Sputter-Coated TiO 2 Films as Passivation and Hole Transfer Layers for Improved Energy Conversion with Solar Fuel WO 3 /CuWO 4 Photoanodes
Atomic layer deposited (ALD) “leaky” TiO 2 have gained interest as charge-selective protection layers for semiconductor solar fuel electrodes. Here we demonstrate the use of sputter-deposited TiO 2 layers as hole selective contacts for WO 3 /CuWO 4 type 2 heterojunction water oxidation photoanodes for the first time. TiO 2 protection layers with varying thicknesses (2 to 128 nm) were deposited using the RF magnetron sputtering technique. The resulting TiO 2 films are amorphous based on Raman spectroscopy and powder XRD. Photoelectrochemical scans and Vibrating Kelvin probe photovoltage spectroscopy show that 2-8 nm TiO 2 layers nearly double the photocurrent to 0.97 mA cm -2 under AM 1.5 illumination (19% AQE at 350 nm), increase the surface photovoltage signal by 25%, and increase the WO 3 /CuWO 4 bandgap. These effects can be attributed to the selectivity of TiO 2 for photoholes. Additionally, SPV data suggest that TiO 2 overlayers suppress copper-based surface recombination defects. Reduced photocurrent and the photovoltage are seen in thicker TiO 2 films (16 to 128 nm) as a result of an increasing hole transfer resistance and because of light shading effects according to photoaction spectra. The TiO 2 films also improve the stability of the WO 3 /CuWO 4 photoelectrodes, allowing nearly constant O 2 evolution over 3 hours after an initial 20-35% loss. Overall, this work establishes RF magnetron sputtering as a useful method to install amorphous TiO 2 passivation layers for improved WO 3 /CuWO 4 solar fuel photoelectrodes. Furthermore, we show how the combination of PEC with SPV measurements provides insight into the function of the TiO 2 coatings.