Results for “graphitization”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 271 records · Page 15
All sourcesNASA NTRSDOE OSTI
NASA NTRS1978

Effect of thermal exposure on lubricating properties of polyimide films and polyimide-bonded graphite fluoride films

The effect of thermal exposure on the weight loss, adherence, friction, and wear properties of polyimide films and polyimide bonded graphite fluoride films was investigated. Films bonded to 304 stainless steel or 440C-HT steel were thermally exposed at temperatures of 315 ,345, 370, or 400 C for 100 hours or more and then evaluated, using a pin-on-disk machine, at temperatures of 25, 315, or 345 C in atmospheres of dry or moist air. Polyimide films were brittle after thermal exposure. Polyimide bonded graphite fluoride films had adherence and gave low friction and wear results; thus, they appear to be good candidates for solid lubrication applications where long thermal soaks are prevalent.

Fusaro, R. L.↗
NASA NTRS1978

Lubrication and failure mechanisms of graphite fluoride films

An optical microscope, equipped with a vertical illuminator and two polaroid filters (one rotatable), was used to visually study 440C HT steel surfaces lubricated with rubbed graphite fluoride films. Friction and wear results were compared to visual observations as a function of sliding distance for films applied to three surface finishes - polished, sanded, and sand-blasted. In general, the lubricating process was one of initial deformation or wear of metallic asperities into flat plateaus and then the formation of thin, layer-like, dynamic films which sheared between the flats and eventually flowed through the contact area. Failure was due to depletion of the graphite fluoride with the subsequent formation of excessive powdery metallic debris that formed a heavy, powdery film on both the rider and disk surfaces.

Fusaro, R. L.↗
NASA NTRS1978

Temperature profile of graphite surface burning in a stream of oxygen

Using methods for the objective measurement of the spectrum line reversal temperature in burning gases, the temperature profile at a graphite surface burning in a stream of oxygen was measured. From the behavior of the reversal temperature, it follows that particles in long-lived, high-energy states are present in the burning gas, and these bring about an overexcitation of the atomic species emitting the reversal line. Qualitative measurements show that a temperature maximum occurs at the expected distance of 1-2 mm from the graphite surface.

Kisch, D.↗
NASA NTRS1978

A Comparison of the Lubricating Mechanisms of Graphite Fluoride and Molybdenum Disulfide Films

A microscopic study of 440C steel sliding surfaces lubricated by graphite fluoride or molybdenum disulfide solid lubricant rubbed films was conducted. The sliding surfaces, along with the friction, wear, and wear life were observed as a function of the number of sliding revolutions in three different atmospheres: moist air, dry air, or dry argon. In general, the lubricating mechanisms of the two solid lubricants were found to be relatively similar; that is, a dynamic, thin, layer-like film was formed between the two metallic surfaces. The mechanisms of failure were found to be somewhat different, however. Failure of MoS2 films was very dependent on atmospheric degradation, while that of graphite fluoride films was more dependent on flow of the lubricant film out of the contact zone.

Fusaro, R. L.↗
NASA NTRS1978

Design and Fabrication of a Ring-Stiffened Graphite-Epoxy Corrugated Cylindrical Shell

Design and fabrication of supplement test panels that represent key portions of the cylinder are described, as are supporting tests of coupons, sample joints, and stiffening ring elements. The cylindrical shell is a ring-stiffened, open corrugation design that uses T300/5208 graphite-epoxy tape as the basic material for the shell wall and stiffening rings. The test cylinder is designed to withstand bending loads producing the relatively low maximum load intensity in the shell wall of 1,576 N/cm. The resulting shell wall weight, including stiffening rings and fasteners, is 0.0156 kg/m. The shell weight achieved in the graphite-epoxy cylinder represents a weight saving of approximately 23 percent, compared to a comparable aluminum shell. A unique fabrication approach was used in which the cylinder wall was built in three flat segments, which were then wrapped to the cylindrical shape. Such an approach, made possible by the flexibility of the thin corrugated wall in a radial direction, proved to be a simple approach to building the test cylinder. Based on tooling and fabrication methods in this program, the projected costs of a production run of 100 units are reported.

Johnson, R., Jr.↗
NASA NTRS1979

Effects of graphite fiber stability on the properties of PMR polyimide composites

The effect of the stability of graphite fibers on composite properties after exposure in air at 600 F was investigated. Composites were fabricated from PMR-15 and PMR-2 monomer solutions, using HTS-2 and Celion 6000 graphite fibers as the reinforcement. The effect of long-term exposure in air at 600 F on composite weight loss and mechanical properties was determined. These composites exhibited a significantly increased lifetime at that temperature compared to composites fabricated from HTS fiber sold prior to 1975. The effect of the PMR-15 and PMR-II resin compositions on long-term composite performance at 600 F is also discussed.

Delvigs, P.↗
NASA NTRS1979

Feasibility Study of Graphite Epoxy Antenna for a Microwave Limb Sounder Radiometer (MLSR)

Results are presented of a feasibility study to design graphite epoxy antenna reflectors for a jet propulsion laboratory microwave limb sounder instrument (MLSR). Two general configurations of the offset elliptic parabolic reflectors are presented that will meet the requirements on geometry and reflector accuracy. The designs consist of sandwich construction for the primary reflectors, secondary reflector support structure and cross-tie members between reflector pairs. Graphite epoxy materials of 3 and 6 plies are used in the facesheets of the sandwich. An aluminum honeycomb is used for the core. A built-in adjustment system is proposed to reduce surface distortions during assembly. The manufacturing and environmental effects are expected to result in surface distortions less than .0015 inch and pointing errors less than .002 degree.

Source record↗
NASA NTRS1979

Advanced risk assessment of the effects of graphite fibers on electronic and electric equipment, phase 1

A model was developed to generate quantitative estimates of the risk associated with the release of graphite fibers during fires involving commercial aircraft constructed with graphite fiber composite materials. The model was used to estimate the risk associated with accidents at several U.S. airports. These results were then combined to provide an estimate of the total risk to the nation.

Pocinki, L. S.↗
NASA NTRS1978

A comparison of the lubricating mechanisms of graphite fluoride and molybdenum disulfide films

A microscopic study of 440 C steel sliding surfaces lubricated by graphite fluoride or molybdenum disulfide solid lubricant rubbed films was conducted. The sliding surfaces, along with the friction, wear, and wear life were observed as a function of the number of sliding revolutions in three different atmospheres: moist air (10,000 ppm H2O), dry air (less than 20 ppm H2O), or dry argon (less than 20 ppm H2O). In general, the lubricating mechanisms of the two solid lubricants were found to be relatively similar; that is, a dynamic, thin, layer-like film (which sheared on relative motion) was formed between the two metallic surfaces. The mechanisms of failure were found to be somewhat different, however. Failure of MoS2 films was very dependent on atmospheric degradation, while that of graphite fluoride films was more dependent on flow of the lubricant film out of the contact zone

Fusaro, R. L.↗
NASA NTRS1978

Glass matrix composites. I - Graphite fiber reinforced glass

An experimental program is described in which graphite fibers of Hercules HMS and HTS, Thornel 300, and Celanese DG-12 were used to reinforce, both uniaxially and biaxially, borosilicate pyrex glass. Composite flexural strength distribution, strength as a function of test temperature, fracture toughness and oxidative stability were determined and shown to be primarily a function of fiber type and the quality of fiber-matrix bond formed during composite fabrication. It is demonstrated that the graphite fiber reinforced glass system offers unique possibilities as a high performance structural material.

Prewo, K. M.↗
NASA NTRS1979

Effects of graphite fiber stability on the properties of PMR polyimide composites

Studies were performed to investigate the effect of the stability of graphite fibers on composite properties after exposure in air at 600 F. Composites were fabricated from PMR-15 and PMR-II monomer solutions, using HTS-2 and Celion 6000 graphite fibers as the reinforcement. The effect of long-term exposure in air at 600 F on composite weight loss and mechanical properties was determined. These composites exhibited a significantly increased lifetime at 600 F compared to composites fabricated from HTS fiber sold prior to 1975. The effect of the PMR-15 and PMR-II resin compositions on long-term composite performance at 600 F is also discussed.

Delvigs, P.↗
NASA NTRS1979

Electrical hazards posed by graphite fibers

The direct electrical resistance and the electrical contact resistance of graphite fibers released from both burned and unburned Fiberite T300/1034 composite were measured. The voltage at which arcing occurs due to fibers settling on electrical conductors was also determined. On the basis of results obtained, an assessment was made of the hazards posed by graphite fibers to electrical equipment.

Springer, G. S.↗
NASA NTRS1980

Examining graphite reinforcement in composites

Structure of graphite layers in composite parts can be checked by pyrolizing epoxy portion of composite samples. After 2-3 hours in nitrogen atmosphere at 540 C, only graphite fibers remain. These can be separated and checked for proper number, thickness, and orientation.

Sanders, R. E.↗
NASA NTRS1979

Aging problems in graphite phenolic nozzle liners

Age related cracks in the graphite phenolic linear and/or ATJ insert in several nine year old Altair IIA solid rocket nozzles were investigated and determined to be limited to a single lot of nozzles. Test results and photomicrographs of fracture surfaces are presented which establish that in the discrepant nozzles the bond between the graphite fibers and the phenolic resin was tenacious, resulting in a nearly homogenous behavior. These materials are shown to have a relatively weak resin - fiber bond and behave more like a released fiber composite. Lot qualification fiber directional tensile strength and the chemical composition of the two materials were comparable, indicating that standard acceptance testing could not have differentiated between the desirable and undesirable material. Review of processing records failed to reveal any cause for the difference in the aging characteristics.

Mccorkle, G. S.↗
NASA NTRS1980

The 737 graphite composite flight spoiler flight service evaluation

The flight service experience of 111 graphite-epoxy spoilers on 737 transport aircraft and related ground based enviromental exposure of graphite-epoxy material specimens is reported. Spoilers were installed on 28 aircraft representing seven major airlines operating throughout the world. Over 1,188,367 spoiler flight hours and 1,786,837 spoiler landings were accumulated by this fleet. Tests of removed spoilers and ground-based exposure specimens after the fifth year of service indicate modest changes in composite strength properties. Two incidents of trailing edge delamination with subsequent core corrosion were observed. Based on visual, ultrasonic, and destructive testing, there has been no evidence of moisture migration into the honeycomb core and no core corrosion.

Hoffman, D. J.↗
NASA NTRS1980

Properties of PMR Polyimide composites made with improved high strength graphite fibers

High strength, intermediate modulus graphite fibers were obtained from various commercial suppliers, and were used to fabricate PMR-15 and PMR-2 polyimide composites. The effects of the improved high strength graphite fibers on composite properties after exposure in air at 600 F were investigated. Two of the improved fibers were found to have an adverse effect on the long term performance of PMR composites. The influence of various factors such as fiber physical properties, surface morphology and chemical composition were also examined.

Vannucci, R. D.↗
NASA NTRS1980

Graphite-epoxy panel compression strength reduction due to local impact

A review of results from on-going research to investigate the effects of low-velocity impact on the compressive strength of graphite-epoxy structures is presented. Extensive tests have been conducted on sandwich beams, laminated plates and stiffened panels. Conditions for failures were investigated by impact tests on statically loaded test specimens. The effects of compression load intensity were such that lightly loaded graphite structures (such as aircraft secondary structure) were insensitive to impact damage. In more heavily loaded structures, (such as wing panels), however, appreciable reductions in compressive strength occurred. The implications of the tests for structural design are discussed by comparing panel masses for designs where ultimate strains have been reduced due to impact considerations with the masses of designs with higher ultimate strains. Finally, preliminary test data is presented to show the possibility of improvements in damage tolerance achievable by using an alternate matrix material.

Card, M. P.↗
NASA NTRS1980

Hybrid composites that retain graphite fibers on burning

A laboratory scale program was conducted to determine fiber release tendencies of graphite reinforced/resinous matrix composites currently used or projected for use in civil aircraft. In the event of an aircraft crash and burn situation, there is concern that graphite fibers will be released from the composites once the resin matrix is thermally decomposed. Hybridizing concepts aimed at preventing fiber release on burning were postulated and their effectiveness evaluated under fire, impact, and air flow during an aircraft crash.

House, E. E.↗