Analysis of Deformation and Fracture Mechanisms in the Harvested High-Dose Baffle-Former Bolt with Stress-Corrosion Cracks Formed While in Service

This report presents the results of advanced mechanical testing conducted on miniature tensile specimens excised from an irradiated baffle-former bolt, a commercial pressurized water reactor component. The specimens were extracted from the midsection of the bolt shank, where the estimated damage dose reached 23 displacements per atom. The mechanical testing included the following tests: (1) conventional tensile testing at room temperature, augmented by digital image correlation (DIC) to enable noncontact strain measurements, and (2) in situ tensile testing within a scanning electron microscopy (SEM) instrument equipped with energy-dispersive x-ray spectroscopy (EDS) and electron backscatter diffraction (EBSD) detectors to evaluate active deformation and fracture mechanisms. Additionally, SEM fractographic analysis revealed alterations in the fracture mechanism from a predominantly ductile fracture in nonirradiated steel to a mixed fracture mode (still dominating ductile and minor cleavage spots) in irradiated specimens derived from the baffle bolts. The findings indicate a complex strain localization behavior for in-service irradiated steel specimens. Beyond conventional necking at the macro scale and defect-free channel formation at the micro scale, DIC results identified the presence of deformation bands approximately 100 μm in width. These bands consist of chains of grains exhibiting elevated local strain levels and may be considered an intermediate or mesoscale level of strain localization. These bands become discernible near the yield stress as localized hot spots, areas of elevated strain, persisting throughout most of the experiment. The formation of mesoscale deformation bands as a strain localization mechanism may exacerbate the defect-free channel formation in irradiated materials, further promoting irradiation-assisted stress corrosion crack initiation.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2025

ATF Cladding Mechanical Properties Report: Capability Demonstration

This report documents mechanical testing capability demonstration activities performed in fiscal year (FY)2025 at Oak Ridge National Laboratory(ORNL)on chromium-coated (Cr-coated) and uncoated advanced zirconium alloy claddings irradiated in the High Flux Isotope Reactor (HFIR) to approximately 4 displacements per atom (dpa), corresponding to ~13GWd/t burnup. Specimens were prepared in axial tension (ATT) and ring tension (RTT) geometries, and passive silicon carbide(SiC)thermometry (TM) was employed to determine irradiation temperatures, which averaged 38–43 °C below the 330 °C design target. Mechanical testing at ambient temperature demonstrated the expected irradiation-induced hardening, with yield strength(YS)and ultimate tensile strength(UTS)values increasing substantially relative to unirradiated counterparts. However, this strengthening was accompanied by a reduction in ductility, as indicated by lower uniform and total elongations(UE and TE). Both coated and uncoated claddings exhibited similar mechanical response, though Cr-coated specimens showed surface cracking perpendicular to the loading direction, attributable to the hardness mismatch between the coating and substrate. Fracture in all cases remained ductile, and no coating spallation was observed following HFIR irradiation. Complementary efforts were directed toward the fabrication of test specimens from commercially irradiated cladding (rod 47I, ~31.1 GWd/t average burnup). Axial sectioning and computer numerical control(CNC)machining successfully produced ATT geometries suitable for benchmarking against HFIR-irradiated specimens. This capability enables direct comparison of cladding behavior between test reactor and commercial reactor environments, thereby supporting the validation of HFIR as a surrogate irradiation platform for accident tolerant fuel (ATF) development. Once HFIR irradiations are completed in FY26,the relevant comparison tests will be completed. Collectively, the FY 2025 PIE campaign has provided mechanical performance data for irradiated advanced claddings The demonstrated capabilities support the framework for mechanical testing and further evaluations in subsequent years. These efforts will represent an important contribution toward the licensing and deployment of Cr-coated zirconium alloy cladding as a near-term ATF solution.

36 MATERIALS SCIENCE↗

DOE OSTI2025

ATF Cladding Mechanical Properties Report: Capability Demonstration

This report documents post-irradiation examination (PIE) activities performed in FY 2025 at Oak Ridge National Laboratory on chromium-coated (Cr-coated) and uncoated advanced zirconium alloy claddings irradiated in the High Flux Isotope Reactor (HFIR) to approximately 4 displacements per atom (dpa), corresponding to ~40 GWd/t burnup. Specimens were prepared in axial tension (ATT) and ring tension (RTT) geometries, and passive silicon carbide thermometry was employed to determine irradiation temperatures, which averaged 38–43 °C below the 330 °C design target.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

Crack Growth Rate and Fracture Toughness Tests on Irradiated Ex-Plant Materials

The performance of structural materials is critical for the safe and economic operation of light water reactors. Exposed to neutron irradiation during service, the reactor core internal materials can undergo significant microstructural and microchemical changes, leading to irradiation hardening and embrittlement. To ensure the structural integrity and functionality of nuclear reactor components during long-term operation, material degradation and damage mechanisms must be understood and managed adequately. In this work, irradiated materials harvested from the decommissioned Zorita reactor were studied for their cracking susceptibility and fracture resistance as a function of irradiation dose up to 47 displacement per atom (dpa). The material is a Type 304 stainless steel sectioned from the baffle plates of this pressurized water reactor with 38 years of service. Crack growth rate and fracture toughness J-resistance (J-R) curve tests were performed in low-corrosion-potential environments at ~315°C. All samples behaved similarly under cyclic loading, and no deteriorated corrosion-fatigue behavior was observed in the test environments. Under constant stress intensity factors, most samples did not show elevated crack growth rates, suggesting an adequate stress corrosion cracking resistance in the test environments. However, an unstable cracking behavior was observed in a 47-dpa sample, resulting in significantly higher crack growth rates than expected at high stress intensity factors. Crack instability was also observed in a 0.06-dpa sample but did not lead to a sustained high crack growth rate. The impact of neutron irradiation was more evident in the fracture toughness J-R curve tests. As the dose increased, the J-R curve declined considerably and became very shallow at high doses. A fully intergranular fracture morphology was also observed among the high-dose samples ruptured in an air atmosphere at room temperature. This brittle fracture mode in the absence of high temperature water environment confirmed a high degree of embrittlement of this material resulting from its service exposure to neutron irradiation.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2022

Micropillar Compression of Additively Manufactured 316L Stainless Steels after 2 MeV Proton Irradiation: A Comparison Study between Planar and Cross-Sectional Micropillars

A micropillar compression study with two different techniques was performed on proton-irradiated additively manufactured (AM) 316L stainless steels. The sample was irradiated at 360 °C using 2 MeV protons to 1.8 average displacement per atom (dpa) in the near-surface region. A comparison study with mechanical test and microstructure characterization was made between planar and cross-sectional pillars prepared from the irradiated surface. While a 2 MeV proton irradiation creates a relatively flat damage zone up to 12 µm, the dpa gradient by a factor of 2 leads to significant dpa uncertainty along the pillar height direction for the conventional planar technique. Cross-sectional pillars can significantly reduce such dpa uncertainty. From one single sample, three cross-sectional pillars were able to show dpa-dependent hardening. Furthermore, post-compression transmission electron microscopy allows the determination of the deformation mechanism of individual micropillars. Cross-sectional micropillar compression can be used to study radiation-induced mechanical property changes with better resolution and less data fluctuation.

transmission electron microscopy↗

DOE OSTI2025

Primary and Low-Strain Creep Models for 9Cr Tempered Martensitic Steels Including the Effects of Irradiation Softening and High-Helium Re-Hardening

Primary and low-strain creep represents a very important integrity challenge to large, complex structures, like fusion reactors. Here, we develop a predictive empirical primary creep model for 9Cr tempered martensitic steels (TMS), relating the applied stress (σ) to strain (ε), time (t) and temperature (T). The most accurate model is based on the applied σ normalized by the steel’s T-dependent ultimate tensile stress (σo), σ/σo(T). The model, fit to 17 heats of 9Cr TMS, yielded a σ root mean square error (RMSE) of ≈±11 MPa. Notably, the model also provides robust predictions for all the other TMS, when calibrated only by the fusion candidate Eurofer97 database. The model was extended to explore two possible effects of neutron irradiation, which produces both displacements per atom (dpa) and helium (He in atomic parts per million, appm) damage. These effects, which have not been previously considered, include: (a) softening, as a function of dpa, at T > ≈400–450 °C, in low-He fission environments (<1 He/dpa); and (b) subsequent re-hardening in high-He (≥10 He/dpa) fusion first-wall environments. The irradiation effect models predict (a) accelerated primary creep due to irradiation softening; and (b) fully arrested creep due to high-He re-hardening.

Alam, Md Ershadul (ORCID:0000000345968026)↗

DOE OSTI2025

Comparison of Ion and Neutron Irradiations to 3 dpa at 500C in Ferritic-Martensitic Alloys

The growing global demand for energy will increasingly call upon advanced nuclear fission reactors to supply safe and reliable electricity. The structural and fuel cladding components of these reactors will be subject to extreme conditions of irradiation damage up to several hundred displacements per atom (dpa) at temperatures as high as 700°C. Ferritic-martensitic (F-M) steels are leading candidates for these challenging conditions due to their strength and dimensional stability under irradiation. In order to accelerate the process for evaluating F-M alloys, charged particles are increasingly being used to emulate neutron irradiations. Charged particle irradiations allow the possibility of conducting irradiation experiments within a shorter time period (i.e. at a rate up to 4 orders of magnitude faster) and with minimal radioactivation of the material, enabling lower cost and faster turnaround of post irradiation examination and analysis. However, the irradiation dose rate, damage cascade morphologies, and irradiation damage depth profiles all differ widely between protons, heavier ions, and neutrons. Currently, there is limited understanding of the significance of these physical differences and how they manifest in the irradiated microstructure and mechanical properties of F-M steels. The objective of this study is to evaluate charged particles as a surrogate for neutron irradiations in F-M alloys by assessing common irradiation conditions using Fe++ ions, protons, and neutrons. Keeping the temperature and dose consistent enables isolation of the effects of each irradiating particle and their respective dose rates and cascade morphologies.

Swenson, M.J.↗

DOE OSTI2025

Flux effects in precipitation under irradiation simulation of Fe-Cr alloys

Radiation-enhanced precipitation of Cr-rich α’ in irradiated Fe-Cr alloys, which results in hardening and embrittlement, depends on the irradiating particle and the displacement per atom (dpa) rate. Here, we utilize a Cahn-Hilliard phase-field based approach, that includes simple models for nucleation, irradiating particle and rate dependent radiation-enhanced diffusion and cascade mixing to simulate α’ evolution under neutrons, heavy ions, and electron irradiations. Different irradiating particles manifest very different cascade mixing efficiencies. The model was calibrated using neutron data. For cascade inducing neutron/heavy-ion dpa rates at 300 °C between 10-8 and 10-6 dpa/s the model predicts approximately constant number density, decreasing radius, decreasing α’ Cr composition, and lower α’ volume fraction. The model then predicts a dramatic transition to no α’ formation above approximately 10-5 dpa/s, while electron irradiation, with weak mixing, had little effect at dpa rates up to 10-3 dpa/s. These model predictions are consistent with experiments. We explain the results in terms of the flux dependence of the radiation enhanced diffusion, cascade mixing, and their ratio, which all vary significantly in relevant flux ranges for neutron and cascade inducing ion irradiations. These results show that both cascade mixing and radiation enhanced diffusion must be accounted for when attempting to emulate neutron-irradiation effects using accelerated ion irradiations.

Ke, Jia-Hong↗

DOE OSTI2026

PM-HIP Mechanical Data Archive

This is the mechanical testing data archive from a neutron irradiation campaign of nuclear structural alloys fabricated by powder metallurgy with hot isostatic pressing (PM-HIP). Data in this archive include uniaxial tensile testing data, fractography of selected tensile bars, and nanoindentation. The irradiation campaign was designed to facilitate a direct comparison of PM-HIP to conventional casting or forging. Five common nuclear structural alloys were included in the campaign: 316L stainless steel, SA508 pressure vessel steel, Grade 91 ferritic steel, and Ni-base alloys 625 and 690. Irradiations were carried out in the Advanced Test Reactor (ATR) at Idaho National Laboratory (INL) to target doses of 1 and 3 displacements per atom (dpa) at target temperatures of 300ºC and 400ºC through the DOE Office of Nuclear Energy, Nuclear Science User Facilities (NSUF) project 15-8242.

Wharry, Janelle↗

DOE OSTI2026

Fractography

This is the mechanical testing data archive from a neutron irradiation campaign of nuclear structural alloys fabricated by powder metallurgy with hot isostatic pressing (PM-HIP). Data in this archive include uniaxial tensile testing data, fractography of selected tensile bars, and nanoindentation. The irradiation campaign was designed to facilitate a direct comparison of PM-HIP to conventional casting or forging. Five common nuclear structural alloys were included in the campaign: 316L stainless steel, SA508 pressure vessel steel, Grade 91 ferritic steel, and Ni-base alloys 625 and 690. Irradiations were carried out in the Advanced Test Reactor (ATR) at Idaho National Laboratory (INL) to target doses of 1 and 3 displacements per atom (dpa) at target temperatures of 300ºC and 400ºC through the DOE Office of Nuclear Energy, Nuclear Science User Facilities (NSUF) project 15-8242.

Wharry, Janelle↗

DOE OSTI2026

G91-P_400C_1DPA_(ID-403)

This is the mechanical testing data archive from a neutron irradiation campaign of nuclear structural alloys fabricated by powder metallurgy with hot isostatic pressing (PM-HIP). Data in this archive include uniaxial tensile testing data, fractography of selected tensile bars, and nanoindentation. The irradiation campaign was designed to facilitate a direct comparison of PM-HIP to conventional casting or forging. Five common nuclear structural alloys were included in the campaign: 316L stainless steel, SA508 pressure vessel steel, Grade 91 ferritic steel, and Ni-base alloys 625 and 690. Irradiations were carried out in the Advanced Test Reactor (ATR) at Idaho National Laboratory (INL) to target doses of 1 and 3 displacements per atom (dpa) at target temperatures of 300ºC and 400ºC through the DOE Office of Nuclear Energy, Nuclear Science User Facilities (NSUF) project 15-8242.

Wharry, Janelle↗

DOE OSTI2026

G91-P_400C_3DPA_(ID-670)

This is the mechanical testing data archive from a neutron irradiation campaign of nuclear structural alloys fabricated by powder metallurgy with hot isostatic pressing (PM-HIP). Data in this archive include uniaxial tensile testing data, fractography of selected tensile bars, and nanoindentation. The irradiation campaign was designed to facilitate a direct comparison of PM-HIP to conventional casting or forging. Five common nuclear structural alloys were included in the campaign: 316L stainless steel, SA508 pressure vessel steel, Grade 91 ferritic steel, and Ni-base alloys 625 and 690. Irradiations were carried out in the Advanced Test Reactor (ATR) at Idaho National Laboratory (INL) to target doses of 1 and 3 displacements per atom (dpa) at target temperatures of 300ºC and 400ºC through the DOE Office of Nuclear Energy, Nuclear Science User Facilities (NSUF) project 15-8242.

Wharry, Janelle↗

DOE OSTI2026

Sample1

This is the mechanical testing data archive from a neutron irradiation campaign of nuclear structural alloys fabricated by powder metallurgy with hot isostatic pressing (PM-HIP). Data in this archive include uniaxial tensile testing data, fractography of selected tensile bars, and nanoindentation. The irradiation campaign was designed to facilitate a direct comparison of PM-HIP to conventional casting or forging. Five common nuclear structural alloys were included in the campaign: 316L stainless steel, SA508 pressure vessel steel, Grade 91 ferritic steel, and Ni-base alloys 625 and 690. Irradiations were carried out in the Advanced Test Reactor (ATR) at Idaho National Laboratory (INL) to target doses of 1 and 3 displacements per atom (dpa) at target temperatures of 300ºC and 400ºC through the DOE Office of Nuclear Energy, Nuclear Science User Facilities (NSUF) project 15-8242.

Wharry, Janelle↗

DOE OSTI2026

Nanoindentation

This is the mechanical testing data archive from a neutron irradiation campaign of nuclear structural alloys fabricated by powder metallurgy with hot isostatic pressing (PM-HIP). Data in this archive include uniaxial tensile testing data, fractography of selected tensile bars, and nanoindentation. The irradiation campaign was designed to facilitate a direct comparison of PM-HIP to conventional casting or forging. Five common nuclear structural alloys were included in the campaign: 316L stainless steel, SA508 pressure vessel steel, Grade 91 ferritic steel, and Ni-base alloys 625 and 690. Irradiations were carried out in the Advanced Test Reactor (ATR) at Idaho National Laboratory (INL) to target doses of 1 and 3 displacements per atom (dpa) at target temperatures of 300ºC and 400ºC through the DOE Office of Nuclear Energy, Nuclear Science User Facilities (NSUF) project 15-8242.

Wharry, Janelle↗

DOE OSTI2026

316-F_400C_3DPA_(ID-643)

This is the mechanical testing data archive from a neutron irradiation campaign of nuclear structural alloys fabricated by powder metallurgy with hot isostatic pressing (PM-HIP). Data in this archive include uniaxial tensile testing data, fractography of selected tensile bars, and nanoindentation. The irradiation campaign was designed to facilitate a direct comparison of PM-HIP to conventional casting or forging. Five common nuclear structural alloys were included in the campaign: 316L stainless steel, SA508 pressure vessel steel, Grade 91 ferritic steel, and Ni-base alloys 625 and 690. Irradiations were carried out in the Advanced Test Reactor (ATR) at Idaho National Laboratory (INL) to target doses of 1 and 3 displacements per atom (dpa) at target temperatures of 300ºC and 400ºC through the DOE Office of Nuclear Energy, Nuclear Science User Facilities (NSUF) project 15-8242.

Wharry, Janelle↗

DOE OSTI2026

316-P_400C_3DPA_(ID-464)

This is the mechanical testing data archive from a neutron irradiation campaign of nuclear structural alloys fabricated by powder metallurgy with hot isostatic pressing (PM-HIP). Data in this archive include uniaxial tensile testing data, fractography of selected tensile bars, and nanoindentation. The irradiation campaign was designed to facilitate a direct comparison of PM-HIP to conventional casting or forging. Five common nuclear structural alloys were included in the campaign: 316L stainless steel, SA508 pressure vessel steel, Grade 91 ferritic steel, and Ni-base alloys 625 and 690. Irradiations were carried out in the Advanced Test Reactor (ATR) at Idaho National Laboratory (INL) to target doses of 1 and 3 displacements per atom (dpa) at target temperatures of 300ºC and 400ºC through the DOE Office of Nuclear Energy, Nuclear Science User Facilities (NSUF) project 15-8242.

Wharry, Janelle↗

DOE OSTI2026

625-F_400C_1DPA_(ID-448)

This is the mechanical testing data archive from a neutron irradiation campaign of nuclear structural alloys fabricated by powder metallurgy with hot isostatic pressing (PM-HIP). Data in this archive include uniaxial tensile testing data, fractography of selected tensile bars, and nanoindentation. The irradiation campaign was designed to facilitate a direct comparison of PM-HIP to conventional casting or forging. Five common nuclear structural alloys were included in the campaign: 316L stainless steel, SA508 pressure vessel steel, Grade 91 ferritic steel, and Ni-base alloys 625 and 690. Irradiations were carried out in the Advanced Test Reactor (ATR) at Idaho National Laboratory (INL) to target doses of 1 and 3 displacements per atom (dpa) at target temperatures of 300ºC and 400ºC through the DOE Office of Nuclear Energy, Nuclear Science User Facilities (NSUF) project 15-8242.

Wharry, Janelle↗

DOE OSTI2026

625-F_400C_3DPA_(ID-615)

This is the mechanical testing data archive from a neutron irradiation campaign of nuclear structural alloys fabricated by powder metallurgy with hot isostatic pressing (PM-HIP). Data in this archive include uniaxial tensile testing data, fractography of selected tensile bars, and nanoindentation. The irradiation campaign was designed to facilitate a direct comparison of PM-HIP to conventional casting or forging. Five common nuclear structural alloys were included in the campaign: 316L stainless steel, SA508 pressure vessel steel, Grade 91 ferritic steel, and Ni-base alloys 625 and 690. Irradiations were carried out in the Advanced Test Reactor (ATR) at Idaho National Laboratory (INL) to target doses of 1 and 3 displacements per atom (dpa) at target temperatures of 300ºC and 400ºC through the DOE Office of Nuclear Energy, Nuclear Science User Facilities (NSUF) project 15-8242.

Wharry, Janelle↗