DOE OSTI2020

Nanoscale serration characteristics of additively manufactured superalloys

Structural elements made of nickel-based superalloys usually operate at high temperatures. Many surface failure mechanisms such as creep, fatigue, fretting fatigue, corrosion, and stress corrosion cracking start from the surface. Thus, studying the surface mechanical properties and deformation behavior of materials is vital in order to draw a correlation between the surface properties and failures. Herein, a nanoindentation technique was implemented to characterize surface properties of a widely used additively manufactured (AM) superalloy, i.e., Inconel 625. The specimens were tested in a range of temperatures in a vacuum chamber. Serrated plastic flow characterized by pop-in events during nanoindentation, known as Portevin-Le Chatelier (PLC) effect, was observed in all three tested elevated temperatures. This phenomenon depicts itself as bursts of plasticity in the loading section of the load-displacement curves. These bursts were studied comprehensively to explore incipient plasticity. Hertzian contact mechanics were implemented to extract the maximum shear stress beneath the indenter from the pop-in loads. The results show that the initial pop-in load increases as the temperature increases. The average initial pop-in load increases by almost four times from 300 °C to 650 °C. This was attributed to the formation of strengthening precipitates. The average size of the serrations and the magnitude of dislocation nucleation increase from 300 °C to 500 °C and decrease from 500 °C to 650 °C. Finally, the serrations are attributed to the dislocation generation and movement as well as their interaction with the solute atoms and precipitates.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Catalyzed oxidation of nuclear graphite by simulated fission products Sr, Eu, and I

The influence of three fission products Sr, Eu, and I on the oxidation of IG-110 nuclear graphite was studied in the temperature range of 400 to 1000 °C. Sr and Eu were introduced as chlorides, and I was introduced as NaI. The temperature dependence of both CO 2 and CO production during the graphite oxidation measured with mass spectroscopy and infrared spectrometry shows that the introduction of these three compounds to graphite significantly decreases the onset temperature for the oxidation of graphite. Among the three compounds, NaI is the most active towards the oxidation reaction, characterized by a significant decrease of the onset temperature from approximately 650 to 400 °C before and after its introduction to graphite. Separate measurements of CO 2 and CO concentration at varying temperatures enable the calculation of the activation energy for the formation of CO 2 and CO. The activation energies for the oxidation of pure and fission product-impregnated graphite samples decrease in the following order: standard IG-110 graphite, EuCl 3 -impregnated IG-110, SrCl 2 -impregnated IG-110, and NaI-impregnated IG-110. This trend indicates that the three compounds catalyze the oxidation of graphite at temperatures relevant to the operation of high-temperature gas-cooled reactors. Furthermore, it is found that the three compounds can also affect the molar ratio of reaction products CO 2 and CO, and the rates of the graphite oxidation. At temperatures higher than about 850 °C, the impregnated samples exhibit lower CO 2 : CO ratios than the pure graphite. Different from EuCl 3 and NaI, the introduction of SrCl 2 decreases the graphite oxidation rates at temperatures higher than about 770 °C. Their catalytic mechanism can be understood based on a redox cycle of the intermediate active species, promoting the dissociation of molecular oxygen and transfer to the carbon.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2026

Review of SiC material development for nuclear fusion applications: Cross-cutting research and emerging opportunities

The SiC-based materials, particularly SiC-fiber-reinforced SiC matrix (SiC/SiC) composites, show strong potential for structural and functional applications in future fusion power plants because they can operate at high temperatures with a range of coolants and breeders, thereby enabling higher energy conversion efficiency. Here, this paper presents recent advancements in the development of SiC-based materials, focusing on processing techniques and material performance and resistance under fusion-relevant environments. The processing activities have emphasized near-net-shape fabrication and the joining of SiC subcomponents, with processing methods and material compositions informed by previous irradiation experiments on various grades of SiC. Research on irradiation effects has remained focused on degradation mechanisms and the microstructural optimization of SiC/SiC composites irradiated to high neutron damage levels. Analysis of irradiation defects in SiC has advanced via the application of cutting-edge characterization methods, among which Raman spectroscopy is becoming a common tool to assess atomic-scale chemical disorder. Fusion–fission crosscutting irradiation research has explored combined effects in SiC/SiC composites with application-relevant geometries, including bowing of SiC/SiC composite channels under neutron flux gradients, stress evolution in SiC/SiC composite tubes under through-thickness temperature gradients, and irradiation-enhanced corrosion in SiC. Finally, research opportunities for component testing and assessment under fusion-relevant conditions, in support of emerging concepts from the private fusion sector, are discussed.

Advanced manufacturing↗
DOE OSTI2021

Developing an experimental-computational framework to investigate the deformation mechanisms and mechanical properties of Al-8Ce-10Mg alloys at micro and macroscales

There is a promising future for the use of aluminum-cerium-magnesium alloys in a broad range of applications, including devices that operate at high temperatures. With cerium currently considered a waste product of rare earth mining validation studies of possible applications are essential to reduce the environmental waste. Here, a computational-experimental framework is developed to investigate the role both the intermetallic and matrix have on the mechanical properties of these alloys. A set of experiments, including SEM/EBSD imaging, nanoindentation, in-situ SEM tensile testing, and in-situ SEM-DIC tests are performed to characterize the microstructure and mechanical properties of these alloys. Furthermore, the elastic, plastic, and failure deformation mechanisms of the microstructure, and their correlation with the bulk scale mechanical properties are investigated. Experimental results are also used to calibrate parameters for a crystal plasticity finite element model, by performing a computational framework that minimizes the error between the computational and experimental results. This model is then utilized to investigate how the area percentage of intermetallics and the crystallographic texture control the mechanical properties of the alloy. Simulation results show that an increase in the percentage of intermetallics increase the strength but decrease the ductility of the alloy. Also, a change in material texture improves strength and reduces damage that leads to material failure. The development of the crystal plasticity model, as discussed in this work, opens opportunities for future investigations of similar aluminum-cerium-magnesium alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Tuning Surface, Phase, and Magnetization of Superparamagnetic Magnetite by Ionic Liquids: Single-Step Microwave-Assisted Synthesis

Achieving colloidal and chemical stability in ferrofluids by surface modification requires multiple steps, including purification, ex situ modification steps, and operation at high temperatures. In this study, a single-step microwave-assisted methodology is developed for iron oxide nanoparticle (IONP) synthesis utilizing a series of imidazolium-based ionic liquids (ILs) with chloride, bis(trifluoromethylsulfonyl)imide, and pyrrolide anions as the reaction media, thus eliminating the use of volatile organics while enabling rapid synthesis at 80 °C as well as in situ surface functionalization. The characterized surface functionality, hydrodynamic particle size, magnetization, and colloidal stability of the IONPs demonstrate a strong dependence on the IL structure, ion coordination strength, reactivity, and hydrophilicity. The IONPs present primarily a magnetite (Fe 3 O 4 ) phase with superparamagnetism with the highest saturation magnetization at 81 and 73 emu/g at 10 and 300 K, respectively. Depending on the IL coating, magnetization and exchange anisotropy decrease by 20 and 2–3 emu/g (at 35 wt % IL), respectively, but still represent the highest magnetization achieved for coated IONPs by a coprecipitation method. Further, the surface-functionalized superparamagnetic magnetite nanoparticles show good dispersibility and colloidal stability in water and dimethyl sulfoxide at 0.1 mg/mL concentration over the examined 3 month period. This study reports on the intermolecular and chemical interactions between the particle surface and the ILs under synthetic conditions as they relate to the magnetic and thermal properties of the resulting IONPs that are well suited for a variety of applications, including separation and catalysis.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Superior zero thermal expansion dual-phase alloy via boron-migration mediated solid-state reaction

Rapid progress in modern technologies demands zero thermal expansion (ZTE) materials with multi-property profiles to withstand harsh service conditions. Thus far, the majority of documented ZTE materials have shortcomings in different aspects that limit their practical utilization. Here, we report on a superior isotropic ZTE alloy with collective properties regarding wide operating temperature windows, high strength-stiffness, and cyclic thermal stability. A boron-migration-mediated solid-state reaction (BMSR) constructs a salient “plum pudding” structure in a dual-phase Er-Fe-B alloy, where the precursor ErFe 10 phase reacts with the migrated boron and transforms into the target Er 2 Fe 14 B (pudding) and α-Fe phases (plum). The formation of such microstructure helps to eliminate apparent crystallographic texture, tailor and form isotropic ZTE, and simultaneously enhance the strength and toughness of the alloy. These findings suggest a promising design paradigm for comprehensive performance ZTE alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Balancing elementary steps enables coke-free dry reforming of methane

Balancing kinetics, a crucial priority in catalysis, is frequently achieved by sacrificing activity of elementary steps to suppress side reactions and enhance catalyst stability. Dry reforming of methane (DRM), a process operated at high temperature, usually involves fast C-H activation but sluggish carbon removal, resulting in coke deposition and catalyst deactivation. Studies focused solely on catalyst innovation are insufficient in addressing coke formation efficiently. Herein, we develop coke-free catalysts that balance kinetics of elementary steps for overall thermodynamics optimization. Beginning from a highly active cobalt aluminum oxide (CoAl 2 O 4 ) catalyst that is susceptible to severe coke formation, we substitute aluminum (Al) with gallium (Ga), reporting a CoAl 0.5 Ga 1.5 O 4 -R catalyst that performs DRM stably over 1000 hours without observable coke deposition. We find that Ga enhances DRM stability by suppressing C-H activation to balance carbon removal. A series of coke-free DRM catalysts are developed herein by partially substituting Al from CoAl 2 O 4 with other metals.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Bio-inspired gas sensing: boosting performance with sensor optimization guided by “machine learning”

The performance of existing gas sensors often degrades in field conditions because of the loss of measurement accuracy in the presence of interferences. Thus, new sensing approaches are required with improved sensor selectivity. We are developing a new generation of gas sensors, known as multivariable sensors, that have several independent responses for multi-gas detection with a single sensor. In this study, we analyze the capabilities of natural and fabricated photonic three-dimensional (3-D) nanostructures as sensors for the detection of different gaseous species, such as vapors and non-condensable gases. We employed bare Morpho butterfly wing scales to control their gas selectivity with different illumination angles. Next, we chemically functionalized Morpho butterfly wing scales with a fluorinated silane to boost the response of these nanostructures to the vapors of interest and to suppress the response to ambient humidity. Further, we followed our previously developed design rules for sensing nanostructures and fabricated bioinspired inorganic 3-D nanostructures to achieve functionality beyond natural Morpho scales. These fabricated nanostructures have embedded catalytically active gold nanoparticles to operate at high temperatures of ≈300 °C for the detection of gases for solid oxide fuel cell (SOFC) applications. Our performance advances in the detection of multiple gaseous species with specific nanostructure designs were achieved by coupling the spectral responses of these nanostructures with machine learning (a.k.a. multivariate analysis, chemometrics) tools. Our newly acquired knowledge from studies of these natural and fabricated inorganic nanostructures coupled with machine learning data analytics allowed us to advance our design rules for sensing nanostructures toward the required gas selectivity for numerous gas monitoring scenarios at room and high temperatures for industrial, environmental, and other applications.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Metal–ceramic composite structures for fabrication of high power density plasmonic devices

The recent decade brought many advances to plasmonics, but high power density plasmonic antennas designed to behave as heaters or operate in high temperature environments are still facing material stability challenges preventing their ultimate use. Gold has been the optimal choice among plasmonic materials but experiences morphology changes at temperature that result in device efficiency reduction and failure. Bulk titanium nitride has been explored as a solution but has deal-breaking tradeoffs in device quality factor. In this paper, we explore via proof-of-concept the use of a metal–ceramic composite structure to determine whether a bulk Au nanorod can provide strong plasmonic resonances while coated with an ultrathin conformal layer of titanium nitride or silica to provide morphological stability and sufficient plasmonic activity without excessive resonance quality degradation. We show SEM-level morphological stability for temperatures up to 500 °C with coatings below 4 nm. Computer modeling suggests the ultrathin titanium nitride has detrimental effects on the strong plasmonic resonances of a Au nanorod. Here, we then looked into other possible coatings for solutions to stabilize high power density plasmonic antennas including plasmonic oxides, metal adhesion layers, and silica, the latter appearing to be the best option while lowering the overall peak electric field intensity, the silica increases the electric field intensity at its boundary.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Gas-phase microactuation using kinetically controlled surface states of ultrathin catalytic sheets

Biological systems convert chemical energy into mechanical work by using protein catalysts that assume kinetically controlled conformational states. Synthetic chemomechanical systems using chemical catalysis have been reported, but they are slow, require high temperatures to operate, or indirectly perform work by harnessing reaction products in liquids (e.g., heat or protons). Here, we introduce a bioinspired chemical strategy for gas-phase chemomechanical transduction that sequences the elementary steps of catalytic reactions on ultrathin (<10 nm) platinum sheets to generate surface stresses that directly drive microactuation (bending radii of 700 nm) at ambient conditions (T = 20 °C; P total = 1 atm). When fueled by hydrogen gas and either oxygen or ozone gas, we show how kinetically controlled surface states of the catalyst can be exploited to achieve fast actuation (600 ms/cycle) at 20 °C. Finally, we also show that the approach can integrate photochemically controlled reactions and can be used to drive the reconfiguration of microhinges and complex origami- and kirigami-based microstructures.

42 ENGINEERING↗
DOE OSTI2021

Accelerated molecular dynamics simulations of dislocation climb in nickel

We report the mechanical behavior of materials operating under high temperatures is strongly influenced by creep mechanisms such as dislocation climb, which is controlled by the diffusion of vacancies. However, atomistic simulations of these mechanisms have traditionally been impractical due to the long time scales required. To overcome these time scale challenges, we use Parallel Trajectory Splicing (ParSplice), an accelerated molecular dynamics method, to simulate dislocation climb in nickel. We focus on modeling the activity of a vacancy near a jog on an edge dislocation in order to observe vacancy pipe diffusion and vacancy absorption at the jog. From rigorously constructed trajectories encompassing more than 2000 vacancy absorption events over a simulation time of more than 4μs at 900 K, a comprehensive sampling of available atomistic mechanisms is collated and analyzed further with molecular statics calculations. We estimate average rates for pipe diffusion and vacancy absorption into the jog using data from the dynamic and static calculations, finding very good agreement. Our results strongly suggest that the dominant mechanism for vacancy absorption by jogs is via biased diffusion to the dislocation core followed by fast pipe diffusion to the jog.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Performance of Public Film Cooling Geometries Produced Through Additive Manufacturing

Abstract Film cooling is an essential cooling technology to allow modern gas turbines to operate at high temperatures. For years, researchers in this community have worked to improve the effectiveness of film cooling configurations by maximizing the coolant coverage and minimizing the heat flux from the hot gas into the part. Working toward this goal has generated many promising film cooling concepts with unique shapes and configurations. However, until recently, many of these designs were challenging to manufacture in actual turbine hardware due to limitations with legacy manufacturing methods. Now, with the advances in additive manufacturing, it is possible to create turbine parts using high-temperature nickel alloys that feature detailed and unique geometry features. Armed with this new manufacturing power, this study aims to build and test the promising designs from the public literature that were previously difficult or impossible to implement. In this study, different cooling hole designs were manufactured in test coupons using a laser powder bed fusion process. Each nickel alloy coupon featured a single row of engine scale cooling holes, fed by a microchannel. To evaluate performance, the overall cooling effectiveness of each coupon was measured using a matched Biot test at engine relevant conditions. The results showed that certain hole shapes are better suited for additive manufacturing than others and that the manufacturing process can cause significant deviations from the performance reported in the literature.

Engineering↗
DOE OSTI2022

Quantification of Lanthanides in a Molten Salt Reactor Surrogate Off-Gas Stream Using Laser-Induced Breakdown Spectroscopy

To enable the deployment of molten salt reactor technology, the development of off-gas treatment systems and advanced monitoring tools capable of operating with high temperatures and radiation fields while delivering near real-time information is necessary. Here, we aim to fulfill this requirement and proposes laser-induced breakdown spectroscopy (LIBS) for monitoring molten salt aerosol streams. A sheath gas measuring method was developed to protect optical elements from aerosol particles and to ensure a relatively constant aerosol stream for measurement. An aqueous system was studied to demonstrate the utility of LIBS for monitoring possible fission products in an aerosol stream: Gd, Nd, and Sm up to 2000 parts per million (ppm). A calibration model was built using partial least squares (PLS) regression with five, six, and nine latent variables for Gd, Nd, and Sm, respectively. This calibration model successfully estimated the concentrations of three test samples, which were validated with inductively charged plasma optical emission spectroscopy measurements at a 99.9% confidence interval. To enhance these models, a genetic algorithm was used to filter the spectra before entering the PLS model, thereby limiting the spectral features being regressed to those with greater correlations to concentration. This allowed for the number of latent variables used in the PLS models to be reduced to four, three, and three for Gd, Nd, and Sm, respectively. Finally, the genetic algorithm-filtered PLS models were used to predict the concentrations of the aerosol stream on a real-time dataset and resulted in a 73%, 18%, and 25% improvement in root mean squared error of prediction compared to the original PLS models developed.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2020

An Investigation of Liquefaction in Irradiated TRIGA Fuel Exposed to Relatively High Temperatures

This report presents the findings of an investigation into high temperature fuel cladding chemical interactions (FCCI) in Training, Research, Isotopes, General Atomics (TRIGA) fuel rods. A TRIGA fuel-rod core or meat is principally composed of uranium (U) particles dispersed in a zirconium hydride (Zr H) matrix. The fuel is clad in sealed 304SS or Incoloy 800 tubes. At high temperatures, the fuel will interact with the cladding, resulting in FCCI. To investigate the FCCI (in this case, liquefaction), irradiated TRIGA fuel rods were exposed to relatively high temperatures in furnace tests. The tests were performed at different temperatures using segments from an irradiated TRIGA fuel rod at the Hot Fuel Examination Facility located at Idaho National Laboratory (INL). The data from this study is important for developing a better understanding of the performance of U-ZrH fuel type during transient events (e.g., a Loss of Coolant Accident (LOCA) event) that may result in high temperatures while operating a TRIGA reactor. Furnace tests were run for 6 hours at 730, 800, 900, 950, and 1,000°C. One test was run for 12 hours at 950°C. Post-test microstructural characterization was performed on the heat-treated samples using optical metallography to look for evidence of liquefaction. Additionally, microstructural characterization was performed using scanning electron microscopy to investigate the microstructure of the as-irradiated fuel before heat treatment and the microstructural changes that occurred after heat treating for the 730 and 950°C heat treatments for 6 hours. Results of the analysis were compared to those produced during diffusion studies performed using unirradiated TRIGA fuel meat and type 304 stainless steel. A gap is typically present in as-irradiated fuel that limits any possibility for chemical interaction between the fuel and cladding. Optical metallography (OM) was used to identify areas in the specimens heat treated at 950 and 1000°C where fuel and cladding contact was satisfactory for the FCCI to transpire. The bulk of the interaction zones that form due to FCCI developed in the fuel meat and not as much in the cladding. Even in the sample tested at 1,000°C, no evidence was found that gross fuel meat or cladding melting had occurred. Only limited porosity was found in the fuel meat that possibly could have been due to melting of a particular precipitate phase or phases that had formed during FCCI. These results agreed with those reported for the unirradiated diffusion couple studies.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

Synergistic Coating-Alloy Development for Harsh Environments

The primary objective of the work was to demonstrate model alloy-coating combinations with: A. Improved oxidation resistance with a barrier coating by at least 2x vs. uncoated alloy; B. Uniform coating on a greater than 100:1 aspect ratio structure; and C. Expected reduction of lifecycle cost of a component of >25% based on customer inputs. All three objectives have been achieved.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Ultra-fast and Thick Boriding of Geothermal Casing to Enhance Reliability

Harnessing the heat that is continuously generated underneath the Earth’s crust (geothermal) is a clean and renewable source of energy. Geothermal energy can be used to heat and cool buildings, including greenhouses, and to generate electrical power. Compared to other renewable energy sources such as solar and wind, geothermal energy is more reliable because it is available all the time and versatile in its many forms of application and deployment. Nonetheless, the deployment and extensive use of geothermal energy still lags behind other renewable sources due to some technical, but mainly economic challenges. Upfront costs of geothermal power well development are relatively high. Some of this high cost is attributed to the use of expensive construction materials to ensure adequate performance during operation. For example, Inconel 625, super duplex 2507, and titanium alloy materials are used in downhole casings, piping, and other components exposed to brine solution to withstand harsh operating environments (high temperature and corrosive environments). Relatively low-cost carbon steel can be used in many of these components in geothermal power plants; however, they are susceptible to excessive corrosion, thereby limiting their useful lifespan. Ultra-fast boriding (UFB) surface treatment of carbon steel may drastically increase its corrosion resistance thereby providing a cost-effective material solution in geothermal applications. Scientists at Argonne National Laboratory (ANL) recently developed a technique to accelerate the boriding process using a high-temperature electrochemical process to produce relatively thick boride layers on various metal and alloy materials in minutes rather than the several hours it takes through the typical pack boriding process; hence, the process is designated UFB. The process uses molten borax salt at 900– 1000°C in an electrochemical cell in which the material to be borided is the cathode and a graphite plate is the anode. Continuous and durable boride layers with thicknesses of 100–300 µm have been produced on a variety of metals and alloys in one hour. Such a surface layer can indeed be a cost-effective pathway to prevent corrosion of casing materials in contact with the chemically aggressive and corrosive geothermal brine fluids.

15 GEOTHERMAL ENERGY↗
DOE OSTI2023

Particle Separator for Improved Flameless Pressurized Oxy-Combustion

The team of Southwest Research Institute® (SwRI®), ITEA, Electric Power Research Institute, Inc. (EPRI), and General Electric Global Research (GE) is advancing Flameless Pressurized Oxy-combustion (FPO), a novel coal technology. This effort seeks to develop a particle separator for the hot-gas stream leaving the FPO loop. In order to maximize the energy extracted from the cycle, the hot gas is put through a turbo-expander before flue-gas treatment. The particle separator designed under this project sought to operate at high temperature and with low-pressure drop, protecting the turbo-expander from erosion damage. The team engaged potential vendors for the test, developed plans for the pilot test loop modification, and refined requirements for the commercial turbo-expander.

01 COAL, LIGNITE, AND PEAT↗
DOE OSTI2024

Additively Manufactured Molten Salt to Supercritical Carbon Dioxide Heat Exchanger

Design, fabrication, and experimental characterization of the performance of a molten salt (MS)-to-supercritical carbon dioxide (sCO 2 ) heat exchanger (HE) for concentrating solar power (CSP) applications using laser powder bed fusion (LPBF) additive manufacturing (AM) of nickel-based superalloys is presented in this report. The hypothesis is that such additively manufactured HEs will result in a monolithic, compact, low-pressure drop HE that is durable under cyclic operation at high temperature and high pressure in a corrosive salt environment. Two nickel-based superalloys were considered in the project- Haynes 230 (H230) and Haynes 282 (H282). Process windows for LPBF AM were established to provide dense low porosity parts for both alloys. Creep tests results on heat treated AM H230 and H282 samples showed that the AM fabricated specimens were as robust as the wrought specimens and showed no deficit in creep strength at high temperatures. Haynes 282 was down selected for the HE fabrication based on better dimensional tolerance, better corrosion resistance to chloride salt, and higher creep strength.

14 SOLAR ENERGY↗