NASA NTRS2005

Effects of High-Temperature Exposures on the Fatigue Life of Disk Superalloys Examined

Tests used to characterize the low-cycle-fatigue resistance of disk superalloys are usually performed at cyclic frequencies of 0.33 Hz or faster. However, service conditions for disks in some aerospace and land-based gas turbine engines can produce major cycle periods extending from minutes to hours and days. Over a service life, this can produce total service times near the maximum temperature that exceed 100 hr for aerospace applications and 100,000 hr for land-based applications. Such time-dependent effects of realistic mission cycles on fatigue resistance can be significant in superalloy disks, and need to be considered for accurate disk life prediction. The purpose of this study at the NASA Glenn Research Center was to examine the effects of extended exposures and extended cycle periods on the fatigue resistance of two disk superalloys. Current alloy Udimet 720 (Special Metals Corporation, Huntington, WV) disk material was provided by Solar Turbines/Caterpillar Co., and advanced alloy ME3 was provided by the NASA Ultra-Efficient Engine Technologies (UEET) Project, in powder-metallurgy-processed, supersolvus heat-treated form. Fatigue specimens were fully machined and exposed in air at temperatures of 650 to 704 C for extended times. Then, they were tested using conventional fatigue tests with a total strain range of 0.70 percent and a minimum-to-maximum strain ratio of zero to determine the effects of prior exposure on fatigue resistance. Subsequent tests with extended dwells at minimum strain in each fatigue cycle were performed to determine cyclic exposure effects.

Gabb, Timothy P.↗

NASA NTRS1988

The analysis of fatigue crack growth mechanism and oxidation and fatigue life at elevated temperatures

Two quantitative models based on experimentally observed fatigue damage processes have been made: (1) a model of low cycle fatigue life based on fatigue crack growth under general-yielding cyclic loading; and (2) a model of accelerated fatigue crack growth at elevated temperatures based on grain boundary oxidation. These two quantitative models agree very well with the experimental observations.

Liu, H. W.↗

NASA NTRS1978

Fractographic evaluation of creep effects on strain-controlled fatigue-cracking of AISI 304LC and 316 stainless steel

Analysis of high temperature low cycle fatigue of AISI 304LC and 316 stainless steels by the method of strainrange partitioning results in four separate strainrange versus life relationships, depending upon the way in which creep-strain and plastic strain are combined within a cycle. Fractography is used in this investigation of the creep-fatigue interaction associated with these cycles. The PP and PC-cycle fractures were transgranular. The PC-cycle resulted in fewer cycles of initiation and shorter total cyclic life for the same applied inelastic strainrange. The CC-cycle had mixed transgranular and intergranular fracture, fewer cycles of initiation and shorter cycle life than PP or PC. The CP-cycle had fully integranular cracking, and failed in fewer cycles than were required for cracks to initate for PP,PC, and CC.

Oldrieve, R. E.↗

NASA NTRS1993

An analysis of isothermal, bithermal, and thermomechanical fatigue data of Haynes 188 and B1900+Hf by energy considerations

The low-cycle fatigue behavior of Haynes 188 and B1900+Hf under isothermal, bithermal, and thermomechanical loading conditions has been analyzed on the basis of the total hysteresis energy expended per cycle. It has been observed that in the case of isothermal fatigue the total hysteresis energy correlates well with the fatigue life. In the case of bithermal 'high rate' fatigue, for a given total hysteresis energy per cycle, the fatigue life is equal to or greater than the isothermal fatigue life at the maximum bithermal temperature. This observation could be used to establish a lower bound on life for design purposes. In one case of bithermal creep-fatigue and in thermomechanical fatigue, the life is shorter than that corresponding to the isothermal life at the maximum temperature. The energy supplied, per se, may not always give a systematic correlation with the fatigue life in the cases where time-dependent creep and environmental effects are encountered. Thus, in bithermal creep-fatigue and thermomechanical fatigue, the role of creep and environment and their dependence on the energy supplied have to be properly accounted for before the energy term can be used for life prediction.

Radhakrishnan, V. M.↗

NASA NTRS1980

Evaluation of the cyclic behavior of aircraft turbine disk alloys, part 2

Several nickel-base aircraft turbine disk superalloys were evaluated at 650 C for resistance to fatigue crack initiation and propagation under cyclic and cyclic/dwell conditions. Controlled strain low cycle fatigue (LCF) and controlled load crack propagation tests were performed and results utilized to provide a direct comparison among the alloys. Tests were performed on selected alloys to evaluate the effects of hold times, mean stresses, stress-dwell cycle types, inert environment, and contractor test methods. At the lower total strain ranges of interest, the alloys exhibited generally increasing initiation life with increasing tensile strength for both cyclic (0.33 Hz) and cyclic/dwell (900-sec hold per cycle) conditions. Rank order of the alloys by LCF initiation life changed substantially at higher strain ranges, approaching the rank order expected from monotonic tensile ductilities. The effect of the 900 sec (15 min) hold time fatigue life varied significantly from alloy to alloy. Generally, the higher-strength, finer-grained alloys exhibited more significant reductions in fatigue life due to the dwell. The effects of mean strain were found to be negligible and the effects of mean stress were pronounced. At high strain ranges the mean stress was near zero and did not contribute to reduction in life. At low strain ranges, however, mean stresses were large and significant reductions in LCF lives occurred.

Cowles, B. A.↗

DOE OSTI2022

Employing sequential experiments to gain insights on the interaction between creep and fatigue damage in Ni‐base superalloys

Abstract The interaction between creep and fatigue damage in Ni‐base superalloy CMSX‐8 was explored using a sequential workflow that decouples creep and fatigue steps to quantify how accumulated creep damage interacts with subsequent isothermal low‐cycle fatigue (LCF) and vice versa. Two workflows were considered: creep followed by LCF and LCF followed by creep. For the first workflow, the subsequent LCF was evaluated at temperatures of 20°C, 750°C, and 1100°C. It was found that the extent of deleterious interaction of prior creep on LCF depended on increasing subsequent fatigue test temperature. For the LCF followed by creep, fatigue tests were first conducted at 20°C and 1100°C to 60% of life, and then creep was conducted at 800°C, where primary creep is promoted, or 900°C, where primary creep is absent. LCF damage accumulated at 1100°C accelerated creep and decreased ductility, while fatigue damage at room temperature had minimal effect on the creep behavior.

Gorgannejad, Sanam↗

NASA NTRS1992

Elevated temperature axial and torsional fatigue behavior of Haynes 188

The results of high-temperature axial and torsional low-cycle fatigue experiments performed on Haynes 188, a wrought cobalt-base superalloy, are reported. Fatigue tests were performed at 760 C in air on thin-walled tubular specimens at various ranges under strain control. Data are also presented for coefficient of thermal expansion, elastic modulus, and shear modulus at various temperatures from room to 1000 C, and monotonic and cyclic stress-strain curves in tension and in shear at 760 C. The data set is used to evaluate several multiaxial fatigue life models (most were originally developed for room temperature multiaxial life prediction) including von Mises equivalent strain range (ASME boiler and pressure vessel code), Manson-Halford, Modified Multiaxiality Factor (proposed here), Modified Smith-Watson-Topper, and Fatemi-Socie-Kurath. At von Mises equivalent strain ranges (the torsional strain range divided by the square root of 3, taking the Poisson's ratio to be 0.5), torsionally strained specimens lasted, on average, factors of 2 to 3 times longer than axially strained specimens. The Modified Multiaxiality Factor approach shows promise as a useful method of estimating torsional fatigue life from axial fatigue data at high temperatures. Several difficulties arose with the specimen geometry and extensometry used in these experiments. Cracking at extensometer probe indentations was a problem at smaller strain ranges. Also, as the largest axial and torsional strain range fatigue tests neared completion, a small amount of specimen buckling was observed.

Bonacuse, Peter J.↗

NASA NTRS1992

Deformation mechanisms of NiAl cyclicly deformed near the brittle-to-ductile transformation temperature

One of the ongoing challenges of the aerospace industry is to develop more efficient turbine engines. Greater efficiency entails reduced specific strength and larger temperature gradients, the latter of which means higher operating temperatures and increased thermal conductivity. Continued development of nickel-based superalloys has provided steady increases in engine efficiency and the limits of superalloys have probably not been realized. However, other material systems are under intense investigation for possible use in high temperature engines. Ceramic, intermetallic, and various composite systems are being explored in an effort to exploit the much higher melting temperatures of these systems. NiAl is considered a potential alternative to conventional superalloys due to its excellent oxidation resistance, low density, and high melting temperature. The fact that NiAl is the most common coating for current superalloy turbine blades is a tribute to its oxidation resistance. Its density is one-third that of typical superalloys and in most temperature ranges its thermal conductivity is twice that of common superalloys. Despite these many advantages, NiAl requires more investigation before it is ready to be used in engines. Binary NiAl in general has poor high-temperature strength and low-temperature ductility. On-going research in alloy design continues to make improvements in the high-temperature strength of NiAl. The factors controlling low temperature ductility have been identified in the last few years. Small, but reproducible ductility can now be achieved at room temperature through careful control of chemical purity and processing. But the mechanisms controlling the transition from brittle to ductile behavior are not fully understood. Research in the area of fatigue deformation can aid the development of the NiAl system in two ways. Fatigue properties must be documented and optimized before NiAl can be applied to engineering systems. More importantly though, probing the deformation mechanisms operating in fatigue will lead to a better understanding of NiAl's unique characteristics. Low cycle fatigue properties have been reported on binary NiAl in the past year, yet those studies were limited to two temperature ranges: room temperature and near 1000 K. Eventually, fatigue property data will be needed for a wide range of temperatures and compositions. The intermediate temperature range near the brittle-to-ductile transition was chosen for this study to ascertain whether the sharp change occurring in monotonic behavior also occurs under cyclic conditions. An effort was made to characterize the dislocation structures which evolved during fatigue testing and comment on their role in the deformation process.

Antolovich, Stephen D.↗

NASA NTRS1996

Mechanisms of High-Temperature Fatigue Failure in Alloy 800H

The damage mechanisms influencing the axial strain-controlled Low-Cycle Fatigue (LCF) behavior of alloy 800H at 850 C have been evaluated under conditions of equal tension/compression ramp rates (Fast-Fast (F-F): 4 X 10(sup -3)/s and Slow-Slow (S-S): 4 X 10(sup -5)/s) and asymmetrical ramp rates (Fast-Slow (F-S): 4 x 10(sup -3)/s / 4 X 10(sup -5/s and Slow-Fast (S-F): 4 X 10(sup -5) / 4 X 10(sup -3)/s) in tension and compression. The fatigue life, cyclic stress response, and fracture modes were significantly influenced by the waveform shape. The fatigue lives displayed by different loading conditions were in the following order: F-F greater than S-S greater than F-S greater than S-F. The fracture mode was dictated by the ramp rate adopted in the tensile direction. The fast ramp rate in the tensile direction led to the occurrence of transgranular crack initiation and propagation, whereas the slow ramp rate caused intergranular initiation and propagation. The time-dependent processes and their synergistic interactions, which were at the basis of observed changes in cyclic stress response and fatigue life, were identified. Oxidation, creep damage, dynamic strain aging, massive carbide precipitation, time-dependent creep deformation, and deformation ratcheting were among the several factors influencing cyclic life. Irrespective of the loading condition, the largest effect on life was exerted by oxidation processes. Deformation ratcheting had its greatest influence on life under asymmetrical loading conditions. Creep damage accumulated the greatest amount during the slow tensile ramp under S-F conditions.

BhanuSankaraRao, K.↗

NASA NTRS1989

Torsional and biaxial (tension-torsion) fatigue damage mechanisms in Waspaloy at room temperature

Strain controlled torsional and biaxial (tension-torsion) low cycle fatigue behavior of Waspaloy was studied at room temperature as a function of heat treatment. Biaxial tests were conducted under proportional and nonproportional cyclic conditions. The deformation behavior under these different cyclic conditions was evaluated by slip trace analysis. For this, a Schmidt-type factor was defined for multiaxial loading conditions, and it was shown that when the slip deformation is predominant, nonproportional cycles are more damaging than proportional or pure axial or torsional cycles. This was attributed to the fact that under nonproportional cyclic conditions, deformation was through multiple slip, as opposed to single slip for other loading conditions, which gave rise to increased hardening. The total life for a given test condition was found to be independent of heat treatment. This was interpreted as being due to the differences in the cycles to initiation and propagation of cracks.

Jayaraman, N.↗

DOE OSTI2025

Fatigue Performance of an Improved Creep Strength 10%Cr Steel

The deployment of 9-12% Cr steels for elevated temperature applications up to 650 °C presents a cost-effective alternative to more expensive nickel-based alloys in steam turbine power generation. To enhance creep resistance at this temperature range, a novel ferritic-martensitic steel, designated CPJ7, was developed and fabricated at the National Energy Technology Laboratory. The alloy design aimed to mitigate the transformation of strengthening carbides into deleterious phases that degrade creep performance. Results have demonstrated that CPJ7 exhibits favorable creep and oxidation resistance at 650 °C. However, its fatigue performance remains unexplored. This study builds upon prior research by evaluating the low cycle fatigue behavior of CPJ7 and verifying that modifications beneficial to creep performance were not detrimental to the fatigue performance. The alloy was tested at both 650 °C and ambient temperature under fully reversed bending conditions (R = − 1) and a load ratio of 0.05. Furthermore, the alloy exhibits cyclic softening, a behavior consistent with other 9-10 wt.% Cr steels. Analysis of the microstructure and hysteresis loops further corroborate cyclic softening mechanisms typical of ferritic-martensitic steels. Overall, the fatigue performance of CPJ7 meets or exceeds that of P91 steel, demonstrating its potential for high-temperature structural applications.

9% Cr ferritic-martensitic steel↗

NASA NTRS1973

Methods for structural design at elevated temperatures

A procedure which can be used to design elevated temperature structures is discussed. The desired goal is to have the same confidence in the structural integrity at elevated temperature as the factor of safety gives on mechanical loads at room temperature. Methods of design and analysis for creep, creep rupture, and creep buckling are presented. Example problems are included to illustrate the analytical methods. Creep data for some common structural materials are presented. Appendix B is description, user's manual, and listing for the creep analysis program. The program predicts time to a given creep or to creep rupture for a material subjected to a specified stress-temperature-time spectrum. Fatigue at elevated temperature is discussed. Methods of analysis for high stress-low cycle fatigue, fatigue below the creep range, and fatigue in the creep range are included. The interaction of thermal fatigue and mechanical loads is considered, and a detailed approach to fatigue analysis is given for structures operating below the creep range.

Ellison, A. M.↗

NASA NTRS1985

Results of an interlaboratory fatigue test program conducted on alloy 800H at room and elevated temperatures

The experimental approach adopted for low cycle fatigue tests of alloy 800H involved the use of electrohydraulic test systems, hour glass geometry specimens, diametral extensometers, and axial strain computers. Attempts to identify possible problem areas were complicated by the lack of reliable data for the heat of Alloy 800H under investigation. The method adopted was to generate definitive test data in an Interlaboratory Fatigue Test Program. The laboratories participating in the program were Argonne National Laboratory, Battelle Columbus, Mar-Test, and NASA Lewis. Fatigue tests were conducted on both solid and turbular specimens at temperatures of 20, 593, and 760 C and strain ranges of 2.0, 1.0, and 0.5 percent. The subject test method can, under certain circumstances, produce fatigue data which are serious in error. This approach subsequently was abandoned at General Atomic Company in favor of parallel gage length specimens and axial extensiometers.

Ellis, J. R.↗

NASA NTRS1987

Results of an interlaboratory fatigue test program conducted on alloy 800H at room and elevated temperatures

Ellis, J. R.↗

NASA NTRS1989

Results of inphase axial-torsional fatigue experiments on 304 stainless steel

A series of axial-torsional, inphase, strain-controlled, low-cycle fatigue tests were performed at room temperature on tubular specimens of 304 stainless steel. The program was conducted in cooperation with the task group on multiaxial fatigue research of ASTM committee E-09. The objective was to quantify the variability in multiaxial test results among several laboratories. Only included is data which was generated at the NASA Lewis Research Center's High Temperature Fatigue and Structures Laboratory. The experimental equipment and procedures used are described. The tubular specimens were polished on the outer surface to aid in the use of a cellulose film surface replication technique for crack detection. However, cracking initiated predominantly on the internal surface for all specimens. Honing of the bore of the tubular specimens lessened but did not entirely eliminate this problem. The observed fatigue lives are compared with lives calculated from three multiaxial life models. Constants for the life prediction models were obtained from uniaxial and torsional tests performed on the same heat of material. The observed fatigue lives agreed with calculated lives to within a factor of two for all but one of the life prediction models.

Bonacuse, Peter J.↗

NASA NTRS1995

Predicting Fatigue Lives Under Complex Loading Conditions

Cyclic Damage Accumulation (CDA) computer program performs high-temperature, low-cycle-fatigue life prediction for materials analysis. Designed to account for effects on creep-fatigue life of complex loadings involving such factors as thermomechanical fatigue, hold periods, wave-shapes, mean stresses, multiaxiality, cumulative damage, coatings, and environmental attack. Several features practical for application to actual component analysis using modern finite-element or boundary-element methods. Although developed for use in predicting crack-initiation lifetimes of gas-turbine-engine materials, also applied to other materials as well. Written in FORTRAN 77.

Mcgaw, Michael A.↗

NASA NTRS1995

Elevated temperature axial and torsional fatigue behavior of Haynes 188

The results are reported for high-temperature axial and torsional low-cycle fatigue experiments performed at 760 C in air on thin-walled tubular specimens of Haynes 188, a wrought cobalt-based superalloy. Data are also presented for mean coefficient of thermal expansion, elastic modulus, and shear modulus at various temperatures from room to 1000 C, and monotonic and cyclic stress-strain curves in tension and in shear at 760 C. This data set is used to evaluate several multiaxial fatigue life models (most were originally developed for room temperature multiaxial life prediction) including von Mises equivalent strain range (ASME Boiler and Pressure Code), Manson-Halford, modified multiaxiality factor (proposed in this paper), modified Smith-Watson-Topper, and Fatemi-Socie-Kurath. At von Mises equivalent strain ranges (the torsional strain range divided by the square root of 3, taking the Poisson's ratio to be 0.5), torsionally strained specimens lasted, on average, factors of 2 to 3 times longer than axially strained specimens. The modified multiaxiality factor approach shows promise as a useful method of estimating torsional fatigue life from axial fatigue data at high temperatures. Several difficulties arose with the specimen geometry and extensometry used in these experiments. Cracking at extensometer probe indentations was a problem at smaller strain ranges. Also, as the largest axial and torsional strain range fatigue tests neared completion, a small amount of specimen buckling was observed.

Bonacuse, Peter J.↗

DOE OSTI2025

In situ Visible Light and Thermal Imaging Data from a Laser Powder Bed Fusion Additive Manufacturing Process Co-Registered to X-ray Computed Tomography and Fatigue Data

This dataset is comprised of in situ sensing data collected during a laser-based powder bed fusion additive manufacturing process, as well as rasterized scan path information, post-build X-ray computed tomography (XCT), and fatigue test results. A total of 64 cylinders, approximately 15 mm in diameter and 102 mm tall, were printed out of stainless steel 316H on a Colibrium Additive Concept Laser M2 Series 5 machine. Parameters known to produce dense material were used to construct 56 of these cylinders, while the remaining 8 cylinders were printed with relatively high energy density parameters prone to producing keyhole pores. In addition, two spatter generation blocks were constructed upstream of the 64 cylinders such that ejecta produced during the melting of the spatter generators were stochastically seeded onto the 64 cylinders. Based on previous experiments, these spatter particles were theorized to produce stochastic lack-of-fusion pores. During the construction of the build, high-resolution images of reflected light in the visible spectrum were captured both before and after recoating for each print layer. Additionally, temporally integrated thermal imaging in the near infrared spectrum produced integrated sum and max images on a layerwise basis. The multimodal in situ data has been co-registered to the build plate coordinate system, allowing for identification of process anomalies (e.g., spatter particles) apparent in the two sensors. Following construction of the build, the cylinders were subjected to XCT to identify internal flaws, and the resulting data have also been registered to the build plate coordinate system. Finally, 60 of the 64 cylinders were machined into fatigue coupons conforming to ASTM E466 and subsequently subjected to either high- or -low-cycle fatigue testing. The results of the fatigue tests have also been included in the dataset, and the XCT data corresponded to the approximate location of the gauge sections of the machine fatigue specimen geometry.

42 ENGINEERING↗