NASA NTRS1992

High temperature furnace modeling and performance verifications

Analytical, numerical, and experimental studies were performed on two classes of high temperature materials processing sources for their potential use as directional solidification furnaces. The research concentrated on a commercially available high temperature furnace using a zirconia ceramic tube as the heating element and an Arc Furnace based on a tube welder. The first objective was to assemble the zirconia furnace and construct parts needed to successfully perform experiments. The 2nd objective was to evaluate the zirconia furnace performance as a directional solidification furnace element. The 3rd objective was to establish a data base on materials used in the furnace construction, with particular emphasis on emissivities, transmissivities, and absorptivities as functions of wavelength and temperature. A 1-D and 2-D spectral radiation heat transfer model was developed for comparison with standard modeling techniques, and were used to predict wall and crucible temperatures. The 4th objective addressed the development of a SINDA model for the Arc Furnace and was used to design sample holders and to estimate cooling media temperatures for the steady state operation of the furnace. And, the 5th objective addressed the initial performance evaluation of the Arc Furnace and associated equipment for directional solidification. Results of these objectives are presented.

Smith, James E., Jr.↗
NASA NTRS1997

Temperature Distribution in a Composite of Opaque and Semitransparent Spectral Layers

The analysis of radiative transfer becomes computationally complex for a composite when there are multiple layers and multiple spectral bands. A convenient analytical method is developed for combined radiation and conduction in a composite of alternating semitransparent and opaque layers. The semi- transparent layers absorb, scatter, and emit radiation, and spectral properties with large scattering are included. The two-flux method is used, and its applicability is verified by comparison with a basic solution in the literature. The differential equation in the two-flux method Is solved by deriving a Green's function. The solution technique is applied to analyze radiation effects in a multilayer zirconia thermal barrier coating with internal radiation shields for conditions in an aircraft engine combustor. The zirconia radiative properties are modeled by two spectral bands. Thin opaque layers within the coating are used to decrease radiant transmission that can degrade the zirconia insulating ability. With radiation shields, the temperature distributions more closely approach the opaque limit that provides the lowest metal wall temperatures.

Siegel, Robert↗
NASA NTRS1997

Alternative Processing Method Leads to Stronger Sapphire-Reinforced Alumina Composites

The development of advanced engines for aerospace applications depends on the availability of strong, tough materials that can withstand increasingly higher temperatures under oxidizing conditions. The need for such materials led to the study of an oxide-based composite composed of an alumina matrix reinforced with zirconia-coated sapphire fibers. Because the nonbrittle behavior of this system depends on the interface and its ability to prevent fiber-to-matrix bonding and reduce interfacial shear stress, the microstructure of the zirconia must be carefully controlled during both coating application and composite processing. When it was both porous and unstabilized, zirconia (which does not react easily with alumina) was found to be the most effective material tested in reducing interfacial shear strength between the fiber and matrix.

Jaskowiak, Martha H.↗
NASA NTRS2003

Creep Resistance of ZrO2 Ceramic Improved by the Addition of a Small Amount of Er2O3

Zirconia (ZrO2) has great technological importance in structural, electrical, and chemical applications. It is the crucial component for state-of-the art thermal barrier coatings and an enabling component as a solid electrolyte for solid-oxide fuel cell systems. Pure ZrO2 is of limited use for industrial applications because of the phase transformations that occur. Upon the addition of stabilizers, cubic (c-ZrO2) and tetragonal (t-ZrO2) forms can be preserved. It is the stabilized and partially stabilized forms of zirconia that function as thermal barrier coatings, solid electrolytes, and oxygen sensors and that have numerous applications in the electrochemical industry. The cubic form of ZrO2 is typically stabilized through Y2O3 additions. However, Y2O3-stabilized zirconia is susceptible to deformation at high temperatures (greater than 900 C) because of the large number of slip systems and the high oxygen diffusion rates, which result in high creep rates at high temperatures. Successful use of ZrO2 at high temperatures requires that new dopant additives be found that will retain or enhance the desirable properties of cubic ZrO2 and yet produce a material with lower creep rates. At the NASA Glenn Research Center, erbium oxide (Er2O3) was identified as a promising dopant for improving the creep resistance of. ZrO2. The selection of Er2O3 was based on the strong interactions of point defects and dislocations. Single crystals of 5 mol% Er2O3- doped ZrO2 rods (4 mm in diameter) and monofilaments (200 to 300 mm in diameter and 30 cm long) were grown using the laser-heated float zone technique, and their creep behavior was measured as a function of temperature. The addition of 5 mol% Er2O3 to single-crystal ZrO2 improved its creep resistance at high temperatures by 2 to 3 orders of magnitude over state-of-the-art Y2O3-doped crystals. Detailed microstructural characterization of ZrO2-Er2O3 single crystals has identified new mechanisms for improving the creep resistance of this class of materials. Adding Er2O3 to ZrO2 results in microstructure of stable and metastable tetragonal precipitates that with thermal treatment evolve to a tweed structure of nanosize tetragonal lamellae. The superior high-temperature creep resistance of Er2O3-doped ZrO2 is attributed to nanoscale precipitation hardening. Doping with Er2O3 will significantly increase the upper-use temperature limit of ZrO2. Potential applications include using Er2O3-doped ZrO2 as a high-temperature fiber for structural applications and adding Er2O3 to reduce the sintering rates of ZrO2 thermal barrier coatings. This work was conducted at Dpto. de F sica de la Materia Condensada, Universidad de Sevilla, Spain, and at NASA Glenn.

Martinez-Fernandez, Julian↗
NASA NTRS2003

Collaboration of the NASA Glenn Research Center and Rolls-Royce Developed Thin Film Multilayered Dielectrics for Harsh Environments

The use of thin films to electrically insulate thin film sensors on engine components minimizes the intrusiveness of the sensors and allows a more accurate measurement of the environment. A variety of insulating films were investigated for preventing electrical shorting caused by insulator failure between the sensor and the component. By alternating layers of sputtered high-temperature ceramics, a sequence of insulating layers was devised that (1) prevents pinholes from forming completely through the insulator and (2) maintains high electrical resistivity at high temperatures. The total thickness is only a fraction of that needed for conventional insulating techniques. The Sensors and Electronics Technology Branch of the NASA Glenn Research Center has an in-house effort to develop thin film sensors for surface measurement in propulsion system research. Thin film sensors do not require special machining of the components on which they are mounted, and they are considerably thinner (less than 10 mm thick) than wire or foil sensors. The thin film sensors are thus much less disturbing to the operating environment and have a minimal impact on the physical characteristics of the supporting component. To further this research, NASA Glenn and Rolls-Royce (Derby, UK), with assistance from the Ohio Aerospace Institute (OAI) and the Akima Corporation, pursued a joint investigation using multilayered thin film dielectrics as a reliable insulator in harsh environments. The use of a multilayered scheme is thought to be promising for the fabrication of electrically insulating thin films. A major cause of conduction in thin film dielectrics is the presence of defects, such as pinholes, that propagate through the film to the underlying substrate surface. By alternating the insulating material, each new growth pattern would deviate from the previous one, eliminating direct pathways for conduction to the substrate. The film depositions and testing were conducted in the Instrument Research Laboratory at Glenn. The multilayered insulator test samples were made from alumina and stainless steel shims that were first covered with a sputtered underlayer of either yttria-stabilized zirconia or chromium carbide, and then overcoated with a sputtered top layer of alumina. An example of a test sample is shown in the following photograph. Each multilayered insulator sample was 5 mm thick, at least an order of magnitude thinner than conventional insulators. The insulating properties of the samples were tested in a high-temperature air oven to determine their suitability. The multilayer insulators tested showed a stabilized film at temperatures in excess of 800 C (1472 F). The underlying materials in these multilayers allow thermal expansion stresses produced during the heating to be graded. The chromium carbide-alumina multilayer had the best adhesion at high temperatures, presumably from the induced chemical bonding between the substrate and the chromium carbide underlayer. However, the zirconia-alumina multilayer proved to have slightly better insulating properties when adhering. The application of the zirconia-alumina insulator has been demonstrated on a nickel-alloy fan blade, as shown. The insulators using thin film sensors still need to be tested in a relevant high-temperature combustion environment.

Wrbanek, John D.↗
NASA NTRS2003

Lower-Conductivity Thermal-Barrier Coatings

Thermal-barrier coatings (TBCs) that have both initial and post-exposure thermal conductivities lower than those of yttria-stabilized zirconia TBCs have been developed. TBCs are thin ceramic layers, generally applied by plasma spraying or physical vapor deposition, that are used to insulate air-cooled metallic components from hot gases in gas turbine and other heat engines. Heretofore, yttria-stabilized zirconia (nominally comprising 95.4 atomic percent ZrO2 + 4.6 atomic percent Y2O3) has been the TBC material of choice. The lower-thermal-conductivity TBCs are modified versions of yttria-stabilized zirconia, the modifications consisting primarily in the addition of other oxides that impart microstructural and defect properties that favor lower thermal conductivity.

Miller, Robert A.↗
NASA NTRS1961

Development of Ceramic Fibers for Reinforcement in Composite Materials

Refinements of the vertical arc fiberizing apparatus resulted in its ability to fiberize very different refractory glasses having wide ranges of properties. Although the apparatus, was originally designed as a laboratory research tool for the evaluation of many compositions daily, up to one quarter pound of fibers of a single composition could be produced in an 8-hour day. Fibers up to six and a half feet long were produced with the apparatus. Studies were conducted of two methods of fiberizing refractory glasses requiring rapid freezing from the melt. The first method consisted of fiberizing droplets of molten glass passing through an annular nozzle. The second method consisted of reconstructing the annular nozzle in. the shape of a horseshoe to achieve a shorter delay in blasting a molten droplet from the tip of a rod. Both methods were judged feasible for producing fibers of glasses requiring rapid freezing. The first method would be more amenable to volume fiber production. Studies of induction heating for fiber formation did not lead to its designation as a very efficient heating method. Problems. remain to be solved, in the design of a suitable susceptor for a higher heating rate, in protecting the susceptor from oxidation with an inert gas, in contamination of the melt from a refractory crucible, and in the protective radiation shielding of the induction concentrator coil. It is not considered practical to continue studies of this heating method. In the course of this program 151 refractory glass compositions were evaluated for fiber, forming characteristics. Of the various types of materials studied, the following showed promise in producing acceptable refractory fibers: sIlica- spinel (magnesium aluminate), silica- spinel-zirconia, silica-zirconia, silica-zinc spinel, aluminum phosphate glasses, and fluoride glasses. Compositions which did not produce acceptable fibers were high zirconia materials, barium spinels, and calcium aluminates. Improvements in the. testing apparatus for single fiber tensile strength increased the precision. of tests conducted on nine fibers. The highest mean tensile strength, a value of 295,000 pounds per square inch, was obtained with R-141 fibers. Treatment of R-74 fibers with anhydrous Linde A-1100 silane finish improved its mean fiber tensile strength by 25 percent. The lapse of time after fiber formation had no measurable effect on tensile strength. A static heating test conducted with various high melting fibers indicated that Fiberfrax and R-108 underwent no significant changes in bulk volume or resiliency on exposure to 2750 degrees Fahrenheit (1510 degrees Centigrade) in an oxidizing atmosphere. For fiber-resin composition fabrication, ten fiber materials were selected on the bases of high fiber yield, fusion temperature, and type of composition. Fiberfrax, a commercial ceramic fiber, was included for comparison. A new, more effective method of removing pellets from blown fibers was developed. The de-pelletized fibers were treated with a silane finish and felted into ten-inch diameter felts prior to resin impregnation. Composites containing 30 percent by weight of CTL 91-LD phenolic resin were molded under high pressure from the impregnated felts and post-cured to achieve optimum properties. Flexural strength, flexural modules of elasticity, and punch shear strength tests were conducted on the composite specimens. The highest average flexural strength obtained was 19,958 pounds per square inch with the R-74-fiber-resin composite. This compares very favorably with the military specification of 13,000 pounds per square inch flexural strength for randomly oriented fiber reinforced composites. The highest punch shear strength (11,509 pounds per square inch) was obtained with the R-89 fiber-resin composite. The effects of anhydrous fiber finishes on composite strength were not clearly indicated. Plasma arc tests at a heat flux of 550 British Thermal Units per square foot per second on eight composite materials indicated ablation rates generally equivalent to Fiberglas-Micarta No. 259-2. The composite reinforced with R-99 fibers had an average ablation rate of 0.008 inch per second and appears quite promising on the basis of these tests. Preliminary studies for processing fibers into yarn and fabric were conducted with R-99 fibers. The use of certain organic gums aided in 2 fabricating by hand several relatively strong yarns and a crude fabric swatch. This indicated the practicality of developing techniques for processing these fibers into yarn and fabric without significant damage to the fibers.

Gates, L. E.↗
DOE OSTI2021

Ball-on-ring test validation for equibiaxial flexural strength testing of engineered ceramics

The validation of a ball-on-ring, equibiaxial flexural strength method to obtain the transverse rupture strength (TRS) of right cylindrical ceramic specimens was performed in this study. Validation of the test method was achieved using commercially available engineered high purity alumina disks and finite element (FE) model analysis. The validated fixture was then used to obtain the TRS and Weibull statistical analysis of MgO-partially stabilized zirconia (MSZ) and Y 2 O 3 -partially stabilized zirconia (YSZ) ceramic disks. TRS data for alumina, MSZ, and YSZ agreed with the TRS values reported in the literature. A statistically relevant number of samples (N > 30) for each material were tested to allow for a Weibull statistical analysis. Weibull parameters for these materials were within the expected values for engineered ceramics. The characteristic strength for alumina, MSZ, and YSZ were determined to be 289, 786, and 814 MPa, respectively. The Weibull modulus was determined between 10 and 25 for each material, which is typical of engineered ceramics. In addition, FE model results were in close agreement with experimental fracture values for the three ceramic materials tested in this study.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Broad Applicability of Electrochemical Impedance Spectroscopy to the Measurement of Oxygen Nonstoichiometry in Mixed Ion and Electron Conductors

Oxygen non-stoichiometry is a fundamental feature of mixed ion and electron conductors (MIECs). In this work a general electrochemical method for determining non-stoichiometry in thin film MIECs, via measurement of the chemical capacitance, is demonstrated using ceria and ceria-zirconia (Ce 0.8 Zr 0.2 O 2-δ ) as representative materials. A.C. impedance data are collected from both materials at high temperature (750-900 °C) under reducing conditions with oxygen partial pressure (pO 2 ) in the range 10-13 to 10-20 atm. Additional measurements of ceria-zirconia films are made under relatively oxidizing conditions with pO 2 in the range 0.2 to 10 -4 atm and temperatures of 800-900 °C. Under reducing conditions, the impedance spectra are described by a simple circuit in which a resistor is in series with a resistor and capacitor in parallel, and thickness dependent measurements are used to resolve the capacitance into interfacial and chemical terms. Under more oxidizing conditions, the impedance spectra (of Ce 0.8 Zr 0.2 O 2-δ ) reveal an additional diffusional feature, which enables determination of the ionic resistance of the film in addition to the capacitance, and hence the transport properties. A generalized mathematical formalism is presented for recovering the non-stoichiometry from the chemical capacitance, without recourse to defect chemical models. The ceria non-stoichiometry values are in good agreement with literature values determined by thermogravimetric measurements but display considerably less scatter and are collected on considerably shorter timescales. Here, the thermodynamic analysis of Ce 0.8 Zr 0.2 O 2-δ corroborates earlier findings that introduction of Zr into ceria enhances its reducibility.

08 HYDROGEN↗
DOE OSTI2020

Enhancing the efficiency benefit of thermal barrier coatings for homogeneous charge compression ignition engines through application of a low-k oxide

Prior experiments reported by the authors have proven the hypothesis that achieving a dynamic temperature swing on the combustion chamber surface will lead to improved thermal and combustion efficiencies of the homogeneous charge compression ignition engine. A thin layer of yttria-stabilized zirconia, roughly 150 μm, was plasma sprayed on the piston top. It led to markedly advanced ignition and heat release in the gasoline homogeneous charge compression ignition engine, accompanied with reduced unburnt hydrocarbon and carbon monoxide emissions, improved combustion efficiency, and a higher thermal efficiency. A related computational study highlighted the critical role of coating thermal conductivity in achieving a desired dynamic response; hence, the second phase of experimental investigations focused on introducing structured porosity in the yttria-stabilized zirconia coating, as a means of reducing effective conductivity. Indeed, additional incremental improvements were observed, as well as limitations related to adverse effects of the surface roughness and the fuel interactions with the surface roughness and open pores. Erosion can also be a problem in a direct injection engine. Therefore, the third round of investigations focused on a material with a natively low conductivity (low-k), sprayed on the top of an Al piston in a relatively dense form, and in a way that yields a smooth surface. The objective was to capitalize on the low conductivity, while avoiding the pitfalls accompanying high-porosity formulations. The heat-storage capacity was limited by keeping the thickness relatively low. The results verify the paramount importance of thermal conductivity in the context of high “temperature swing” behavior and indicate a potential to improve the homogeneous charge compression ignition engine’s combustion efficiency roughly 1.5%, with the overall indicated efficiency improvement on the order of 5%, on a relative basis. In addition, the low-k oxide thermal barrier applied to the piston extended significantly the low-load homogeneous charge compression ignition operability limit.

42 ENGINEERING↗
DOE OSTI2025

Reactive Carbide‐Based Synthesis and Microstructure of NASICON Sodium Metal All Solid‐State Electrolyte

Reactive carbide precursor-based synthesis of NASICON-type NZSP (Na 1+x Zr 2 Si x P 3-x O 12 ) solid-state electrolyte (SSE) is demonstrated, in contrast to the established oxide-based approach. Exothermic decomposition of ZrC and SiC in air homogenizes microstructure, yielding 98% compact density after conventional sintering at 1200 °C. Quantitative stereology demonstrates that significant microstructural differences are present. Compacts of carbide-derived Carb-NZSP are 98% dense with a secondary zirconium oxide (ZrO 2 ) volume fraction of 0.2% ± 0.3%, versus 93% dense and 3% ± 1% for oxide-derived baseline. For Carb-NZSP, the secondary glassy phosphate phase is agglomerated, while for baseline, it is dispersed and percolated. Electrochemical testing combined with post-mortem analysis demonstrates how microstructural control of secondary phases is critical for dendrite suppression: Carb-NZSP critical current density (CCD) is 3.1 ± 0.8 mA cm −2 at 0.1 mAh cm −2 , versus 1.0 ± 0.7 mA cm −2 at 0.1 mAh cm −2 . Cryogenic focused ion beam (cryo-FIB) analysis demonstrates that in both materials, the porous 2D sheet-like sodium metal dendrites propagate around and subsume NZSP grains, likely following a path enriched with glassy phase and with porosity. Dendrites also flow around isolated zirconia particles. Phase field simulation reveals deflection of dendrites by mechanically tough zirconia, while brittle glassy phase accelerates dendrite growth, especially when finely distributed.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Development of direct ink write radially graded alumina/zirconia

Functionally graded materials (FGMs) are of interest in multiple fields, yet many materials combinations are limited by coefficient of thermal expansion (CTE) mismatch. Here, a radially graded alumina/yttria-doped zirconia (Al 2 O 3 /8YZ) FGM is used to demonstrate processing strategies to mitigate CTE and sintering behavior differences between these oxides. FGM materials are especially sensitive to ink stability during printing, as all components (in this case, Al 2 O 3 and 8YZ) must be stabilized in the same dispersant or additive solution. Thus, this system is also ideal to demonstrate ink optimization best practices. Materials were characterized throughout processing to correlate the effects of common additives on both the ceramic particle suspensions and final sintered components. Aggregation observed in the initial additive-containing suspensions were present in the sintered component. The differences in sintering onset temperature and shrinkage rate resulted in internal stresses within the sintered component, which ultimately caused mechanical failure of the component under low stress. In conclusion, a processing strategy was recommended to mitigate the sintering behavior mismatch of alumina and 8 wt% yttria-stabilized zirconia.

Lamm, Benjamin W. [Oak Ridge National Laboratory (↗
DOE OSTI2024

Dispersal of high-burnup fuel fragment surrogate particles during and after loss-of-coolant accident tests

The issue of fuel fragmentation, relocation, and dispersal is critical in the licensing and use of high-burnup (>62 GWd/MTU) nuclear fuel in light water reactors (LWRs). In this work, two test series are reported that examine the fragment dispersal during a burst event and an additional dispersal following the burst due to vibrations in the rod, such as those induced by accident recovery systems. To examine dispersal during the balloon and burst portion of a Loss-of-Coolant Accident event, HfO 2 fragments and yttria-stabilized zirconia pellets were filled into an as-fabricated cladding tube, which was then pressurized and subjected to loss-of-coolant accident testing in steam. Results from this test were found to be highly non-prototypic, and dispersal was both significantly more violent and significantly greater in magnitude than identified for actual fuel tests. These findings were attributed to the conservative (more dispersive) nature of the particles chosen for dispersal and to the details of the test conditions used that led to particularly wide bursts. Further, the second set of tests examined dispersal following the burst when vibrations were induced in the rod, primarily via recovery activities such as Emergency Core Cooling System actuation leading to rapid water addition. Post-burst dispersal testing was performed by inducing sinusoidal oscillations with 2–25 nm peak-to-peak amplitude and 2–5 Hz frequencies in pre-burst rods that had been refilled with HfO 2 fragments or high-burnup fragment surrogate mixture of HfO 2 fragments and yttria-stabilized zirconia sands. Testing revealed that rods with large burst openings (7 mm wide in this work) led to unmitigated dispersal from above the burst zone but that smaller bursts (5 mm wide), although still much larger than the mean fragment size of 3 mm, led to effectively no dispersal because of interparticle locking. Additionally, mixture and moisture were found to impact the amount of dispersal: mixtures increased dispersal, and moisture drastically reduced it. The implications of these findings on likely dispersal from actual fuel are discussed.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Understanding the morphology and chemical activity of model ZrO x /Au (111) catalysts for CO 2 hydrogenation

In this study, the growth of ZrO x on Au (111) was investigated using scanning tunneling microscopy (STM) and synchrotron-based ambient pressure X-ray photoelectron spectroscopy (AP-XPS). Nanostructures of ZrO x (x= 1,2) at the sub-monolayer (≤ 0.3 ML) level were prepared by vapor depositing Zr metal onto Au (111) followed by oxidation with O 2 or CO 2 . At low coverages of the admetal (< 0.05 ML), the formed ZrO x nanostructures were dispersed randomly on the terraces and steps of the Au(111) substrate. Strong oxide-metal interactions prevented the formation of islands of zirconia. The ZrO x nanostructures displayed a reactivity towards CO 2 and H 2 not seen for bulk zirconia. C 1 s AP-XPS results indicated that CO 2 molecules adsorbed on Zr/ZrO x /Au(111) surfaces could undergo partial decomposition on Zr (CO 2 , gas → CO gas + O ads ), or react with oxygen sites from ZrO x to yield carbonates (Zr-CO 3, ads ). Further, after exposing ZrO 2 /Au (111) surfaces to 1:3 mixtures of CO 2 :H 2 , the formation of HCOO, CO 3 , and CH 3 O was detected in AP-XP spectra. These chemical species decomposed at temperatures in the range of 400-600 K, making them possible reaction intermediates for methanol synthesis.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2024

Impact of Sr-Containing Secondary Phases on Oxide Conductivity in Solid-Oxide Electrolyzer Cells

Solid-oxide electrolyzer cells (SOECs) based on a yttria-stabilized zirconia (YSZ) oxide electrolyte produce hydrogen from water with the assistance of excess thermal energy; however, Sr diffusion within the Gd-doped CeO 2 (GDC) barrier layer during processing or operation can lead to the formation of unwanted secondary phases such as SrO and SrZrO 3 . Here, to establish and compare the degree of impact of these phases on SOEC performance, we conduct first-principles calculations to study their bulk oxide conductivities and compare them to that of the YSZ electrolyte. We find that SrO has a low conductivity arising from the poor mobility and low concentration of mobile oxygen vacancies, and its presence in SOECs should therefore be avoided. SrZrO 3 also has a lower oxide conductivity than YSZ; however, this discrepancy is primarily due to lower vacancy concentrations rather than low mobility. We find that sufficient levels of Y-doping on the Zr site can increase oxygen vacancy concentrations in SrZrO 3 to achieve an oxide ionic conductivity on par with that of YSZ, thereby mitigating any potential deleterious effect on transport performance. Energy-dispersive X-ray spectroscopy confirms that Y is the most common minority element present in SrZrO 3 forming near the GDC–YSZ interface, alleviating concerns regarding the impact of SrZrO 3 on device performance. These results from our combined computational–experimental analysis can inform future engineering strategies designed to limit the detrimental effects of Sr-induced secondary phase formation on SOEC performance.

08 HYDROGEN↗
DOE OSTI2020

Metal Oxide Sorbents for the Separation of Radium and Actinium

The inorganic, normal-phase sorbents alumina, titania, and zirconia were evaluated and screened for the separation of Ba, La, 228 Ra, 228 Ac, and 212 Pb in a dilute acid matrix. The results show that the sorbents are capable of fractionating the ions between pH 1 and 8. A stationary zirconia column was used to isolate Ba from La and Ra from Ac/Pb; elution profiles of each separation are presented. The utility and implications of these sorbents are discussed with respect to large-scale production of 225 Ac from radium targets.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Capacitive discharge in flash experiments: A discussion of the charged species

Abstract We report on the discharge of the capacitance formed at the electrodes in flash experiments with yttria stabilized zirconia. The experiments were carried out by disconnecting the current, and, instead, short circuiting the electrodes through a resistor. The time dependent voltage across the resistor was measured; the ratio yielded the discharge current. The current decayed exponentially with time, as expected in an RC circuit, which allowed the measurement of the capacitance. Experiments were carried out in two ways. In one case the specimens were flashed within a glove box filled with Ar (< 1 ppm O 2 ): these yielded electronic conductors. In the other case the specimens were flashed in ambient air: while electronically conducting in‐flash these specimens recover their prior insulating behavior as soon as the current is turned off. The stored charge was two orders of magnitude greater in the Ar experiments. Rather unexpectedly, the sign of the voltage expressed at the electrodes was opposite in experiments carried out in air and in Ar. The capacitance measured in the discharge experiments is attributed to the formation of space charge adjacent to the electrodes. In the case of Ar experiments, the capacitance is very large, approaching 1 F; in this case the space charge is expected to be constituted from ions. In the air experiments the specimen becomes insulating, trapping the electrons as a space charge. Hall effect measurements of the carrier density and X‐ray photoelectron spectroscopy characterization of electronically conducting single crystal specimen of cubic zirconia are reported.

Materials Science↗