Coordinated Microstructural and Isotopic Characterization of Diamond Inclusions within the Kenna Ureilite
Introduction: The origin of diamonds in ureilitic meteorites, a major family of ultramafic achondrites, has long been debated, with various formation mechanisms inferred, including: 1) shock conversion of preexisting graphite due to a hypervelocity impact on the ureilite parent body [e.g., 1]; 2) vapor deposition during condensation of the solar nebula [e.g., 2]; or 3) static transformation in the mantle of a large planetesimal (>1000 km in diameter) [e.g., 3]. The Kenna ureilite is a 10.9 kg stone that was found in Kansas in 1972 and is dominantly composed of olivine and pigeonite (68% and 22% modal abundance, respectively), together with minor metal and carbon-rich regions. Within the carbon-rich domains researchers have identified microdiamonds up to ~10 µm in size [4]. Methods: Due to the proximity of the extremely hard microdiamonds with soft graphite and moderately hard silicates, achieving an appropriately flat surface for electron backscatter diffraction (EBSD) analysis has proven challenging. We have, therefore, employed a Hitachi ArBlade 5000 broad beam Ar ion milling system to prepare a sample with an adequately uniform surface flatness across the various minerals. The ion milling dramatically im-proved indexing of the EBSD patterns and facilitated high-resolution microstructural analysis of the carbon-rich domains. After microstructural EBSD analyses using an Oxford Symmetry detector we collected coordinated hy-perspectral cathodoluminescence (CL) analyses using a Gatan Monarc system mounted on a JEOL 7900F field emission (FE) scanning electron microscope at NASA Johnson Space Center. A focused ion beam (FIB) foil was extracted from a region of interest and analyzed using a JEOL 2500 FE scanning transmission electron microscope (STEM). In situ carbon and nitrogen isotopic analyses were collected from diamond-bearing domains using a Cameca NanoSIMS 50L at NASA JSC. Results: The carbon rich regions occur as tabular domains between polygonal olivine and pigeonite, and are composed of aggregates of micrometer-scale diamond with intermediate graphite, oxides and metal grains. Within the microdiamonds, {111} twins are abundant, many of which form ragged lamellae consistent with mechanical twinning. The microdiamond assemblages appear to pseudomorph tabular graphite habits, which together with the abundant deformation twins, support a shock transformation mechanism for microdiamond formation within the Kenna meteorite. Further supporting this observation, the diamond laths show close alignment of <111> and <110> between domains, consistent with a solid-state transformation from graphite along <0001> and <1-210>, respec-tively [5]. A FIB foil was extracted from a region with mechanical twins, and high resolution STEM analyses reveal cross-cutting veins of graphite and oriented kamacite crystals together with additional sets of {111} nano-twins formed in at least three orientations. Isotopic analyses of C and N reveal sector zoning patterns [cf. 3] that are unre-lated to the diamond substructure identified by EBSD yet consistent with hyperspectral CL images. Conclusions: These data provide new constraints on microdiamond formation within ureilites. The microdia-monds exhibit orientation variants defined by aligned <111> and <110> axes consistent with inherited crystallo-graphic orientations from transformation of a single hexagonal graphite parent crystal [5]. Crosscutting the micro-diamonds are veins of graphite and kamacite, together with additional {111} nanotwins. Taken together these data suggest that microdiamonds from ureilites formed from a solid state, diffusionless transformation from graphite, likely associated with a major shock event, which was subject to subsequent reversion either during decompression or a later deformation event. The N and C isotopic sector zoning is unrelated to diamond microstructures and likely reflects inheritance from the parent graphite crystal.