Results for “diffusion barrier” — Page 15

NASA NTRS2025

Thermochemical Stability of Ca2Yb8(SiO4)6O2 Apatite in Presence of Molten Calcium-Magnesium-AluminoSilicate (CMAS)

Thermochemical stability of ytterbium silicon oxyapatite Ca 2 Yb 8 (SiO 4 ) 6 O 2 (CYbS) in the presence of molten calcium-magnesium aluminosilicate (CMAS) has been investigated at elevated temperatures. CYbS apatite powder was synthesized from the constituent oxides via solid state reaction method. Hot pressed apatite substrates were exposed to molten CMAS at 1200, 1300, and 1400 °C for 1, 10, and 50 h. Development of phases in the interaction region of the heat-treated specimens was monitored using scanning electron microscopy, transmission electron microscopy, high angle annular dark field imaging, selected area electron diffraction and energy dispersive X-ray spectroscopy. Monoclinic cyclosilicate Ca 3 Yb 2 (Si 3 O 9 ) 2 formed from interaction of CYbS apatite with CaO in the CMAS melt at the apatite-CMAS reaction front and continued to nucleate and grow within the residual CMAS in diffusion couples annealed for 1-50 h at 1200 °C and those heat treated at 1300 °C for 1 h. Residual CMAS was Ca-depleted when cyclosilicate was present. Dendritic wollastonite CaSiO 3 was observed within the residual CMAS in couples annealed at 1200 and 1300 °C. Ingress of molten CMAS, because of its exponential decrease in viscosity, occurred through open pores and along the grain boundaries of the apatite substrates without any detectable chemical reaction at 1300 and 1400 °C. Results of this study indicate that Ca 2 Yb 8 (SiO 4 ) 6 O 2 apatite has the potential to mitigate the CMAS corrosion up to about 1200 °C but not at higher temperatures.

X-ray diffraction↗

NASA NTRS2015

Extreme Oxidative Durability of TBCs on Ti2AlC MAX Phases

APS and PS-PVD YSZ thermal barrier coatings, applied directly to oxidation resistant Ti2AlC substrates, were oxidized in interrupted furnace tests. Temperature was advanced in 50C intervals from 1100 to 1300C, each 500 h long with eleven cooling cycles. Damage only initiated on the APS coating at 1300C after 15 h, with complete delamination after 500 h. The PS-PVD coating survived all testing. Weight change and metallographic analyses indicate that the YSZ-Ti2AlC systems sustained alumina scale growth of 30-40 m. In comparison, widely used Pt-aluminide bondcoats on single crystal superalloy turbine blades exhibit TBC lives equivalent to alumina scale growth up to 7 m, equivalent to just 200 h at 1200C. It is demonstrated that 25x TBC life improvement (or 180C temperature increase) resulted from the close CTE match of Ti2AlC with those of alumina and YSZ.

protective coating↗

NASA NTRS2023

Combined Experimental and Modeling Study of the Interactions of Acid Gas with Common Spacecraft Surfaces for Fire Safety Applications

A fire in a spacecraft poses detrimental consequences and risks mission success in addition to crew safety. This is compounded during long-duration missions when the crew has limited options to recover from a fire. A common spacecraft fire concern is the smoldering of wire insulation, typically made from Polyvinyl chloride (PVC) or Polytetrafluoroethylene (PTFE). This creates acid gases such as Hydrogen Chloride (HCl), Hydrogen Fluoride (HF) and Hydrogen Cyanide (HCN). These poisonous gases are hazardous to the crew. They also interact with common surfaces within the spacecraft more than dominant combustion products such as CO2 and H2O. This makes them more difficult to track for potential fire detection techniques, or for postfire clean-up. It is imperative to be able to understand and predict the fate of these poisonous species in a microgravity environment in order to design a safe vehicle. HCl interacts with a number of materials inside a spacecraft. Primary among these materials is aluminum, which is abundantly used due to its strong and light weight nature. Aluminum has a natural oxide layer that protects it from corrosion but is typically treated to enhance this oxide layer. Among these treatments is a chromate conversion coating (CCC), which provides a thin enough protective oxide layer to still conduct electricity, and a traditional anodized material that has a thicker oxide layer that does not conduct electricity. Nomex is another common material found inside a spacecraft. It is a flame-resistant woven polymer that is related to nylon. This commercially available material is used for cargo storage bags and as a fire barrier. Physics-based models were developed to predict the uptake of HCl by these materials. The ultimate objective of these models is to predict the fate of HCl within the spacecraft so that sensors can be placed in meaningful locations in future missions based on the model predictions. To support these modeling efforts, experiments were performed in a cast acrylic test cell that measured the difference between the inlet and outlet concentration of HCl after inserting a sample rod of the test material. Different uptake capacities were realized for each type of sample tested. A computational fluid dynamics model (CFD) model of the reactor was then constructed that used a one-step global reaction rate with calibratable reaction (or kinetic) constants. These constants were calibrated to match the HCl uptake on the CCC aluminum samples, and the same kinetic constants were then tested for the stock and anodized aluminum samples. Model predictions matched the experimental data for the stock aluminum, and to a much lesser extent, the anodized aluminum. The model was additionally validated at different flow rates, sample surface areas, and inlet concentrations, and showed good agreement for all stock and CCC samples. The model did not accurately predict the HCl uptake in the anodized samples compared to the other two types of aluminum. Adjusting the kinetic constants and transport properties did little to improve the prediction. X-Ray Photoelectron Spectroscopy (XPS) was used to determine that the oxide layer thickness of anodized aluminum is approximately 5,000 nm, compared to 250 nm for CCC and 50 nm for stock. XPS also revealed presence of chlorine further down in the aluminum oxide layer in anodized samples than CCC and stock samples after the samples were saturated with HCl, indicating that accounting for diffusion of HCl into the oxide layer is important for accurate prediction of HCl uptake onto anodized aluminum. Consequently, a multi-scale model was developed and tested. First, a single pore inside the anodized aluminum oxide layer was modeled and is referred to as the pore-scale model. In this model, HCl diffused through the pore and reacted with the aluminum oxide pore wall to create aluminum chloride. The sample was then saturated when the mass transfer resistance through the growing aluminum chloride layer became too large for the HCl to reach the aluminum oxide wall and continue the reaction. This pore-scale model was coupled to the reactor-scale model using a concentration-dependent diffusion coefficient, resulting in much more accurate predictions (approximately half the sum square error of the aforementioned reactor-scale model that produced good agreement for stock and CCC) for a variety of operating conditions. The amount of water vapor or relative humidity (RH) in the flow during a reactor experiment was determined to influence HCl uptake. Experiments were performed to understand the interaction of gaseous HCl with aluminum surfaces in the presence of water vapor. The results show that increasing levels of RH increased the capacity of aluminum to adsorb HCl but decreased the capacity of Nomex to uptake HCl. A series of tests were performed on individual aluminum samples after they had been saturated with a fixed concentration of HCl in dry air conditions with the goal of determining how their HCl uptake capacity changes after various treatments with water relative to the original saturation tests. HCl-saturated aluminum samples subjected to a second dry air flow at the same HCl concentration as the original test had an uptake of 23.5% of the original sample with no treatment in between. Saturated aluminum samples subjected to an air flow with a RH of 90% in between tests had an uptake of 35.6% of the original. Saturated aluminum samples submerged in distilled water for 12 hours in between tests had an uptake of 82.2% of the original sample. Previously saturated aluminum tested with HCl and a 50% RH air flow resulted in similar uptake characteristics in multiple repeated tests. The experiments show the profound effect water vapor has on HCl uptake onto aluminum surfaces. In the samples subjected to water vapor or liquid water, capillary condensation and capillary diffusion alters the transport of HCl significantly. A model was proposed that developed a relationship between RH and the coefficient of HCl diffusion in aluminum chloride. This produced an “S-shaped” curve with diffusion coefficient as a function of RH, with 45% RH represented as the point where the diffusion coefficient is halfway between no water saturation and 100% water saturation in the aluminum chloride product layer. No difference in uptake characteristics for the experiment or model were realized between 50% and 62% RH. The results from the large-scale microgravity experiment, Saffire, are discussed as they pertain to the fate of HCl throughout a spacecraft. HCl was released, both as a standalone event, and in concurrence with the burning of a structured cloth. These events only produced a small response in the far field HCl sensor, while a PMMA burn that did not produce HCl had a significantly greater response. A ground-based large-scale facility was constructed to flow acid gas at the scale and configuration realized in the Saffire experiments. A CFD model of this duct was constructed to test kinetic parameters developed in this work at a larger scale and different geometric configuration and to predict the results of the large-scale facility. The models developed in this work were used to interpret the results of the microgravity tests and lead the discussion on what further experiments and models are needed in order to predict the fate of acid gas in a spacecraft environment. To summarize, the major contributions of this work are as follows: the capacity to uptake HCl, with and without the presence of water vapor, was measured for a variety of real spacecraft surfaces. Several different models (single reactor-scale, multiscale, spacecraft-scale) were developed and with the aid of modeling, the rate of uptake for those surfaces was also predicted and validated. The kinetic parameters determined from the small-scale reactor experiments and models were used to predict large-scale and microgravity tests. Conclusions from this research will be used in the design of spacecraft vehicles and large-scale microgravity fire safety experiments. The models built by this work will aid designers in sensor placement and could be used to predict acid gas transport from fires in partial gravity, as would be seen in Lunar and Martian habitats.

fire safety↗

NASA NTRS2000

TPS Materials and Costs for Future Reusable Launch Vehicles

There is considerable interest in developing new reusable launch vehicles (RLVs) for reducing the cost of transporting payload to and from orbit. This work reviews thirteen candidate thermal protection system (TPS) options currently available for RLVs. It is useful to begin with the current Shuttle TPS layout as a reference. The nose cap and wing leading edge , which reach the highest temperatures, are made of reinforced carbon-carbon (RCC) that is protected from oxidation by an external coating (about 0.020" thick) of silicon-carbide. Most of the windward surface is 9 lb/cubic ft ceramic tiles (LI-900) with a thin (about 0.012") coating of Reaction Cured Glass (RCG). The leeward side of the vehicle is covered largely by AFRSI, a quilted ceramic blanket, and FRSI, a polyamide felt. These four materials can be considered first generation reusable TPS. Since the time of the Shuttle design, considerable progress has been made advancing TPS technologies in terms of thermal performance, robustness, and cost. For each of the major systems, a second generation ceramic TPS has been developed, tested, and characterized. Metallic-based systems have also been developed. For applications requiring RCC in the past, advanced carbon-carbon (ACC) is now available. This material has better mechanical properties, somewhat higher temperature capability to 2900F and greatly increased oxidation resistance. New carbon fiber reinforced silicon-carbide matrix composites (C/SiCs) have shown additional improvement in properties over ACC with use temperatures to 3000F and above. For rigid tiles, NASA Ames has made two significant advancements. The first is a tile substrate called Alumina Enhanced Thermal Barrier, or AETB, that incorporates alumina fibers for improved dimensional stability at high temperatures, to 2600F and above. This material can be made to densities as low as 8 lb/cubic ft. The second is a coating preparation called Toughened Uni-piece Fibrous Insulation, or TUFT, that penetrates about 0.1 in. into the tile substrate. The resulting composite, with a functionally gradient density near the surface, provides orders of magnitude increased damage resistance compared with RCG coated LI-900, with only a small weight increase. The TPS that combines these two developments is called AETB-8/TUFI and has been adopted for high damage areas on the Shuttles. Two notable developments have occur-red in flexible ceramic blanket technology. The first is aluminoborosilicate-based fibers with use temperatures of 2200F and above," in comparison to quartz and silica fiber used in AFRSI which have multi-use temperature limits of 1200 to 1400F. Blankets incorporating these new high temperature fibers are referred to as AFRSI-HT. The second is an integral weaving techniques that produces a fluted core blanket with a smoother surface and greater resistance to aero-acoustic noise, to levels as high as 170 dB. This Ames innovation is called Tailorable Advanced Blanket Insulation, or TABI. Finally, for felt-based TPS, Boeing is developing Polybenzimidazole Blanket Insulation, or PBI, with a multi-use temperature limit of 1000F and above, in contrast to Shuttle FRSI which has a multi-use temperature limit of about 700F. 1.6 NASA Langley and BF Goodrich (formerly Rohr Corp.) have led the development of metallic-based TPS. This activity uses essentially three approaches: metallic tiles which encase a fibrous ceramic batting in a box fabricated largely from metallic honeycombs, typically Nickel based alloys; metallic honeycomb sheets, made of Nickel-based alloys, incorporating a fibrous back-side insulation encapsulated in a metallic foil bag, providing reduced weight; and metallic multi-wall, which is comprised of dimpled Titanium metal sheets, which are stacked and then diffusion bonded at contact points to form the TPS. The Nickel-based systems can be used up to temperatures of about 1800F, and the Titanium system to about 100F. These thirteen TPS materials have pros and cons to their usage in terms of temperature capability, weight, initial cost, and maintenance. Carbon-carbon and C/SiC systems have the highest temperature capability but are relatively expensive and heavy, requiring significant time, expertise, and costly facilities and tools for design and fabrication. Second generation ceramic tiles are relatively light, durable, simple to fabricate and easy to install; however, waterproofing is a concern. Blankets and felts are light, simple, inexpensive, and easy to install over curved vehicle surfaces, but durability and waterproofing are concerns. Metallics are robust and appear to have eliminated waterproofing, but they tend to be heavy and relatively expensive, requiring costly facilities and tools. If thin metal sheets are used to reduce weights, then issues arise from possible metal fatigue and corrosion caused by thermal cycling, pressure oscillations, and environmental exposure. For application to future RLVs, system analyses show that a significant component of the vehicle life cycle cost is from the TPS; however, it is difficult to quantify and to compare the potential savings of advanced systems without performing full vehicle designs using each of the different options. Because this entails a considerable effort and also tends to submerge TPS cost impacts under unrelated vehicle design assumptions, there is a clear need for a simpler quantitative method to evaluate the cost impact of different TPS options. To this end, this work introduces a TPS life-cycle cost parameter which is easily computed and applicable to generic RLVs.

Rasky, Dan J.↗

NASA NTRS2014

High Efficiency Centrifugal Compressor for Rotorcraft Applications

The report "High Efficiency Centrifugal Compressor for Rotorcraft Applications" documents the work conducted at UTRC under the NRA Contract NNC08CB03C, with cost share 2/3 NASA, and 1/3 UTRC, that has been extended to 4.5 years. The purpose of this effort was to identify key technical barriers to advancing the state-of-the-art of small centrifugal compressor stages; to delineate the measurements required to provide insight into the flow physics of the technical barriers; to design, fabricate, install, and test a state-of-the-art research compressor that is representative of the rear stage of an axial-centrifugal aero-engine; and to acquire detailed aerodynamic performance and research quality data to clarify flow physics and to establish detailed data sets for future application. The design activity centered on meeting the goal set outlined in the NASA solicitation-the design target was to increase efficiency at higher work factor, while also reducing the maximum diameter of the stage. To fit within the existing Small Engine Components Test Facility at NASA Glenn Research Center (GRC) and to facilitate component re-use, certain key design parameters were fixed by UTRC, including impeller tip diameter, impeller rotational speed, and impeller inlet hub and shroud radii. This report describes the design effort of the High Efficiency Centrifugal Compressor stage (HECC) and delineation of measurements, fabrication of the compressor, and the initial tests that were performed. A new High-Efficiency Centrifugal Compressor stage with a very challenging reduction in radius ratio was successfully designed, fabricated and installed at GRC. The testing was successful, with no mechanical problems and the running clearances were achieved without impeller rubs. Overall, measured pressure ratio of 4.68, work factor of 0.81, and at design exit corrected flow rate of 3 lbm/s met the target requirements. Polytropic efficiency of 85.5 percent and stall margin of 7.5 percent were measured at design flow rate and speed. The measured efficiency and stall margin were lower than pre-test CFD predictions by 2.4 percentage points (pt) and 4.5 pt, respectively. Initial impressions from the experimental data indicated that the loss in the efficiency and stall margin can be attributed to a design shortfall in the impeller. However, detailed investigation of experimental data and post-test CFD simulations of higher fidelity than pre-test CFD, and in particular the unsteady CFD simulations and the assessment with a wider range of turbulence models, have indicated that the loss in efficiency is most likely due to the impact of unfavorable unsteady impeller/diffuser interactions induced by diffuser vanes, an impeller/diffuser corrected flow-rate mismatch (and associated incidence levels), and, potentially, flow separation in the radial-to-axial bend. An experimental program with a vaneless diffuser is recommended to evaluate this observation. A subsequent redesign of the diffuser (and the radial-to-axial bend) is also recommended. The diffuser needs to be redesigned to eliminate the mismatching of the impeller and the diffuser, targeting a slightly higher flow capacity. Furthermore, diffuser vanes need to be adjusted to align the incidence angles, to optimize the splitter vane location (both radially and circumferentially), and to minimize the unsteady interactions with the impeller. The radial-to-axial bend needs to be redesigned to eliminate, or at least minimize, the flow separation at the inner wall, and its impact on the flow in the diffuser upstream. Lessons were also learned in terms of CFD methodology and the importance of unsteady CFD simulations for centrifugal compressors was highlighted. Inconsistencies in the implementation of a widely used two-equation turbulence model were identified and corrections are recommended. It was also observed that unsteady simulations for centrifugal compressors require significantly longer integration times than what is current practice in industry.

Gorazd Medic↗

NASA NTRS2014

High Efficiency Centrifugal Compressor for Rotorcraft Applications

The report "High Efficiency Centrifugal Compressor for Rotorcraft Applications" documents the work conducted at UTRC under the NRA Contract NNC08CB03C, with cost share 2/3 NASA, and 1/3 UTRC, that has been extended to 4.5 years. The purpose of this effort was to identify key technical barriers to advancing the state-of-the-art of small centrifugal compressor stages; to delineate the measurements required to provide insight into the flow physics of the technical barriers; to design, fabricate, install, and test a state-of-the-art research compressor that is representative of the rear stage of an axial-centrifugal aero-engine; and to acquire detailed aerodynamic performance and research quality data to clarify flow physics and to establish detailed data sets for future application. The design activity centered on meeting the goal set outlined in the NASA solicitation-the design target was to increase efficiency at higher work factor, while also reducing the maximum diameter of the stage. To fit within the existing Small Engine Components Test Facility at NASA Glenn Research Center (GRC) and to facilitate component re-use, certain key design parameters were fixed by UTRC, including impeller tip diameter, impeller rotational speed, and impeller inlet hub and shroud radii. This report describes the design effort of the High Efficiency Centrifugal Compressor stage (HECC) and delineation of measurements, fabrication of the compressor, and the initial tests that were performed. A new High-Efficiency Centrifugal Compressor stage with a very challenging reduction in radius ratio was successfully designed, fabricated and installed at GRC. The testing was successful, with no mechanical problems and the running clearances were achieved without impeller rubs. Overall, measured pressure ratio of 4.68, work factor of 0.81, and at design exit corrected flow rate of 3 lbm/s met the target requirements. Polytropic efficiency of 85.5 percent and stall margin of 7.5 percent were measured at design flow rate and speed. The measured efficiency and stall margin were lower than pre-test CFD predictions by 2.4 percentage points (pt) and 4.5 pt, respectively. Initial impressions from the experimental data indicated that the loss in the efficiency and stall margin can be attributed to a design shortfall in the impeller. However, detailed investigation of experimental data and post-test CFD simulations of higher fidelity than pre-test CFD, and in particular the unsteady CFD simulations and the assessment with a wider range of turbulence models, have indicated that the loss in efficiency is most likely due to the impact of unfavorable unsteady impeller/diffuser interactions induced by diffuser vanes, an impeller/diffuser corrected flow-rate mismatch (and associated incidence levels), and, potentially, flow separation in the radial-to-axial bend. An experimental program with a vaneless diffuser is recommended to evaluate this observation. A subsequent redesign of the diffuser (and the radial-to-axial bend) is also recommended. The diffuser needs to be redesigned to eliminate the mismatching of the impeller and the diffuser, targeting a slightly higher flow capacity. Furthermore, diffuser vanes need to be adjusted to align the incidence angles, to optimize the splitter vane location (both radially and circumferentially), and to minimize the unsteady interactions with the impeller. The radial-to-axial bend needs to be redesigned to eliminate, or at least minimize, the flow separation at the inner wall, and its impact on the flow in the diffuser upstream. Lessons were also learned in terms of CFD methodology and the importance of unsteady CFD simulations for centrifugal compressors was highlighted. Inconsistencies in the implementation of a widely used two-equation turbulence model were identified and corrections are recommended. It was also observed that unsteady simulations for centrifugal compressors require significantly longer integration times than what is current practice in industry.

Gorazd Medic↗

NASA NTRS2017

High Efficiency Centrifugal Compressor for Rotorcraft Applications

The report "High Efficiency Centrifugal Compressor for Rotorcraft Applications" documents the work conducted at UTRC under the NRA Contract NNC08CB03C, with cost share 2/3 NASA, and 1/3 UTRC, that has been extended to 4.5 years. The purpose of this effort was to identify key technical barriers to advancing the state-of-the-art of small centrifugal compressor stages; to delineate the measurements required to provide insight into the flow physics of the technical barriers; to design, fabricate, install, and test a state-of-the-art research compressor that is representative of the rear stage of an axial-centrifugal aero-engine; and to acquire detailed aerodynamic performance and research quality data to clarify flow physics and to establish detailed data sets for future application. The design activity centered on meeting the goal set outlined in the NASA solicitation-the design target was to increase efficiency at higher work factor, while also reducing the maximum diameter of the stage. To fit within the existing Small Engine Components Test Facility at NASA Glenn Research Center (GRC) and to facilitate component re-use, certain key design parameters were fixed by UTRC, including impeller tip diameter, impeller rotational speed, and impeller inlet hub and shroud radii. This report describes the design effort of the High Efficiency Centrifugal Compressor stage (HECC) and delineation of measurements, fabrication of the compressor, and the initial tests that were performed. A new High-Efficiency Centrifugal Compressor stage with a very challenging reduction in radius ratio was successfully designed, fabricated and installed at GRC. The testing was successful, with no mechanical problems and the running clearances were achieved without impeller rubs. Overall, measured pressure ratio of 4.68, work factor of 0.81, and at design exit corrected flow rate of 3 lbm/s met the target requirements. Polytropic efficiency of 85.5 percent and stall margin of 7.5 percent were measured at design flow rate and speed. The measured efficiency and stall margin were lower than pre-test CFD predictions by 2.4 percentage points (pt) and 4.5 pt, respectively. Initial impressions from the experimental data indicated that the loss in the efficiency and stall margin can be attributed to a design shortfall in the impeller. However, detailed investigation of experimental data and post-test CFD simulations of higher fidelity than pre-test CFD, and in particular the unsteady CFD simulations and the assessment with a wider range of turbulence models, have indicated that the loss in efficiency is most likely due to the impact of unfavorable unsteady impeller/diffuser interactions induced by diffuser vanes, an impeller/diffuser corrected flow-rate mismatch (and associated incidence levels), and, potentially, flow separation in the radial-to-axial bend. An experimental program with a vaneless diffuser is recommended to evaluate this observation. A subsequent redesign of the diffuser (and the radial-to-axial bend) is also recommended. The diffuser needs to be redesigned to eliminate the mismatching of the impeller and the diffuser, targeting a slightly higher flow capacity. Furthermore, diffuser vanes need to be adjusted to align the incidence angles, to optimize the splitter vane location (both radially and circumferentially), and to minimize the unsteady interactions with the impeller. The radial-to-axial bend needs to be redesigned to eliminate, or at least minimize, the flow separation at the inner wall, and its impact on the flow in the diffuser upstream. Lessons were also learned in terms of CFD methodology and the importance of unsteady CFD simulations for centrifugal compressors was highlighted. Inconsistencies in the implementation of a widely used two-equation turbulence model were identified and corrections are recommended. It was also observed that unsteady simulations for centrifugal compressors require significantly longer integration times than what is current practice in industry.

Centrifugal compressor↗