NASA NTRS1973

Development of a process for producing ribbon shaped boron filaments

A ribbon-shaped boron filament with a tensile strength of 138 KN/sq cm (200 ksi) was investigated. The investigation was carried out using both carbon and tungsten as substrate materials. No satisfactory results were obtained utilizing uncoated, copper-plated or silicon carbide coated tungsten ribbon substrates. Carbon ribbon substrates were prepared by pyrolysis of stretched polyimide tape. A severe deposition gradient occurred in all dc reactor experiments due to convective cooling at the edge of the substrate that resulted in a weak, nonuniform filament. RF heating, however, completely eliminated this gradient problem and a 90 cm (35.5 in.) long boron ribbon was produced at .85 cm/sec (100 ft/hr) using a frequency of 40.68 megahertz. This boron ribbon, however, exhibited a light-bulb effect during deposition to 59 KN/sq cm (85.7 ksi) were obtained from this ribbon. Several silicon carbide ribbon shaped filaments were also produced during this investigation by decomposition of CH3SiHCl2 onto carbon substrates. Contrary to the boron work, silicon carbide ribbon was readily prepared in dc static reactors. A very uniform and smooth deposition was obtained with strengths up to 71.1 KN/sq cm (103.5 ksi).

Basche, M.↗
DOE OSTI2025

Effective Polarizability in Near-Field Microscopy of Phonon-Polariton Resonances

We investigate the resonant characteristics of planar surfaces and distinct edges of structures with the excitation of phonon-polaritons. We analyze two materials supporting phonon-polariton excitations in the mid-infrared spectrum: silicon carbide, characterized by an almost isotropic dielectric constant, and hexagonal boron nitride, notable for its pronounced anisotropy in a spectral region exhibiting hyperbolic dispersion. We formulate a theoretical framework that accurately captures the excitations of the structure involving phonon-polaritons, predicts the response in scattering-type near-field optical microscopy, and is effective for complex resonant geometries where the locations of hot spots are uncertain. We account for the tapping motion of the probe, perform analysis for different heights of the probe, and demodulate the signal using a fast Fourier transform. Using this Fourier demodulation analysis, we show that light enhancement across the entire apex is the most accurate characteristic for describing the response of all resonant excitations and hot spots. We demonstrate that computing the demodulation orders of light enhancement in the microscope probe accurately predicts its imaging.

Chemistry↗
NASA NTRS2020

Tensile Creep Behavior of SiC(f)/SiC Ceramic Matrix Minicomposites

Single fiber-tow minicomposites represent the major load-bearing element of woven and laminate ceramic matrix composites (CMCs). To understand the effects of fiber type, fiber content, and matrix cracking on tensile creep in SiCf/SiC CMCs, single-tow SiCf/SiC minicomposites with different fiber types and contents were investigated. The minicomposites studied contained either Hi-Nicalon™ or Hi-Nicalon™ Type S SiC fibers with a boron nitride (BN) interphase and a chemical-vapor-infiltrated-silicon-carbide (CVI-SiC) matrix. Tensile creep was performed at 1200 °C in air. A bottom-up creep modeling approach was applied where creep parameters of the fibers and matrix were obtained separately at 1200 °C. Next, a theoretical model based on the rule of mixtures was derived to model the fiber and matrix creep-time-dependent stress redistribution. Fiber and matrix creep parameters, load transfer model results, and numerical modeling were used to construct a creep strain model to predict creep damage evolution of minicomposites with different fiber types and contents.

SiC/SiC Minicomposites Creep↗
NASA NTRS1998

Oxidation of Boron Nitride in Composites

Boron nitride (BN) is a prime candidate for fiber coatings in silicon carbide (SiC) fiber-reinforced SiC matrix composites. The properties of BN allow the fiber to impart beneficial composite properties to the matrix, even at elevated temperatures. The problem with BN is that it is readily attacked by oxygen. Although BN is an internal component of the composite, a matrix crack or pore can create a path for hot oxygen to attack the BN. This type of attack is not well understood. A variety of phenomena have been observed. These include borosilicate glass formation, volatilization of the BN, and under some conditions, preservation of the BN. In this study at the NASA Lewis Research Center, a series of BN materials and BN-containing model composites were methodically examined to understand the various issues dealing with the oxidation of BN in composites. Initial studies were done with a series of monolithic BN materials prepared by hot pressing and chemical vapor deposition (CVD). From these studies, we found that BN showed a strong orientation effect in oxidation and was extremely sensitive to the presence of water vapor in the environment. In addition, CVD material deposited at a high temperature showed much better oxidation behavior than CVD material deposited at a lower temperature.

Jacobson, Nathan S.↗
NASA NTRS2020

Hierarchical Coupling of Molecular Dynamics and Micromechanics to Predict the Elastic Properties of Three-Phase and Four-Phase Silicon Carbide Composites

The results obtained from previously conducted molecular dynamics analysis of silicon carbide (-SiC (6H, 4H, & 2H-SiC), -SiC (3C SiC)), silicon and boron nitride, were utilized as inputs in the MAC/GMC micromechanics software to model and evaluate the elastic properties of three-phase SiC/BN/SiC and four-phase SiC/BN/Si/SiC composites. This method of analysis eliminates the need for back-calculation of the apparent properties of the base constituents from the measured ceramic matrix composites properties. The multiscale models are validated against the available data in literature.

Aluko, Olanrewaju↗
NASA NTRS1962

PYROLYTIC GRAPHITE ROCKET THRUST CHAMBER INVESTIGATION PROJECT. MONTHLY LETTER

This is the Monthly Letter Progress Report for the eighth month of a twelve month technical study directed toward the following objectives: A. Determining analytically and experimentally the feasibility and attractiveness of using free-standing pyrolytic graphite for a radiation cooled liquid rocket thrust chamber and exit nozzle for space application. B. Establishing through analysis and experimental demonstration, a set of design principles to facilitate the design of a reliable pyrolytic graphite thrust chamber assembly for a specific range of operating conditions. C. Demonstrate by means of test firings of complete thrust chamber assemblies, the validity of the design data and principles developed during the program. Preparations have been completed for test firing the two 100 lb. thrust Boron Pyralloy chambers at Marquardt during the first week in March 1962. These two chambers will first be static pressure checked with water to a pressure of 135 psig. The chambers will then be test fired with N204/N2H4-MMH propellants . Test samples of eleven different pyrolytic carbide and nitride materials have been ordered for high temperature oxidation tests and should be delivered by the end of March for evaluation in the plasma torch facility. The specific materials ordered in free- standing condition in thicknesses from 0.030 inch to 0.065 inch were as follows: (a) Pyrolytic graphite (on hand) (b) Pyrolytic graphite-boron alloy (on hand) (c) Pyrolytic graphite-tungsten alloy (d)Boron nitride (e) Titanium nitride (f) Silicon carbide (g) Titanium carbide (h) Zirconium carbide (i) Hafnium carbide (j) Niobium carbide (k) Tantalum carbide (l) High density (1 1-90) graphite (m) High density graphite (heat treated) These materials were ordered from Raytheon, HTM, and American Meta 1 Products . A summary of the available data on the oxidation rates of pyrolytic materials under slow air and rocket motor conditions is shown in Figure 1. High Temperature Materials, Inc. has been contacted relative to providing Pyrographite thrust chambers with extra-thick walls . They believe they can deliver chambers with substantially thicker walls than were possible a short time ago. Such a configuration, with acceptable residual stresses, would provide a longer firing life since it is ultimately limited by the oxidation rate of the chamber wall material. Stress and structural studies have continued. The analytical stress studies point out some of the problems associated with the experimental determination of the elastic constants of this highly anisotropic material. Further analysis may shed light on improved techniques for making these experimental determinations. The large potential weight saving available with the use of pyrolytic graphite as a thrust chamber wall material in a radiation cooled rocket motor has been calculated and is shown graphically in Figure 2. Figure A presents the program progress schedule and the actual expenditures as of 7 February 1962.

ROCKET ENGINE↗
NASA NTRS1973

Arc melting and homogenization of ZrC and ZrC + B alloys

A description is given of the methods used to arc-melt and to homogenize near-stoichiometric ZrC and ZrC-boron alloys, giving attention to the oxygen contamination problem. The starting material for the carbide preparation was ZrC powder with an average particle size of 4.6 micron. Pellets weighing approximately 3 g each were prepared at room temperature from the powder by the use of an isostatic press operated at 50,000 psi. These pellets were individually melted in an arc furnace containing a static atmosphere of purified argon. A graphite resistance furnace was used for the homogenization process.

Darolia, R.↗
NASA NTRS1997

Effects of Fiber Coatings on Tensile Properties of Hi-Nicalon SiC/RBSN Tow Composites

Uncoated Hi-Nicalon silicon carbide (SiC) fiber tows and those coated with a single surface layer of pyrolytic boron nitride (PBN), double layers of PBN/Si-rich PBN, and boron nitride (BN)/SiC coatings deposited by chemical vapor deposition (CVD) method were infiltrated with silicon slurry and then exposed to N2, for 4 hr at 1200 and 1400 C. Room temperature ultimate tensile fracture loads and microstructural characterization of uncoated and CVD coated Hi-Nicalon SiC fiber reinforced reaction-bonded silicon nitride (RBSN) tow composites were measured to select suitable interface coating(s) stable under RBSN processing conditions. Results indicate that room temperature ultimate fracture loads of the uncoated Hi-Nicalon SiC/RBSN tow composites nitrided at both temperatures were significantly lower than those of the uncoated Hi-Nicalon tows without slurry infiltration. In contrast, all CVD coated Hi-Nicalon SiC/RBSN tow composites retained a greater fraction of the dry tow fracture load after nitridation at 1200 C, but degraded significantly after nitridation at 1400 C. Reaction between metal impurities (Fe and Ni) present in the attrition milled silicon powder and uncoated regions of SiC fibers appears to be the probable cause for fiber degradation.

Bhatt, Ramakrishna T.↗
NASA NTRS1999

Modal Acoustic Emission Used at Elevated Temperatures to Detect Damage and Failure Location in Ceramic Matrix Composites

Ceramic matrix composites are being developed for elevated-temperature engine applications. A leading material system in this class of materials is silicon carbide (SiC) fiber-reinforced SiC matrix composites. Unfortunately, the nonoxide fibers, matrix, and interphase (boron nitride in this system) can react with oxygen or water vapor in the atmosphere, leading to strength degradation of the composite at elevated temperatures. For this study, constant-load stress-rupture tests were performed in air at temperatures ranging from 815 to 960 C until failure. From these data, predictions can be made for the useful life of such composites under similar stressed-oxidation conditions. During these experiments, the sounds of failure events (matrix cracking and fiber breaking) were monitored with a modal acoustic emission (AE) analyzer through transducers that were attached at the ends of the tensile bars. Such failure events, which are caused by applied stress and oxidation reactions, cause these composites to fail prematurely. Because of the nature of acoustic waveform propagation in thin tensile bars, the location of individual source events and the eventual failure event could be detected accurately.

Morscher, Gregory N.↗
DOE OSTI2024

Characterization of Precipitation-Strengthening Heat-Resistant Austenitic Stainless Steels for Life-Prediction Modeling

In this study, the role of minor alloying additions in 347H stainless steels (UNS34709, ASTM A240/240M) on creep-rupture properties at 650-750°C and microstructure evolution during isothermal exposure at 750°C has been investigated, aiming to provide the experimental dataset as boundary conditions of physics-based modeling for material/component life prediction. Four different 347H heats containing various amounts of boron and nitrogen additions were prepared and evaluated. The combined additions of B and N are found to stabilize the strengthening secondary M23C6 carbides and retarding the transition from M23C6 to sigma phase precipitates during thermal exposure. The observed kinetics of microstructure evolution reasonably explains the improvement of creep-rupture properties of 347H stainless steels with the B and N additions.

Yamamoto, Yukinori↗
NASA NTRS2015

Concept Demonstration of Dopant Selective Reactive Etching (DSRIE) in Silicon Carbide

Accurate quantification of combustor pressure dynamics for the primary purpose of experimental validation of computational fluid dynamics (CFD) codes requires the use of robust, reliable and sensitive pressure sensors that can resolve sub--pound-per-square-inch pressure levels in high temperature environments (i.e., combustor). The state of the art microfabricated piezoresistive silicon carbide (SiC) pressure sensors that we have developed are capable of operating reliably at 600 degrees Centigrade. This technology was used in support of the ARMD ISRP-ERA (NASA's Aeronautics Research Mission Directorate, Integrated System Research Project - Environmentally Responsible Aviation) program to quantify combustor thermoacoustic instabilities. The results showed that while the SiC pressure sensors survived the high temperature and measured instabilities, the diaphragm (force collector) was not thin enough to be sensitive in resolving sub-pound-per-square-inch pressures; 30 meters is the thinnest diaphragm achievable with conventional reactive ion etching (RIE) processes. Therefore, this precludes its use for sub-pound-per-square-inch pressure measurement with high fidelity. In order to effectively resolve sub-pound-per-square-inch pressures, a thinner more sensitive diaphragm (10 meters) is needed. To achieve this would require a new and innovative fabrication process technique.

static↗
NASA NTRS2010

Methods for producing silicon carbide architectural preforms

Methods are disclosed for producing architectural preforms and high-temperature composite structures containing high-strength ceramic fibers with reduced preforming stresses within each fiber, with an in-situ grown coating on each fiber surface, with reduced boron within the bulk of each fiber, and with improved tensile creep and rupture resistance properties for each fiber. The methods include the steps of preparing an original sample of a preform formed from a pre-selected high-strength silicon carbide ceramic fiber type, placing the original sample in a processing furnace under a pre-selected preforming stress state and thermally treating the sample in the processing furnace at a pre-selected processing temperature and hold time in a processing gas having a pre-selected composition, pressure, and flow rate. For the high-temperature composite structures, the method includes additional steps of depositing a thin interphase coating on the surface of each fiber and forming a ceramic or carbon-based matrix within the sample.

DiCarlo, James A.↗
NASA NTRS2014

Methods for Producing High-Performance Silicon Carbide Fibers, Architectural Preforms, and High-Temperature Composite Structures

Methods are disclosed for producing architectural preforms and high-temperature composite structures containing high-strength ceramic fibers with reduced preforming stresses within each fiber, with an in-situ grown coating on each fiber surface, with reduced boron within the bulk of each fiber, and with improved tensile creep and rupture resistance properties tier each fiber. The methods include the steps of preparing an original sample of a preform formed from a pre-selected high-strength silicon carbide ceramic fiber type, placing the original sample in a processing furnace under a pre-selected preforming stress state and thermally treating the sample in the processing furnace at a pre-selected processing temperature and hold time in a processing gas having a pre-selected composition, pressure, and flow rate. For the high-temperature composite structures, the method includes additional steps of depositing a thin interphase coating on the surface of each fiber and forming a ceramic or carbon-based matrix within the sample.

DiCarlo, James A.↗
NASA NTRS1989

Effect of processing on fracture toughness of silicon carbide as determined by Vickers indentations

Several alpha-SiC materials were processed by hot isostatic pressing (HIPing) and by sintering an alpha-SiC powder containing boron and carbon. Several beta-SiC materials were processed by HIPing a beta-SiC powder with boron and carbon additions. The fracture toughnesses K(sub 1c) of these beta- and alpha-SiC materials were estimated from measurements of Vickers indentations. The three formulas used to estimate K(sub 1c) from the indentation fracture patterns resulted in three ranges of K(sub 1c) estimates. Furthermore, each formula measured the effects of processing differently. All three estimates indicated that fine-grained HIPed alpha-SiC has a higher K(sub 1c) than coarsed-grained sintered alpha-SiC. Hot isostatically pressed beta-SiC, which had an ultrafine grain structure, exhibited a K(sub 1c) comparable to that of HIPed alpha-SiC.

Dannels, Christine M.↗
DOE OSTI2023

Ab Initio Prediction of Ultra‐Wide Band Gap B x Al 1− x N Materials

Abstract Ultra‐wide bandgap (UWBG) materials are poised to play an important role in the future of power electronics. Devices made from UWBG materials are expected to operate at higher voltages, frequencies, and temperatures than current silicon and silicon‐carbide‐based devices and can even lead to significant miniaturization of such devices. In the UWBG field, aluminum nitride and boron nitride have attracted great interest; however, the B x Al 1− x N alloys are much less studied. In this work, using first‐principles simulations combining density‐functional theory and the cluster expansion method, the crystal structure of B x Al 1− x N alloys is predicted. Seventeen ground state structures of B x Al 1− x N with formation energies between 0.11 and 0.25 eV atom ‐1 are found. All of these structures are found to be dynamically stable. The B x Al 1− x N structures are found to have predominantly a tetrahedral bonding environment; however, some structures exhibit sp 2 bonds similar to hexagonal BN. This work expands knowledge of the structures, energies, and bonding in B x Al 1− x N which aids their synthesis, the innovation of lateral or vertical devices, and discovery of compatible dielectric and Ohmic contact materials.

36 MATERIALS SCIENCE↗
NASA NTRS1987

Adhesion, friction, and deformation of ion-beam-deposited boron nitride films

The tribological properties and mechanical strength of boron nitride films were investigated. The BN films were predominantly amorphous and nonstoichiometric and contained small amounts of oxides and carbides. It was found that the yield pressure at full plasticity, the critical load to fracture, and the shear strength of interfacial adhesive bonds (considered as adhesion) depended on the type of metallic substrate on which the BN was deposited. The harder the substrate, the greater the critical load and the adhesion. The yield pressures of the BN film were 12 GPa for the 440C stainless steel substrate, 4.1 GPa for the 304 stainless steel substrate, and 3.3 GPa for the titanium substrate.

Miyoshi, Kazuhisa↗
NASA NTRS1987

Adhesion, friction and deformation of ion-beam-deposited boron nitride films

The tribological properties and mechanical strength of boron nitride films were investigated. The BN films were predominantly amorphous and nonstoichiometric and contained small amounts of oxides and carbides. It was found that the yield pressure at full plasticity, the critical load to fracture, and the shear strength of interfacial adhesive bonds (considered as adhesion) depended on the type of metallic substrate on which the BN was deposited. The harder the substrate, the greater the critical load and the adhesion. The yield pressures of the BN film were 12 GPa for the 440C stainless steel substrate, 4.1 GPa for the 304 stainless steel substrate, and 3.3 GPa for the titanium substrate.

Miyoshi, K.↗