesses by Plasma Enhanced Magnetron Sputtering (PEMS) to two similar Ni-based disk alloys. One coating also received a thin ZrO2 overcoat. The low cycle fatigue (LCF) life of each coating was determined at 760 °C and was less than that of the uncoated specimens. In this followon effort, shot peening was examined as a means to improve the as-deposited coating morphology as well as impart a residual compressive stress in the near-surface region. After evaluating the effect of the shot peening on the LCF life, the effectiveness of the shot-peened coating in protecting the disk alloy from oxidation and hot corrosion attack was evaluated. This evaluation was accomplished by exposing coated and shot-peened specimens to 500 h of oxidation followed by 50 h of hot corrosion, both at 760 °C in air. These exposed specimens were then tested in fatigue and compared to similarly treated and exposed uncoated specimens. For all cases, shot peening improved the LCF life of the coated specimens. More specifically, the highest Cr coating showed the best LCF life of the coated specimens after shot peening, as well as after the environmental exposures. Characterization of the coatings after shot peening, oxidation, hot corrosion and LCF testing is presented and discussed.

James A Nesbitt↗
NASA NTRS1997

New Anti-Corrosive Coatings with Resin-Bonded Polyaniline and Related Electroactive Groups

It is already known that polyaniline (an electroactive polymer) functions as a corrosion inhibitor for steel and in view of the fact that it is known to perform in the presence of hydrochloric acid, it has been considered likely that it may be useful to NASA for protecting launch structures at KSC which are exposed to not only continual ocean-side salt spray but also to hydrochloric acid at the times that solid-fuel boosters are fired. The currently used zinc-rich silicate-bonded coating is not wholly protective against the hydrochloric acid. Water pollution from zinc salts is another concern. Other earlier and concurrent NASA sponsored projects have been focussed on polyaniline specifically. Our project, administered for NASA by Dr. K. Thompson of KSC and these more-specifically polyaniline-related projects are included in a CRADA coordinated by Dr. F. Via of Akzo Nobel. A parallel project at Polytechnic under Prof K. Levon concentrated more specifically on polyaniline with various dopants. Our exploratory project reported herein was aimed at broadening the range of such corrosion inhibitors, to give protective paint compounders a wider latitude for adding corrosion inhibitors having polyaniline-like performance, and thus we diverged in several probing directions from polyaniline. Our working hypothesis was that physical variants of polyaniline, such as supported formulations on pigments or carriers, and chemical variants of polyaniline, including those having no electroconductive character, may have enhanced anticorrosion activity. We also hypothesized that small (non-polymeric) molecules having structures related to those occurring in polyaniline, may be active as corrosion inhibitors. We did preliminary testing, using an ASTM salt spray method at a nearby commercial paint testing laboratory. Our most interesting findings were that a non-electroconductive meta-isomer of polyaniline showed some corrosion activity, suggesting that the features of the polyaniline molecule associated with conductivity are not necessary for the anticorrosion action. Also, signtficantly, small molecular weight aromatic diamines and diimines resembling the reduced and the oxidized repeating unit in polyaniline showed an interesting degree of anticorrosive activity, suggesting that the polymeric feature of polyaniline is not necessary for anticorrosion action.

Weil, Edward D.↗
NASA NTRS1985

Hot corrosion of sintered alpha-SiC at 1000 C

The hot corrosion of sintered alpha-SiC by thin films of Na2SO4 and Na2CO3 was studied at 1000 C in controlled gas atmospheres. Under all conditions, corrosion led to 10 to 20 times the amount of SiO2 formed in pure oxidation after a 48-h exposure. In addition, small amounts of sodium silicate formed. Melts of Na2SO4/SO3 caused uniform pitting of the SiC substrate; Na2CO3/CO2 melts caused localized pitting and grain-boundary attack. In all cases, the protective SiO2 layer dissolved to form silicate, leading to corrosion. In the sulfate case, free carbon in the SiC promotes this process. In all cases the presence of liquid films is responsible for rapid transport rates and the subsequent rapid reaction.

Jacobson, N. S.↗
NASA NTRS1976

Hot corrosion studies of four nickel-base superalloys: B-1900, NASA-TRW VIA, 713C and IN738

The susceptibility to hot corrosion of four nickel base superalloys has been studied at 900 deg and 1000 deg C in one atmosphere of slowly flowing oxygen. Hot corrosion was induced by coating the samples with known doses of NaSO4 and oxidizing the coated samples isothermally on a sensitive microbalance. In general, the order of susceptibility found was: B-1900 is greater than 713C is greater than NASA-TRW VIA and is greater than IN738. This order corresponds to the order of decreasing molybdenum content of the alloys. Chemical evidence for B-1900 indicates that hot corrosion is instigated by acid fluxing of the protective Al2O3 coating by MoO3.

Fryburg, G. C.↗