Low-cycle fatigue evaluation for regeneratively cooled panels
Design data for regeneratively cooled panels from low cycle fatigue evaluation of Hastelloy X and Inconel 625 sheet and sandwich panel specimens
Richard, C. E.↗
SEARCH · Engineering Papers
Results for “Inconel”
Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.
Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.
Noncontaminating technique for making holes in existing process systems
Technique is developed for making cleanly-contoured holes in assembled process systems without introducing chips or other contaminants into system. Technique uses portable equipment and does not require dismantling of system. Method was tested on Inconel, stainless steel, ASTMA-53, and Hastelloy X in all positions.
Hecker, T. P.↗
Stress corrosion cracking of several high strength ferrous and nickel alloys
The stress corrosion cracking resistance of several high strength ferrous and nickel base alloys has been determined in a sodium chloride solution. Results indicate that under these test conditions Multiphase MP35N, Unitemp L605, Inconel 718, Carpenter 20Cb and 20Cb-3 are highly resistant to stress corrosion cracking. AISI 410 and 431 stainless steels, 18 Ni maraging steel (250 grade) and AISI 4130 steel are susceptible to stress corrosion cracking under some conditions.
Nelson, E. E.↗
A technique for making clean holes in metallic piping and components
Testing was conducted to develop a technique of providing clean holes in process piping or in a metal surface accessible from one side only without disassembling the system. The method was performed on sample pieces of piping and worked successfully with no contaminants being found on the inside of the pipe. The materials tested were Inconel 600, 304 stainless steel, Hastelloy X, and ASTM-A53 black steel. The technique was developed such that it could be done in the field with hand-held power tools and a portable tungsten inert gas welding machine.
Hecker, T. P.↗
Cryogenic glass-filament-wound tank evaluation
High-pressure glass-filament-wound fluid storage vessels with thin aluminum liners were designed, fabricated, and tested at ambient and cryogenic temperatures which demonstrated the feasibility of producing such vessels as well as high performance and light weight. Significant developments and advancements were made in solving problems associated with the thin metal liners in the tanks, including liner bonding to the overwrap and high strain magnification at the vessel polar bosses. The vessels had very high burst strengths, and failed in cyclic fatigue tests by local liner fracture and leakage without structural failure of the composite tank wall. The weight of the tanks was only 40 to 55% of comparable 2219-T87 aluminum and Inconel 718 tanks.
Morris, E. E.↗
Effect of cryogenic irradiation on NERVA structural alloys
Several alloys (Hastelloy X, AISI 347, A-286 bolts, Inconel 718, Al 7039-T63 and Ti-5Al-2.5Sn ELI) were irradiated in liquid nitrogen (140 R) to neutron fluences between 10 to the 17th power and 10 to the 19th power nvt (E greater than 1.0 Mev). After irradiation, tensile properties were obtained in liquid nitrogen without permitting any warmup except for some specimens which were annealed at 540 R. The usual trend of radiation damage typical for materials irradiated at and above room temperature was observed, such as an increase in strength and decrease in ductility. However, the damage at 140 R was greater because this temperature prevented the annealing of radiation-induced defects which occurs above 140 R.
Dixon, C. E.↗
NASA-EPA automotive thermal reactor technology program
The status of the NASA-EPA automotive thermal reactor technology program is summarized. This program is concerned primarily with materials evaluation, reactor design, and combustion kinetics. From engine dynamometer tests of candidate metals and coatings, two ferritic iron alloys (GE 1541 and Armco 18-SR) and a nickel-base alloy (Inconel 601) offer promise for reactor use. None of the coatings evaluated warrant further consideration. Development studies on a ceramic thermal reactor appear promising based on initial vehicle road tests. A chemical kinetic study has shown that gas temperatures of at least 900 K to 1000 K are required for the effective cleanup of carbon monoxide and hydrocarbons, but that higher temperatures require shorter combustion times and thus may permit smaller reactors.
Blankenship, C. P.↗
Spin test of turbine rotor
Experimental data are presented for the tangential and radial stresses in the disks of the 36,000 horsepower, 4000 rpm turbine for the M-1 engine oxidizer turbopump. The two-stage Curtis turbine is a special light-weight design utilizing thin conical disks with hollow sheet metal blades attached by electron-beam welding techniques. The turbine was fabricated from Inconel 718, a nickel-chromium alloy. The stresses were obtained by strain-gage measurements using a slip-ring assembly to transmit the electrical signals. Measurements were made at different rotative speeds and different thermal loads. In addition to presenting test data, the report describes test equipment, design of associated hardware, test procedures, instrumentation, and tests for the selection and calibration of strain gages.
Vavra, M. H.↗
NERVA materials development
Materials development topics include: development of analysis techniques to adjust heterogeneous data; determination of thermal conductivity for AISI 347 stainless steel and elastic moduli and Poisson's ratio for Inconel 718 and Ti 5Al-2.5Sn; embrittlement effects of 1400 psi gaseous hydrogen for alloy 718 and Ti 5Al-2.5Sn; cryogenic radiation damage of Ti 5Al-2.5Sn; and evaluation of prepreg, impregnation, and fabric materials for optimum fibrous graphite properties. Component support topics include: tensile design allowable development of Ti 5Al-2.5Sn for turbopump applications; evaluation of fatigue, fracture toughness, and stress corrosion properties of AA 7039-T63 for pressure vessel applications; development of AISI 347 sheet tensile and creep properties for nozzle applications; evaluation of orbital weld techniques for aluminum line fabrication; material selection of shield materials; development of high load friction and wear properties of hard chrome/gold plate combinations; and evaluation of weld processes for NASS duct coolant channel fabrication.
Mandell, B.↗
Ultra high vacuum adhesion testing of NERVA engine materials
The primary objective of this research program was to determine the effects of surface cleaning and deliberate gaseous contamination on the adhesion behavior of selected candidate materials for use in the NERVA nuclear rocket engine program. Using a torsion balance technique, the relationship between the normal compressive load applied to crossed rod samples and the resultant contact resistance was used to ascertain the extent of adhesion under each set of experimental conditions. In addition to an evaluation of the static adhesion behavior of selected materials combinations, the experimental apparatus was modified to permit a similar investigation relating to the effects of specific tangential displacements of the sample wires, i.e., their sliding friction behavior. During the course of this subcontract, the materials combinations 440 C vs. 440 C. pyrographite vs ZTA graphite, Nbc (graphite) vs. Nbc (graphite), and Electrolize Inconel 718 vs. Au electroplated 302 S/S were evaluated.
Source record↗
Metal-metal laminar composites for high temperature applications
A study was conducted to obtain indications of the potentialities of laminar metal-metal composites for elevated temperature use. Most of the composites consisted of multiple layers or laminae of tungsten alternated with laminae of Nichrome V, a ductile, weaker but oxidation-resistant alloy. Composites with 50 volume percent of each phase were tested in tension and stress rupture at temperatures of 871 and 1093 C (1600 and 2000 F) and in impact at 23 and 524 C (73 and 975 F). A tension and a short time stress-rupture test was conducted on specimens of 77 v/o W-Re-Hf-C/23 v/o Inconel alloy 600 at 1093 C (2000 F).
Hoffman, C. A.↗
Thermal conductivity, electrical resistivity, and thermopower of aerospace alloys from 4 to 300 K.
Measurement of thermal conductivity, electrical resistivity, and thermopower for several aerospace alloys: titanium alloy A110-AT, aluminum alloy 7039, Inconel 718, and Hastelloy X. Tables and graphs of the measured properties and Lorenz ratio are presented over the range from 4 to 300 K. Comparisons to other measurements and theoretical analysis of the data are included. The uncertainties of the property data are estimated as 0.7 to 2.5% for thermal conductivity, 0.25% in electrical resistivity, and about 0.1 microvolt/K in thermopower.
Hust, J. G.↗
Brazing of refractory, superalloy, and composite materials for Space Shuttle applications.
Research work concerning the metallic portion of the shuttle-orbiter heat shield (expected to experience temperatures up to 2500 F) is described. The five metals being evaluated are TD-Ni-Cr, Cb-C129Y, Cb752, Hayes 188, and Inconel 625. Brazing techniques whereby pairs of these materials are joined into thin-membered assemblies for heat shield applications are described. Results obtained with the vacuum-furnace brazing process are examined. In addition, the use of brazed aluminum-boron metal-matrix-contoured composite structures for heat shield applications is evaluated.
Beuyukian, C. S.↗
The effect of hot salt on the mechanical properties of several superalloys
The effect of sodium chloride on unstressed, transverse, tensile, metal specimens at elevated temperatures was determined. Results indicate that the mechanical properties of Inconel 718, Rene 41, titanium base alloy 13V-11Cr-3Al, Hastelloy X, HS25 (L605), HS188, and TDNiCr suffer degradation in tensile strength and ductility due to hot salt exposure.
Nelson, E. E.↗
Time-dependent edge-notch sensitivity of oxide and gamma prime dispersion strengthened sheet materials at 1000 to 1800 F (538 - 982 C)
Research was carried out to determine whether an oxide dispersion hardened alloy, TD-Ni, Cr, and low volume fraction gamma prime strengthened nickel-base alloy, Modified Waspaloy, were susceptible to time-dependent edge-notch sensitivity. The results were evaluated in terms of the mechanical characteristics of the alloys and the dislocation motion mechanisms operative. As far as could be determined, the results of the investigation were consistent with the following important concepts developed for Waspaloy and Inconel 718: (1) Time-dependent edge-notch sensitivity occurs when notched specimens are loaded below the approximate 0.2 percent smooth specimen offset yield strength and when data from smooth specimens indicate that small amounts of creep consume large rupture life fractions. (2) When precipitate particles are sheared by dislocations, the deformation is localized and time-dependent notch sensitivity occurs. When dislocations by-pass precipitate particles the deformation is homogeneous. Under these conditions, no time-dependent notch sensitivity has been observed.
Wilson, D. J.↗
Hydrogen adsorption and diffusion, and subcritical-crack growth in high strength steels and nickel base alloys
Embrittlement, or the enhancement of crack growth by gaseous hydrogen in high strength alloys, is of primary interest in selecting alloys for various components in the space shuttle. Embrittlement is known to occur at hydrogen gas pressures ranging from fractions to several hundred atmospheres, and is most severe in the case of martensitic high strength steels. Kinetic information on subcritical crack growth in gaseous hydrogen is sparse at this time. Corroborative information on hydrogen adsorption and diffusion is inadequate to permit a clear determination of the rate controlling process and possible mechanism in hydrogen enhanced crack growth, and for estimating behavior over a range of temperatures and pressures. Therefore, coordinated studies of the kinetics of crack growth, and adsorption and diffusion of hydrogen, using identical materials, have been initiated. Comparable conditions of temperature and pressure will be used in the chemical and mechanical experiments. Inconel 718 alloy and 18Ni(200) maraging steel have been selected for these studies. Results from these studies are expected to provide not only a better understanding of the gaseous hydrogen embrittlement phenomenon itself, but also fundamental information on hydrogen adsorption and diffusion, and crack growth information that can be used directly for design.
Wei, R. P.↗
Glass Fiber Reinforced Metal Pressure Vessel Design Guide
The Engineering Guide presents curves and general equations for safelife design of lightweight glass fiber reinforced (GFR) metal pressure vessels operating under anticipated Space Shuttle service conditions. The high composite vessel weight efficiency is shown to be relatively insensitive to shape, providing increased flexibility to designers establishing spacecraft configurations. Spheres, oblate speroids, and cylinders constructed of GFR Inconel X-750, 2219-T62 aluminum, and cryoformed 301 stainless steel are covered; design parameters and performance efficiencies for each configuration are compared at ambient and cryogenic temperature for an operating pressure range of 690 to 2760 N/sq cm (1000 to 4000 psi). Design variables are presented as a function of metal shell operating to sizing (proof) stress ratios for use with fracture mechanics data generated under a separate task of this program.
Landes, R. E.↗
Space nuclear system expansion joints
The engineering, design, and fabrication status of the expansion joint unit (EJU) to be employed in the NaK primary coolant piping loop of the 5-kwe Reactor thermoelectric system are described. Four EJU's are needed in the NaK primary coolant piping loop. The four EJU's which will be identical, utilize bellows as the flexing member, are hermetically sealed, and provide double containment. The bellows are of a nested-formed design, and are to be constructed of 1-ply thickness of 0.010-in. Inconel 718. The EJU's provide a minimum piping load margin of safety of +0.22.
Whitaker, W. D.↗