DOE OSTI2025
The primary challenge preventing the deployment of reactor designs that leverage wrought FeCrAl as an advanced light-water reactor (LWR) cladding is irradiation hardening and embrittlement. Wrought FeCrAl alloys experience a loss of post-irradiation ductility and fracture toughness under low-temperature neutron irradiation (< 350°C) resulting from the combined effects of dislocation loop formation and the irradiation-enhanced precipitation of Cr-rich alpha-prime precipitates throughout the microstructure. Over the past decade, significant improvements in our understanding regarding the effect of Cr and Al content have been enabled through neutron irradiations, but even optimized wrought alloys such as C26M remain vulnerable to brittle failure during storage, transportation, and handling following irradiation. This report summarizes multiple irradiation campaigns initiated over the past 7 years and provides recent insights into the effect of (1) minor alloying composition, (2) alloy processing strategy, (3) crystal structure, and (4) the use of advanced oxide dispersion strengthened (ODS) alloys. The first irradiation campaign irradiated body-centered cubic FeCrAl alloy C26M with and without elements such as Mo and Y. It also included face-centered cubic alumina-forming austenitic (AFA) alloys that have a steeper neutronic penalty but that have far superior high-temperature strength than wrought FeCrAl. Finally, this campaign compared conventional wrought C26M with the same material produced using modern powder metallurgical hotisostatic pressing (PM-HIP). The second irradiation campaign, initiated in 2018, irradiated wrought and FeCrAl-ODS materials up to 50 dpa to assess their irradiation resistance to high-doses. The results of this work indicate that wrought C26M suffers significant degradation following neutron irradiation at LWR-relevant temperatures regardless of Mo and Y content. The PM-HIP variant appears to be more resilient to irradiation-induced ductility loss in comparison with wrought variants but still loses almost all ductility by 8 dpa. Notably, the AFAs retained at least 5% total elongation after irradiation at the same dose and temperature condition, although additional deterioration may be expected at higher fluence levels. FeCrAl-ODS materials show the greatest promise as a transformative longer-term accident-tolerant fuel (LT-ATF) cladding material. The extruded 106ZY10C alloy retained 10% total elongation after 16 dpa irradiation and retained 8% total elongation after 50 dpa. Additional challenges with FeCrAl-ODS alloys also remain, including optimization of end cap joining methodologies, enhancement of fracture toughness, scaling production to prove economic viability, and optimizing post-pilger heat treatments to maximize ductility and irradiation resistance. This series of irradiations demonstrates the efficacy of the LWR testbed available within the United States for the rapid irradiation and down-selection of LT-ATF candidates. As the country rapidly accelerates its timeline for the deployment of advanced reactor concepts, the effective utilization of the High Flux Isotope Reactor for separate-effects style irradiations should continue to be prioritized to answer the final questions pertaining to LT-ATF candidates necessary for the deployment of advanced boiling water reactors and small modular reactors.
11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗