DOE OSTI2023

Development, Characterization, and Testing of Solid-State Electrolytes for Batteries

Traditional liquid electrolytes used in lithium (Li) metal batteries (LMBs) have severe safety issues, poor power density, as well as thermal and electrochemical instability that prevents their scaling to newer applications, such as electric vehicles. Using sulfide-based solid-state electrolytes (SSEs) is a viable method to address many of the issues that plague LMBs. However, the key issue preventing the expansion of sulfide-based SSEs is an interplay between poor interfacial stability with the electrodes and massive external stack pressure required to maintain electrode-electrolyte contact. The need for extensive pressure requires large system-level (i.e., battery pack used in an electric vehicle) housing that causes a disconnect between performance at a smaller scale and actual application. Secondary prevention to sulfide-based SSE adoption are difficulties in manufacturing, as toxic deterioration occurs when these materials are exposed to humidity, as well as drastic reduction in SSE performance at low temperature. This work hypothesizes that unique interfacial designs of electrodes and the modification of the sulfide-based SSE will enable reduction of necessary external cell pressure, and therefore support the design of practical LMBs. This will be done through collaboration within Idaho National Laboratory (INL), where manufacturing practices will be parameterized to produce low defect, low porosity SSEs with slight modifications. Next, artificial interfaces will be produced on electrodes to observe the conformality and mass transport properties between the modified SSE and pre-treated anode. External pressure on Li-metal cells will also be parameterized to reduce interfacial impedance while a reduction in the pressure will allot reasonable housing design for larger scale applications. Focus on novelty in this work occurs by modifications to the solid-solid interfaces between electrolyte and electrode, done through doping of the electrolyte and production of artificial interfaces on the Li-metal anode. The modifications at these interfaces, in addition to modified external pressure could identify and address the poor interfacial impedance that hinders high performance SSEs. Fundamental understanding on how to reduce the key hindrances of all-solid-state batteries (ASSBs) will support the advancement for larger scale production and performance, of which will be held in perspective for future works. Beyond battery development, the knowledge gained from process control and defect analysis is applicable to other ceramic systems, such as nuclear fuel coatings and high temperature electrolyzers.

25 ENERGY STORAGE↗
DOE OSTI2023

Development, Characterization, and Testing of Solid-State Electrolytes for Batteries

Traditional liquid electrolytes used in lithium (Li) metal batteries (LMBs) have severe safety issues, poor power density, as well as thermal and electrochemical instability that prevents their scaling to newer applications, such as electric vehicles. Using sulfide-based solid-state electrolytes (SSEs) is a viable method to address many of the issues that plague LMBs. However, the key issue preventing the expansion of sulfide-based SSEs is an interplay between poor interfacial stability with the electrodes and massive external stack pressure required to maintain electrode-electrolyte contact. The need for extensive pressure requires large system-level (i.e., battery pack used in an electric vehicle) housing that causes a disconnect between performance at a smaller scale and actual application. Secondary prevention to sulfide-based SSE adoption are difficulties in manufacturing, as toxic deterioration occurs when these materials are exposed to humidity, as well as drastic reduction in SSE performance at low temperature. This work hypothesizes that unique interfacial designs of electrodes and the modification of the sulfide-based SSE will enable reduction of necessary external cell pressure, and therefore support the design of practical LMBs. This will be done through collaboration within Idaho National Laboratory (INL), where manufacturing practices will be parameterized to produce low defect, low porosity SSEs with slight modifications. Next, artificial interfaces will be produced on electrodes to observe the conformality and mass transport properties between the modified SSE and pre-treated anode. External pressure on Li-metal cells will also be parameterized to reduce interfacial impedance while a reduction in the pressure will allot reasonable housing design for larger scale applications. Focus on novelty in this work occurs by modifications to the solid-solid interfaces between electrolyte and electrode, done through doping of the electrolyte and production of artificial interfaces on the Li-metal anode. The modifications at these interfaces, in addition to modified external pressure could identify and address the poor interfacial impedance that hinders high performance SSEs. Fundamental understanding on how to reduce the key hindrances of all-solid-state batteries (ASSBs) will support the advancement for larger scale production and performance, of which will be held in perspective for future works. Beyond battery development, the knowledge gained from process control and defect analysis is applicable to other ceramic systems, such as nuclear fuel coatings and high temperature electrolyzers.

25 ENERGY STORAGE↗
DOE OSTI2026

Improving perovskite solar module stability by understanding and mitigating scribe-induced chemo-thermomechanical degradation

Recognizing the correlation between the design of perovskite solar module (PSM) and their degradation mechanisms under environmental stressors helps to enable their long- term reliability. This work reports on the impact of the hole-transport layer (HTL) on thermal cyclability and degradation mechanisms of p-i-n PSMs by comparing 3 HTLs: NiO x , MeO-2PACz (a self-assembled monolayer), and a bilayer HTL of MeO-2PACz on NiO x . We observe surprising thermal cyclability from a performance standpoint despite generating clear degradation products. We find that without a fully dense HTL, seemingly insignificant moisture/oxygen ingress through the edge of the PSMs can lead to rapid destabilization of the metal halide perovskite (MHP) layer due to reactions between MHP degradation byproducts and the indium-tin oxide layer. We also show that illumination-induced cation phase segregation is dependent on the presence of an inactive area (regions of the substrate uncovered by the top electrode). As such, we find that a dense interface between the MHP and ITO is necessary for chemically robust PSMs and highlight criteria for testing field-relevant configurations in lab-scale architectures.

14 SOLAR ENERGY↗
DOE OSTI2023

Revealing the effect of LiOH on forming a SEI using a Co magnetic “probe”

The solid-electrolyte-interphase (SEI) plays a critical role in lithium-ion batteries (LIBs) because of its important influence on electrochemical performance, such as cycle stability, coulombic efficiency, etc. Although LiOH has been recognized as a key component of the SEI, its influence on the SEI and electrochemical performance has not been well clarified due to the difficulty in precisely controlling the LiOH content and characterize the detailed interface reactions. Here, a gradual change of LiOH content is realized by different reduction schemes among Co(OH) 2 , CoOOH and CoO. With reduced Co nanoparticles as magnetic “probes”, SEI characterization is achieved by operando magnetometry. By combining comprehensive characterization and theoretical calculations, it is verified that LiOH leads to a composition transformation from lithium ethylene di-carbonate (LEDC) to lithium ethylene mono-carbonate (LEMC) in the SEI and ultimately results in capacity decay. This work unfolds the detailed SEI reaction scenario involving LiOH, provides new insights into the influence of SEI composition, and has value for the co-development between the electrode materials and electrolyte.

25 ENERGY STORAGE↗
DOE OSTI2024

Reactive capture and electrochemical conversion of CO 2 with ionic liquids and deep eutectic solvents

Ionic liquids (ILs) and deep eutectic solvents (DESs) have tremendous potential for reactive capture and conversion (RCC) of CO 2 due to their wide electrochemical stability window, low volatility, and high CO 2 solubility. There is environmental and economic interest in the direct utilization of the captured CO 2 using electrified and modular processes that forgo the thermal- or pressure-swing regeneration steps to concentrate CO 2 , eliminating the need to compress, transport, or store the gas. The conventional electrochemical conversion of CO 2 with aqueous electrolytes presents limited CO 2 solubility and high energy requirement to achieve industrially relevant products. Additionally, aqueous systems have competitive hydrogen evolution. In the past decade, there has been significant progress toward the design of ILs and DESs, and their composites to separate CO 2 from dilute streams. In parallel, but not necessarily in synergy, there have been studies focused on a few select ILs and DESs for electrochemical reduction of CO 2 , often diluting them with aqueous or non-aqueous solvents. The resulting electrode–electrolyte interfaces present a complex speciation for RCC. In this review, we describe how the ILs and DESs are tuned for RCC and specifically address the CO 2 chemisorption and electroreduction mechanisms. Critical bulk and interfacial properties of ILs and DESs are discussed in the context of RCC, and the potential of these electrolytes are presented through a techno-economic evaluation.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Pt Nanoparticles on Atomic-Metal-Rich Carbon for Heavy-Duty Fuel Cell Catalysts: Durability Enhancement and Degradation Behavior in Membrane Electrode Assemblies

Proton exchange membrane fuel cells (PEMFCs) are a promising zero-emission power source for heavy-duty vehicles (HDVs). However, long-term durability of up to 25,000 h is challenging because current carbon support, catalyst, membrane, and ionomer developed for traditional light-duty vehicles cannot meet the stringent requirement. Therefore, understanding catalyst degradation mechanisms under the HDV condition is crucial for rationally designing highly active and durable platinum group metal (PGM) catalysts for high-performance membrane electrode assemblies (MEAs). Herein, we report a PGM catalyst consisting of platinum nanoparticles with a high content (40 wt %) on atomic-metal-site (e.g., MnN 4 )-rich carbon support. MEAs with the Pt (40 wt %)/Mn–N–C cathode catalyst achieved significantly enhanced performance and durability, generating 1.41 A cm –2 at 0.7 V under HDV conditions (0.25 mgPt cm –2 and 250 kPa abs pressure) and retaining 1.20 A cm –2 after an extended and accelerated stress test up to 150,000 voltage cycles. Electron microscopy studies indicate that most fine Pt nanoparticles are retained on or/and in the carbon support covered with the ionomer throughout the catalyst layer at the end of life. During the long-term stability test, the observed electrochemical active surface area reduction and performance loss primarily result from Pt depletion in the catalyst layer due to Pt dissolution and redeposition at the interface of the cathode and membrane. Importantly, the first-principle density functional theory calculations further reveal a support entrapment effect of the Mn–N–C, in which the MnN 4 site can specifically adsorb the Pt atom and further retard the Pt dissolution and migration, therefore enhancing long-term MEA durability.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

A Superior Carbonate Electrolyte for Stable Cycling Li Metal Batteries Using High Ni Cathode

Li metal batteries pairing Li metal anode with high-nickel layer structured oxide cathode are a promising energy storage technology to achieve high energy density. To obtain long cycling life for Li metal batteries, the electrolyte plays a pivotal role in stabilizing both the Li metal anode and the high-nickel cathode upon electrochemical cycling. Herein, we report a carbonate electrolyte that enables a Li||LiNi 0.8 Mn 0.1 Co 0.1 O 2 pouch cell to achieve a high gravimetric energy density of 366 Wh/kg and unprecedented cycling stability with 80% capacity retention after 335 cycles. Here, the 19 F quantitative nuclear magnetic resonance spectroscopy and interface characterization demonstrate that FEC and LiDFOB can reduce the consumption rate of each other and the electrolyte, form a robust LiF-rich SEI on Li metal anode, and improve the microstructure integrity of the high-nickel cathode.

25 ENERGY STORAGE↗
DOE OSTI2025

Effect of Propagating Dopant Reactivity on Lattice Oxygen Loss in LLZO Solid Electrolyte Contacted with Lithium Metal

Lithium lanthanum zirconium oxide (LLZO) is widely known as the most stable solid electrolyte against lithium metal electrodes. This thermodynamic stability can be lost by the presence of dopants which are required to stabilize the cubic phase of LLZO and can be reduced by lithium metal. However, the role of oxygen in such reactions is taken for granted. In this work, the reduction of Nb-substituted LLZO (Nb-LLZO) is explored by Li metal and shows that interfacial reactions propagate and lead to the decomposition with substantial Nb 5+ reduction deep into the bulk electrolyte. Scanning Transmission Electron Microscopy with Energy Dispersive X-ray Spectroscopy and thermogravimetric analyses show much of the reduction is due to oxygen vacancies formed, leading to increased electronic conductivity mapped with conductive Atomic Force Microscopy. Density functional theory calculations indicate oxygen release is favored by increased excess lithiation of Nb-LLZO. Electrochemical impedance of polycrystalline Nb-LLZO shows the continuous evolution of ionically resistive interphases near the lithium metal interface with Nb-LLZO while single crystals show little reactivity at room temperature and self-limiting reduction at 60°C. This work underlines the role of grain boundaries in propagating destructive solid electrolyte reactions and highlights previously unseen mechanisms involving lattice oxygen in LLZO.

Li metal, solid-state electrolytes↗
DOE OSTI2021

Metal fluoride passivation coatings prepared by atomic layer deposition for Li-ion batteries

The fabrication of robust interfaces between transition metal oxides and non-aqueous electrolytes is one of the great challenges of lithium ion batteries. Atomic layer deposition (ALD) of aluminum tungsten fluoride (AlWxFy) improves the electrochemical stability of LiCoO2. AlWxFy thin films were deposited by combining trimethylaluminum and tungsten hexafluoride. in-situ quartz crystal microbalance and transmission electron microscopy studies show that the films grow in a layer-by-layer fashion and are amorphous nature. Ultrathin AlWxFy coatings (<10 Å) on LiCoO2 significantly enhance stability relative to bare LiCoO2 when cycled to 4.4 V. The coated LiCoO2 exhibited superior rate capability (up to 400 mA/g) and discharge capacities at a current of 400 mA/g were 51% and 92% of the first cycle capacities for the bare and AlWxFy coated materials. These results open new possibilities for designing ultrathin and electrochemically robust coatings of metal fluorides via ALD to enhance the stability of Li-ion electrodes.

Mane, Anil U.↗
DOE OSTI2025

Interface chemistry informs about cathode and anode degradation during fast charging

Here, the aim of this study is to examine the development and makeup of the Solid Electrolyte Interphase (SEI) and Cathode Electrolyte Interphase (CEI) in lithium-ion batteries during rapid charging. Using X-ray photoelectron spectroscopy (XPS) and depth profiling, we investigate the chemical modifications occurring on the electrode surfaces during the initial formation and subsequent fast charge-discharge cycles. Our research shows that the anode's SEI initially comprises a thin layer rich in ketones, which then transforms into a thicker layer dominated by carbonaceous compounds during rapid charging cycles. Following assembly, lithium fluoride (LiF) quickly becomes a key element of the SEI, and its presence continues to grow substantially during the formation cycle, remaining the primary component throughout subsequent cycles. Initially, the cathode forms a thin oxide layer rich in ketones, with no noticeable carbonaceous CEI. The CEI primarily comprises LiF, which experiences an increase during the formation cycle and retains a thin layer of carbon coating after the initial rapid discharge. These findings show how the interphase layers impact the performance and stability of lithium-ion batteries, especially during fast charging for electric vertical take-off and landing (eVTOL) vehicles.

Fast charging↗
DOE OSTI2022

On-Demand Designing of Cathode Internal Surface Architecture for Dramatic Enhancement of SOFC Performance and Durability

This project is aimed to design and modify the internal surfaces of porous composite cathode from currently commercially viable Solid Oxide Fuel Cells (SOFCs), using additive manufacturing process of Atomic Layer Deposition (ALD). The material systems being investigated are commercial composite electrodes complex three-dimensional topographies. In term of the chemistry of the ALD layer applied on the internal surface of the porous cathode, this project has employed commercially relevant electrolyte, electrocatalyst and noble metal materials set. Such materials are fully compatible with the commercial fuel cells, and this project has developed special nanostructure on the surface of the commercial composite cathodes. The formation of the designed nanoarchitecture on the surface of SOFC cathode has been achieved through precise control of ALD parameters and their effect on overall cell performance and resultant electrochemical reaction mechanism of cathodes has been investigated through full cell electrochemical performance testing and nanostructure characterization by transmission electron microscopy (TEM). Under the support of this award, following has been achieved: (1). For cathode materials in solid oxide fuel cells (SOFCs), such as perovskite mixed conductor La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3-x (LSCF), cation surface segregation and consequently losing conductivity and active sites for the oxygen reduction reaction (ORR) are problematic. To mitigate the cation segregation and enhance SOFC durability, further decorating the internal backbone surface using the desired electrocatalysts could be a promoting approach. Commonly, the cation segregation such as Sr is very volatile, so the effective surface decoration is ideally conformal. Nevertheless, the conformal surface coating would inevitably alter the ORR pathways that initially take place on the surface of the backbone. To reveal the impact of the conformal coating on both the catalytic activity and the conductivity of the cathode, the unary electrocatalyst of Pt or CoO x , was applied to the LSCF/SDC composite electrode of inherently functional SOFCs, respectively. Both ALD coating layers evolve strong interaction with the LSCF composite cathode. Upon operations, the Pt coating layer remains conformal on LSCF grain surfaces but turns into discrete particles on SDC grain surfaces. Meanwhile, CoO x conformal coating grows to be the discrete nanograins on both the LSCF and SDC grains. ALD coating of the cathode alone reduces the ohmic resistance up to 28 % for the entire cells. The increased conductivity induced by the ALD coating of Pt or CoO x is ascribed to different mechanisms. For the inherent functional SOFCs, the present study presents a novel and feasible approach to apply a conformal, dense coating layer on the surface of a mixed conductor, simultaneously increasing the conductivity and durability of the SOFC cathode. (2). High resistance of the oxygen electrode still significantly hinders the state-of-the-art Solid Oxide Fuel Cells (SOFCs). In particular, for an oxygen electrode consisting of mixed electronic and ionic conductors, such as perovskite lanthanum strontium cobalt ferrite (LSCF), it deteriorates due to its low chemical stability of the grain surface. Such degradation is often associated with the segregation of cations. To prevent the cation surface segregation and its resultant perovskite phase decomposition, we demonstrate a conformal ultra-thin (7-10 nm) surface heterogeneous coating layer consisting of subjacent discrete Pt nanoparticles capped with a superjacent fully dense conformal CoO x layer. The performance studies indicate the ALD coating reduces the cell series resistance by up to 40 %. The conformal CoO x layer consists of randomly orientated but single-layered nanograins, with high-density intergranular and surface grain boundaries serving as the electrochemical reaction sites and facilitating mass transport. The conformal coating layer appears to have successfully suppressed the Sr outward diffusion and confined the Sr enriched layer to a ~ 2 nm interface perovskite phase between the coating layer and the LSCF grain surface. Moreover, this ultra-thin Sr enriched perovskite layer presumably possesses high oxygen vacancy and high ionic conductivity and further imposes tensile strain to the LSCF grain surfaces. With the combination of a conformal CoO x nanoionics, Sr enriched layer, and its strained interface, the ALD coating induced surface layer is estimated to have a conductivity of ~ 1.27x10 4 S/cm, which is over two orders magnitude of that from LSCF at 750 ºC.

30 DIRECT ENERGY CONVERSION↗
DOE OSTI2024

Metal fluoride passivation coatings prepared by atomic layer deposition for Li-ion batteries

The fabrication of robust interfaces between transition metal oxides and non-aqueous electrolytes is one of the great challenges of lithium ion batteries. Atomic layer deposition (ALD) of aluminum tungsten fluoride (AlWxFy) improves the electrochemical stability of LiCoO 2 . AlWxFy thin films were deposited by combining trimethylaluminum and tungsten hexafluoride. in-situ quartz crystal microbalance and transmission electron microscopy studies show that the films grow in a layer-by-layer fashion and are amorphous nature. Ultrathin AlWxFy coatings (<10 Å) on LiCoO 2 significantly enhance stability relative to bare LiCoO 2 when cycled to 4.4 V. The coated LiCoO 2 exhibited superior rate capability (up to 400 mA/g) and discharge capacities at a current of 400 mA/g were 51% and 92% of the first cycle capacities for the bare and AlWxFy coated materials. These results open new possibilities for designing ultrathin and electrochemically robust coatings of metal fluorides via ALD to enhance the stability of Li-ion electrodes.

Mane, Anil U.↗
DOE OSTI2020

Enabling High Capacity and Coulombic Efficiency for Li-NCM811 Cells Using a Highly Concentrated Electrolyte

Lithium metal batteries suffer from dendrite formation and the associated safety hazards of thermal runaway reactions. In this study, we report the performances of a highly concentrated electrolyte (HCE) and a dilute LiPF6 electrolyte in lithium metal cells using LiNi 0.8 Co 0.1 Mn0.1O 2 . While the HCE exhibits lower bulk ionic conductivity than the dilute LiPF6 electrolyte, the cell conductivity is higher for the HCE system, indicating higher thermodynamic stability of the electrolyte against the electrodes. Full cell cycling demonstrates higher capacity for the HCE system, which declines as a function of cycle number due to the formation of decomposition products, similar to the dilute LiPF 6 system. The origin of the enhanced performance is the higher stability of the HCE against a Li metal anode as compared to the dilute LiPF 6 electrolyte. Cycling at higher temperatures further enhances the performance of the HCE, which is more thermally stable than the dilute LiPF 6 electrolyte.

25 ENERGY STORAGE↗
DOE OSTI2021

Emerging investigator series: local pH effects on carbon oxidation in capacitive deionization architectures

In this work, the effect of pH and potential is examined for the oxidation of carbon cloth electrodes used in capacitive deionization (CDI) processes. The degree of oxidation of the electrode surface, examined using the electrode's potential of zero charge (E pzc ) and measured using chronoamperometry and cyclic voltammetry, is found to be strongly correlated to the pH of the solution at the interface. Local pH measurements are examined at anodes and cathodes in full CDI and membrane-assisted capacitive deionization (MCDI) cells at cell voltages ranging from 0.3–1.2 V. The cathode is shown to be basic under charging potentials while the anode is found to be acidic. This local pH is found to be highly transient during charging and discharging in CDI cells while the pH is found to be relatively static in the MCDI cells, maintaining a basic pH at the cathode and an acidic pH at the anode even when the cell is discharged. Ion exchange membranes (IEM) are found to have two functions: (1) limiting co-ion expulsion that results from specific ion adsorption and (2) limiting the effects of parasitic Faradaic reactions on the separation process by stabilizing the local pH thereby mitigating dissolved oxygen reduction at the cathode and lessening carbon oxidation at the anode. Performance comparisons including the salt adsorption capacity and charge efficiency are also compared for these systems.

54 ENVIRONMENTAL SCIENCES↗
DOE OSTI2023

Electrolyte Reactivity on the MgV 2 O 4 Cathode Surface

Predictive understanding of the solvation-dependent reactivity and molecular interaction of electrolyte ions and solvent molecules on reactive electrodes has been a major challenge but is essential for addressing instabilities and surface passivation that occur at electrode-electrolyte interface (EEI) of multivalent Mg batteries. In this work, the isolated intrinsic reactivities of prominent chemical species present in magnesium bis(trifluoromethanesulfonimide) (Mg(TFSI) 2 ) in diglyme (G2) electrolytes, including ionic (TFSI - , [Mg(TFSI)] + , [Mg(TFSI):G2] + , [Mg(TFSI):2G2] + ) as well as neutral molecules (G2) on magnesium vanadate cathode (MgV 2 O 4 ) surface has been studied using a combination of first-principles calculations and multimodal analysis of well-defined cathode electrolyte interphase (CEI) layers. Here, our calculations show that non-solvated [Mg(TFSI)] + is the strongest adsorbing species on the MgV 2 O 4 surface compared to all other ions while fully solvated [Mg(TFSI):2G2] + are least favorable to decomposition. The cleavage of C-S bonds in TFSI - to form CF 3 - is predicted to be most desired pathway for all ionic species, which is followed by the cleavage of C-O bonds of G2 to yield CH 3 + or OCH 3 - species. The strong stabilization and electron transfer between ionic electrolyte species and MgV 2 O 4 is found to significantly favor these decomposition reactions on the surface compared to intrinsic gas phase dissociation. Experimentally, we used state-of-the-art ion soft landing to selectively deposit mass-selected TFSI - , [Mg(TFSI):G2] + and [Mg(TFSI):2G2] + on MgV 2 O 4 thin film to form well-defined electrolyte-MgV 2 O 4 interface. Analysis of soft-landed interphase using X-ray photoelectron, X-ray absorption near edge structure, electron energy-loss spectroscopies as well as transmission electron microscopy confirmed the presence of decomposition species (e.g., MgFx, carbonates) formed in the interfacial region and the higher amount of MgFx with [Mg(TFSI):G2] + , which corroborates the theoretical observation. Overall, we established the mechanistic pathway for the electrolyte-induced formation of passivating fluorides on MgV 2 O 4 cathode facilitated by the surface adsorption and charge transfer, which provided essential knowledge for rational design of stable electrolytes for multivalent cathodes.

Cathode-electrolyte interphase formation↗
DOE OSTI2026

Mechanism of ion pairing–induced co-ion penetration into the stern layer

In classical electric double layer (EDL) theory, co-ions—ions carrying the same charge as the electrode—are assumed to be excluded from the Stern layer because of electrostatic repulsion. However, ion pairing with adsorbed counterions may enable co-ions to access the EDL, a phenomenon that remains underexplored. Key questions therefore remain unresolved, including how deeply co-ions penetrate, how ion-specific properties govern them, and how ion pairing within the EDL differs from bulk solution. Here, in this study, we employ molecular dynamics simulations combined with well-tempered metadynamics to quantify co-ion penetration and ion-pairing thermodynamics at positively charged Mg-Al layered double hydroxide interfaces (σ = +20.6 μC/cm 2 ) in aqueous chloride electrolytes across 0.005–3 M range. We reveal a concentration-driven crossover: at dilute conditions, counterion–co-ion contact ion pairing (CIP) is thermodynamically unfavorable or only weakly favorable (ΔG CIP = +0.12 kcal/mol for Li + to −0.42 kcal/mol for K + ), leading to co-ion exclusion. As concentration increases (≥0.5 M), enhanced screening reduces surface repulsion and stabilizes CIP thermodynamics (ΔG CIP = −0.89 kcal/mol for Li + to −1.05 kcal/mol for K + at 3 M), enabling monovalent co-ions to penetrate the Stern layer following the hydration hierarchy K + > Na + > Li + , while divalent co-ions (Mg 2+ , Ca 2+ ) remain in the diffuse layer, forming only solvent-separated pairs. Comparison with bulk solution shows interfacial ion pairing is suppressed at low concentrations but converges to bulk-like thermodynamics at high concentrations, indicating surface effects vanish under strong screening. These results establish a quantitative framework linking ion-pairing thermodynamics to co-ion penetration and providing strategies to design electrochemical interfaces.

Co-ion penetration↗
DOE OSTI2020

Biomimetic composite architecture achieves ultrahigh rate capability and cycling life of sodium ion battery cathodes

Sodium ion batteries are an emerging candidate to replace lithium ion batteries in large-scale electrical energy storage systems due to the abundance and widespread distribution of sodium. Despite the growing interest, the development of high-performance sodium cathode materials remains a challenge. In particular, polyanionic compounds are considered as a strong cathode candidate owing to their better cycling stability, a flatter voltage profile, and stronger thermal stability compared to other cathode materials. Here, we report the rational design of a biomimetic bone-inspired polyanionic Na3V2(PO4)3-reduced graphene oxide composite (BI-NVP) cathode that achieves ultrahigh rate charging and ultralong cycling life in a sodium ion battery. At a charging rate of 1 C, BI-NVP delivers 97% of its theoretical capacity and is able to retain a voltage plateau even at the ultra-high rate of 200 C. It also shows long cycling life with capacity retention of 91% after 10 000 cycles at 50 C. The sodium ion battery cells with a BI-NVP cathode and Na metal anode were able to deliver a maximum specific energy of 350 W h kg−1 and maximum specific power of 154 kW kg−1. In situ and postmortem analyses of cycled BI-NVP (including by Raman and XRD spectra) HRTEM, and STEM-EELS, indicate highly reversible dilation–contraction, negligible electrode pulverization, and a stable NVP-reduced graphene oxide layer interface. The results presented here provide a rational and biomimetic material design for the electrode architecture for ultrahigh power and ultralong cyclability of the sodium ion battery full cells when paired with a sodium metal anode.

25 ENERGY STORAGE↗
DOE OSTI2023

Stabilizing High–Nickel Cathodes with High–Voltage Electrolytes

Electrolytes connect the two electrodes in a lithium battery by providing Li + transport channels between them. Advanced electrolytes are being explored with high-nickel cathodes and the lithium-metal anode to meet the high energy density and cycle life goals, but the origin of the performance differences with different electrolytes is not fully understood. Here, the mechanisms involved in protecting the high-capacity, cobalt-free cathode LiNiO 2 with a model high-voltage electrolyte (HVE) are delineated. The kinetic barrier posed by a thick surface degradation layer with poor Li + -ion transport is found to be the major contributor to the fast capacity fade of LiNiO 2 with the conventional carbonate electrolyte. In contrast, HVE reduces the side reactions between the electrolyte and the electrodes, leading to a thinner nano-interphase layer comprised of more beneficial species. Crucially, the HVE leads to a different surface reorganization pathway involving the formation of a thinner nanoscale LiNi 2 O 4 spinel phase on the LiNiO 2 surface. Finally, with a high 3D Li + -ion and electronic conductivity, the spinel LiNi 2 O 4 reorganization nanolayer preserves fast Li + transport across the cathode–electrolyte interface, reduces reaction heterogeneity in the electrode and alleviates intergranular cracking within secondary particles, resulting in superior long-term cycle life.

25 ENERGY STORAGE↗